CN110511502A - Toughened PVC composite material - Google Patents
Toughened PVC composite material Download PDFInfo
- Publication number
- CN110511502A CN110511502A CN201810492050.4A CN201810492050A CN110511502A CN 110511502 A CN110511502 A CN 110511502A CN 201810492050 A CN201810492050 A CN 201810492050A CN 110511502 A CN110511502 A CN 110511502A
- Authority
- CN
- China
- Prior art keywords
- particle
- calcium carbonate
- pvc composite
- composite material
- compatilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of toughened PVC composite materials, including plastics, compatilizer, lubricant, toughener, the weight proportion of each component are as follows: plastics 70~75%, compatilizer 8~11%, lubricant 7~8%, toughener 2~4%, inorganic glass fiber 4~10%;Further improvement lies in that: it further include montmorillonite particle, calcium carbonate particle, the montmorillonite particle, calcium carbonate particle proportion are 3~5%;Montmorillonite particle, calcium carbonate particle are handled using silane.Good toughness of the present invention, shock resistance, manufacturing expense are low.
Description
Technical field
The present invention relates to a kind of polymer composite, especially a kind of PVC composite material.
Background technique
PVC composite material has the characteristics that corrosion-resistant, light, but toughness is not high, is not able to satisfy the needs in high tenacity place.
Summary of the invention
In view of the deficiencies of the prior art, the present invention proposes a kind of toughened PVC composite materials that can significantly improve toughness.
The present invention is achieved through the following technical solutions technical goal.
Toughened PVC composite material, including plastics, compatilizer, lubricant, toughener, the weight proportion of each component are as follows: modeling
Material 70~75%, compatilizer 8~11%, lubricant 7~8%, toughener 2~4%;It is theed improvement is that: further including inorganic
Glass fibre, matching is 4~10%.
Further improvement lies in that: it further include montmorillonite particle, calcium carbonate particle, the montmorillonite particle, calcium carbonate particle
Proportion is 3~5%.
Further improvement lies in that: the montmorillonite particle, calcium carbonate particle are handled using silane.
Compared with prior art, the present invention having the positive effect that:
1, inorganic glass fiber is added, toughness of the present invention is significantly improved.
2, montmorillonite particle, calcium carbonate particle is added, improves present invention stretching, shock resistance;On the other hand, calcium carbonate
Particle price is lower, significantly reduces manufacturing expense of the invention.
3, montmorillonite particle, calcium carbonate particle are handled using silane, further increase mechanical property of the present invention.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1:
Toughened PVC composite material, including plastics, compatilizer, lubricant, toughener, the weight proportion of each component are as follows: plastics 70
~75%, compatilizer 8~11%, lubricant 7~8%, toughener 2~4%, inorganic glass fiber 4~10%.
Embodiment 2:
Toughened PVC composite material, including plastics, compatilizer, lubricant, toughener, the weight proportion of each component are as follows: plastics 70
~75%, compatilizer 8~11%, lubricant 7~8%, toughener 2~4%, inorganic glass fiber 4~10%, montmorillonite grain
Son, calcium carbonate particle 3~5%, in the present embodiment, montmorillonite particle, calcium carbonate particle are handled using silane.
Claims (3)
1. a kind of toughened PVC composite material, including plastics, compatilizer, lubricant, toughener, the weight proportion of each component are as follows:
Plastics 70~75%, compatilizer 8~11%, lubricant 7~8%, toughener 2~4%;It is characterized by also including inorganic glass
Glass fiber, matching is 4~10%.
2. toughened PVC composite material according to claim 1, it is characterised in that: further include montmorillonite particle, calcium carbonate
Particle, the montmorillonite particle, calcium carbonate particle proportion are 3~5%.
3. toughened PVC composite material according to claim 2, it is characterised in that: the montmorillonite particle, carbonic acid calcium grain
Son is handled using silane.