CN110680115A - Preparation method of mattress with antibacterial, mite-killing and natural far infrared functions - Google Patents
Preparation method of mattress with antibacterial, mite-killing and natural far infrared functions Download PDFInfo
- Publication number
- CN110680115A CN110680115A CN201910975594.0A CN201910975594A CN110680115A CN 110680115 A CN110680115 A CN 110680115A CN 201910975594 A CN201910975594 A CN 201910975594A CN 110680115 A CN110680115 A CN 110680115A
- Authority
- CN
- China
- Prior art keywords
- mattress
- fibers
- far infrared
- fiber cloth
- fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites relates to the technical field of living appliances. The invention aims to solve the problems that the energy consumption is high, the environment is not favorable, the material running phenomenon of the mattress is easy to occur, the mattress is easy to mildew or breed bacteria, mites and peculiar smell, and the body health of people is influenced in the manufacturing process of the traditional mattress. The method comprises the following steps: pretreating the Meyer sedge raw grass to obtain Meyer sedge fine fibers; mixing the fine Meyer sedge fibers with the collodion cotton fibers and the ES fibers to obtain mixed fibers; the mixed fiber is lapped and formed, and the mattress core is formed by hot-pressing and forming; covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the functions of resisting bacteria, removing mites and natural far infrared rays. The invention can obtain the preparation method of the mattress with the natural far infrared functions of resisting bacteria and removing mites.
Description
Technical Field
The invention relates to the technical field of living appliances, in particular to a preparation method of a mattress with antibacterial and mite-killing natural far infrared functions.
Background
Most of mattresses in the current market are woven by chemical fibers, so that resources are consumed, the environment is not facilitated, even if some selected materials adopt natural materials as mattress core layer materials to achieve the health care effect, some selected traditional Chinese medicine raw materials are crushed into powder in a free state and added into the powder, and the mattress is difficult to ensure that the material leakage phenomenon is not generated after vibration, the quality is influenced or the expected effect is not achieved; the purpose of the health-care mattress is achieved by adding chemical synthesis and post-finishing, the durability is difficult to achieve, the air permeability and the moisture dissipation of the latex mattress and the sponge mattress are poor, the latex mattress and the sponge mattress are easy to mildew or breed bacteria, mites, peculiar smell and the like after long-term use, and some palm material products are analyzed and considered by related experts that cardiovascular and cerebrovascular diseases such as thromboembolism, myocardial infarction and the like can be caused by long-term use of the palm product; the mattress core is also woven by taking the Meyer sedge as the raw material, but the manufacturing process is rough and simple, lacks elasticity and has single function.
Disclosure of Invention
The invention provides a preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites.
A preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites comprises the following steps:
firstly, pretreating the Meyer sedge raw grass to obtain Meyer sedge fine fibers; mixing the fine carex meyeriana fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine carex meyeriana fibers to the glue-sprayed cotton is (50-70): 25-40, and the mass ratio of the fine carex meyeriana fibers to the ES fibers is (50-70): 5-10);
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
and thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the antibacterial and acarid-removing natural far infrared functions.
The invention has the beneficial effects that:
first, Wula grass has the ability to resist fungal attack and fungal parasitism for a lifetime of ten years, one hundred years, and no mildew according to the compendium of materia Medica. Wula grass is one of the traditional three treasures in northeast, and is a pure natural wild plant. Carex meyeriana (Meyer sedge) contains a large amount of volatile oil components, flavonoid compounds, vegetable protein amino acids, calcium, zinc, iron and other components, and is praised by contemporary pharmacians as three-treasure soft acupuncture and moxibustion in northeast China. The pharmaceutical scientific value of the flavonoid compound is as follows: eliminating active oxygen free radicals in vivo, preventing arteriosclerosis, preventing cancer, preventing diabetes, preventing Parkinson disease and resisting aging, and relieving dizziness and headache caused by hypertension; the curative effect of other chemical components is as follows: regulating nerve, and improving circulation in vivo. But also can automatically adjust and maintain the humidity, so that the traditional Chinese medicine has the effects of being warm in winter and cool in summer, has lasting fragrance, removes any peculiar smell, and is a traditional Chinese medicine for keeping warm and dehumidifying. The research shows that the traditional Chinese medicine composition is very suitable for preventing and treating tinea pedis, and has auxiliary treatment effect on rheumatism and arthralgia if being used for a long time. The carex meyeriana has long history of disease prevention and health care by using the carex meyeriana for the workers, such as antibiosis, bacterium prevention, cold protection and warm keeping, fatigue elimination, blood microcirculation improvement and immunity improvement, and the health care effect of the carex meyeriana has great market influence.
Hemp, also known as hemp, is a traditional and ancient plant in China, and has been mainly used for textile use since ancient times. Industrial cannabis (THC < 0.3%) is considered to be of no drug use value, but is still a treasure throughout the body. Hemp is a novel fiber resource, and a large number of research experiments prove that the hemp fiber has the functions of unique moisture absorption, quick drying, ventilation, bacteriostasis, mildew resistance, ultraviolet radiation resistance, self-cleaning adsorption, natural green and the like, and is listed as a material for military equipment in China; the hemp fabric can shield more than 95% of ultraviolet rays, does not fade at the high temperature of 370 ℃, does not burn at the temperature of 1000 ℃, and has excellent heat resistance and ultraviolet resistance; due to the high-quality characteristics of the hemp, the textile made of the hemp becomes the best health textile for people including pregnant women, infants and old people, and is superior to the common textile with the auxiliary chemical addition synthetic health care function existing in the market in both functionality and practicability. Hemp fiber contains various metal elements, phenols and derivatives thereof, organic acid and inorganic salt, and can destroy the structure of thallus. The higher content of over 60 of the separated hemp narcotic components is cannabidiol, tetrahydrocannabinol and its propyl ketone series, cannabigerol, cannabichromene and its propyl ketone series, etc. The cannabinol is a non-soluble, natural antimicrobial substance. Hemp fiber contains more than ten trace elements which are very beneficial to human health, and a large number of experiments prove that: the antibacterial rate of hemp phenolic substances in the hemp textile to staphylococcus aureus, escherichia coli, candida albicans and the like reaches 99%, and the hemp fabric can kill attached bacteria within 1 hour; hemp fiber can be blended with cotton, hemp, silk, wool and chemical fiber, and can also be spun purely, hemp has the moisture-removing property 3 times of that of pure cotton, has higher electric breakdown performance than that of cotton fiber, is better than that of silk and chemical fiber, and has the lowest antistatic performance in cotton and silk. Therefore, the special effect of the hemp fabric is that any fiber fabric cannot be substituted. China hemp is a renewable resource raw material taking agriculture as a source, and is a new and expensive energy substance which is disputed and developed all over the world.
The activated carbon fiber is formed by high-temperature carbonization and activation of natural fiber cloth; the specific surface area is large, and the adsorption and desorption efficiency is high; strong adsorption capacity and large effective adsorption capacity; can be used as a catalyst carrier and is suitable for removing and deodorizing special gas; the product is acid-resistant, alkali-resistant, corrosion-resistant and weather-resistant; the material has good electric conduction and heat conduction performance, less heat storage capacity and high chemical stability; the far infrared emissivity of 8-14 μm at low temperature is up to 89%, and the anion concentration is up to 5000 (pieces/cm)3) The product is widely applied to environmental protection, medical treatment and health, protection of biological, chemical and toxic gas articles, chemical protective clothing and the like, and has light weight, softness, high fiber strength and thin thickness; high temperature resistance, high temperature resistance of over 1000 ℃ in inert gas and ignition point of over 500 ℃ in air. Also used as electrostatic protection material, heat preservation and moisture absorption material; can be used as personal health far infrared ray and anion health product.
Secondly, in the prior art, the energy consumption of the manufacturing process of the mattress woven by the chemical fiber is large, and the mattress is not beneficial to the environment; the natural material is used as the mattress core material, so that the material running phenomenon is easy to occur, the quality is influenced or the expected effect cannot be achieved; the health-care mattress added by chemical synthesis is difficult to have persistence, and the latex mattress and the sponge mattress have poor air permeability and moisture dissipation, so that the health-care mattress is easy to mildew or breed bacteria, mites, peculiar smell and the like after being used for a long time; some mattresses made of palm material products can generate cardiovascular and cerebrovascular diseases such as blood embolism, myocardial infarction and the like after long-term use, and other products are made of harmful adhesive materials and influence the body health of people; at present, the mattress core woven by taking the Meyer sedge as the raw material has the advantages of rough and simple manufacturing process, lack of elasticity and single function;
according to the invention, through the special combination of the natural carex, the industrial hemp fiber fabric and the activated carbon fiber fabric, no chemical additive is needed, the carex fibril yarn is used as the main material of the mattress core, the industrial hemp fiber fabric is used as the surface layer material, and the activated carbon fiber fabric is used as the middle layer functional material, so that the mattress core has multiple natural effects, the functional attributes of the mattress core are fully exerted, the effects of resisting bacteria, inhibiting bacteria, removing mites, removing odor and odor are achieved, the disease prevention and treatment health care function of the far infrared function is achieved, the sleep quality of people is further improved, the sleep is promoted, the health of the public is facilitated, the source of raw materials is wide, the natural degradation is realized, and the environment is protected.
The invention can obtain the preparation method of the mattress with the natural far infrared functions of resisting bacteria and removing mites.
Detailed Description
The first embodiment is as follows: the preparation method of the mattress with the antibacterial and acarid-removing natural far infrared functions comprises the following steps:
firstly, pretreating the Meyer sedge raw grass to obtain Meyer sedge fine fibers; mixing the fine carex meyeriana fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine carex meyeriana fibers to the glue-sprayed cotton is (50-70): 25-40, and the mass ratio of the fine carex meyeriana fibers to the ES fibers is (50-70): 5-10);
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
and thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the antibacterial and acarid-removing natural far infrared functions.
The glue-sprayed cotton fiber endows the mattress core with certain soft support and elasticity, the ES fiber melts in the hot-press forming to play a certain bonding role, the fiber core can be fixed, and the integral tightness of the fiber core is ensured; the industrial hemp fiber cloth is used as the surface layer of the mattress core, and the activated carbon fiber cloth is used as the inner layer of the mattress core.
The beneficial effects of the embodiment are as follows:
first, Wula grass has the ability to resist fungal attack and fungal parasitism for a lifetime of ten years, one hundred years, and no mildew according to the compendium of materia Medica. Wula grass is one of the traditional three treasures in northeast, and is a pure natural wild plant. Carex meyeriana (Meyer sedge) contains a large amount of volatile oil components, flavonoid compounds, vegetable protein amino acids, calcium, zinc, iron and other components, and is praised by contemporary pharmacians as three-treasure soft acupuncture and moxibustion in northeast China. The pharmaceutical scientific value of the flavonoid compound is as follows: eliminating active oxygen free radicals in vivo, preventing arteriosclerosis, preventing cancer, preventing diabetes, preventing Parkinson disease and resisting aging, and relieving dizziness and headache caused by hypertension; the curative effect of other chemical components is as follows: regulating nerve, and improving circulation in vivo. But also can automatically adjust and maintain the humidity, so that the traditional Chinese medicine has the effects of being warm in winter and cool in summer, has lasting fragrance, removes any peculiar smell, and is a traditional Chinese medicine for keeping warm and dehumidifying. The research shows that the traditional Chinese medicine composition is very suitable for preventing and treating tinea pedis, and has auxiliary treatment effect on rheumatism and arthralgia if being used for a long time. The carex meyeriana has long history of disease prevention and health care by using the carex meyeriana for the workers, such as antibiosis, bacterium prevention, cold protection and warm keeping, fatigue elimination, blood microcirculation improvement and immunity improvement, and the health care effect of the carex meyeriana has great market influence.
Hemp, also known as hemp, is a traditional and ancient plant in China, and has been mainly used for textile use since ancient times. Industrial cannabis (THC < 0.3%) is considered to be of no drug use value, but is still a treasure throughout the body. Hemp is a novel fiber resource, and a large number of research experiments prove that the hemp fiber has the functions of unique moisture absorption, quick drying, ventilation, bacteriostasis, mildew resistance, ultraviolet radiation resistance, self-cleaning adsorption, natural green and the like, and is listed as a material for military equipment in China; the hemp fabric can shield more than 95% of ultraviolet rays, does not fade at the high temperature of 370 ℃, does not burn at the temperature of 1000 ℃, and has excellent heat resistance and ultraviolet resistance; due to the high-quality characteristics of the hemp, the textile made of the hemp becomes the best health textile for people including pregnant women, infants and old people, and is superior to the common textile with the auxiliary chemical addition synthetic health care function existing in the market in both functionality and practicability. Hemp fiber contains various metal elements, phenols and derivatives thereof, organic acid and inorganic salt, and can destroy the structure of thallus. The higher content of over 60 of the separated hemp narcotic components is cannabidiol, tetrahydrocannabinol and its propyl ketone series, cannabigerol, cannabichromene and its propyl ketone series, etc. The cannabinol is a non-soluble, natural antimicrobial substance. Hemp fiber contains more than ten trace elements which are very beneficial to human health, and a large number of experiments prove that: the antibacterial rate of hemp phenolic substances in the hemp textile to staphylococcus aureus, escherichia coli, candida albicans and the like reaches 99%, and the hemp fabric can kill attached bacteria within 1 hour; hemp fiber can be blended with cotton, hemp, silk, wool and chemical fiber, and can also be spun purely, hemp has the moisture-removing property 3 times of that of pure cotton, has higher electric breakdown performance than that of cotton fiber, is better than that of silk and chemical fiber, and has the lowest antistatic performance in cotton and silk. Therefore, the special effect of the hemp fabric is that any fiber fabric cannot be substituted. China hemp is a renewable resource raw material taking agriculture as a source, and is a new and expensive energy substance which is disputed and developed all over the world.
The activated carbon fiber is formed by high-temperature carbonization and activation of natural fiber cloth; the specific surface area is large, and the adsorption and desorption efficiency is high; strong adsorption capacity and large effective adsorption capacity; can be used as a catalyst carrier and is suitable for removing and deodorizing special gas; the product is acid-resistant, alkali-resistant, corrosion-resistant and weather-resistant; the material has good electric conduction and heat conduction performance, less heat storage capacity and high chemical stability; the far infrared emissivity of 8-14 μm at low temperature is up to 89%, and the anion concentration is up to 5000 (pieces/cm)3) The product is widely applied to environmental protection, medical treatment and health, protection of biological, chemical and toxic gas articles, chemical protective clothing and the like, and has light weight, softness, high fiber strength and thin thickness; high-temperature resistant, high-temperature resistant 1000 ℃ in inert gasAbove, the ignition point in the air reaches above 500 ℃. Also used as electrostatic protection material, heat preservation and moisture absorption material; can be used as personal health far infrared ray and anion health product.
Secondly, in the prior art, the energy consumption of the manufacturing process of the mattress woven by the chemical fiber is large, and the mattress is not beneficial to the environment; the natural material is used as the mattress core material, so that the material running phenomenon is easy to occur, the quality is influenced or the expected effect cannot be achieved; the health-care mattress added by chemical synthesis is difficult to have persistence, and the latex mattress and the sponge mattress have poor air permeability and moisture dissipation, so that the health-care mattress is easy to mildew or breed bacteria, mites, peculiar smell and the like after being used for a long time; some mattresses made of palm material products can generate cardiovascular and cerebrovascular diseases such as blood embolism, myocardial infarction and the like after long-term use, and other products are made of harmful adhesive materials and influence the body health of people; at present, the mattress core woven by taking the Meyer sedge as the raw material has the advantages of rough and simple manufacturing process, lack of elasticity and single function;
according to the embodiment, through the special combination of the natural carex, the industrial hemp fiber fabric and the activated carbon fiber fabric, no chemical additive is needed, the carex fibril yarns are used as the main material of the mattress core, the industrial hemp fiber fabric is used as the surface layer material, and the activated carbon fiber fabric is used as the middle layer functional material, so that the mattress core has multiple natural effects, the functional attributes of the mattress core are fully exerted, the effects of resisting bacteria, inhibiting bacteria, removing mites, removing odor and odor are achieved, the disease prevention and treatment health care function of the far infrared function is achieved, the sleep quality of people is further improved, the sleep is promoted, the health of the public is facilitated, the raw materials are wide in source and can be naturally degraded, and the environment is protected.
The second embodiment is as follows: the present embodiment differs from the present embodiment in that: the pretreatment in the step one is as follows: mechanically rolling, kneading, splitting and carding the carex meyeriana raw grass to obtain fine carex meyeriana fibers, and ensuring the natural properties of the fine carex meyeriana fibers.
Other steps are the same as those in the first embodiment.
The third concrete implementation mode: the first or second differences from the present embodiment are as follows: in the first step, the mass ratio of the fine Meyer sedge fibers to the collodion cotton is 14: 5.
The other steps are the same as those in the first or second embodiment.
The fourth concrete implementation mode: the difference between this embodiment and one of the first to third embodiments is as follows: in the first step, the mass ratio of the fine Meyer sedge fibers to the ES fibers is 14: 1.
The other steps are the same as those in the first to third embodiments.
The fifth concrete implementation mode: the difference between this embodiment and one of the first to fourth embodiments is: the activated carbon fiber cloth in the third step is woven or non-woven fabric.
The other steps are the same as those in the first to fourth embodiments.
The sixth specific implementation mode: the difference between this embodiment and one of the first to fifth embodiments is as follows: the industrial hemp fiber cloth in the third step is woven or non-woven fabric.
The other steps are the same as those in the first to fifth embodiments.
The seventh embodiment: the difference between this embodiment and one of the first to sixth embodiments is: the content of the industrial hemp fiber in the industrial hemp fiber cloth is 35-100%.
The other steps are the same as those in the first to sixth embodiments.
The specific implementation mode is eight: the difference between this embodiment and one of the first to seventh embodiments is: the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth in the third step is characterized in that the industrial hemp fiber cloth is used as a surface layer, and the activated carbon fiber cloth is used as an inner layer.
The other steps are the same as those in the first to seventh embodiments.
The following examples were used to demonstrate the beneficial effects of the present invention:
the first embodiment is as follows: a preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites comprises the following steps:
firstly, mechanically rolling, rubbing, opening and devillicating the Meyer sedge grass raw grass, and carding to obtain soft and original ecological Meyer sedge fine fiber, wherein the Meyer sedge fine fiber has the length of 2-40 mm and the diameter of 51.8-60.6 mu m; mixing the fine Meyer sedge fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine Meyer sedge fibers to the glue-sprayed cotton is 14:5, and the mass ratio of the fine Meyer sedge fibers to the ES fibers is 14: 1;
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the functions of resisting bacteria, removing mites and naturally producing far infrared rays;
the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth in the third step is characterized in that the industrial hemp fiber cloth is used as a surface layer, the activated carbon fiber cloth is used as an inner layer, the activated carbon fiber cloth in the third step is a woven fabric, the industrial hemp fiber cloth is a woven fabric, and the component content of the industrial hemp fiber in the industrial hemp fiber cloth is more than or equal to 55%.
Example two: a preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites comprises the following steps:
firstly, mechanically rolling, rubbing, opening and devillicating the Meyer sedge grass raw grass, and carding to obtain soft and original ecological Meyer sedge fine fiber, wherein the Meyer sedge fine fiber has the length of 2-40 mm and the diameter of 51.8-60.6 mu m; mixing the fine Meyer sedge fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine Meyer sedge fibers to the glue-sprayed cotton is 20:11, and the mass ratio of the fine Meyer sedge fibers to the ES fibers is 60: 7;
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the functions of resisting bacteria, removing mites and naturally producing far infrared rays;
the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth in the third step is characterized in that the industrial hemp fiber cloth is used as a surface layer, the activated carbon fiber cloth is used as an inner layer, the activated carbon fiber cloth in the third step is a non-woven fabric, the industrial hemp fiber cloth is a woven fabric, and the component content of the industrial hemp fiber in the industrial hemp fiber cloth is 100%.
Example three: a preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites comprises the following steps:
firstly, mechanically rolling, rubbing, opening and devillicating the Meyer sedge grass raw grass, and carding to obtain soft and original ecological Meyer sedge fine fiber, wherein the Meyer sedge fine fiber has the length of 2-40 mm and the diameter of 51.8-60.6 mu m; mixing the fine carex meyeriana fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine carex meyeriana fibers to the glue-sprayed cotton is 12:7, and the mass ratio of the fine carex meyeriana fibers to the ES fibers is 12: 1;
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the functions of resisting bacteria, removing mites and naturally producing far infrared rays;
the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth in the third step is characterized in that the industrial hemp fiber cloth is used as a surface layer, the activated carbon fiber cloth is used as an inner layer, the activated carbon fiber cloth in the third step is a non-woven fabric, the industrial hemp fiber cloth is a woven fabric, and the component content of the industrial hemp fiber in the industrial hemp fiber cloth is more than or equal to 80%.
Claims (8)
1. A preparation method of a mattress with natural far infrared functions of resisting bacteria and removing mites is characterized by comprising the following steps:
firstly, pretreating the Meyer sedge raw grass to obtain Meyer sedge fine fibers; mixing the fine carex meyeriana fibers with the glue-sprayed cotton fibers and the ES fibers to obtain mixed fibers, wherein the mass ratio of the fine carex meyeriana fibers to the glue-sprayed cotton is (50-70): 25-40, and the mass ratio of the fine carex meyeriana fibers to the ES fibers is (50-70): 5-10);
secondly, lapping and forming the mixed fibers, and performing hot-pressing and shaping to form a mattress core;
and thirdly, covering the composite industrial hemp fiber cloth quilted with the activated carbon fiber cloth on the surface of the mattress core body, and cutting and sewing to obtain the mattress with the antibacterial and acarid-removing natural far infrared functions.
2. The method for preparing a natural far infrared functional mattress with antibacterial and acarid-removing functions as claimed in claim 1, wherein the pretreatment in step one is as follows: mechanically rolling, kneading, splitting and carding the carex meyeriana raw grass to obtain the fine carex meyeriana fibers.
3. The method for preparing a natural far infrared functional mattress with antibacterial and acarid-removing functions as claimed in claim 1, wherein the mass ratio of the fine wula sedge fibers to the collodion cotton in the first step is 14: 5.
4. The method for preparing a mattress with natural far infrared functions of antibiosis and mite killing according to claim 1, wherein the mass ratio of the Meyer sedge fine fibers to the ES fibers in the first step is 14: 1.
5. The method for preparing a natural far infrared functional mattress with antibacterial and acarid removing effects as claimed in claim 1, wherein the activated carbon fiber cloth in step three is woven or non-woven fabric.
6. The method for preparing a natural far infrared functional mattress with antibacterial and acarid removing effects as claimed in claim 1, wherein the industrial hemp fiber cloth in step three is woven or non-woven fabric.
7. The method for preparing a natural far infrared functional mattress with antibacterial and acarid-removing functions as claimed in claim 1 or 6, characterized in that the content of the industrial hemp fiber in the industrial hemp fiber cloth is 35% -100%.
8. The method for preparing a natural far infrared functional mattress with antibacterial and acarid removing effects as claimed in claim 1, wherein the composite industrial hemp fiber cloth quilted with activated carbon fiber cloth in the third step is used as a surface layer and the activated carbon fiber cloth is used as an inner layer.