CN110372999A - A kind of glass fibre reinforced composion and production technology - Google Patents
A kind of glass fibre reinforced composion and production technology Download PDFInfo
- Publication number
- CN110372999A CN110372999A CN201910714663.2A CN201910714663A CN110372999A CN 110372999 A CN110372999 A CN 110372999A CN 201910714663 A CN201910714663 A CN 201910714663A CN 110372999 A CN110372999 A CN 110372999A
- Authority
- CN
- China
- Prior art keywords
- glass fibre
- fibre reinforced
- reinforced composion
- resin
- unsaturated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glass fibre reinforced composions, including glass fibre, unsaturated-resin, curing agent, promotor, lubricant and release agent.The invention also discloses a kind of production technology of glass fibre reinforced composion, key step includes: the dry pretreatment of (1) glass fibre;(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are thoroughly mixed in proportion and are configured to infiltration solution;(3) glass fibre is sufficiently infiltrated in infiltration solution;(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into the glass fibre reinforced composion product of specific structure at a certain temperature.Glass fibre reinforced composion production technology curing time provided by the invention is short, low energy consumption, and composite material obtained has many advantages, such as that tensile strength is high, temperature resistance energy is excellent, can be used for the fields such as traffic isolating and protecting column or bumper.
Description
Technical field
The present invention relates to glass fibre reinforced composion field, specially a kind of glass fibre reinforced composion and life
Production. art.
Background technique
Glass fibre is a kind of inorganic non-metallic material haveing excellent performance, and has that good insulating, heat resistance be strong, mechanical strength
The advantages that high, but there is also property is crisp, the poor disadvantage of wearability.It usually require with other materials carry out composite strengthening, such as with
Resin matrix progress is compound to obtain fiberglass reinforced plastics.This composite material has had both the high intensity and plastics of glass fibre
The toughness of matrix can replace steel manufacture machine components and automobile, ship housing etc..
Glass fibre reinforced composion is usually taken is kneaded glass fibre after double screw extruder melts with resin,
Extrusion obtains mixture, and mixture produces to obtain corresponding product again through processing and forming, and there are glass fibres for this production method
Low with resin material compatibility, the problem of dispersing uniformity difference, the performance for directly resulting in composite material is unstable.
Summary of the invention
In order to solve the deficiencies in the prior art, the purpose of the invention is to provide a kind of glass fiber reinforced composite materials
Material and production technology, this method is simple and easy, and curing time is short, low energy consumption, and composite material obtained has tensile strength
Feature high, temperature resistance energy is excellent.
To achieve the goals above, the invention adopts the following technical scheme:
A kind of glass fibre reinforced composion, it is prepared from the following raw materials in parts by weight:
Further, the unsaturated-resin is one of epoxy resin, unsaturated polyester resin, phenolic resin, two
Kind is a variety of.
Further, the curing agent be one of vinyl triamine, aminoethyl piperazine, diaminodiphenyl-methane,
Two or more.
Further, the promotor is one of triethanolamine, triethylene diamine, n,N-Dimethylaniline, two kinds
Or it is a variety of.
Further, the lubricant is one of wax powder, talcum powder, clay, two kinds or more of.
Further, the release agent is one of glycerol, stearic acid, butyl stearate, two kinds or more of.
The invention also includes a kind of glass fibre reinforced composion production technologies, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Compared with prior art, the present invention having the following advantages that and effect:
1, raw material melting mixing reshaping technique is compared, this method simple process, curing time is short, low energy consumption, symbol
Close the requirement of energy conservation and environmental protection, clean manufacturing.
2, the glass fibre reinforced composion that this technique obtains combines glass fiber strength height and resin material toughness
Good advantage, obtained composite property consistency are good.
Specific embodiment
By embodiment in detail below and application example analysis, the invention will be further described.Specific descriptions below
It is to understand the present invention for the ease of other people, the protection scope being not intended to limit the invention.
Embodiment 1:
A kind of glass fibre reinforced composion, it is made of the raw material of following dry weight number:
Preferably, the unsaturated-resin is epoxy resin;The curing agent is vinyl triamine;The promotor is three
Ethanol amine;The lubricant is wax powder;The release agent is stearic acid.
A kind of glass fibre reinforced composion production technology, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Embodiment 2:
A kind of glass fibre reinforced composion, it is made of the raw material of following dry weight number:
Preferably, the unsaturated-resin is epoxy resin;The curing agent is vinyl triamine;The promotor is three
Ethanol amine;The lubricant is wax powder;The release agent is stearic acid.
A kind of glass fibre reinforced composion production technology, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Embodiment 3:
A kind of glass fibre reinforced composion, it is made of the raw material of following dry weight number:
Preferably, the unsaturated-resin is epoxy resin;The curing agent is vinyl triamine;The promotor is three
Ethanol amine;The lubricant is wax powder;The release agent is stearic acid.
A kind of glass fibre reinforced composion production technology, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Embodiment 4:
A kind of glass fibre reinforced composion, it is made of the raw material of following dry weight number:
Preferably, the unsaturated-resin is epoxy resin;The curing agent is vinyl triamine;The promotor is three
Ethanol amine;The lubricant is wax powder;The release agent is stearic acid.
A kind of glass fibre reinforced composion production technology, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Embodiment 5:
A kind of glass fibre reinforced composion, it is made of the raw material of following dry weight number:
Preferably, the unsaturated-resin is epoxy resin;The curing agent is vinyl triamine;The promotor is three
Ethanol amine;The lubricant is wax powder;The release agent is stearic acid.
A kind of glass fibre reinforced composion production technology, the steps include:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltrate
Solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific at a certain temperature
The glass fibre reinforced composion product of structure.
Further to test the property using the glass fibre reinforced composion that formula and method obtain described in each embodiment
Can, it takes the sheet-like article of 10mm thickness to carry out the test of tensile strength, heat resistance to it, is made with the fiberglass products of same specification
For comparison, test result such as table 1.
Table 1
From test data as can be seen that non-reinforced glass fiber material shows as strong and crisp, it is unfavorable for practical application, adopts
The glass fibre reinforced composion tensile strength obtained with production technology of the present invention is high and toughness is obviously improved,
Its heat resistance is wider simultaneously, can be applied to traffic isolating and protecting column, bumper or other part fields.
Those skilled in the art is it will be clearly understood that above preferred embodiment only illustrates of the invention, not structure
At limitation of the present invention.Various variations and equivalence replacement are carried out to technical solution of the present invention, without departing from the technology of the present invention
The principle and range of scheme, should all cover within the scope of the invention.
Claims (7)
1. a kind of glass fibre reinforced composion, it is prepared from the following raw materials in parts by weight:
2. a kind of glass fibre reinforced composion according to claim 1, it is characterised in that: the unsaturated-resin is
One of epoxy resin, unsaturated polyester resin, phenolic resin, two or more.
3. a kind of glass fibre reinforced composion according to claim 1, it is characterised in that: the curing agent is ethylene
One of base triamine, aminoethyl piperazine, diaminodiphenyl-methane, two or more.
4. a kind of glass fibre reinforced composion according to claim 1, it is characterised in that: the promotor is three second
Hydramine, triethylene diamine, N, one of accelerine, two or more.
5. a kind of glass fibre reinforced composion according to claim 1, it is characterised in that: the lubricant is wax
It is one of powder, talcum powder, clay, two kinds or more of.
6. a kind of glass fibre reinforced composion according to claim 1, it is characterised in that: the release agent is sweet
It is one of oil, stearic acid, butyl stearate, two kinds or more of.
7. a kind of production technology of glass fibre reinforced composion described in claim 1, has main steps that:
(1) the dry pretreatment of glass fibre;
(2) unsaturated-resin, curing agent, promotor, lubricant and release agent are sufficiently mixed in proportion and are configured to infiltration solution;
(3) glass fibre is led and is sufficiently infiltrated in infiltration solution;
(4) glass fibre sufficiently after infiltration is led into mold, and solidifying and setting, that is, can be made into specific structure at a certain temperature
Glass fibre reinforced composion product.