CN110819131A - Coffee grounds cork cloth and manufacturing method thereof - Google Patents

Coffee grounds cork cloth and manufacturing method thereof Download PDF

Info

Publication number
CN110819131A
CN110819131A CN201911138791.3A CN201911138791A CN110819131A CN 110819131 A CN110819131 A CN 110819131A CN 201911138791 A CN201911138791 A CN 201911138791A CN 110819131 A CN110819131 A CN 110819131A
Authority
CN
China
Prior art keywords
parts
coffee grounds
cork
cloth
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911138791.3A
Other languages
Chinese (zh)
Inventor
文家涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Dinghao Leather Handbags Co Ltd
Original Assignee
Dongguan Dinghao Leather Handbags Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Dinghao Leather Handbags Co Ltd filed Critical Dongguan Dinghao Leather Handbags Co Ltd
Priority to CN201911138791.3A priority Critical patent/CN110819131A/en
Publication of CN110819131A publication Critical patent/CN110819131A/en
Pending legal-status Critical Current

Abstract

A coffee grounds cork cloth and a manufacturing method thereof relate to the technical field of cloth manufacturing, in particular to a coffee grounds cork cloth and a manufacturing method thereof. The composition comprises the following raw materials: coffee grounds, cork oak bark and acrylic acid glue; the concentration of the acrylic acid glue is 2% -3%. The coffee grounds are recovered from shops such as starbucks, McDonald's and Kendeji, and the recovered coffee grounds are cleaned and then dried in the air or naturally dried in the air by an air dryer. After the technical scheme is adopted, the invention has the beneficial effects that: it is through retrieving coffee sediment and cork oak bark, through the preparation such as processing to coffee sediment and cork oak bark, forms a coffee sediment cork cloth, can be in cyclic utilization coffee sediment, when accomplishing the environmental protection for the cloth more has the characteristic, and the cloth appearance is more pleasing to the eye, and the practicality is stronger.

Description

Coffee grounds cork cloth and manufacturing method thereof
Technical Field
The invention relates to the technical field of cloth manufacturing, in particular to a coffee grounds cork cloth and a manufacturing method thereof.
Background
The cloth is a material commonly used in decorative materials. Comprises various fabrics such as chemical fiber carpets, non-woven wallcoverings, linen, nylon fabrics, colored rubberized fabrics, flannel and the like. Cloth plays a considerable role in decorative displays, often a major non-negligible effort in the overall sales space. A large amount of cloth is used for wall surface decoration, partition and background treatment, and a good commercial space display style can be formed. The weaving mode can be divided into two categories of woven fabric and knitted fabric. The processing technology can be divided into grey cloth, bleached cloth, dyed cloth, printed cloth, colored woven cloth, mixed technical cloth (such as printed cloth, composite cloth, flocked cloth and leather-like woolen cloth) and the like. Can also be divided into cotton cloth, chemical fiber cloth, flax cloth, wool fabric, silk, blended fabric and the like. Coffee is a beverage made from roasted coffee beans, and is a popular main beverage in the world together with cocoa and tea. Coffee is a common arbor belonging to the family of rubiaceae, coffee for daily drinking is made by matching coffee beans with various cooking devices, the coffee beans refer to kernels in coffee fruits and are baked by a proper method, the taste of a standard cup of coffee should not be bitter, a qualified coffeemaker can strictly carry out each step of operation when making coffee, and finally, the coffee presented by a guest can present sweetness, acidity, mellow degree or cleanliness degree in taste. After the coffee is made, a lot of coffee grounds remain, which causes waste and the like.
Disclosure of Invention
The invention aims to provide a coffee slag cork cloth and a manufacturing method thereof aiming at the defects and defects of the prior art, the coffee slag cork cloth is formed by recycling coffee slag and cork oak bark and processing the coffee slag and cork oak bark, the coffee slag cork cloth can be recycled, the environment is protected, the cloth is more distinctive, the appearance of the cloth is more attractive, and the practicability is higher.
In order to achieve the purpose, the invention adopts the following technical scheme:
the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 100-200 parts of coffee grounds, 0-400 parts of cork oak bark and 20-40 parts of acrylic acid glue; the concentration of the acrylic acid glue is 2% -3%.
The manufacturing method comprises the following steps:
step one, coffee grounds are recovered from shops such as starbucks, McDonald's and Kendeji, the recovered coffee grounds are cleaned and then air-dried or naturally air-dried by an air dryer, and the detection result of the recovered coffee grounds is as follows: water content 47.6%; 0.2 percent of caffeine; 41.9% of cellulose; 3.2% of fatty acid; 4.5% of fatty acid ester; 2% of protein; 0.6% of other inorganic elements (0.06% of magnesium, 0.23% of potassium, 0.06% of calcium, 0.07% of phosphorus and 0.18% of others);
step two, obtaining cork oak bark from cork oak, softening the cork oak bark at the temperature of 120-;
step three, taking coffee grounds and sheet cork oak barks in different proportions, stirring the coffee grounds and the sheet cork oak barks uniformly, adding 2-3% of acrylic acid glue, stirring and mixing the mixture, then placing the mixture in a prepared die in advance, and forming blocks with a certain thickness through strong punching;
cutting the formed block into the thickness of a commodity to be manufactured by using a special slicer, adhering the block on the cloth layer by using aqueous glue, and then polishing the surface of the block;
and fifthly, a layer of water-repellent technology is added on the surface layer of the material, and after the surface and the bottom surface are processed by sticking a layer of TPU, EVA, PVL and the like at the high temperature of 100 ℃ and 130 ℃, the effects of water resistance, soil resistance and cold release are better.
After the technical scheme is adopted, the invention has the beneficial effects that: it is through retrieving coffee sediment and cork oak bark, through the preparation such as processing to coffee sediment and cork oak bark, forms a coffee sediment cork cloth, can be in cyclic utilization coffee sediment, when accomplishing the environmental protection for the cloth more has the characteristic, and the cloth appearance is more pleasing to the eye, and the practicality is stronger.
Detailed Description
Example 1
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 100 parts of coffee grounds, 0 part of cork oak bark and 20 parts of acrylic glue; the concentration of the acrylic acid glue is 2.1%.
The manufacturing method comprises the following steps:
the method comprises the following steps: the coffee grounds are recovered from shops such as starbucks, McDonald's and Kendeji, the recovered coffee grounds are cleaned and then dried by an air dryer or naturally dried, and the recovered coffee grounds have the following detection results: water content 47.6%; 0.2 percent of caffeine; 41.9% of cellulose; 3.2% of fatty acid; 4.5% of fatty acid ester; 2% of protein; 0.6% of other inorganic elements (0.06% of magnesium, 0.23% of potassium, 0.06% of calcium, 0.07% of phosphorus and 0.18% of others);
step two: obtaining cork oak bark from cork oak, softening the cork oak bark at the temperature of 120 ℃ and 150 ℃, and then smashing the cork oak bark by a machine to be made into irregular sheets;
step three: taking coffee grounds and sheet cork oak barks in different proportions, stirring, uniformly stirring, adding 2% -3% of acrylic acid glue, stirring and mixing, then placing in a prepared die in advance, and strongly stamping to form blocks with a certain thickness;
step four: cutting the formed block into the thickness of a commodity to be manufactured by a special slicer, adhering the block on a cloth layer by using aqueous glue, and then polishing the surface of the block;
step five: a layer of water-repellent technology is added on the surface layer of the material, and after the surface and the bottom surface are processed at high temperature of 100 ℃ and 130 ℃, a layer of TPU, EVA, PVL and the like is pasted, the effects of water resistance, soil resistance and cold release are better.
Quercus variabilis (lour.) Merr of Fagaceae is deciduous tree of Quercus, with height of 30 m, black brown bark and hairless twigs; conical bud, oval leaf shape like needle or oblong, tip is gradually sharp, and petiole is unhaired. The shaft of the male inflorescence is densely covered by brown villi, and the stamens are more; the female inflorescence generates leaf axilla, the flower column wraps nuts 2/3, the shape of small bract is diamond, the nuts are nearly spherical or wide oval, the top end is round, and the fruit umbilicus is protruded. Blooming in 3-4 months, and fruiting in the next 9-10 months, wherein the wood is a ring-hole wood, the sapwood is light yellow, the heartwood is light red, and the air-dried density is 0.87 g/cubic centimeter; the bark cork layer is developed and is the main raw material for producing cork in China; bark contains 10.56% protein; the oak fruit contains 59.3% of starch and 5.1% of tannin; the bark and the hopper are rich in tannin, and tannin extract can be extracted.
Acrylic acid glue is acrylate adhesive, and polyacrylate is single-component or main component adhesive. Has two types of thermoplasticity and thermosetting property, and has the characteristics of high strength, impact resistance, good weather resistance, capability of being bonded by oil surface, convenient use, impact resistance and strong shearing force. The aqueous glue and the aqueous film-coated glue are methods for processing the surface of the printed matter to improve the surface glossiness and strength of the printed matter and enhance the aesthetic feeling effect. The quality of the film is measured, and the brightness, strength, adhesion and the like of the film are also examined. Aqueous wet-type coating is highly preferred by customers because of the characteristics of high strength, easy recycling, no pollution, and the like of the coated printed matter. Compared with the traditional glue, the water-based laminating adhesive is prepared from imported raw materials, has the advantages of high solid content, low viscosity, good process applicability, strong adhesive force, no toxicity and the like, and is suitable for aluminum foil (OPA), pretreated polyethylene (HDPE, LDPE), polypropylene (OPP, CPP), Polyester (PET), polyamide (PA, ONY) films, metal-sprayed films and double-component solvent type polyurethane adhesives compounded between cellophane.
Example 2
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 100 parts of coffee grounds, 100 parts of cork oak bark and 20 parts of acrylic glue;
the concentration of the acrylic acid glue is 2.2%.
The other raw material compositions and the formula process are the same as those of the example 1.
Example 3
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 130 parts of coffee grounds, 160 parts of cork oak barks and 24 parts of acrylic glue;
the concentration of the acrylic acid glue is 2.3%.
The other raw material compositions and the formula process are the same as those of the example 1.
Example 4
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 160 parts of coffee grounds, 240 parts of cork oak barks and 28 parts of acrylic glue;
the concentration of the acrylic acid glue is 2.4%.
The other raw material compositions and the formula process are the same as those of the example 1.
Example 5
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 190 parts of coffee grounds, 300 parts of cork oak bark and 32 parts of acrylic glue;
the concentration of the acrylic acid glue is 2.5%.
The other raw material compositions and the formula process are the same as those of the example 1.
Example 6
The technical scheme adopted by the specific implementation mode is as follows: the coffee grounds and cork cloth is composed of the following raw materials in parts by weight: 200 parts of coffee grounds, 400 parts of cork oak barks and 40 parts of acrylic glue;
the concentration of the acrylic acid glue is 2.6%.
The other raw material compositions and the formula process are the same as those of the example 1.
After the technical scheme is adopted, the invention has the beneficial effects that: it is through retrieving coffee sediment and cork oak bark, through the preparation such as processing to coffee sediment and cork oak bark, forms a coffee sediment cork cloth, can be in cyclic utilization coffee sediment, when accomplishing the environmental protection for the cloth more has the characteristic, and the cloth appearance is more pleasing to the eye, and the practicality is stronger.
The above description is only for the purpose of illustrating the technical solutions of the present invention and not for the purpose of limiting the same, and other modifications or equivalent substitutions made by those skilled in the art to the technical solutions of the present invention should be covered within the scope of the claims of the present invention without departing from the spirit and scope of the technical solutions of the present invention.

Claims (8)

1. The coffee grounds cork cloth is characterized by comprising the following raw materials in parts by weight: 100-200 parts of coffee grounds, 0-400 parts of cork oak bark and 20-40 parts of acrylic acid glue; the concentration of the acrylic acid glue is 2% -3%.
2. The method for manufacturing the coffee grounds cork cloth is characterized by comprising the following steps of:
step one, coffee grounds are recovered from shops such as starbucks, McDonald's and Kendeji, the recovered coffee grounds are cleaned and then air-dried or naturally air-dried by an air dryer, and the detection result of the recovered coffee grounds is as follows: water content 47.6%; 0.2 percent of caffeine; 41.9% of cellulose; 3.2% of fatty acid; 4.5% of fatty acid ester; 2% of protein; 0.6% of other inorganic elements (0.06% of magnesium, 0.23% of potassium, 0.06% of calcium, 0.07% of phosphorus and 0.18% of others);
step two, obtaining cork oak bark from cork oak, softening the cork oak bark at the temperature of 120-;
step three, taking coffee grounds and sheet cork oak barks in different proportions, stirring the coffee grounds and the sheet cork oak barks uniformly, adding 2-3% of acrylic acid glue, stirring and mixing the mixture, then placing the mixture in a prepared die in advance, and forming blocks with a certain thickness through strong punching;
cutting the formed block into the thickness of a commodity to be manufactured by using a special slicer, adhering the block on the cloth layer by using aqueous glue, and then polishing the surface of the block;
and fifthly, a layer of water-repellent technology is added on the surface layer of the material, and after the surface and the bottom surface are processed by sticking a layer of TPU, EVA, PVL and the like at the high temperature of 100 ℃ and 130 ℃, the effects of water resistance, soil resistance and cold release are better.
3. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 100 parts of coffee grounds and 20 parts of acrylic acid glue; the concentration of the acrylic acid glue is 2.1%.
4. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 100 parts of coffee grounds, 100 parts of cork oak bark and 20 parts of acrylic glue; the concentration of the acrylic acid glue is 2.2%.
5. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 130 parts of coffee grounds, 160 parts of cork oak barks and 24 parts of acrylic glue; the concentration of the acrylic acid glue is 2.3%.
6. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 160 parts of coffee grounds, 240 parts of cork oak barks and 28 parts of acrylic glue; the concentration of the acrylic acid glue is 2.4%.
7. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 190 parts of coffee grounds, 300 parts of cork oak bark and 32 parts of acrylic glue; the concentration of the acrylic acid glue is 2.5%.
8. The coffee grounds cork cloth according to claim 1, characterized in that it is composed of the following raw materials in parts by weight: 200 parts of coffee grounds, 400 parts of cork oak barks and 40 parts of acrylic glue; the concentration of the acrylic acid glue is 2.6%.
CN201911138791.3A 2019-11-20 2019-11-20 Coffee grounds cork cloth and manufacturing method thereof Pending CN110819131A (en)