CN110885239A - Preparation method of high-purity fused quartz powder - Google Patents
Preparation method of high-purity fused quartz powder Download PDFInfo
- Publication number
- CN110885239A CN110885239A CN201911155604.2A CN201911155604A CN110885239A CN 110885239 A CN110885239 A CN 110885239A CN 201911155604 A CN201911155604 A CN 201911155604A CN 110885239 A CN110885239 A CN 110885239A
- Authority
- CN
- China
- Prior art keywords
- quartz
- particles
- magnetic separation
- pickling
- fused quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of novel refractory materials, and discloses a preparation method of high-purity fused quartz powder, which comprises the following steps: crushing; scrubbing with a rod and rubbing, washing with water, and desliming in stages; repeating the magnetic separation; flotation; circularly pickling; drying; smelting; crushing the mixture into fused quartz sand, and performing ball milling and grading on the fused quartz sand to obtain low-iron fused quartz powder. The invention adopts circular acid washing, selects the optimal acid washing condition to remove metal impurities and has good purification effect; the magnetic separation method is used for carrying out repeated magnetic separation, and the magnetic separation effect is good; an internal heating type quartz glass continuous electric melting furnace is adopted, protective gas is not needed, the cost is reduced, and the method is environment-friendly; solves the problems of equipment abrasion and iron pollution of products, and avoids secondary pollution to high-purity quartz powder. The content of SiO2 in the obtained fused quartz powder is 99.999%, and the fused quartz powder has high purity and good quality.
Description
Technical Field
The invention relates to the technical field of novel refractory materials, in particular to a preparation method of high-purity fused quartz powder.
Background
The spherical fused quartz powder is prepared by melting powder formed by processing high-quality natural quartz through a unique treatment process at a temperature higher than 1760 ℃, and then rapidly cooling, wherein the spherical fused quartz powder is quartz glass beads with a certain granularity, crystalline silicon dioxide is converted into an amorphous glass melt in the process, and the molecular structure arrangement is converted into disordered arrangement from ordered arrangement. It is gradually recognized and applied because of its unique properties of smooth surface, large specific surface area, large hardness, stable chemical properties, small expansion coefficient, good rolling property, excellent mechanical properties, etc. The method is widely applied to large-scale integrated circuits, solar polycrystalline silicon ingots, precision casting, optical fibers, lasers, aerospace, military and other aspects. At present, high-quality high-purity vein quartz is mainly selected as a material for preparing high-purity fused quartz powder in China for processing, the process is simple, the content of SiO2 in the fused quartz powder produced in large scale can not break through 99.99 percent all the time, the added value of the product is low, the energy consumption is high, the environmental protection problem is prominent, and the resource waste is serious. The high-efficiency low-cost quartz purification processing technology is a development bottleneck of the domestic quartz processing industry, the demand of the fused quartz ceramic crucible is increased increasingly along with the development of the solar energy industry, the fused quartz is used as a key raw material, the quality requirement is higher and higher, and the breakthrough of the technology and the industrialization are not slow.
Disclosure of Invention
The purpose of the invention is as follows: the invention discloses a preparation method of high-purity fused quartz powder.
The technical scheme is as follows: in order to achieve the above object, the present invention discloses a method for preparing high purity fused silica powder, comprising the steps of:
(1) crushing: crushing the massive quartz stone into quartz sand particles of 10-18 meshes, and picking to remove obvious impurities and foreign matters such as feldspar and mica;
(2) rod rubbing, washing and graded desliming: scrubbing impurities such as soil on the outer surface of quartz sand particles by a rod mill washing machine, and carrying out classification and desliming on a hydraulic classifier;
(3) and (3) repeating magnetic separation: repeatedly performing magnetic separation on the cleaned quartz sand particles by using various magnetic separators for multiple times, specifically, performing repeated magnetic separation on the cleaned quartz sand particles by using the various magnetic separators for multiple times under the field intensity of 1000-20000 gausses, then feeding the quartz sand particles into a wet mill to be milled until the quartz sand particles pass through a 100-mesh sieve to obtain quartz particles with the particle size of less than 0.15mm, and finally feeding the quartz sand particles into a medium magnetic separator to perform magnetic separation under the field intensity of 5000-8000 gausses; the magnetic separation is carried out repeatedly under high and low field intensity by combining a strong, medium and weak magnetic separator, so that the magnetic separation effect is good, and magnetic impurities are removed preliminarily and efficiently;
(4) flotation: and adding water into the quartz particles subjected to magnetic separation to adjust the concentration of the mortar to 30% -35%, and feeding the mixture into a flotation machine for flotation. The flotation solution in the flotation machine comprises mixed solution of sodium dodecyl benzene sulfonate, dodecylamine and dodecyl propyl ether amine, dodecylamine acetate, sulfuric acid with the concentration of 10-15%, kerosene, terpineol and water; the weight portions are as follows: 30-36 parts of sodium dodecyl benzene sulfonate, 30-36 parts of dodecylamine, 10-15 parts of a mixed solution of dodecylpropyl ether amine, 10-12 parts of dodecylamine acetate, 3 parts of sulfuric acid with the concentration of 10-15%, 3-9 parts of kerosene, 3-9 parts of terpineol and 30-60 parts of water.
(5) And (3) cyclic pickling: sending the particles subjected to flotation into an ultrasonic pickling tank for ultrasonic pickling, and ultrasonically cleaning the particles subjected to pickling for 3-5 times; the pickling time is 1 hour, the pickling temperature is 50-60 ℃, and the ultrasonic frequency is 40-50 Hz. The pickling tank is pickling solution containing hydrochloric acid, hydrofluoric acid and nitric acid; the hydrochloric acid concentration of the pickling solution is 10% -15%, the hydrofluoric acid concentration is less than 10%, and the nitric acid concentration is 6% -15%; the method adopts circular pickling, selects the optimal pickling conditions (acid concentration, acid consumption, pickling time, temperature and the like), effectively removes metal impurities and has good purification effect;
(6) drying: putting the washed quartz particles into an oven for drying at the drying temperature of 120-200 ℃ for 2-4 h, and cooling to room temperature after taking out;
(7) smelting: delivering the dried quartz particles into an internal heating type quartz glass continuous electric melting furnace for smelting at 1780-1850 ℃ for 11-12 hours, and taking out the quartz particles after smelting and rapidly cooling the quartz particles to room temperature; the internal heating type quartz glass continuous electric melting furnace is adopted, the protective gas is not needed, the process of using the protective gas in the calcining process is reduced, and the cost and the energy consumption are greatly reduced.
(8) Further crushing the fused quartz sand into fused quartz sand with the particle diameter of less than 2mm by using an impact crusher, and then sending the fused quartz sand into a production line of a ball mill matched with an airflow classifier for ball milling and classification to obtain high-purity fused quartz powder, wherein the content of SiO2 can reach 99.999%.
Further, the ball milling time in the step (8) is 8-10h, and the ball milling medium is zirconia balls or alumina balls; and (3) adding a grinding-aid dispersant accounting for 0.3-1.2% of the weight of the quartz powder raw material in the ball milling process, wherein the grinding-aid dispersant is a silane coupling agent or triacetin.
Further, step (8) the welt of ball mill adopts quartz material or aluminium oxide ceramic material, the inside aluminium oxide ceramic wafer that adopts of system of air classifier carries out ultrapure wear-resisting protection, the impeller blade of air classifier adopts polymer wear-resisting material, has effectively solved equipment wearing and tearing and product iron pollution problem.
The technical scheme shows that the invention has the following beneficial effects: (1) the preparation method of the high-purity fused quartz powder adopts circular pickling, and selects the optimal pickling conditions: the concentration of acid, the dosage of acid, the pickling time, the temperature and the like, effectively removes metal impurities and has good purification effect; (2) the preparation method of the high-purity fused quartz powder adopts the combination of the strong, medium and low magnetic separators under high and low field strengths to carry out repeated magnetic separation, has good magnetic separation effect, and removes magnetic impurities preliminarily and efficiently; (3) the preparation method of the high-purity fused quartz powder has the advantages that the flotation solution adopted by the preparation method is reasonable in proportion, the feldspar is preferentially floated, the separation of the feldspar and the feldspar is realized, and the anion collecting agent under the acidic condition is adopted, so that a good effect is obtained for separating mica and quartz; (4) the invention adopts the internal heating type quartz glass continuous electric melting furnace, does not need protective gas, reduces the process of using the protective gas in the calcining process, greatly reduces the cost and the energy consumption, and is environment-friendly; (5) the lining plate of the ball mill in the ball milling process is made of quartz or alumina ceramic, the alumina ceramic plate is adopted in the subsequent grading airflow grader system to carry out ultra-pure wear-resistant protection, and the impeller of the airflow grader is made of high-molecular wear-resistant material, so that the pollution to high-purity quartz powder is reduced in all aspects, and the problems of equipment abrasion and product iron pollution are effectively solved.
Detailed Description
The invention will be further elucidated by means of several specific examples, which are intended to be illustrative only and not limiting.
Example 1
A preparation method of high-purity fused quartz powder comprises the following steps:
(1) crushing: crushing the massive quartz stone into quartz sand particles of 10-18 meshes, and picking to remove obvious impurities and foreign matters such as feldspar and mica;
(2) rod rubbing, washing and graded desliming: scrubbing impurities such as soil on the outer surface of quartz sand particles by a rod mill washing machine, and carrying out classification and desliming on a hydraulic classifier;
(3) and (3) repeating magnetic separation: firstly, carrying out magnetic separation by using a wet type permanent magnet drum magnetic separator under the field intensity of 15000 gauss, then sending the magnetic separation into a wet type grinding machine to grind until the magnetic separation passes through a 100-mesh sieve to obtain quartz particles with the particle size of less than 0.15mm, and carrying out magnetic separation again under the field intensity of 10000 gauss; finally, the magnetic particles are sent into a middle magnetic separator for magnetic separation under the field intensity of 6000 gausses;
(4) flotation: and adding water into the quartz particles subjected to magnetic separation to adjust the concentration of the mortar to 30% -35%, and feeding the mixture into a flotation machine for flotation. The flotation solution in the flotation machine comprises mixed solution of sodium dodecyl benzene sulfonate, dodecylamine and dodecyl propyl ether amine, dodecylamine acetate, sulfuric acid with the concentration of 10-15%, kerosene, terpineol and water; the weight portions are as follows: 30 parts of sodium dodecyl benzene sulfonate, 36 parts of dodecylamine, 13 parts of a mixed solution of dodecylpropyl ether amine, 11 parts of dodecylamine acetate, 10-15% sulfuric acid, 9 parts of kerosene and 3 parts of terpineol.
(5) And (3) cyclic pickling: sending the particles subjected to flotation into an ultrasonic pickling tank for ultrasonic pickling, and ultrasonically cleaning the particles subjected to pickling for 3 times; the pickling tank is pickling solution containing hydrochloric acid, hydrofluoric acid and nitric acid; the hydrochloric acid concentration of the pickling solution is 10% -15%, the hydrofluoric acid concentration is less than 10%, and the nitric acid concentration is 6% -15%; the pickling time is 1 hour, the pickling temperature is 50-60 ℃, and the ultrasonic frequency is 40 Hz.
(6) Drying: putting the washed quartz particles into an oven for drying at 120 ℃ for 4 hours, and taking out and cooling to room temperature;
(7) smelting: feeding the dried quartz particles into an internal heating type quartz glass continuous electric melting furnace for melting, wherein the melting temperature is 1780-1850 ℃, the melting time is 11 hours, and taking out the quartz particles after melting and rapidly cooling the quartz particles to room temperature;
(8) further crushing the fused quartz sand into fused quartz sand with the particle diameter less than 2mm by adopting an impact crusher, and then sending the fused quartz sand into a production line of a ball mill matched with an airflow classifier for ball milling and classification to obtain high-purity fused quartz powder. Ball milling is carried out for 10 hours, and a ball milling medium is zirconia balls or alumina balls; and (3) adding a grinding-aid dispersant accounting for 0.3 percent of the weight of the quartz powder raw material in the ball milling process, wherein the grinding-aid dispersant is triacetin. The welt of ball mill adopts the quartz material, the inside aluminium oxide potsherd that adopts of system of air classifier carries out ultrapure wear-resisting protection, the impeller blade of air classifier adopts the wear-resisting material of polymer, has effectively solved equipment wear and tear and product iron pollution problem.
SiO in the obtained fused quartz powder2The content was 99.999%.
Example 2
A preparation method of high-purity fused quartz powder comprises the following steps:
(1) crushing: crushing the massive quartz stone into quartz sand particles of 10-18 meshes, and picking to remove obvious impurities and foreign matters such as feldspar and mica;
(2) rod rubbing, washing and graded desliming: scrubbing impurities such as soil on the outer surface of quartz sand particles by a rod mill washing machine, and carrying out classification and desliming on a hydraulic classifier;
(3) and (3) repeating magnetic separation: firstly, carrying out magnetic separation by using a wet type permanent magnet drum magnetic separator under the field intensity of 20000 gausses, then sending the magnetic separator into a wet type grinding machine to grind the magnetic separator until the magnetic separator passes through a 100-mesh sieve to obtain quartz particles with the particle size of less than 0.15mm, and carrying out magnetic separation again under the field intensity of 15000 gausses; finally, the magnetic particles are sent into a middle magnetic separator for magnetic separation under the field intensity of 8000 Gauss;
(4) flotation: and adding water into the quartz particles subjected to magnetic separation to adjust the concentration of the mortar to 30% -35%, and feeding the mixture into a flotation machine for flotation.
(5) And (3) cyclic pickling: sending the particles subjected to flotation into an ultrasonic pickling tank for ultrasonic pickling, and ultrasonically cleaning the particles subjected to pickling for 4 times; the pickling tank is pickling solution containing hydrochloric acid, hydrofluoric acid and nitric acid; the hydrochloric acid concentration of the pickling solution is 10% -15%, the hydrofluoric acid concentration is less than 10%, and the nitric acid concentration is 6% -15%; the pickling time is 1 hour, the pickling temperature is 50-60 ℃, and the ultrasonic frequency is 50 Hz.
(6) Drying: putting the washed quartz particles into an oven for drying at 150 ℃ for 3 hours, and taking out and cooling to room temperature;
(7) smelting: delivering the dried quartz particles into an internal heating type quartz glass continuous electric melting furnace for smelting at 1780-1850 ℃ for 11.5 hours, and taking out the quartz particles after smelting and rapidly cooling the quartz particles to room temperature;
(8) further crushing the fused quartz sand into fused quartz sand with the particle diameter less than 2mm by adopting an impact crusher, and then sending the fused quartz sand into a production line of a ball mill matched with an airflow classifier for ball milling and classification to obtain high-purity fused quartz powder.
Further, the flotation solution in the flotation machine in the step (4) comprises a mixed solution of sodium dodecyl benzene sulfonate, dodecylamine and dodecylpropyl ether amine, dodecylamine acetate, sulfuric acid with the concentration of 10-15%, kerosene, terpineol and water; the weight portions are as follows: 32 parts of sodium dodecyl benzene sulfonate, 33 parts of dodecylamine, 12 parts of mixed solution of dodecylpropyl ether amine, 102 parts of dodecylamine acetate, 4 parts of sulfuric acid with the concentration of 10-15%, 6 parts of coal, 6 parts of terpineol and water.
Further, the ball milling time in the step (8) is 9 hours, and the ball milling medium is zirconia balls or alumina balls; and (3) adding a grinding-aid dispersing agent accounting for 0.9 percent of the weight of the quartz powder raw material in the ball milling process, wherein the grinding-aid dispersing agent is a silane coupling agent.
Further, step (8) the welt of ball mill adopts the aluminium oxide ceramic material, the inside aluminium oxide ceramic wafer that adopts of system of air classifier carries out the wear-resisting protection of ultrapure, the impeller blade of air classifier adopts polymer wear-resisting material, has effectively solved equipment wearing and tearing and product iron pollution problem.
The SiO2 content in the obtained fused quartz powder was 99.998%.
Example 3
A preparation method of high-purity fused quartz powder comprises the following steps:
(1) crushing: crushing the massive quartz stone into quartz sand particles of 10-18 meshes, and picking to remove obvious impurities and foreign matters such as feldspar and mica;
(2) rod rubbing, washing and graded desliming: scrubbing impurities such as soil on the outer surface of quartz sand particles by a rod mill washing machine, and carrying out classification and desliming on a hydraulic classifier;
(3) and (3) repeating magnetic separation: firstly, carrying out magnetic separation by using a wet type permanent magnet drum magnetic separator under the field intensity of 20000 gausses, then feeding the magnetic separator into a wet type grinding machine to be ground until the magnetic separator passes through a 100-mesh sieve, obtaining quartz particles with the particle size of less than 0.15mm, and carrying out magnetic separation again under the field intensity of 10000 gausses; finally, the magnetic particles are sent into a middle magnetic separator for magnetic separation under the field intensity of 5000 gauss;
(4) flotation: and adding water into the quartz particles subjected to magnetic separation to adjust the concentration of the mortar to 30% -35%, and feeding the mixture into a flotation machine for flotation. The flotation solution in the flotation machine comprises mixed solution of sodium dodecyl benzene sulfonate, dodecylamine and dodecyl propyl ether amine, dodecylamine acetate, sulfuric acid with the concentration of 10-15%, kerosene, terpineol and water; the weight portions are as follows: 36 parts of sodium dodecyl benzene sulfonate, 30 parts of dodecylamine, 10 parts of mixed solution of dodecylpropyl ether amine, 12 parts of dodecylamine acetate, 5 parts of sulfuric acid with the concentration of 10-15%, 3 parts of kerosene, 3 parts of terpineol and water.
(5) And (3) cyclic pickling: sending the particles subjected to flotation into an ultrasonic pickling tank for ultrasonic pickling, and ultrasonically cleaning the particles subjected to pickling for 5 times; the pickling tank is pickling solution containing hydrochloric acid, hydrofluoric acid and nitric acid; the hydrochloric acid concentration of the pickling solution is 10% -15%, the hydrofluoric acid concentration is less than 10%, and the nitric acid concentration is 6% -15%; the pickling time is 1 hour, the pickling temperature is 50-60 ℃, and the ultrasonic frequency is 45 Hz.
(6) Drying: putting the washed quartz particles into an oven for drying at 150 ℃ for 3 hours, and taking out and cooling to room temperature;
(7) smelting: feeding the dried quartz particles into an internal heating type quartz glass continuous electric melting furnace for melting at 1780-1850 ℃ for 12 hours, and taking out the quartz particles after melting and rapidly cooling the quartz particles to room temperature;
(8) further crushing the fused quartz sand into fused quartz sand with the particle diameter less than 2mm by adopting an impact crusher, and then sending the fused quartz sand into a production line of a ball mill matched with an airflow classifier for ball milling and classification to obtain high-purity fused quartz powder. The ball milling time is 8h, and the ball milling medium is zirconia balls or alumina balls; and adding a grinding-aid dispersant accounting for 1.2 percent of the weight of the quartz powder raw material in the ball milling process, wherein the grinding-aid dispersant is triacetin. The welt of ball mill adopts the aluminium oxide ceramic material, the inside aluminium oxide ceramic wafer that adopts of system of air classifier carries out the wear-resisting protection of super pure, the impeller blade of air classifier adopts polymer wear-resistant material, has effectively solved equipment wear and tear and product iron pollution problem.
The SiO2 content in the obtained fused quartz powder was 99.999%.
The foregoing is only a preferred embodiment of the present invention, and it should be noted that modifications can be made by those skilled in the art without departing from the principle of the present invention, and these modifications should also be construed as the protection scope of the present invention.
Claims (10)
1. A preparation method of high-purity fused quartz powder is characterized by comprising the following steps: the method comprises the following steps:
(1) crushing: crushing the massive quartz stone into quartz sand particles of 10-18 meshes, and picking to remove obvious impurities and foreign matters such as feldspar and mica;
(2) rod rubbing, washing and graded desliming: scrubbing impurities such as soil on the outer surface of quartz sand particles by a rod mill washing machine, and carrying out classification and desliming on a hydraulic classifier;
(3) and (3) repeating magnetic separation: carrying out magnetic separation on the cleaned quartz sand particles by using a high-field-intensity magnetic separator, then feeding the quartz sand particles into a wet grinding mill for grinding to obtain quartz particles with the particle size of less than 0.15mm, and finally feeding the quartz sand particles into a medium-field-intensity magnetic separator for magnetic separation;
(4) flotation: adding water into the quartz particles subjected to magnetic separation to adjust the concentration of the mortar to 30-35%, and feeding the mixture into a flotation machine for flotation; the flotation solution in the flotation machine comprises 30-36 parts of sodium dodecyl benzene sulfonate, 30-36 parts of dodecylamine, 10-15 parts of mixed solution of dodecylpropyl ether amine, 10-12 parts of dodecylamine acetate, 3-5 parts of sulfuric acid with the concentration of 10-15%, 3-9 parts of kerosene, 3-9 parts of terpineol and 30-60 parts of water;
(5) and (3) cyclic pickling: sending the particles subjected to flotation into an ultrasonic pickling tank for ultrasonic pickling, and ultrasonically cleaning the particles subjected to pickling for 3-5 times;
(6) drying: putting the washed quartz particles into an oven for drying, taking out and cooling to room temperature;
(7) smelting: sending the dried quartz particles into an internal heating type quartz glass continuous electric melting furnace for smelting, taking out after smelting, and rapidly cooling to room temperature;
(8) further crushing the fused quartz sand into fused quartz sand with the particle diameter less than 2mm by adopting an impact crusher, and then sending the fused quartz sand into a production line of a ball mill matched with an airflow classifier for ball milling and classification to obtain high-purity fused quartz powder.
2. The method for preparing a high purity fused silica powder according to claim 1, wherein: the repeated magnetic separation process of the step (3) comprises the following steps: repeatedly performing magnetic separation for many times by using various magnetic separators under the field intensity of 10000-20000 gausses, then feeding the magnetic separators into a wet mill for milling to obtain quartz particles with the particle size of less than 0.15mm, and finally feeding the quartz particles into a medium magnetic separator for magnetic separation under the field intensity of 5000-8000 gausses; and (3) combining a strong, medium and weak magnetic separator with high and low field strengths to perform repeated magnetic separation.
3. The method for preparing a high purity fused silica powder according to claim 1, wherein: the pickling tank in the step (5) is pickling solution containing hydrochloric acid, hydrofluoric acid and nitric acid; the hydrochloric acid concentration of the pickling solution is 10% -15%, the hydrofluoric acid concentration is less than 10%, and the nitric acid concentration is 6% -15%; the pickling time is 1 hour, the pickling temperature is 50-60 ℃, and the ultrasonic frequency is 40-50 Hz.
4. The method for preparing a high purity fused silica powder according to claim 1, wherein: and (6) drying at the temperature of 120-200 ℃ for 2-4 h.
5. The method for preparing a high purity fused silica powder according to claim 1, wherein: and (7) the smelting temperature of the internal heating type quartz glass continuous electric melting furnace is 1780-1850 ℃, and the smelting time is 11-12 hours.
6. The method for preparing a high purity fused silica powder according to claim 1, wherein: and (5) performing ball milling for 8-10h, wherein the ball milling medium is zirconia balls or alumina balls.
7. The method for preparing a high purity fused silica powder according to claim 1, wherein: adding a grinding aid dispersant accounting for 0.3-1.2% of the weight of the quartz powder raw material in the ball milling process in the step (8); the grinding-aid dispersing agent is a silane coupling agent or triacetin.
8. The method for preparing a high purity fused silica powder according to any one of claim 1, wherein: and (8) adopting a quartz material or an aluminum oxide ceramic material as a lining plate of the ball mill.
9. The method for preparing a high purity fused silica powder according to claim 1, wherein: and (8) carrying out ultra-pure wear-resistant protection by adopting an aluminum oxide ceramic chip in the system of the airflow classifier.
10. The method for preparing a high purity fused silica powder according to claim 1, wherein: and (8) adopting a high-molecular wear-resistant material for impeller blades of the airflow classifier.