CN110467886A - A kind of bright decorative film - Google Patents
A kind of bright decorative film Download PDFInfo
- Publication number
- CN110467886A CN110467886A CN201910905214.6A CN201910905214A CN110467886A CN 110467886 A CN110467886 A CN 110467886A CN 201910905214 A CN201910905214 A CN 201910905214A CN 110467886 A CN110467886 A CN 110467886A
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- film
- colour developing
- plating layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bright decorative film, including substrate layer, it further include the upper priming coat set gradually by the front of substrate layer, colour developing coating, 1 ~ 5 layer of upper film plating layer, transparent double face glue-line, colour developing coating is as made of the slurry coating mixed with pigment, and the overall thickness of upper film plating layer is 10nm-400nm, reflectivity 4%-90%, substrate layer is with a thickness of 23 μm -730 μm, upper primer thickness is 10nm-200nm, and colour developing coating layer thickness is 0.3 μm -5 μm, and transparent double face bondline thickness is 20 μm -150 μm.Overall color is mainly determined by colour developing coating, the color of colour developing coating is modulated by pigment, guarantee various colors and uniformly, even the production of different batches also can guarantee identical color, yield is high, the high standards for meeting client shows mirror surface light texture on colour developing coating in conjunction with upper film plating layer.
Description
Technical field
The present invention relates to a kind of bright decorative films.
Background technique
A kind of bright decorative film as a kind of new decorative material, primary effect be it is decorative, for product shape, room
Interior environment and design reach beautiful and economic finishing effect.It can be with the bases such as timber, plastic plate, aluminium sheet, iron plate, glass wall
Material is compound, be widely used in mobile phone housing-plate, household electrical appliance, sound equipment incrustation, interior decoration, aircraft, steamer, train it is interior
Decoration etc..A kind of explosion-proof bright decorative film, a kind of heat-insulated bright decorative film are fabricated in conjunction with the manufacture crafts such as explosion-proof, heat-insulated.From
And when being attached on glass, glass encounter external impacts it is broken when, can be avoided casualty accident caused by splashing because of fragment,
Play explosion-proof effect.
And a kind of bright decorative film, the realization of color, effect of shadow are surrounded on substrate layer in the prior art
What nano impression combination coating process or mimeograph technique were realized.Since current plated film coloring process still remains technology limitation,
Thus color is less, can only make such as blue, red, green and a small number of colors of pink, and in few several colors
In, form and aspect are often impure, as in dominant hue blue part may general green, local degree of saturation has depth difference, this is
It is determined by coating process itself.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of bright decorative films.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is that: a kind of bright decorative film, including substrate
Layer further includes the upper priming coat set gradually by the front of the substrate layer, colour developing coating, film plating layer, transparent double face on 1-5 layer
Glue-line, the colour developing coating are as made of the slurry coating mixed with pigment, and the overall thickness of upper film plating layer is 10nm-400nm, instead
Penetrating rate is 4%-90%, and for the substrate layer with a thickness of 23 μm -730 μm, the upper primer thickness is 10nm-200nm, the colour developing
Coating layer thickness is 0.3 μm -5 μm, and the transparent double face bondline thickness is 20 μm -150 μm.
In some embodiments, the reverse side of the substrate layer is disposed with lower priming coat, nano-imprinted layers, under described
Primer thickness is 10nm-200nm, and the nano-imprinted layers are with a thickness of 1 μm -30 μm.
In some embodiments, be covered with 1-5 layers of lower film plating layer in the nano-imprinted layers, the lower film plating layer it is total
With a thickness of 10nm-400nm, reflectivity 4%-90%.
In some embodiments, the upper film plating layer and lower film plating layer are respectively indium, indium tin mixture, aluminium oxide, oxygen
Change zirconium, silica, niobium oxide, titanium oxide, silicon nitride, silicon, germanium, vanadium oxide, hafnium oxide, tantalum oxide, copper oxide, in chromium oxide
Single layer or lamination.
In some embodiments, the nano-imprinted layers are UV resin, and the groove width of texture is 0.2 μm of -100 μ
M, trench depth are 0.2 μm -30 μm, and fin width is 0.2 μm -100 μm.
In some embodiments, the substrate layer is that polyethylene terephthalate thin film (PET film), polyimides are thin
Film (PI film), polycarbonate film (PC film), polymethyl methacrylate film (PMMA film), polyester plastics film, epoxy
One of plastic film.
In some embodiments, be covered with release film layer on the transparent double face glue-line, the release film layer with a thickness of
20μm-130μm。
The scope of the present invention, however it is not limited to technical solution made of the specific combination of above-mentioned technical characteristic, while should also contain
Cover the other technical solutions for being carried out any combination by above-mentioned technical characteristic or its equivalent feature and being formed.Such as features described above and this
(but being not limited to) disclosed in application have the technical characteristic of similar functions replaced mutually and the technical solution etc. that is formed.
Due to the above technical solutions, the present invention has the following advantages over the prior art: bright decorative of the present invention
Film is to increase the colour developing coating realized using the slurry combination coating process mixed with pigment based on substrate layer, and overall color is main
It is determined by colour developing coating, the color for the coating that develops the color is modulated by pigment, guarantees various colors and uniformly, even different batches
Secondary production also can guarantee identical color, and yield is high, meet the high standards of client, in conjunction with upper film plating layer, apply in colour developing
Mirror surface light texture is showed on layer.
Detailed description of the invention
Attached drawing 1 is structure layer diagrammatic cross-section of the present invention；
Wherein: 1, substrate layer；11, upper priming coat；12, develop the color coating；13, upper film plating layer；14, transparent double face glue-line；15, release
Film layer；21, lower priming coat；22, nano-imprinted layers；23, lower film plating layer；24, printing ink layer.
Specific embodiment
A kind of bright decorative film, comprising:
Substrate layer 1, substrate layer 1 is polyethylene terephthalate thin film (PET film), with a thickness of 125 μm；
Upper priming coat 11, is covered in the front of substrate layer 1, and thickness can be 50nm；
Develop the color coating 12, is coated with, is covered on priming coat 11, with a thickness of 2 μm by the lemon yellow slurry that pigment is deployed.Mesh
Preceding slurry is mixed colours rich in color, rich choice of products, technical maturity, being capable of demand modulation according to client to color and various colors out
Coloured silk, such as various this season popular colours, candy color, such as lilac, cameo brown, smog ash, coral orange；
The overall thickness of upper film plating layer 13 is 200nm, and reflectivity 60%, upper film plating layer 13 is to set with two layers of plated film stacking,
Alumina layer, zirconium oxide layer respectively are based on colour developing coating 12；
Transparent double face glue-line 14 is covered on colour developing coating 12, with a thickness of 80 μm；
Release film layer 15 is covered on transparent double face glue-line 14 and plays a protective role with a thickness of 100 μm, and when use need to remove.
Bright decorative film can only process the front of substrate layer 1, combine coating using the slurry mixed with pigment by increasing
The colour developing coating 12 that technique is realized, overall color are mainly determined that the color of colour developing coating 12 is by pigment tune by colour developing coating 12
It produces, guarantees various colors and uniformly, even the production of different batches also can guarantee identical color, yield is high, meets
The high standards of client shows mirror surface light texture on colour developing coating 12 in conjunction with upper film plating layer.
The reverse side of substrate layer 1 can also be processed, another bright decorative film is formed, comprising:
Lower priming coat 21, is covered in the reverse side of substrate layer 1, and with a thickness of 50nm, upper priming coat 11 and lower priming coat 21 are all preparatory
It is formed coated on stretching after on substrate layer raw material therewith, the adhesive force between substrate layer 1 and follow-up coating can be increased.
Nano-imprinted layers 22, the nano-imprinted layers 22 are UV resin, and with a thickness of 15 μm, the groove width of texture is 50
μm, trench depth is 12 μm, and fin width is 50 μm；
The lower film plating layer 23 is to set with the stacking of four layers of plated film, based on nano-imprinted layers 22 respectively be niobium oxide,
Silica, indium, 4 layers of silica, the overall thickness of the lower film plating layer 23 are 250nm, reflectivity 65%.
Descend film plating layer that can not do color in the prior art, if only done brilliant white reflecting effect in the present embodiment, develop the color coating 12
Show that a dominant hue, display coating 12 are considered except lower film plating layer 23 combines the part light of nano-imprinted layers 22, when decorating film bends
When just form light beam, upper film plating layer 13 makes film surface have mirror surface reflecting effect, is rich in stereovision, more aobvious texture.The lower plating
Film layer can still do other colors, such as blue, red, green and pink, constitute a color with the colour developing collocation of coating 12
Shadow visual effect is arranged in pairs or groups richer.
" upper priming coat " referred to above, " lower priming coat ", " upper film plating layer ", the upper and lower position word in " lower film plating layer ",
It is benchmark with reference to the accompanying drawings.Substrate layer 1 it is front and back, be only intended to the opposite two sides of difference substrate layer 1.
When production, the substrate layer 1 that will be covered with priming coat 11 and lower priming coat 21 is packed into coating machine, to substrate layer 1
Front is first processed, and is coated with colour developing coating 12 on upper priming coat 11 using coating process, is coated with transparent double face glue-line after doing
14, then release film layer 15 is sticked to protect by make-up machine.
The reverse side of substrate layer 1 is processed again as needed, by nanometer embossing to being made on lower priming coat 21
Nano-imprinted layers 22, then using magnetron sputtering technique successively in nano-imprinted layers 22 successively sputter vaporization plated film niobium oxide layer,
Silicon oxide layer, indium layer, silicon oxide layer form film plating layer 23, constitute bright decorative film.Overall color shadow visual effect is richer.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention.It is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of bright decorative film, including substrate layer (1), it is characterised in that: further include by the substrate layer (1) front successively
The upper priming coat (11) that is arranged, colour developing coating (12), film plating layer (13), transparent double face glue-line (14) on 1-5 layer, the colour developing painting
Layer (12) is as made of the slurry coating mixed with pigment, and the overall thickness of upper film plating layer (13) is 10nm-400nm, and reflectivity is
4%-90%, for the substrate layer (1) with a thickness of 23 μm -730 μm, the upper priming coat (11) is described aobvious with a thickness of 10nm-200nm
Color coating (12) is with a thickness of 0.3 μm -5 μm, and the transparent double face glue-line (14) is with a thickness of 20 μm -150 μm.
2. a kind of bright decorative film according to claim 1, it is characterised in that: the reverse side of the substrate layer (1) is successively set
It is equipped with lower priming coat (21), nano-imprinted layers (22), the lower priming coat (21) is with a thickness of 10nm-200nm, the nanometer pressure
Layer (22) are printed with a thickness of 1 μm -30 μm.
3. a kind of bright decorative film according to claim 2, it is characterised in that: be covered on the nano-imprinted layers (22)
1-5 layers lower film plating layer (23), the overall thickness of the lower film plating layer (23) is 10nm-400nm, reflectivity 4%-90%.
4. a kind of bright decorative film according to claim 3, it is characterised in that: the upper film plating layer (13) and lower film plating layer
It (23) is respectively indium, indium tin mixture, aluminium oxide, zirconium oxide, silica, niobium oxide, titanium oxide, silicon nitride, silicon, germanium, oxidation
Vanadium, hafnium oxide, tantalum oxide, copper oxide, single layer or lamination in chromium oxide.
5. a kind of bright decorative film according to claim 2, it is characterised in that: the nano-imprinted layers (22) are UV tree
Rouge, the groove width of texture are 0.2 μm -100 μm, and trench depth is 0.2 μm -30 μm, and fin width is 0.2 μm -100 μm.
6. a kind of bright decorative film according to claim 1, it is characterised in that: the substrate layer (1) is poly- terephthaldehyde
Sour two ester film of second, Kapton, polycarbonate film, polymethyl methacrylate film, polyester plastics film, epoxy
One of plastic film.
7. a kind of bright decorative film according to claim 1, it is characterised in that: covered on the transparent double face glue-line (14)
Have release film layer (15), the release film layer (15) is with a thickness of 20 μm -130 μm.