CN110527288A - A kind of high temperature resistant nylon automotive material - Google Patents
A kind of high temperature resistant nylon automotive material Download PDFInfo
- Publication number
- CN110527288A CN110527288A CN201910972880.1A CN201910972880A CN110527288A CN 110527288 A CN110527288 A CN 110527288A CN 201910972880 A CN201910972880 A CN 201910972880A CN 110527288 A CN110527288 A CN 110527288A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- temperature resistant
- resistant nylon
- automotive material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistant nylon automotive materials, part by weight, constitutive material include: 55~80 parts of polyamide, 30~50 parts of ABS, 20~45 parts of expansible graphite fiber, 0.1~1.2 part of antioxidant, 10~20 parts of compatilizer, 5~8 parts of toughener.Compared with prior art, product of the present invention has taken into account the high temperature resistant type and waterproof performance of nylon material, while also using a large amount of existing mature technologies, thus this product can be widely applied to automobile plastic manufacture field.
Description
Technical field
The present invention relates to automobile plastic manufacture field, in particular to a kind of high temperature resistant nylon automotive materials.
Background technique
Polyamide polymer, such as nylon 6, nylon66 fiber have mechanical strength, wearability and self-lubrication, therefore this
Class material is widely used in the fields such as building, power electronics and automobile.But as a kind of organic matter, polyamide material has
Inborn defect, such as under high temperature environment, performance has significant decline, while polyamide material has certain water suction
Property, these all to bringing many troubles in actual use, thus a large amount of company carries out various change to polyamide material
Into.
A kind of high-intensitive modified plastics of automobile plastic that Chinese invention patent authorization public CN106046766B is proposed,
This kind of plastics improve the intensity of nylon material, high temperature resistant type, while also achieving lightweight；Chinese invention patent authorization is public
A kind of automobile connector nylon PA12 composite material for high glaze that number CN103588937B is proposed, this kind of material lift Buddhist nun
The glossiness and lubricity of imperial material.Although the above patent of invention improves certain performances of nylon material, but it is to automobile
The high temperature resistance and waterproof performance of nylon material fail to propose a kind of effective technological means.
Summary of the invention
To solve the above technical problem, the present invention provides a kind of high temperature resistant nylon automotive material, the high temperature resistant nylons
Automotive material includes following component:
Further, the polyamide is PA6.
Further, the ABS is high temperature resistant type ABS.
Further, 0.3~0.5mm of the expansible graphite fibre diameter.
Further, the antioxidant is Brueggemann antioxidant.
Further, the compatilizer is compatilizer 1033.
Further, the toughener is toughener NG7002.
Further, 55 parts of the PA6,30 parts of the high temperature resistant type ABS, 20 parts of the expansible graphite fiber, institute
State 0.1 part of Brueggemann antioxidant, 1,033 10 parts of the compatilizer, 5 parts of the toughener NG7002.
Further, 67.5 parts of the PA6,40 parts of the high temperature resistant type ABS, the expansible graphite fiber 32.5
Part, 0.65 part of the Brueggemann antioxidant, 1,033 15 parts of the compatilizer, 6.5 parts of the toughener NG7002.
Further, 80 parts of the PA6,50 parts of the high temperature resistant type ABS, 45 parts of the expansible graphite fiber, institute
State 1.2 parts of Brueggemann antioxidant, 1,033 20 parts of the compatilizer, 8 parts of the toughener NG7002.
Specific embodiment
The present invention is described in further details below in conjunction with embodiment, but it is to be understood that, in following embodiment
Related number, scientific and technical terminology and process etc. are intended merely to preferably describe to explain the content of present invention, not
It is to limit the present invention, protection scope of the present invention is not limited only to this.
Embodiment one
The high temperature resistant nylon automotive material of the present embodiment, Ingredients Weight meter part are as follows: 55 parts of PA6, high temperature resistant type ABS
30 parts, 20 parts of expansible graphite fiber, 0.1 part of Brueggemann antioxidant, 1,033 10 parts of compatilizer, 5 parts of toughener NG7002.
Embodiment two
The high temperature resistant nylon automotive material of the present embodiment, Ingredients Weight meter part are as follows: 67.5 parts of PA6, high temperature resistant type
40 parts of ABS, 32.5 parts of expansible graphite fiber, 0.65 part of Brueggemann antioxidant, 1,033 15 parts of compatilizer, toughener
NG70026.5 parts.
Embodiment three
The high temperature resistant nylon automotive material of the present embodiment, Ingredients Weight meter part are as follows: 80 parts of PA6, high temperature resistant type ABS
50 parts, 45 parts of expansible graphite fiber, 1.2 parts of Brueggemann antioxidant, 1,033 20 parts of compatilizer, 8 parts of toughener NG7002.
The above is all a specific embodiment of the invention, any without creativeness in claim of the invention
The variations and alternatives of labour belong in protection scope of the present invention.
Claims (10)
1. a kind of high temperature resistant nylon automotive material, by weight part, it is characterised in that: the high temperature resistant nylon automotive material includes
Following component:
。
2. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the polyamide is PA6.
3. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the ABS is high temperature resistant type
ABS。
4. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the expansible graphite fiber is straight
0.3~0.5mm of diameter.
5. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the antioxidant is Brueggemann
Antioxidant.
6. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the compatilizer is compatilizer
1033。
7. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the toughener is toughener
NG7002。
8. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: 55 parts of the polyamide,
30 parts of the ABS, 20 parts of the expansible graphite fiber, 0.1 part of the antioxidant, 10 parts of the compatilizer, the toughener
5 parts.
9. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: the polyamide 67.5
Part, 40 parts of the ABS, 32.5 parts of the expansible graphite fiber, 0.65 part of the antioxidant, 15 parts of the compatilizer are described
6.5 parts of toughener.
10. a kind of high temperature resistant nylon automotive material as described in claim 1, it is characterised in that: 80 parts of the polyamide,
50 parts of the ABS, 45 parts of the expansible graphite fiber, 1.2 parts of the antioxidant, 20 parts of the compatilizer, the toughener
8 parts.