CN108003734A - A kind of water-based inner-outer wall anti-cracking waterproof primary coat and preparation method - Google Patents
A kind of water-based inner-outer wall anti-cracking waterproof primary coat and preparation method Download PDFInfo
- Publication number
- CN108003734A CN108003734A CN201711375165.7A CN201711375165A CN108003734A CN 108003734 A CN108003734 A CN 108003734A CN 201711375165 A CN201711375165 A CN 201711375165A CN 108003734 A CN108003734 A CN 108003734A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- paint waste
- primary coat
- water paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to build environment-friendly materials technical field, a kind of water-based inner-outer wall anti-cracking waterproof primary coat and preparation method thereof is disclosed, component is made of water paint waste water, industrial bactericide, organosilicon-modified styrene-acrylic supernatant liquid, water, water paint waste water, film forming agent, defoamer, amine neutralizer, preservative, thickener, grey rock powder, water paint waste residue, quartz sand, resin fibre A and resin fibre by weight.Grey rock powder is added in the present invention, mainly increase dry film finished product pliability and adhesive force, additive amount is less than 20% or so quartz sand, so not only increases the effect of subsequent construction, (batch Puttying, paste ceramic tile) plays interfacial effect, and adds and increase to ground grasping force；The resin fibre of 0.6 0.8% (weight ratio) is added in the present invention, master is to ensure film integrity after drying, increases effect of prestressed.
Description
Technical field
The invention belongs to build environment-friendly materials technical field, more particularly to a kind of water-based inner-outer wall anti-cracking waterproof primary coat and system
Preparation Method.
Background technology
As skyscraper is more and more, high-rise wall is more and more using air brick, hollow brick ratio, and exterior wall cement is husky
It is serious all the more to starch cracking problem, in order to overcome disadvantages mentioned above, so as to cause exterior coating, external wall tile to cause coating due to splitting
Cracking, ceramic tile leak cause the problems such as coming off.
As hollow brick, air brick are using more and more, the inner-outer wall mortar cracking more aobvious protrusion of problem, existing exterior wall prevents
The general coloured silk bouncing putty of cracking, but its water resistance, water proofing property are poor.Patch grid cloth prevents cracking work progress from need to increase manually
Cost, the present invention fully overcome above two method drawback.
Product using the present invention, i.e., effect waterproof and that grid cloth can be reached, and save labour cost.
In conclusion problem existing in the prior art is：
The waste water to aqueous industrial coating generation, waste residue do not recycle for existing inner-outer wall anti-cracking waterproof primary coat；
Inner-outer wall wall crazing cannot be effectively solved, causes the crack of wall coating, and has the problem of water-impervious, leak；It is and existing
Inner-outer wall anti-cracking waterproof primary coat manufacture is of high cost.
The content of the invention
In view of the problems of the existing technology, the present invention provides a kind of water-based inner-outer wall anti-cracking waterproof primary coat and preparation side
Method.
The present invention is achieved in that a kind of water-based inner-outer wall anti-cracking waterproof primary coat, the water-based inner-outer wall anti-cracking waterproof
Primary coat component by weight by 3 parts -5 parts of water paint waste water, 0.1 part of industrial bactericide, 35 parts of organosilicon-modified styrene-acrylic supernatant liquid -
38 parts, 7 parts -8 parts of water, 3 parts -5 parts of water paint waste water, 1.5 parts -1.8 parts of film forming agent, 0.2 part -0.3 part of defoamer, amine neutralize
0.15 part -0.20 part of agent, 0.15 part of preservative, 1 part of thickener, grey 20 parts -22 parts of rock powder, 5 parts -7 parts of water paint waste residue, stone
English is 18 parts -20 parts husky, 0.2 part of -0.3 part of composition of 0.45 part -0.5 part of resin fibre A and resin fibre B.
The water paint waste water is by pretreatment；The water paint waste residue is by pretreatment.
Another object of the present invention is to provide a kind of preparation method of water-based inner-outer wall anti-cracking waterproof primary coat, including：
Water paint waste water adds aqueous microbiocidal, and water paint waste water is anti-by weight the sterilization of 0.1-0.15% coating is added
Rotten agent by mixer high speed dispersor high speed dispersion 30min, it is scattered after test mixing liquid corruption and mildew micro-organism
Least concentration；
By weight 0.1-0.15% coating sterilization antiseptics are added, addition 3-4% coating disperses water paint waste residue, high
Speed is dispersed into slurry, and slurry concentration is in 85-90kv, and fineness is in below 45um；
600-800 revs/min of mixer speed is controlled, is sufficiently stirred under this rotating speed；Treated after being stirred by mixer
With；
It is stand-by that water paint waste residue adds aqueous microbiocidal, dispersant by mixer to stir into slurry；
Water paint waste water add mixture in tap water, silicone modified styrene-acrylate emulsion, film forming agent, paint antifoaming agent, amine,
Preservative, after adding and stir evenly one by one plus thickener is sufficiently stirred thickening again；Winner's liquid；
Grey rock powder is added one by one to main fluid viscosity and adds water paint waste residue after stirring evenly and quartz sand is abundant again
Stirring, it is stand-by；
After above-mentioned material is sufficiently stirred, the lower addition resin fibre A of low and middle-grade 600-800 turns/min stirrings and resin fibre
B is stirred, packaging.
Further, water paint waste water adds aqueous microbiocidal, by stand-by after mixer stirring 30min.
Further, after addition thickener is sufficiently stirred thickening again, main fluid viscosity 105KV.
Another object of the present invention is to provide a kind of building for being painted with above-mentioned water-based inner-outer wall anti-cracking waterproof primary coat
Groups of building.
Advantages of the present invention and good effect are：
The present invention solves the pollution problem of waste water, waste sludge discharge that aqueous industrial coating produces；The present invention utilizes water-based painting
The assorted industrial wastewater of material, waste residue play waste utilization；The present invention solves inner-outer wall wall crazing, causes splitting for wall coating
Seam, and play the role of water-impervious, leak；Final products construction technology of the present invention is simple, can roller coating, batch painting；Can save manually into
This.
Traditional elastic priming paint is to use elastomeric propylene acid resin, because its resin particle diameter is thicker, to cement matrix grasping force
Not as styrene-acrylic emulsion, and lotion amount is less than 45%, and epistasis is bad, of high cost, and the present invention connects skill silane using styrene-acrylic emulsion,
Greatly increase to ground (cement mortar) grasping force, and add quantity and also lacked 10% or so, therefore reduce cost.
Grey rock powder is added in the present invention, mainly increases dry film finished product pliability and adhesive force, additive amount is left less than 20%
Right quartz sand, so not only increases the effect of subsequent construction, and (batch Puttying, paste ceramic tile) plays interfacial effect, and adds and increase
To ground grasping force.
The resin fibre of 0.6-0.8% (weight ratio) is added in the present invention, master is to ensure film integrity after drying, increase
Effect of prestressed.
The present invention replaces conventional mesh cloth, possesses and saves labour cost advantage, one to two road working procedure is saved, so as to carry
High efficiency and saving are artificial.
The present invention replaces traditional elastic putty, and equal film thickness drying time speeds when small (speed 12 or so)；Equally
Improve adhesive force and water resistance of the paint film to base material.
The present invention uses silicone modified styrene-acrylate emulsion, and not only its water resistance greatly improves, but also to the adhesive force of base material
Also it is corresponding to improve, coordinate a certain proportion of quartz sand to improve grasping force of the coating to base material again, so as to improve rear road construction
The grasping force (batch Puttying or patch ceramic tile etc.) of program has good grasping force.
The present invention uses organic fiber plurality of specifications, and to improve paint film tension temperature, satisfaction prevents from drawing because mortar is cracked
Infiltration is played to come off.
The present invention is using part coating waste-water and precipitation waste residue, the industrial waste residue disposal of the most water paint enterprise of solution
The problem of.
Brief description of the drawings
Fig. 1 is the preparation method flow chart of water-based inner-outer wall anti-cracking waterproof primary coat provided in an embodiment of the present invention.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Water paint colors industrial wastewater, waste residue are adjusted to water-based inner-outer wall anti-cracking waterproof bottom by the present invention by formula
Apply.
Below in conjunction with the accompanying drawings and specific embodiment is further described the application principle of the present invention.
The present invention water-based inner-outer wall anti-cracking waterproof primary coat have environmental protection, to aqueous industrial coating waste water, waste residue it is effective
Utilize, paint film quick-drying, waterproof, cracking resistance.
With reference to specific embodiment, the invention will be further described.
Water-based inner-outer wall anti-cracking waterproof primary coat component provided in an embodiment of the present invention is by weight by water paint waste water 3
- 5 parts of part, 0.1 part of industrial bactericide, 35 parts -38 parts of organosilicon-modified styrene-acrylic supernatant liquid, 7 parts -8 parts of water, water paint waste water (warp
After crossing pretreatment) 3 parts -5 parts, 1.5 parts -1.8 parts of film forming agent, 0.2 part -0.3 part of defoamer, 0.15 part -0.20 part of amine neutralizer,
0.15 part of preservative, 1 part of thickener, grey 20 parts -22 parts of rock powder (clay), 5 part -7 of water paint waste residue (after pretreatment)
0.2 part of part, 18 parts -20 parts of quartz sand, 0.45 part -0.5 part of resin fibre A, resin fibre B -0.3 part of composition.
As shown in Figure 1, the preparation method of water-based inner-outer wall anti-cracking waterproof primary coat provided in an embodiment of the present invention, including：
S101：Water paint waste water adds aqueous microbiocidal, by stand-by after mixer stirring 30min；
S102：It is stand-by that water paint waste residue (powder) plus aqueous microbiocidal, dispersant by mixer stir into slurry；
S103：Water paint waste water is added in tap water, silicone modified styrene-acrylate emulsion, film forming agent, paint antifoaming agent, amine
Mixture, preservative, after adding and stir evenly one by one plus thickener is sufficiently stirred thickening again, by testing main fluid viscosity 105KV
Viscosity；
S104：Add grey rock powder one by one after main fluid viscosity reaches and add water paint waste residue and quartz after stirring evenly
Sand is sufficiently stirred again, stand-by；
S105：After above-mentioned material is sufficiently stirred, the lower addition resin fibre A of middle-grade stirring resin fibre B stirrings, packaging.
Traditional elastic priming paint is to use elastomeric propylene acid resin, because its resin particle diameter is thicker, to cement matrix grasping force
Not as styrene-acrylic emulsion, and lotion amount is less than 45%, and epistasis is bad, of high cost, and the present invention connects skill silane using styrene-acrylic emulsion,
Greatly increase to ground (cement mortar) grasping force, and add quantity and also lacked 10% or so, therefore reduce cost.
Grey rock powder is added in the present invention, mainly increases dry film finished product pliability and adhesive force, additive amount is left less than 20%
Right quartz sand, so not only increases the effect of subsequent construction, and (batch Puttying, paste ceramic tile) plays interfacial effect, and adds and increase
To ground grasping force.
The resin fibre of 0.6-0.8% (weight ratio) is added in the present invention, master is to ensure film integrity after drying, increase
Effect of prestressed.
With reference to specific embodiment, the invention will be further described.
Embodiment 1
Water-based inner-outer wall anti-cracking waterproof primary coat component provided in an embodiment of the present invention is by weight by water paint waste water 3
Part, 0.1 part of industrial bactericide, 35 parts of organosilicon-modified styrene-acrylic supernatant liquid, 7 parts of water, water paint waste water (after pretreatment) 3
Part, 1.5 parts of film forming agent, 0.2 part of defoamer, 0.15 part of amine neutralizer, 0.15 part of preservative, 1 part of thickener, grey rock powder (clay)
20 parts, 5 parts of water paint waste residue (after pretreatment), 18 parts of quartz sand, 0.45 part of resin fibre A, resin fibre B 0.2
Part composition
Embodiment 2
Water-based inner-outer wall anti-cracking waterproof primary coat component provided in an embodiment of the present invention is by weight by water paint waste water 5
Part, 0.1 part of industrial bactericide, 38 parts of organosilicon-modified styrene-acrylic supernatant liquid, 8 parts of water, water paint waste water (after pretreatment) 5
Part, 1.8 parts of film forming agent, 0.3 part of defoamer, 0.20 part of amine neutralizer, 0.15 part of preservative, 1 part of thickener, grey rock powder (clay)
22 parts, 7 parts of water paint waste residue (after pretreatment), 20 parts of quartz sand, 0.5 part of resin fibre A, 0.3 part of resin fibre B
Composition.
Embodiment 3
Water-based inner-outer wall anti-cracking waterproof primary coat component provided in an embodiment of the present invention is by weight by water paint waste water 4
Part, 0.1 part of industrial bactericide, 36.5 parts of organosilicon-modified styrene-acrylic supernatant liquid, 7.5 parts of water, water paint waste water are (by pretreatment
4 parts afterwards), 1.65 parts of film forming agent, 0.25 part of defoamer, 0.175 part of amine neutralizer, 0.15 part of preservative, 1 part of thickener, limestone
21 parts of powder (clay), 6 parts of water paint waste residue (after pretreatment), 19 parts of quartz sand, 0.475 part of resin fibre A, resin
0.25 part of composition of fiber B.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of water-based inner-outer wall anti-cracking waterproof primary coat, it is characterised in that the water-based inner-outer wall anti-cracking waterproof primary coat component is pressed
Parts by weight are by 3 parts -5 parts of water paint waste water, 0.1 part of industrial bactericide, 35 parts -38 parts of organosilicon-modified styrene-acrylic supernatant liquid, water 7
- 8 parts of part, 3 parts -5 parts of water paint waste water, 1.5 parts -1.8 parts of film forming agent, 0.2 part -0.3 part of defoamer, amine neutralizer 0.15
- 0.20 part of part, 0.15 part of preservative, 1 part of thickener, grey 20 parts -22 parts of rock powder, 5 parts -7 parts of water paint waste residue, quartz sand 18
0.2 part of -20 parts of part, 0.45 part -0.5 part of resin fibre A and resin fibre B -0.3 part of composition.
2. water-based inner-outer wall anti-cracking waterproof primary coat as claimed in claim 1, it is characterised in that the water paint waste water passes through
Pretreatment；The water paint waste residue is by pretreatment.
3. a kind of preparation method of water-based inner-outer wall anti-cracking waterproof primary coat as claimed in claim 1, it is characterised in that described water-based
The preparation method of inner-outer wall anti-cracking waterproof primary coat includes：
Water paint waste water adds aqueous microbiocidal, and water paint waste water is by weight addition 0.1-0.15% coating sterilization antiseptics
By mixer high speed dispersor high speed dispersion 30min, it is scattered after test mixing liquid corruption and mildew micro-organism it is minimum
Concentration；
Water paint waste residue disperses, divides at a high speed by weight 0.1-0.15% coating sterilization antiseptics, addition 3-4% coating is added
Dissipate into slurry, slurry concentration is in 85-90kv, and fineness is in below 45um；
600-800 revs/min of mixer speed is controlled, is sufficiently stirred under this rotating speed；It is stand-by after being stirred by mixer；
It is stand-by that water paint waste residue adds aqueous microbiocidal, dispersant by mixer to stir into slurry；
Water paint waste water is added mixture, anti-corrosion in tap water, silicone modified styrene-acrylate emulsion, film forming agent, paint antifoaming agent, amine
Agent, after adding and stir evenly one by one plus thickener is sufficiently stirred thickening again；Winner's liquid；
Grey rock powder is added one by one to main fluid viscosity and adds water paint waste residue after stirring evenly and quartz sand is sufficiently stirred again,
It is stand-by；
After above-mentioned material is sufficiently stirred, the lower addition resin fibre A and resin fibre B of low and middle-grade 600-800 turns/min stirrings is stirred
Mix, pack.
4. the preparation method of water-based inner-outer wall anti-cracking waterproof primary coat as claimed in claim 3, it is characterised in that water paint gives up
Water adds aqueous microbiocidal, by stand-by after mixer stirring 30min.
5. the preparation method of water-based inner-outer wall anti-cracking waterproof primary coat as claimed in claim 3, it is characterised in that addition thickener
After being sufficiently stirred thickening again, main fluid viscosity 105KV.
A kind of 6. building constructions group for being painted with the water-based inner-outer wall anti-cracking waterproof primary coat described in claim 1.