CN110744723A - 一种蓝宝石小圆片加工方法 - Google Patents
一种蓝宝石小圆片加工方法 Download PDFInfo
- Publication number
- CN110744723A CN110744723A CN201910970694.4A CN201910970694A CN110744723A CN 110744723 A CN110744723 A CN 110744723A CN 201910970694 A CN201910970694 A CN 201910970694A CN 110744723 A CN110744723 A CN 110744723A
- Authority
- CN
- China
- Prior art keywords
- sapphire
- protective glass
- piece
- rosin
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种蓝宝石小圆片加工方法，依次包括以下步骤：A：配制粘结剂，B：粘接处理，C：内圆切割处理，D：改圆粗磨处理，E：无心磨精磨，F：化料，G：清洗，所述粘结剂为松香和石蜡按照质量配比(1.4‑1.8):1的比例配制而成，本发明可以有效提升蓝宝石小圆片加工良率，减低制造成本。
Description
技术领域
本发明涉及光学镜片制造技术领域，尤其是指一种蓝宝石小圆片加工方法。
背景技术
目前蓝宝石小圆片加工方式主要是激光切割技术，直接将要求厚度的蓝宝石衬底直接切割成圆片或是将蓝宝石衬底粘接后切割成小方料再进行磨圆，激光切割设备不仅比较昂贵，而且激光切割边缘一般有一定锥度，且当蓝宝石衬底镀膜之后切割问题更大；另一方面由于蓝宝石硬度非常高，传统的是利用松香石蜡配比或精蜡直接叠加一起粘接后切割有很大问题，其中切割大致有多线切割、外圆切割和内圆切割，多线切割是一种切割效果很好的切割方式，但随着蓝宝石小圆片规格变化，其所用的罗拉也要不停地更换，而且切割蓝宝石的线成本也比较高，造成这种切割方式成本很高；外圆切割则是刀缝相对较大，很影响基材利用率；内圆切割则是一种成本相对较低的一种切割方式，但不论是外圆切割还是内圆切割时很容易将粘接好的蓝宝石震散开，导致后工序无法进行磨圆加工，良率低成本也随之增加。
发明内容
(一)要解决的技术问题
本发明目的在于提供一种蓝宝石小圆片加工方法，可以有效提升蓝宝石小圆片加工良率，减低制造成本。为实现上述之目的，本发明采取如下技术方案：
(二)技术方案
一种蓝宝石小圆片加工方法，依次包括以下步骤：A：配制粘结剂，B：粘接处理，C：内圆切割处理，D：改圆粗磨处理，E：无心磨精磨，F：化料，G：清洗，所述粘结剂为松香和石蜡按照质量配比(1.4-1.8):1的比例配制而成。
进一步，所述粘结剂为松香和石蜡按照质量配比1.6:1放置在加热容器中，将其加热至160℃熔化并搅拌5-10min使松香石蜡混合均匀，然后降低温度使其控制在110±5℃。
进一步，所述B步骤中的粘接先将捞片夹具放置在粘结剂中，再将两片保护玻璃片依次放进捞片夹具中，然后在依次放1-3片蓝宝石叠放到捞片夹具中，再叠放一片保护玻璃片，然后再依次叠放1-3片蓝宝石，再叠放一片保护玻璃片，依此类方式叠放到捞片夹具内，浸泡在粘结剂内10±1min后捞至气压台进行压制冷却，气压大小为0.3±0.03MPa，时间3±1min，所述保护玻璃片厚度为1.0-1.5mm，粘接蓝宝石总片数不多于6片。
进一步，所述C步骤内切割的切割速度控制在5-6mm/min。
(三)有益效果
本发明与现有技术相比具有明显的优点和有益效果，具体而言，本发明是将松香和石蜡按照(1.4-1.8):1的配比制成粘结剂，用粘结剂将多片蓝宝石粘接在一起，粘接时蓝宝石中间用保护玻璃片隔开，使得蓝宝石内圆切割效果得到明显改善，可以有效提升蓝宝石小圆片加工良率，减低制造成本。
附图说明
图1是蓝宝石粘接示意图。
附图标号说明：
1、保护玻璃片 2、蓝宝石
具体实施方式
下面详细描述本发明的实施例，所述实施例的示例在附图中示出，其中自始至终相同或类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的实施例是示例性的，旨在用于解释本发明，而不能理解为对本发明的限制。
下面结合附图与具体实施方式对本发明作进一步描述。
一种蓝宝石小圆片加工方法，依次包括以下步骤：A：配制粘结剂，B：粘接处理，C：内圆切割处理，D：改圆粗磨处理，E：无心磨精磨，F：化料，G：清洗，所述粘结剂为松香和石蜡按照质量配比(1.4-1.8):1的比例配制而成。
为使粘结剂效果最佳，所述粘结剂为松香和石蜡按照质量配比1.6:1放置在加热容器中，将其加热至160℃熔化并搅拌5-10min使松香石蜡混合均匀，然后降低温度使其控制在110±5℃。
请参阅图1所示，所述B步骤中的粘接先将捞片夹具放置在粘结剂中，再将两片保护玻璃片1依次放进捞片夹具中，然后在依次放1-3片蓝宝石2叠放到捞片夹具中，再叠放一片保护玻璃片1，然后再依次叠放1-3片蓝宝石2，再叠放一片保护玻璃片1，依此类方式叠放到捞片夹具内，浸泡在粘结剂内10±1min后捞至气压台进行压制冷却，气压大小为0.3±0.03MPa，时间3±1min，所述保护玻璃片1厚度为1.0-1.5mm，粘接蓝宝石2总片数不多于6片。
所述C步骤内切割的切割速度控制在5-6mm/min。
本发明的设计要点是将松香和石蜡按照(1.4-1.8):1的配比制成粘结剂，用粘结剂将多片蓝宝石粘接在一起，粘接时蓝宝石中间用保护玻璃片隔开，使得蓝宝石内圆切割效果得到明显改善，可以有效提升蓝宝石小圆片加工良率，减低制造成本。
以上所述，仅是本发明较佳实施例而已，并非对本发明的技术范围作任何限制，故凡是依据本发明的技术实质对以上实施例所作的任何细微修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (4)
1.一种蓝宝石小圆片加工方法，其特征在于：依次包括以下步骤：A：配制粘结剂，B：粘接处理，C：内圆切割处理，D：改圆粗磨处理，E：无心磨精磨，F：化料，G：清洗，所述粘结剂为松香和石蜡按照质量配比(1.4-1.8):1的比例配制而成。
2.根据权利要求1所述一种蓝宝石小圆片加工方法，其特征在于：所述粘结剂为松香和石蜡按照质量配比1.6:1放置在加热容器中，将其加热至160℃熔化并搅拌5-10min使松香石蜡混合均匀，然后降低温度使其控制在110±5℃。
3.根据权利要求2所述一种蓝宝石小圆片加工方法，其特征在于：所述B步骤中的粘接先将捞片夹具放置在粘结剂中，再将两片保护玻璃片依次放进捞片夹具中，然后在依次放1-3片蓝宝石叠放到捞片夹具中，再叠放一片保护玻璃片，然后再依次叠放1-3片蓝宝石，再叠放一片保护玻璃片，依此类方式叠放到捞片夹具内，浸泡在粘结剂内10±1min后捞至气压台进行压制冷却，气压大小为0.3±0.03MPa，时间3±1min，所述保护玻璃片厚度为1.0-1.5mm，粘接蓝宝石总片数不多于6片。
4.根据权利要求1所述一种蓝宝石小圆片加工方法，其特征在于：所述C步骤内切割的切割速度控制在5-6mm/min。