CN110526233A - A kind of device and preparation method for quickly producing graphene crystal - Google Patents
A kind of device and preparation method for quickly producing graphene crystal Download PDFInfo
- Publication number
- CN110526233A CN110526233A CN201910771326.7A CN201910771326A CN110526233A CN 110526233 A CN110526233 A CN 110526233A CN 201910771326 A CN201910771326 A CN 201910771326A CN 110526233 A CN110526233 A CN 110526233A
- Authority
- CN
- China
- Prior art keywords
- graphite
- glass plate
- motor
- driving rack
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of device and preparation method for quickly producing graphene crystal, it be take 64% graphite powder be added 36% clay powder, it is uniformly mixed, prepare a roll shaft again, then uniformly mixed graphite powder is pressed into cylindrical graphite roller around roll shaft, one piece of glass plate cut out is placed above in glass base again, left bearing and right bearing are set up in the two sides of graphite roller with driving rack, with the movement of driving rack, when graphite roller is rolled to the other end from one end of glass plate, a small amount of graphite powder is just had to be sticked to above glass plate, in these a small amount of graphite powders, some is exactly the graphene of layer less, some is exactly the graphene of single layer.
Description
Technical field
The present invention relates to a kind of devices and preparation method for quickly producing graphene crystal.
Background technique
Graphene be one kind by carbon atom with sp2Hybridized orbit forms the Two-dimensional Carbon nanometer material that hexangle type is in honeycomb lattice
Material, it optics, electricity, mechanics, materialogy, micro-nano technology, the energy, in terms of play an important role.Currently,
There are many kinds of the existing methods for producing graphene, wherein common method has mechanical stripping method, oxidation-reduction method, epitaxial growth
Method, chemical vapour deposition technique in these methods, there is that the production cost is very high, and user can not receive for product price, some production
Complex process, it is not easy to operate, the pollution that some generates in process of production is too big, and is shown using the above method
A common feature be the graphene produced quality it is undesirable, be not able to satisfy requirement.
Summary of the invention
To overcome in existing situation, in common production method, there is that the production cost is very high, product price allows user can not
Receive, some production technologies are complicated, it is not easy to operate, the pollution that some generates in process of production is too big, and more than use
The common feature that these methods are shown is that the quality for the graphene produced is undesirable, is not able to satisfy requirement
Deficiency, the present invention provides a kind of devices and preparation method for quickly producing graphene crystal, its operating process is easy, technique letter
Single, production cost is low, and production process is pollution-free.
The technical solution adopted by the present invention to solve the technical problems is: taking the clay of 64% graphite powder addition 36%
Powder is uniformly mixed, then prepares a roll shaft, and uniformly mixed graphite powder is then pressed into cylindrical graphite around roll shaft
Roller, a then pedestal is arranged, the both ends of pedestal are respectively set left support and right support, and left support upper end is arranged sliding rail, on sliding rail
Left bearing is set, and right bearing is arranged in right support upper end, then in submounts setting electric machine support and support spring, electric machine support
Motor and motor shaft are installed, has attaching plug on motor, glass base is installed, glass base is placed above one above support spring
The glass plate that block is cut out, then driving gear is installed on motor shaft, driving rack is installed in one end of roll shaft, then with transmission
Left bearing and right bearing are set up in the two sides of the graphite roller of rack gear, are attached to graphite roller tightly on following glass plate, are ready to it
Afterwards, power on, motor rotation, motor and motor shaft drive driving gear rotation, and driving gear drives driving rack to move back
It is dynamic, with the movement of driving rack, be fixed on the graphite roller above driving rack also on following glass plate back and forth
It is mobile, when graphite roller is rolled to the other end from one end of glass plate, just has a small amount of graphite powder and be sticked to above glass plate, this
In a little a small amount of graphite powders, some is exactly the graphene of layer less, and some is exactly the graphene of single layer.
The invention has the advantages that keeping the technique for producing graphene simpler, cost is reduced, and the economy for reducing user is negative
Load.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is the sectional front view of graphite roller in the present invention.
Fig. 2 is the sectional view of Fig. 1.
Fig. 3 is that apparatus of the present invention face structural map.
Fig. 4 is the top view of Fig. 3.
Fig. 5 is the right view of Fig. 4.
1. graphite powder in figure, 2. graphite rollers, 3. roll shafts, 4. left bearings, 5. driving racks, 6. driving gears, 7. right bearings,
8. right support, 9. motors and motor shaft, 10. electric machine supports, 11. pedestals, 12. support springs, 13. glass bases, 14. glass
Plate, 15. left supports, 16. sliding rails, 17. attaching plugs.
Specific embodiment
In Fig. 1, the clay powder of 64% addition of graphite powder 1 36% is taken, is uniformly mixed, then prepare a roll shaft 3, then
Uniformly mixed graphite powder 1 is pressed into cylindrical graphite roller 2 around roll shaft 3.
It is the stone as made of the clay powder compacting of 64% addition of graphite powder 1 36% around the outside of roll shaft 3 in Fig. 2
Ink roller 2.
In Fig. 3, a pedestal 11 is set, left support 15 and right support 8, left support 15 is respectively set in the both ends of pedestal 11
Sliding rail 16 is arranged in upper end, and left bearing 4 is arranged on sliding rail 16, and right bearing 7 is arranged in 8 upper end of right support, then face is arranged on the pedestal 11
Electric machine support 10 and support spring 12 install motor and motor shaft 9 on electric machine support 10, have attaching plug 17 on motor, support
Spring 12 installs glass base 13 above, and one piece of glass plate cut out 14 is placed above in glass base 13, then pacifies on motor shaft
Driving gear 6 is filled, driving rack 5 is installed in one end of roll shaft 3, then a left side is set up in the two sides of the graphite roller 2 with driving rack 5
Bearing 4 and right bearing 7 are attached to graphite roller 2 tightly on following glass plate 14, after being ready to, power on, and motor turns
Dynamic, motor and motor shaft 9 drive driving gear 6 to rotate, and driving gear 6 drives driving rack 5 to move back and forth, with driving rack
5 movement, the graphite roller 2 being fixed on above driving rack 5 moves back and forth also on following glass plate 14, in graphite
It when roller 2 is rolled to the other end from one end of glass plate 14, just has a small amount of graphite powder and is sticked to above glass plate 14, these are a small amount of
Graphite powder in, some be exactly less layer graphene, some is exactly the graphene of single layer.
In 4 figures, one piece of glass plate cut out 14 is placed above in glass base, then driving gear is installed on motor shaft,
Driving rack 5 is installed in one end of roll shaft 3, then left bearing 4 and right axle are set up in the two sides of the graphite roller 2 with driving rack 5
7 are held, graphite roller 2 is attached to tightly on following glass plate 14, after being ready to, powers on, motor rotates, motor and motor
Axis drives driving gear rotation, and driving gear drives driving rack 5 to move back and forth, with the movement of driving rack 5, is fixed on biography
Graphite roller 2 above carry-over bar 5 moves back and forth also on following glass plate 14, in graphite roller 2 from glass plate 14
It when one end is rolled to the other end, just has a small amount of graphite powder and is sticked to above glass plate 14, in these a small amount of graphite powders, have
It is exactly the graphene of layer less, some is exactly the graphene of single layer.
In Fig. 5, motor and motor shaft 9 drive driving gear 6 to rotate, and driving gear 6 drives driving rack 5 to move back
It is dynamic, with the movement of driving rack 5, the graphite roller 2 above driving rack 5 is fixed on also on following glass plate 14
Move back and forth, when graphite roller 2 is rolled to the other end from one end of glass plate 14, just has a small amount of graphite powder and be sticked to glass plate
Above 14, in these a small amount of graphite powders, some is exactly the graphene of layer less, and some is exactly the graphene of single layer.
Claims (1)
1. one kind quickly produces the device and preparation method of graphene crystal, it is characterized in that: 64% graphite powder is taken to be added 36%
Clay powder, be uniformly mixed, then prepare a roll shaft, uniformly mixed graphite powder is then pressed into cylinder around roll shaft
Graphite roller, then a pedestal is set, left support and right support is respectively set in the both ends of pedestal, and sliding rail is arranged in left support upper end,
Left bearing is set on sliding rail, and right bearing is arranged in right support upper end, then electric machine support and support spring, motor is arranged in submounts
Motor and motor shaft are installed on bracket, have attaching plug on motor, glass base is installed above support spring, above glass base
One piece of glass plate cut out is placed, then driving gear is installed on motor shaft, driving rack is installed in one end of roll shaft, then band
There are the two sides of the graphite roller of driving rack to set up left bearing and right bearing, is attached to graphite roller tightly on following glass plate, it is quasi-
After getting ready, power on, motor rotation, motor and motor shaft drive driving gear rotation, and driving gear drives driving rack
Move back and forth, with the movement of driving rack, is fixed on the graphite roller above driving rack also on following glass plate
Face moves back and forth, and when graphite roller is rolled to the other end from one end of glass plate, just has a small amount of graphite powder and is sticked to glass plate
Above, in these a small amount of graphite powders, some is exactly the graphene of layer less, and some is exactly the graphene of single layer.