CN110903061A - Adhesive for building ceramic tiles - Google Patents
Adhesive for building ceramic tiles Download PDFInfo
- Publication number
- CN110903061A CN110903061A CN201911281794.2A CN201911281794A CN110903061A CN 110903061 A CN110903061 A CN 110903061A CN 201911281794 A CN201911281794 A CN 201911281794A CN 110903061 A CN110903061 A CN 110903061A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- waterproof
- ethanol
- antioxidant
- cement clinker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive for building tiles, which comprises the following raw material components: the cement paste comprises portland cement clinker, hydroxypropyl methyl cellulose, ethanol, an antioxidant, an organic silicon waterproof agent, paraffin and hydrogenated castor oil, wherein the portland cement clinker, the hydroxypropyl methyl cellulose, the ethanol, the antioxidant, the organic silicon waterproof agent, the paraffin and the hydrogenated castor oil are 55-67 parts by weight: 23-49: 10-26: 3-27: 5-39: 1-18: 1; the utility model discloses mainly be applicable to aspects such as bathroom ceramic tile bonding, the ratio through each component combines together and promotes each other on the comprehensive properties of construction, especially waterproof performance, and homodisperse, guarantees the homogeneity of waterproof adhesive quality, the interface bonding strength and the waterproof performance of better reinforcing bonding waterproofing agent and other materials to the demand that ceramic tile etc. were pasted in the different building occasions of adaptation improves bonding strength and waterproof performance greatly, saves time and cost for later maintenance.
Description
Technical Field
The invention belongs to the technical field of building materials, and particularly relates to an adhesive for building ceramic tiles.
Background
At present, most of tile bottom layer waterproof materials are used for toilet tile waterproof materials, the existing materials and technologies need to brush waterproof paint for the first time and lay waterproof coiled materials in the first step when water is prevented, the second time is carried out after the paint for the first time is dried, and then cement materials are smeared for bonding tiles after the water is prevented from being dried completely. There are the following problems: the construction process is complicated, the efficiency is low, and the cost is high.
In view of the above, the present invention is particularly proposed.
Disclosure of Invention
Aiming at the problems in the prior art, the invention aims to provide an adhesive for building tiles, which is mainly suitable for the aspects of bonding tiles in a toilet and the like, and is improved in a series of performances such as waterproofness, sealing property, elasticity, impact resistance and the like, so that the building decoration quality can be improved, the attractiveness and comfort are improved, the construction process can be improved, the building construction efficiency and quality can be improved, and the like.
In order to achieve the purpose, the invention provides an adhesive for building tiles, which comprises the following raw material components: the cement clinker aggregate is 55-67 parts by weight of Portland cement clinker, hydroxypropyl methyl cellulose, ethanol, an antioxidant, an organic silicon waterproof agent, paraffin and hydrogenated castor oil: 23-49: 10-26: 3-27: 5-39: 1-18: 1.
preferably, the Portland cement clinker, the hydroxypropyl methyl cellulose, the ethanol, the antioxidant, the organosilicon waterproofing agent, the paraffin and the hydrogenated castor oil are 55: 49: 10: 27: 5:18: 1;
preferably, the Portland cement clinker, the hydroxypropyl methyl cellulose, the ethanol, the antioxidant, the organosilicon waterproofing agent, the paraffin and the hydrogenated castor oil are 67 parts by weight: 23: 26: 3: 39: 1: 1;
preferably, the Portland cement clinker, the hydroxypropyl methyl cellulose, the ethanol, the antioxidant, the organosilicon waterproofing agent, the paraffin and the hydrogenated castor oil are 61: 36: 18: 15: 22: 9: 1;
preferably, the antioxidant comprises 1, 3-tris (ethylmethyl-4-hydroxy-5-tert-butylphenyl) butane, DLTP (dilauryl sulfodipropionate) and a 1:1 composition of 1, 3-tris (ethylmethyl-4-hydroxy-5-tert-butylphenyl) butane and DLTP (dilauryl sulfodipropionate) in parts by weight;
preferably, the ethanol concentration is not less than 98%;
preferably, the waterproof adhesive is coated to a thickness of 0.3cm to 1 cm.
The adhesive for the building ceramic tiles provided by the invention has the following beneficial effects:
the ratio of each component of injecing according to this application combines together and promotes each other on building construction's comprehensive properties, especially waterproof performance, and the homodisperse, guarantee the homogeneity of bonding waterproofing agent quality, effectively avoid among the prior art problem that the bathroom pastes that ceramic tile waterproofing measure is complicated and water-proof effects is low, the interface bonding strength and the waterproof performance of better reinforcing bonding waterproofing agent and other materials, with the demand that the ceramic tile etc. were pasted in the different building occasions of adaptation, bond strength and waterproof performance are greatly improved, save time and cost for later maintenance, also overcome the technical problem that the waterproofing agent that needs additionally to add the poison in the use can reach waterproof effect simultaneously.
Detailed Description
The present invention will be further described with reference to specific examples to assist understanding of the invention.
The invention provides an adhesive for building ceramic tiles, which comprises the following raw material components: the cement paste comprises portland cement clinker, hydroxypropyl methyl cellulose, ethanol, an antioxidant, an organic silicon waterproof agent, paraffin and hydrogenated castor oil, wherein the portland cement clinker, the hydroxypropyl methyl cellulose, the ethanol, the antioxidant, the organic silicon waterproof agent, the paraffin and the hydrogenated castor oil are 55-67 parts by weight: 23-49: 10-26: 3-27: 5-39: 1-18: 1. wherein, the antioxidant comprises 1, 3-tri (ethylmethyl-4-hydroxy-5-tert-butylphenyl) butane, DLTP (dilauryl sulfodipropionate) and a composition of 1, 3-tri (ethylmethyl-4-hydroxy-5-tert-butylphenyl) butane and DLTP (dilauryl sulfodipropionate) in a weight ratio of 1:1, and the ethanol concentration is not less than 98%. The coating thickness of the waterproof adhesive is 0.3cm-1 cm.
Example 1: the cement clinker aggregate is 55 parts by weight of Portland cement clinker aggregate, hydroxypropyl methyl cellulose, ethanol, an antioxidant, an organic silicon waterproof agent, paraffin and hydrogenated castor oil: 49: 10: 27: 5:18: 1, and uniformly mixing and stirring to obtain the waterproof adhesive, wherein the antioxidant comprises 1:1 composition of 1, 3-tri (ethylmethyl-4-hydroxy-5-tert-butylphenyl) butane and DLTP (dilauryl sulfodipropionate) in parts by weight.
Coating 1cm on a tile with the square meter of 1m to prepare a sample for a bonding strength test, naturally drying the sample for 6h to test the bonding strength to be 2.4Mpa, soaking the sample in water for 48 h to ensure that the bonding layer does not fall off, bubble or crack, and testing the bonding strength to be 1.2Mpa after soaking the sample in water. The waterproof adhesive is firmly adhered to the ceramic tile, is quick in drying time, does not bulge after being soaked in water for a long time, and has high adhesion strength and high waterproofness.
Example 2: the cement mortar comprises portland cement clinker, hydroxypropyl methyl cellulose, ethanol, DLTP (dilauryl sulfodipropionate), an organic silicon waterproof agent, paraffin and hydrogenated castor oil, wherein the weight parts of the organic silicon waterproof agent, the paraffin and the hydrogenated castor oil are 67: 23: 26: 3: 39: 1:1, uniformly mixing and stirring to obtain the waterproof adhesive.
Coating a tile of 1 square meter with 0.7cm to prepare a sample for bonding strength test, naturally drying the sample for 5.5h to test the bonding strength to be 2.0Mpa, soaking in water for 48 h to ensure that the bonding layer does not fall off, bubble or crack, and testing the bonding strength to be 1.2Mpa after soaking in water. The waterproof adhesive is firmly adhered to the ceramic tile, is quick in drying time, does not bulge after being soaked in water for a long time, and has high adhesion strength and high waterproofness.
Example 3: the cement mortar comprises portland cement clinker, hydroxypropyl methyl cellulose, ethanol, 1, 3-tri (ethyl methyl-4 hydroxy-5 tert-butyl phenyl) butane, an organic silicon waterproof agent, paraffin and hydrogenated castor oil, wherein the weight parts of the raw materials are 61: 36: 18: 15: 22: 9: 1, uniformly mixing and stirring to obtain the waterproof adhesive.
Coating a tile of 1 square meter with 0.5cm to prepare a sample for bonding strength test, naturally drying the sample for 4h to test the bonding strength to be 1.8Mpa, soaking in water for 48 h to ensure that the bonding layer does not fall off, bubble or crack, and testing the bonding strength to be 1Mpa after soaking in water. The waterproof adhesive is firmly adhered to the ceramic tile, is quick in drying time, does not bulge after being soaked in water for a long time, and has high adhesion strength and high waterproofness.
The result shows that the proportions of the components defined in the application are combined to promote each other on the waterproof performance of building construction, so that the interface bonding strength and the waterproof performance of the waterproof adhesive and other materials can be better enhanced, the requirements of different building occasions are met, the bonding strength and the waterproof performance are greatly improved, and the technical problems that hollowing and dropping caused by low bonding strength exist in the using process and a toxic waterproof agent needs to be additionally added to achieve the waterproof effect are solved. It can be seen from the data of the above examples that the synergistic effect of the components can greatly improve the comprehensive performance of the waterproof adhesive and improve the adhesive strength and waterproof performance of the waterproof adhesive.
The inventive concept is explained in detail herein using specific examples, which are given only to aid in understanding the core concepts of the invention. It should be understood that any obvious modifications, equivalents and other improvements made by those skilled in the art without departing from the spirit of the present invention are included in the scope of the present invention.
Claims (7)
1. The adhesive for the building tiles is characterized by comprising the following raw material components: the cement clinker aggregate is 55-67 parts by weight of Portland cement clinker, hydroxypropyl methyl cellulose, ethanol, an antioxidant, an organic silicon waterproof agent, paraffin and hydrogenated castor oil: 23-49: 10-26: 3-27: 5-39: 1-18: 1.
2. an adhesive for construction tiles according to claim 1, wherein the portland cement clinker, hydroxypropyl methylcellulose, ethanol, an antioxidant, a silicone-based waterproofing agent, paraffin wax, and hydrogenated castor oil are 55: 49: 10: 27: 5:18: 1.
3. an adhesive for construction ceramic tiles as claimed in claim 1, wherein the portland cement clinker, hydroxypropyl methylcellulose, ethanol, antioxidant, silicone-based waterproofing agent, paraffin wax and hydrogenated castor oil are 67: 23: 26: 3: 39: 1: 1.
4. an adhesive for construction tiles according to claim 1, wherein the portland cement clinker, hydroxypropyl methylcellulose, ethanol, an antioxidant, a silicone-based waterproofing agent, paraffin wax and hydrogenated castor oil are 61: 36: 18: 15: 22: 9: 1.
5. an adhesive for construction tiles according to any one of claims 1 to 4, wherein the antioxidant comprises 1, 3-tris (ethylmethyl-4 hydroxy-5 t-butylphenyl) butane, DLTP (dilauryl sulfodipropionate) and a combination of 1, 3-tris (ethylmethyl-4 hydroxy-5 t-butylphenyl) butane and DLTP (dilauryl sulfodipropionate) in a weight ratio of 1: 1.
6. An adhesive for construction tiles according to any one of claims 1 to 4, wherein the concentration of ethanol is not less than 98%.
7. An adhesive for construction tiles according to any one of claims 1 to 4, wherein the waterproof adhesive is applied to a thickness of 0.3cm to 1 cm.