CN110496759A - A kind of rustless steel container surface treatment method with laser light color effect - Google Patents
A kind of rustless steel container surface treatment method with laser light color effect Download PDFInfo
- Publication number
- CN110496759A CN110496759A CN201910756944.4A CN201910756944A CN110496759A CN 110496759 A CN110496759 A CN 110496759A CN 201910756944 A CN201910756944 A CN 201910756944A CN 110496759 A CN110496759 A CN 110496759A
- Authority
- CN
- China
- Prior art keywords
- steel container
- rustless steel
- radium
- shine
- container surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of rustless steel container surface treatment methods with laser light color effect, comprising the following steps: a. takes rustless steel container, is surface-treated to the rustless steel container;B. transparent colored acrylic resin paint A is made;C. it takes transparent colored acrylic resin paint A to carry out aerial spraying operation to the surface of rustless steel container, forms the color layers of light;D. radium-shine honorable film is decomposed;E. the pattern of radium-shine honorable film is transferred in rustless steel container surface, forms radium-shine colored design layer;F. the acrylic resin paint B of transparent light is made;G. it takes the acrylic resin paint B of transparent light to carry out aerial spraying operation to the radium-shine colored design layer on rustless steel container, forms laser light coloured picture case, complete the surface treatment of rustless steel container.By above step, laser light coloured picture case finally can be formed on the surface of rustless steel container, can preferably meet people's lives demand.
Description
Technical field
The present invention relates to rustless steel container surface treatment method more particularly to a kind of stainless steel appearances with laser light color effect
Device surface treatment method.
Background technique
For at present rustless steel container surface treatment technique for, traditional lacquer spraying technique is to apply acrylic resin
Material is by dilution dilution agent, then carries out spraying operation with traditional spray gun, and the pattern handled out is simple, and color is dull, Bu Nengman
Demand of the sufficient consumer to fashion color needs to make this improvement.
Summary of the invention
The present invention is lacked for the simple, dull coloring of pattern etc. that existing lacquer spraying technique existing in the prior art is handled out
It falls into, provides a kind of new rustless steel container surface treatment method with laser light color effect.
In order to solve the above-mentioned technical problem, the invention is realized by the following technical scheme:
A kind of rustless steel container surface treatment method with laser light color effect, comprising the following steps:
A. rustless steel container is taken, the rustless steel container is surface-treated;
B. the component of following weight proportion is weighed:
50 parts of acrylic resin,
Colored colorant 5-50 parts,
4-50 parts of filler,
The component matched above is thoroughly mixed, transparent colored acrylic resin paint A is made;
C. transparent colored acrylic resin paint A is taken to carry out aerial spraying operation to the surface of rustless steel container, wherein pressing
Contracting air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-0.25mpa,
The color coating that film thickness is 15-20um is formed on rustless steel container surface after spraying, the color coating is solidified, is solidified
Temperature is 90-100 DEG C, curing time 10-20min, to form the color layers of light on rustless steel container surface;
D. it takes radium-shine honorable film to be put into curved draped stream film device, and sprays activator in radium-shine honorable film surface, wherein compressing
Air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-0.25mpa, spray
Radium-shine brilliance film decomposes under the action of activator after painting, and the pattern of radium-shine brilliance film is swum on the water surface;
E. step of learning from else's experience c treated rustless steel container is simultaneously fixed with fixture, and fixture control rustless steel container carries out on the water surface
Transfer is rolled, so that the pattern of radium-shine brilliance film is transferred in rustless steel container surface, it is described not with clear water flushing after the completion of transfer
Become rusty steel container surface, then toasted, baking temperature be 120-130 DEG C, baking time 10-20min, thus it is described not
The surface of rust steel container forms radium-shine colored design layer;
F. the component of following weight proportion is weighed:
0.8-1.0 parts of acrylic acid AA,
20.0-24.0 parts of n-butyl acrylate,
8.0-10.0 parts of acrylic acid-2-ethyl ethyl ester,
8.0-10.0 parts of 2-hydroxypropyl acrylate,
30.0-36.0 parts of ethyl methacrylate,
10.0-12.0 parts of n-BMA,
20.0-24.0 parts of styrene,
3.2-6.4 parts of propylene acrylic fibers,
The component matched above is thoroughly mixed, the acrylic resin paint B of transparent light is made;
G. the acrylic resin paint B of transparent light is taken to carry out aerial spraying work to the radium-shine colored design layer on rustless steel container
Industry, wherein compressed air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-
0.25mpa forms film thickness for the light coating of 20-30um and to the light coating in radium-shine multicolour pattern layer surface after spraying
Solidification baking is carried out, solidification temperature is 150-160 DEG C, curing time 10-20min, thus in the surface shape of rustless steel container
At laser light coloured picture case, the surface treatment of rustless steel container is completed.
Step a is surface-treated the greasy dirt etc. that can remove rustless steel container surface to rustless steel container, guarantees subsequent
When spraying operation, acrylic resin paint A can be firmly adhered to rustless steel container surface.
Step b selects transparent colored acrylic resin paint A made of the above ratio, can be closely adhered on not
Rust steel container surface forms the color layers of light on the surface of rustless steel container, while guaranteeing the color layers and stainless steel of light
The compactness of vessel surface connection, wherein acrylic resin has excellent adhesion, tensile strength, tearing toughness, high-quality
Wearability, water resistance, impact resistance, oil resistivity so that the color layers of light and rustless steel container surface and radium-shine colour
Pattern layer links together well, and colored colorant makes acrylic resin paint A show color, to promote acrylic acid
Apparent after cold coating A spraying, colored colorant is the GMX-15-SQ model face of Ciba (China) Co., Ltd
Material, filler play skeleton, filling effect in acrylic resin paint A, can increase coating thickness, keep film plentiful solid, together
When can also adjust the rheological property of acrylic resin paint A, such as thickening, anti-precipitating are filled out so as to improve the mechanical strength of paint film
Material can also improve wearability and durability, adjust the optical property of acrylic resin paint A, film is enable effectively to stop light
Line penetrates, and improves its weatherability, extends the service life of film, and filler chemically can also help out to film, rises
To the effect for enhancing antirust, moisture-resistant, anti-flammability, filler can reduce acrylic resin dosage, reduce production cost.
The transparent colored acrylic resin paint A that step b is obtained is sprayed on stainless steel by spraying operation by step c to be held
Device surface, wherein rustless steel container surface itself has color, has background color layer, and acrylic resin paint A passes through spraying operation
The color layers of light are formed in rustless steel container background color layer surface, so that rustless steel container surface shows colour, are promoted
Product is apparent, wherein the air pressure sprayed is selected as the above numberical range, acrylic resin paint A can be made to be sprayed on stainless
Reach the dispersibility of ideal coating when steel container surface, compressed air pressure, atomizing pressure, shaping air pressure be selected as with
Upper numberical range can allow acrylic resin paint A to reach ideal atomizing effect in spraying, so that acrylic resin paint
Coating is more uniform when A is sprayed on rustless steel container surface, and coating forms film thickness on rustless steel container surface after spraying and is
The color coating of 15-20um, and according to the solidification baking temperature of the above numberical range and solidification baking time to color coating into
Row solidification can form the color layers of light on the surface of rustless steel container after acrylic resin paint A solidifies baking.
Step d is for decomposing radium-shine honorable film, so that the pattern of radium-shine brilliance film is swum on the water surface, convenient for subsequent by radium
It penetrates honorable film and is transferred to rustless steel container surface.
Step e is used to the pattern of radium-shine honorable film being transferred to rustless steel container surface, rinses and holds for removing stainless steel
Remaining radium-shine honorable film on device surface, and will be radium-shine according to the solidification baking temperature of the above numberical range and solidification baking time
The pattern of honorable film is fixed on rustless steel container surface, solidifies baking by the pattern to radium-shine honorable film, in rustless steel container
The color layer surface of light form radium-shine colored design layer, improve the apparent of rustless steel container.
Step f selects the acrylic resin paint B of transparent light made of the above ratio can be in radium-shine colored design layer
It is upper to form radium-shine brilliance, while guaranteeing the compactness that the pattern of radium-shine honorable film is connect with rustless steel container surface, acrylic acid tree
Rouge is this kind of coating of the synthetic resin coating of main film forming substance, can be cut with scissors by radium-shine colored design layer and light coating
Chain, have the characteristics that color is shallow, transparency is high, light is plentiful, it is weather-proof, protect that color, to protect light, adhesive force strong, corrosion-resistant, hard, flexible.
Step g is used to form laser light coloured picture case in radium-shine multicolour pattern layer surface, and further promotion product is apparent, wherein
Compressed air pressure, atomizing pressure, shaping air pressure are selected as the above numberical range, and acrylic resin paint B can be allowed to exist
Reach ideal atomizing effect when spraying, so that spraying is more uniform, coating is formed after spraying on rustless steel container surface
Film thickness is the light coating of 20-30um, and after carrying out solidification baking to the light coating, is formed on the surface of rustless steel container
Laser light coloured picture case.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
Colored colorant is silver color or black in rapid b.
Colored colorant is silver color or black, can form the silver color layer or light of light on rustless steel container surface
Black layer can cover the background color layer on rustless steel container surface, promote the aesthetics of rustless steel container surface color.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
Clear water flushing pressure is 1.5 ㎏, washing time 10min in rapid e.
Clear water flushing pressure and washing time are set as the above numerical value, can wash away the radium remained on surface of rustless steel container
Honorable film is penetrated, while avoiding damage to the pattern for being transferred to rustless steel container surface, and by solidifying baking for radium-shine honorable film
Pattern is fixed on rustless steel container surface.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
Fixture in rapid e is manipulator.
Manipulator can be improved the stability of clamping rustless steel container, while convenient for the velocity of rotation of control rustless steel container
Consistency, so that the pattern of radium-shine honorable film is completely transferred to rustless steel container surface.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
Surface treatment in rapid a the following steps are included:
A1. wire drawing, fine polishing light processing are carried out to rustless steel container surface, the dirt for removing rustless steel container surface is then taken turns with cotton
Stain;
A2. the rustless steel container is fixed, and drifting dust wiping, dedusting operation are carried out to rustless steel container surface.
Wire drawing process can form imperceptible convex-concave effect on rustless steel container surface, promote rustless steel container surface
Apparently, while also the adhesive force that can further promote rustless steel container surface, allow subsequent spraying acrylic resin paint A,
Acrylic resin paint B can adhere better to rustless steel container surface.Polishing treatment can allow after wire drawing process not
Rust steel container surface is more smooth, removes the burr generated after wire drawing process.And to rustless steel container surface carry out drifting dust wiping,
Dedusting operation can remove the dust of rustless steel container surface attachment, guarantee the cleannes on rustless steel container surface, be subsequent
Spraying operation is ready.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
In rapid a1, wire drawing process, then the cotton wheel pair for passing through 1200 mesh are carried out to rustless steel container surface by the emery band of 180 mesh
Rustless steel container surface carries out fine polishing light processing.
Emery band when wire drawing process by 180 mesh, which carries out processing, can play the effect of rough polishing, and at polishing
Cotton wheel when reason by 1200 mesh, which carries out processing, can play the effect of fine polishing, can make stainless steel by the above processing mode
Vessel surface is more smooth clean.
Preferably, a kind of rustless steel container surface treatment method with laser light color effect described above, the step
In rapid a2, the rustless steel container is fixed with conductive fixture, the industrial alcohol for being 98% by purity is to rustless steel container surface
It is wiped, then operation is dusted to rustless steel container surface by ion electrostatic air pressure gun.
The industrial alcohol volatility that purity is 98% or more is fast, does not have water quality residual, can rise to rustless steel container surface
To preferably dust removing effects, ion electrostatic air pressure gun can further remove the dust on rustless steel container surface.
Specific embodiment
Present invention is further described in detail With reference to embodiment, but they are not to limit of the invention
System:
Embodiment 1
A kind of rustless steel container surface treatment method with laser light color effect, comprising the following steps:
A. rustless steel container is taken, the rustless steel container is surface-treated;
B. the component of following weight proportion is weighed:
50 parts of acrylic resin,
5 parts of colored colorant,
4 parts of filler,
The component matched above is thoroughly mixed, transparent colored acrylic resin paint A is made;
C. transparent colored acrylic resin paint A is taken to carry out aerial spraying operation to the surface of rustless steel container, wherein pressing
Contracting air pressure is 2.0kg, and atomization air pressure 0.30mpa, shaping air pressure is 0.15mpa, in stainless steel after spraying
Vessel surface forms the color coating that film thickness is 15um, solidifies to the color coating, and solidification temperature is 90 DEG C, when solidification
Between be 10min, thus rustless steel container surface formed light color layers;
D. it takes radium-shine honorable film to be put into curved draped stream film device, and sprays activator in radium-shine honorable film surface, wherein compressing
Air pressure is 2.0kg, and atomization air pressure 0.30mpa, shaping air pressure is 0.15mpa, radium-shine brilliance film after spraying
It is decomposed under the action of activator, the pattern of radium-shine brilliance film is swum on the water surface;
E. step of learning from else's experience c treated rustless steel container is simultaneously fixed with fixture, and fixture control rustless steel container carries out on the water surface
Transfer is rolled, so that the pattern of radium-shine brilliance film is transferred in rustless steel container surface, it is described not with clear water flushing after the completion of transfer
Rust steel container surface, is then toasted, and baking temperature is 120 DEG C, baking time 10min, to hold in the stainless steel
The surface of device forms radium-shine colored design layer;
F. the component of following weight proportion is weighed:
0.8-1.0 parts of acrylic acid AA,
20.0-24.0 parts of n-butyl acrylate,
8.0-10.0 parts of acrylic acid-2-ethyl ethyl ester,
8.0-10.0 parts of 2-hydroxypropyl acrylate,
30.0-36.0 parts of ethyl methacrylate,
10.0-12.0 parts of n-BMA,
20.0-24.0 parts of styrene,
3.2-6.4 parts of propylene acrylic fibers,
The component matched above is thoroughly mixed, the acrylic resin paint B of transparent light is made;
G. the acrylic resin paint B of transparent light is taken to carry out aerial spraying work to the radium-shine colored design layer on rustless steel container
Industry, wherein compressed air pressure is 2.0kg, and atomization air pressure 0.30mpa, shaping air pressure is 0.15mpa, after spraying
The light coating that film thickness is 20um is formed in radium-shine multicolour pattern layer surface and solidification baking is carried out to the light coating, is solidified
Temperature is 150 DEG C, curing time 10min, to form laser light coloured picture case on the surface of rustless steel container, completes stainless steel
The surface treatment of container.
Wherein filler is a kind of chemical synthesis latex agent containing acrylate, methacrylate, acrylic acid, first in step b
Base acrylic acid and thickener, filler etc., common filler have copper powder, aluminium powder, iron powder, glass putty, iron oxide, chromium oxide,
Ferroso-ferric oxide, zinc oxide, magnesia, calcium oxide, aluminium oxide, calcium carbonate (lightweight) etc., filler ingredient technology condition is as follows:
Preferably, colored colorant is silver color or black in the step b.
Preferably, clear water flushing pressure is 1.5 ㎏, washing time 10min in the step e.
Preferably, the fixture in the step e is manipulator.
Preferably, surface treatment in the step a the following steps are included:
A1. wire drawing, fine polishing light processing are carried out to rustless steel container surface, the dirt for removing rustless steel container surface is then taken turns with cotton
Stain;
A2. the rustless steel container is fixed, and drifting dust wiping, dedusting operation are carried out to rustless steel container surface.
Preferably, being carried out at wire drawing by the emery band of 180 mesh to rustless steel container surface in the step a1
Reason, then fine polishing light processing is carried out to rustless steel container surface by the cotton wheel of 1200 mesh.
It is 98% by purity preferably, fixing the rustless steel container with conductive fixture in the step a2
Industrial alcohol wipes rustless steel container surface, then is dusted work to rustless steel container surface by ion electrostatic air pressure gun
Industry.
Embodiment 2
A kind of rustless steel container surface treatment method with laser light color effect, comprising the following steps:
A. rustless steel container is taken, the rustless steel container is surface-treated;
B. the component of following weight proportion is weighed:
50 parts of acrylic resin,
27. 5 parts of colored colorant,
27 parts of filler,
The component matched above is thoroughly mixed, transparent colored acrylic resin paint A is made;
C. transparent colored acrylic resin paint A is taken to carry out aerial spraying operation to the surface of rustless steel container, wherein pressing
Contracting air pressure is 2.5kg, and atomization air pressure 0.375mpa, shaping air pressure is 0.2mpa, in stainless steel after spraying
Vessel surface forms the color coating that film thickness is 17.5um, solidifies to the color coating, and solidification temperature is 95 DEG C, solidification
Time is 15min, to form the color layers of light on rustless steel container surface;
D. it takes radium-shine honorable film to be put into curved draped stream film device, and sprays activator in radium-shine honorable film surface, wherein compressing
Air pressure is 2.5kg, and atomization air pressure 0.375mpa, shaping air pressure is 0.20mpa, radium-shine brilliance film after spraying
It is decomposed under the action of activator, the pattern of radium-shine brilliance film is swum on the water surface;
E. step of learning from else's experience c treated rustless steel container is simultaneously fixed with fixture, and fixture control rustless steel container carries out on the water surface
Transfer is rolled, so that the pattern of radium-shine brilliance film is transferred in rustless steel container surface, it is described not with clear water flushing after the completion of transfer
Rust steel container surface, is then toasted, and baking temperature is 125 DEG C, baking time 15min, to hold in the stainless steel
The surface of device forms radium-shine colored design layer;
F. the component of following weight proportion is weighed:
0.8-1.0 parts of acrylic acid AA,
20.0-24.0 parts of n-butyl acrylate,
8.0-10.0 parts of acrylic acid-2-ethyl ethyl ester,
8.0-10.0 parts of 2-hydroxypropyl acrylate,
30.0-36.0 parts of ethyl methacrylate,
10.0-12.0 parts of n-BMA,
20.0-24.0 parts of styrene,
3.2-6.4 parts of propylene acrylic fibers,
The component matched above is thoroughly mixed, the acrylic resin paint B of transparent light is made;
G. the acrylic resin paint B of transparent light is taken to carry out aerial spraying work to the radium-shine colored design layer on rustless steel container
Industry, wherein compressed air pressure is 2.5kg, and atomization air pressure 0.375mpa, shaping air pressure is 0.2mpa, after spraying
The light coating that film thickness is 25um is formed in radium-shine multicolour pattern layer surface and solidification baking is carried out to the light coating, is solidified
Temperature is 155 DEG C, curing time 15min, to form laser light coloured picture case on the surface of rustless steel container, completes stainless steel
The surface treatment of container.
Preferably, colored colorant is silver color or black in the step b.
Preferably, clear water flushing pressure is 1.5 ㎏, washing time 10min in the step e.
Preferably, the fixture in the step e is manipulator.
Preferably, surface treatment in the step a the following steps are included:
A1. wire drawing, fine polishing light processing are carried out to rustless steel container surface, the dirt for removing rustless steel container surface is then taken turns with cotton
Stain;
A2. the rustless steel container is fixed, and drifting dust wiping, dedusting operation are carried out to rustless steel container surface.
Preferably, being carried out at wire drawing by the emery band of 180 mesh to rustless steel container surface in the step a1
Reason, then fine polishing light processing is carried out to rustless steel container surface by the cotton wheel of 1200 mesh.
It is 98% by purity preferably, fixing the rustless steel container with conductive fixture in the step a2
Industrial alcohol wipes rustless steel container surface, then is dusted work to rustless steel container surface by ion electrostatic air pressure gun
Industry.
Embodiment 3
A kind of rustless steel container surface treatment method with laser light color effect, comprising the following steps:
A. rustless steel container is taken, the rustless steel container is surface-treated;
B. the component of following weight proportion is weighed:
50 parts of acrylic resin,
50 parts of colored colorant,
50 parts of filler,
The component matched above is thoroughly mixed, transparent colored acrylic resin paint A is made;
C. transparent colored acrylic resin paint A is taken to carry out aerial spraying operation to the surface of rustless steel container, wherein pressing
Contracting air pressure is 3.0kg, and atomization air pressure 0.45mpa, shaping air pressure is 0.25mpa, in stainless steel after spraying
Vessel surface forms the color coating that film thickness is 20um, solidifies to the color coating, and solidification temperature is 100 DEG C, solidification
Time is 20min, to form the color layers of light on rustless steel container surface;
D. it takes radium-shine honorable film to be put into curved draped stream film device, and sprays activator in radium-shine honorable film surface, wherein compressing
Air pressure is 3.0kg, and atomization air pressure 0.45mpa, shaping air pressure is 0.25mpa, radium-shine brilliance film after spraying
It is decomposed under the action of activator, the pattern of radium-shine brilliance film is swum on the water surface;
E. step of learning from else's experience c treated rustless steel container is simultaneously fixed with fixture, and fixture control rustless steel container carries out on the water surface
Transfer is rolled, so that the pattern of radium-shine brilliance film is transferred in rustless steel container surface, it is described not with clear water flushing after the completion of transfer
Rust steel container surface, is then toasted, and baking temperature is 130 DEG C, baking time 20min, to hold in the stainless steel
The surface of device forms radium-shine colored design layer;
F. the component of following weight proportion is weighed:
0.8-1.0 parts of acrylic acid AA,
20.0-24.0 parts of n-butyl acrylate,
8.0-10.0 parts of acrylic acid-2-ethyl ethyl ester,
8.0-10.0 parts of 2-hydroxypropyl acrylate,
30.0-36.0 parts of ethyl methacrylate,
10.0-12.0 parts of n-BMA,
20.0-24.0 parts of styrene,
3.2-6.4 parts of propylene acrylic fibers,
The component matched above is thoroughly mixed, the acrylic resin paint B of transparent light is made;
G. the acrylic resin paint B of transparent light is taken to carry out aerial spraying work to the radium-shine colored design layer on rustless steel container
Industry, wherein compressed air pressure is 3.0kg, and atomization air pressure 0.45mpa, shaping air pressure is 0.25mpa, after spraying
The light coating that film thickness is 30um is formed in radium-shine multicolour pattern layer surface and solidification baking is carried out to the light coating, is solidified
Temperature is 160 DEG C, curing time 20min, to form laser light coloured picture case on the surface of rustless steel container, completes stainless steel
The surface treatment of container.
Preferably, colored colorant is silver color or black in the step b.
Preferably, clear water flushing pressure is 1.5 ㎏, washing time 10min in the step e.
Preferably, the fixture in the step e is manipulator.
Preferably, surface treatment in the step a the following steps are included:
A1. wire drawing, fine polishing light processing are carried out to rustless steel container surface, the dirt for removing rustless steel container surface is then taken turns with cotton
Stain;
A2. the rustless steel container is fixed, and drifting dust wiping, dedusting operation are carried out to rustless steel container surface.
Preferably, being carried out at wire drawing by the emery band of 180 mesh to rustless steel container surface in the step a1
Reason, then fine polishing light processing is carried out to rustless steel container surface by the cotton wheel of 1200 mesh.
It is 98% by purity preferably, fixing the rustless steel container with conductive fixture in the step a2
Industrial alcohol wipes rustless steel container surface, then is dusted work to rustless steel container surface by ion electrostatic air pressure gun
Industry.
In short, the foregoing is merely presently preferred embodiments of the present invention, made by all ranges according to the present patent application patent
Deng variation and modification, it is all covered by the present invention.
Claims (7)
1. a kind of rustless steel container surface treatment method with laser light color effect, which comprises the following steps:
A. rustless steel container is taken, the rustless steel container is surface-treated;
B. the component of following weight proportion is weighed:
50 parts of acrylic resin,
Colored colorant 5-50 parts,
4-50 parts of filler,
The component matched above is thoroughly mixed, transparent colored acrylic resin paint A is made;
C. transparent colored acrylic resin paint A is taken to carry out aerial spraying operation to the surface of rustless steel container, wherein pressing
Contracting air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-0.25mpa,
The color coating that film thickness is 15-20um is formed on rustless steel container surface after spraying, the color coating is solidified, is solidified
Temperature is 90-100 DEG C, curing time 10-20min, to form the color layers of light on rustless steel container surface;
D. it takes radium-shine honorable film to be put into curved draped stream film device, and sprays activator in radium-shine honorable film surface, wherein compressing
Air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-0.25mpa, spray
Radium-shine brilliance film decomposes under the action of activator after painting, and the pattern of radium-shine brilliance film is swum on the water surface;
E. step of learning from else's experience c treated rustless steel container is simultaneously fixed with fixture, and fixture control rustless steel container carries out on the water surface
Transfer is rolled, so that the pattern of radium-shine brilliance film is transferred in rustless steel container surface, it is described not with clear water flushing after the completion of transfer
Become rusty steel container surface, then toasted, baking temperature be 120-130 DEG C, baking time 10-20min, thus it is described not
The surface of rust steel container forms radium-shine colored design layer;
F. the component of following weight proportion is weighed:
0.8-1.0 parts of acrylic acid AA,
20.0-24.0 parts of n-butyl acrylate,
8.0-10.0 parts of acrylic acid-2-ethyl ethyl ester,
8.0-10.0 parts of 2-hydroxypropyl acrylate,
30.0-36.0 parts of ethyl methacrylate,
10.0-12.0 parts of n-BMA,
20.0-24.0 parts of styrene,
3.2-6.4 parts of propylene acrylic fibers,
The component matched above is thoroughly mixed, the acrylic resin paint B of transparent light is made;
G. the acrylic resin paint B of transparent light is taken to carry out aerial spraying work to the radium-shine colored design layer on rustless steel container
Industry, wherein compressed air pressure is 2.0-3.0kg, and atomization air pressure 0.30-0.45mpa, shaping air pressure is 0.15-
0.25mpa forms film thickness for the light coating of 20-30um and to the light coating in radium-shine multicolour pattern layer surface after spraying
Solidification baking is carried out, solidification temperature is 150-160 DEG C, curing time 10-20min, thus in the surface shape of rustless steel container
At laser light coloured picture case, the surface treatment of rustless steel container is completed.
2. a kind of rustless steel container surface treatment method with laser light color effect according to claim 1, feature exist
In: colored colorant is silver color or black in the step b.
3. a kind of rustless steel container surface treatment method with laser light color effect according to claim 1, feature exist
In: clear water flushing pressure is 1.5 ㎏, washing time 10min in the step e.
4. a kind of rustless steel container surface treatment method with laser light color effect according to claim 1, feature exist
In: the fixture in the step e is manipulator.
5. a kind of rustless steel container surface treatment method with laser light color effect according to claim 1, feature exist
In: surface treatment in the step a the following steps are included:
A1. wire drawing, fine polishing light processing are carried out to rustless steel container surface, the dirt for removing rustless steel container surface is then taken turns with cotton
Stain;
A2. the rustless steel container is fixed, and drifting dust wiping, dedusting operation are carried out to rustless steel container surface.
6. a kind of rustless steel container surface treatment method with laser light color effect according to claim 5, feature exist
In: in the step a1, wire drawing process is carried out to rustless steel container surface by the emery band of 180 mesh, then pass through 1200
Purpose cotton wheel carries out fine polishing light processing to rustless steel container surface.
7. a kind of rustless steel container surface treatment method with laser light color effect according to claim 5, feature exist
In: in the step a2, the rustless steel container is fixed with conductive fixture, the industrial alcohol for being 98% by purity is to stainless
Steel container surface is wiped, then is dusted operation to rustless steel container surface by ion electrostatic air pressure gun.