CN110467848A - Pencil-lead - Google Patents
Pencil-lead Download PDFInfo
- Publication number
- CN110467848A CN110467848A CN201910884541.8A CN201910884541A CN110467848A CN 110467848 A CN110467848 A CN 110467848A CN 201910884541 A CN201910884541 A CN 201910884541A CN 110467848 A CN110467848 A CN 110467848A
- Authority
- CN
- China
- Prior art keywords
- weight percent
- pencil
- pigment
- paraffin
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pencil-leads, it contains clay, microwax, paraffin, stearic acid, hydroxypropyl methyl cellulose, pigment, titanium dioxide, and its fumed silica, wherein, the weight percent of the clay is 40-67%, the weight percent of the microwax is 4-6%, the weight percent of the paraffin is 5-8%, the stearic weight percent is 8-14%, the weight percent of the hydroxypropyl methyl cellulose is 2-6%, the weight percent of the pigment is 8-14%, the weight percent of the titanium dioxide is 4-7%, the weight percent of the fumed silica is 2-5%.The proportion that the pencil-lead passes through the different weight percentage of different component, improve intensity and toughness, so that having very high row yielding in tipping process, it is not easily broken when pencil sharpener is cut, writing quality is improved simultaneously, that is, is coloured when writing, colouring is easy on paper, smoothness is good, to improve work efficiency indirectly.
Description
Technical field
The present invention relates to a kind of pencil-lead more particularly to a kind of colored pencil pen cores.
Background technique
Colored pencil is one of more commonly used stationery, and conventional colored pencil pen core adds mainly using clay as binder
Pigment, constitution raw material (such as talcum powder), adhesive and the wax extrusion forming after mixed grinding.Such colored pencil usually exists
Following problems: if it is intended to writing quality is good, then pen core intensity is not high, and in tipping process, row yielding is low and pencil sharpener is cut
Shi Bixin is easily broken;If improving pen core intensity, writing quality can be reduced, it is hard when such as writing, it is not easy to paint on paper, it is not smooth
Deng.
Summary of the invention
In view of the above drawbacks of the prior art, technical problem to be solved by the invention is to provide a kind of pencil-leads, should
Pencil-lead has good intensity and toughness, and writing quality is good.
To achieve the above object, the present invention provides a kind of pencil-leads, and containing clay, microwax, paraffin is stearic
Acid, hydroxypropyl methyl cellulose, pigment, titanium dioxide and its fumed silica, wherein the weight percent of the clay is 40-
67%, the weight percent of the microwax is 4-6%, and the weight percent of the paraffin is 5-8%, the stearic weight percent
Than being 2-6% for the weight percent of 8-14%, the hydroxypropyl methyl cellulose, the weight percent of the pigment is 8-14%,
The weight percent of the titanium dioxide is 4-7%, and the weight percent of the fumed silica is 2-5%.
The weight percent of the clay is 40%, and the weight percent of the microwax is 6%, the weight percent of the paraffin
It is 8%, which is 14%, and the weight percent of the hydroxypropyl methyl cellulose is 6%, the pigment
Weight percent is 14%, and the weight percent of the titanium dioxide is 7%, and the weight percent of the fumed silica is 5%.
As the first alternate embodiment, the weight percent of the clay is 56%, the weight percent of the microwax
Than being 5.5%, the weight percent of the paraffin is 5.8%, which is 12.7%, the hydroxypropyl methyl
The weight percent of cellulose is 4.5%, and the weight percent of the pigment is 10%, and the weight percent of the titanium dioxide is 3%,
The weight percent of the fumed silica is 2.5%.
As second of alternate embodiment, the weight percent of the clay is 58.5%, the weight hundred of the microwax
Divide than being 4%, the weight percent of the paraffin is 5%, which is 12.5%, hydroxypropyl methyl fibre
The weight percent of dimension element is 4.5%, and the weight percent of the pigment is 10%, and the weight percent of the titanium dioxide is 3%, should
The weight percent of fumed silica is 2.5%.
As the third alternate embodiment, the weight percent of the clay is 49.5%, the weight hundred of the microwax
Divide than being 5.5%, the weight percent of the paraffin is 6.5%, which is 13.5%, the hydroxypropyl first
The weight percent of base cellulose is 4.5%, and the weight percent of the pigment is 14%, and the weight percent of the titanium dioxide is
4%, the weight percent of the fumed silica is 2.5%.
As the 4th kind of alternate embodiment, the weight percent of the clay is 67%, the weight percent of the microwax
Than being 4%, the weight percent of the paraffin is 5%, which is 8%, the hydroxypropyl methyl cellulose
Weight percent be 2%, the weight percent of the pigment is 8%, and the weight percent of the titanium dioxide is 4%, the gas phase two
The weight percent of silica is 2%.
Pencil-lead of the invention improves intensity and toughness by the proportion of the different weight percentage of different component,
So that there is very high row yielding in tipping process, it is not easily broken when pencil sharpener is cut, while improving writing quality, that is, when writing
It colours, colouring is easy on paper, smoothness is good, to improve work efficiency indirectly.
The technical effect of design of the invention, specific structure and generation will be described further below, with fully
Solve the purpose of the present invention, feature and effect.
Specific embodiment
Pencil-lead of the present invention contains clay, microwax, paraffin, stearic acid, hydroxypropyl methyl cellulose, pigment, titanium white
Powder and its fumed silica, wherein the weight percent of the clay is 40-67%, and the weight percent of the microwax is 4-
6%, for improving toughness, the weight percent of the paraffin is 5-8%, which is 8-14%, the hydroxyl
The weight percent of propyl methocel is 2-6%, and for improving intensity, the weight percent of the pigment is 8-14%, should
The weight percent of titanium dioxide is 4-7%, and the weight percent of the fumed silica is 2-5%, for improving intensity.
It is specifically described below by embodiment.
Embodiment one
Embodiment two
Component | Weight percent |
Clay | 56 |
Microwax | 5.5 |
Paraffin | 5.8 |
Stearic acid | 12.7 |
Hydroxypropyl methyl cellulose | 4.5 |
Pigment | 10 |
Titanium dioxide | 3 |
Fumed silica | 2.5 |
Embodiment three
Component | Weight percent |
Clay | 58.5 |
Microwax | 4 |
Paraffin | 5 |
Stearic acid | 12.5 |
Hydroxypropyl methyl cellulose | 4.5 |
Pigment | 10 |
Titanium dioxide | 3 |
Fumed silica | 2.5 |
Example IV
Embodiment five
Component | Weight percent |
Clay | 67 |
Microwax | 4 |
Paraffin | 5 |
Stearic acid | 8 |
Hydroxypropyl methyl cellulose | 2 |
Pigment | 8 |
Titanium dioxide | 4 |
Fumed silica | 2 |
The pencil-lead has very high row yielding in tipping process, and not easily broken when pencil sharpener is cut, the substance used is all
Natural environmental-protective, meet " regulation about chemicals registration, assessment, license and limitation " of European Union, meanwhile, the pencil-lead
Preparation does not need to change existing production technology, does not need to introduce new equipment yet, directly continues to use existing production technology and its set
It is standby to produce in batches.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be within the scope of protection determined by the claims.
Claims (6)
1. a kind of pencil-lead contains clay, microwax, paraffin, stearic acid, hydroxypropyl methyl cellulose, pigment, titanium white
Powder and its fumed silica, wherein the weight percent of the clay is 40-67%, and the weight percent of the microwax is 4-
6%, the weight percent of the paraffin is 5-8%, which is 8-14%, the hydroxypropyl methyl cellulose
Weight percent be 2-6%, the weight percent of the pigment is 8-14%, and the weight percent of the titanium dioxide is 4-7%, should
The weight percent of fumed silica is 2-5%.
2. pencil-lead as described in claim 1, it is characterised in that: the weight percent of the clay is 40%, the microwax
Weight percent be 6%, the weight percent of the paraffin is 8%, which is 14%, the hydroxypropyl
The weight percent of methylcellulose is 6%, and the weight percent of the pigment is 14%, and the weight percent of the titanium dioxide is
7%, the weight percent of the fumed silica is 5%.
3. pencil-lead as described in claim 1, it is characterised in that: the weight percent of the clay is 56%, the microwax
Weight percent be 5.5%, the weight percent of the paraffin is 5.8%, which is 12.7%, should
The weight percent of hydroxypropyl methyl cellulose is 4.5%, and the weight percent of the pigment is 10%, the weight hundred of the titanium dioxide
Divide than being 3%, the weight percent of the fumed silica is 2.5%.
4. pencil-lead as described in claim 1, it is characterised in that: the weight percent of the clay is 58.5%, the crystallite
The weight percent of wax is 4%, and the weight percent of the paraffin is 5%, which is 12.5%, the hydroxyl
The weight percent of propyl methocel is 4.5%, and the weight percent of the pigment is 10%, the weight percent of the titanium dioxide
Than being 3%, the weight percent of the fumed silica is 2.5%.
5. pencil-lead as described in claim 1, it is characterised in that: the weight percent of the clay is 49.5%, the crystallite
The weight percent of wax is 5.5%, and the weight percent of the paraffin is 6.5%, which is 13.5%,
The weight percent of the hydroxypropyl methyl cellulose is 4.5%, and the weight percent of the pigment is 14%, the weight of the titanium dioxide
Percentage is 4%, and the weight percent of the fumed silica is 2.5%.
6. pencil-lead as described in claim 1, it is characterised in that: the weight percent of the clay is 67%, the microwax
Weight percent be 4%, the weight percent of the paraffin is 5%, which is 8%, the hydroxypropyl
The weight percent of methylcellulose is 2%, and the weight percent of the pigment is 8%, and the weight percent of the titanium dioxide is
4%, the weight percent of the fumed silica is 2%.