CN110433319A - A kind of paper urine pad with deodorization functions - Google Patents
A kind of paper urine pad with deodorization functions Download PDFInfo
- Publication number
- CN110433319A CN110433319A CN201910845020.1A CN201910845020A CN110433319A CN 110433319 A CN110433319 A CN 110433319A CN 201910845020 A CN201910845020 A CN 201910845020A CN 110433319 A CN110433319 A CN 110433319A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- liquid
- weight
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of paper urine pads with deodorization functions, including liquid-permeable layer, absorbed layer and the bottom that from top to bottom successively lamination is arranged, the liquid-permeable layer includes polyethylene, polyethylene wax and starch, the absorbed layer includes coconut carbon, copper sulphate, superfine silica gel powder, diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, and the bottom is liquid-tight material.Liquid-permeable layer makes its surface more soft comfortable using polyethylene, polyethylene wax and starch, and coconut carbon, copper sulphate, superfine silica gel powder, diatomite, sodium citrate and ivy extract, which is added, in absorbed layer can improve the assimilation effect of moisture, and be able to achieve deodorization.
Description
Technical field
The present invention relates to amenities technical fields, more particularly to a kind of paper urine pad with deodorization functions.
Background technique
Paper urine pad be using rear i.e. droppable disposable products, it is deeply welcomed by the people since its water absorbing properties is good.
Paper urine pad mainly includes liquid-permeable layer, absorbed layer and bottom.The core of paper urine pad is absorbed layer therein, absorbed layer master
To include Time of Fluff Slurry and water-absorbing resin, so that paper urine pad is absorbed a large amount of moisture, and be not easy to be dehydrated, paper can be kept to urinate to a certain degree
Pad the drying on surface.
Existing paper urine pad mainly solves the problems, such as absorption, can absorb the most of moisture flowed into paper urine pad.Although
Moisture can be absorbed, but stink cannot be removed, such as stays in the urine on paper urine pad surface, can give out an unpleasant smell, seriously affect
The surrounding crowd of user.
Summary of the invention
An object of the present invention is to provide a kind of paper urine pads with deodorization functions, can remove certain stink.
A kind of paper urine pad with deodorization functions, including liquid-permeable layer, absorbed layer and the bottom that from top to bottom successively lamination is arranged
Layer, the liquid-permeable layer include polyethylene, polyethylene wax and starch, the absorbed layer include coconut carbon, copper sulphate, superfine silica gel powder,
Diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, the bottom are liquid-tight material.
The beneficial effects of the present invention are: liquid-permeable layer makes its surface more soft comfortable using polyethylene, polyethylene wax and starch,
Coconut carbon, copper sulphate, superfine silica gel powder, diatomite, sodium citrate and ivy extract, which is added, in absorbed layer can improve the suction of moisture
It produces effects fruit, and is able to achieve deodorization.
In addition, the paper urine pad with deodorization functions provided according to the present invention, can also have following additional technology special
Sign:
Further, in the liquid-permeable layer, the polyethylene accounts for 100~120 parts by weight, and the polyethylene wax accounts for 2~5 weights
Part is measured, the starch accounts for 5~10 parts by weight.
Further, in the absorbed layer, the coconut carbon accounts for 5~8 parts by weight, and the copper sulphate accounts for 10~15 weight
Part, the superfine silica gel powder accounts for 25~30 parts, and the diatomite accounts for 10~15 parts by weight, and the sodium citrate accounts for 3~8 parts by weight,
The ivy extract accounts for 8~12 parts by weight, and the Time of Fluff Slurry accounts for 120~140 parts by weight, and the water-absorbing resin accounts for 30~40
Parts by weight.
Further, the preparation process of the liquid-permeable layer are as follows:
Polyethylene and the polyethylene wax mixing for taking molten condition, stir evenly, obtain transparent liquid mixture；
The 1/3 transparent liquid mixture is taken, starch is added in Xiang Suoshu transparent liquid mixture, is uniformly mixed, it is cooling, obtain transparent liquid
Cooled material；
The transparent liquid cooled material is placed in warm water and is impregnated 1~2 hour, takes out, melting is again heated to, with remaining transparent liquid
Mixture mixing, cooling, aperture obtains the liquid-permeable layer.
Further, the preparation process of the absorbed layer are as follows:
The coconut carbon, copper sulphate, superfine silica gel powder and diatomite are taken, is ground, adds water and stirs uniformly, obtains absorption mixture；
100~120 DEG C are heated to the absorption mixture, constant temperature is kept for 1~2 hour, obtains heating mixture；
The sodium citrate and ivy extract are taken, is ground, is added water and stirred uniformly, fermentation obtains fermentation liquid；
The absorption is heated and is uniformly mixed under mixture, fermentation liquid, Time of Fluff Slurry and water-absorbing resin room temperature, compression moulding,
Obtain absorbed layer.
Further, described to add water and stir in uniform step, described plus water quality is the 60 of the absorption mixture
~80%.
Further, described the step of being heated to 100~120 DEG C to the absorption mixture, includes:
30~40 DEG C are heated to the speed of 2 DEG C/s；
70~80 DEG C are heated to the speed of 5 DEG C/s；
100~120 DEG C are heated to the speed of 1 DEG C/s.
Further, the fermentation uses bacillus subtilis.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Specific embodiment
To keep objects, features and advantages of the present invention more obvious and easy to understand, below with reference to embodiment to of the invention
Specific embodiment is described in detail.But the invention can be realized in many different forms, however it is not limited to this paper institute
The embodiment of description.On the contrary, purpose of providing these embodiments is make it is more thorough and comprehensive to the disclosure.
Embodiment 1
A kind of paper urine pad with deodorization functions, including liquid-permeable layer, absorbed layer and the bottom that from top to bottom successively lamination is arranged
Layer, the liquid-permeable layer include polyethylene, polyethylene wax and starch, the absorbed layer include coconut carbon, copper sulphate, superfine silica gel powder,
Diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, the bottom are liquid-tight material.
It is an advantage of the present invention that liquid-permeable layer makes its surface more soft comfortable using polyethylene, polyethylene wax and starch, inhale
The absorption of moisture can be improved by receiving layer addition coconut carbon, copper sulphate, superfine silica gel powder, diatomite, sodium citrate and ivy extract
Effect, and it is able to achieve deodorization.
Specifically, the polyethylene accounts for 100 parts by weight, and the polyethylene wax accounts for 2 parts by weight, described in the liquid-permeable layer
Starch accounts for 5 parts by weight, and in the absorbed layer, the coconut carbon accounts for 5 parts by weight, and the copper sulphate accounts for 10 parts by weight, the micro mist
Silica gel accounts for 25 parts, and the diatomite accounts for 10 parts by weight, and the sodium citrate accounts for 3 parts by weight, and the ivy extract accounts for 8 weight
Part, the Time of Fluff Slurry accounts for 120 parts by weight, and the water-absorbing resin accounts for 30 parts by weight.
Further, the preparation process of the liquid-permeable layer are as follows:
(1) polyethylene and the polyethylene wax mixing for taking molten condition, stir evenly, obtain transparent liquid mixture；
(2) the 1/3 transparent liquid mixture is taken, starch is added in Xiang Suoshu transparent liquid mixture, is uniformly mixed, it is cooling, it obtains
Transparent liquid cooled material；
(3) the transparent liquid cooled material is placed in warm water and is impregnated 1 hour, taken out, melting is again heated to, with remaining transparent liquid
Mixture mixing, cooling, aperture obtains the liquid-permeable layer.
In addition, the preparation process of the absorbed layer are as follows:
(1) coconut carbon, copper sulphate, superfine silica gel powder and diatomite are taken, is ground, adds water and stirs uniformly, mixing must be absorbed
Object；
(2) 100 DEG C are heated to the absorption mixture, constant temperature is kept for 1 hour, obtains heating mixture；
(3) sodium citrate and ivy extract are taken, grind, add water and stir uniformly, using bacillus subtilis into
Row fermentation, obtains fermentation liquid；
(4) absorption is heated and is uniformly mixed under mixture, fermentation liquid, Time of Fluff Slurry and water-absorbing resin room temperature, is pressed into
Type obtains absorbed layer.
Specifically, described add water and stir in uniform step, described plus water quality be it is described absorb mixture 60~
80%.
Preferably, described the step of being heated to 100 DEG C to the absorption mixture, includes:
(1) 30 DEG C are heated to the speed of 2 DEG C/s；
(2) 70 DEG C are heated to the speed of 5 DEG C/s；
(3) 100 DEG C are heated to the speed of 1 DEG C/s.
Embodiment 2
A kind of paper urine pad with deodorization functions, including liquid-permeable layer, absorbed layer and the bottom that from top to bottom successively lamination is arranged
Layer, the liquid-permeable layer include polyethylene, polyethylene wax and starch, the absorbed layer include coconut carbon, copper sulphate, superfine silica gel powder,
Diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, the bottom are liquid-tight material.
Specifically, the polyethylene accounts for 120 parts by weight, and the polyethylene wax accounts for 5 parts by weight, described in the liquid-permeable layer
Starch accounts for 10 parts by weight, and in the absorbed layer, the coconut carbon accounts for 8 parts by weight, and the copper sulphate accounts for 15 parts by weight, the micro mist
Silica gel accounts for 30 parts, and the diatomite accounts for 15 parts by weight, and the sodium citrate accounts for 8 parts by weight, and the ivy extract accounts for 12 weights
Part is measured, the Time of Fluff Slurry accounts for 140 parts by weight, and the water-absorbing resin accounts for 40 parts by weight.
Further, the preparation process of the liquid-permeable layer are as follows:
(1) polyethylene and the polyethylene wax mixing for taking molten condition, stir evenly, obtain transparent liquid mixture；
(2) the 1/3 transparent liquid mixture is taken, starch is added in Xiang Suoshu transparent liquid mixture, is uniformly mixed, it is cooling, it obtains
Transparent liquid cooled material；
(3) the transparent liquid cooled material is placed in warm water and is impregnated 2 hours, taken out, melting is again heated to, with remaining transparent liquid
Mixture mixing, cooling, aperture obtains the liquid-permeable layer.
In addition, the preparation process of the absorbed layer are as follows:
(1) coconut carbon, copper sulphate, superfine silica gel powder and diatomite are taken, is ground, adds water and stirs uniformly, mixing must be absorbed
Object；
(2) 120 DEG C are heated to the absorption mixture, constant temperature is kept for 2 hours, obtains heating mixture；
(3) sodium citrate and ivy extract are taken, grind, add water and stir uniformly, using bacillus subtilis into
Row fermentation, obtains fermentation liquid；
(4) absorption is heated and is uniformly mixed under mixture, fermentation liquid, Time of Fluff Slurry and water-absorbing resin room temperature, is pressed into
Type obtains absorbed layer.
Specifically, described add water and stir in uniform step, described plus water quality be it is described absorb mixture 60~
80%.
Preferably, described the step of being heated to 120 DEG C to the absorption mixture, includes:
(1) 40 DEG C are heated to the speed of 2 DEG C/s；
(2) 80 DEG C are heated to the speed of 5 DEG C/s；
(3) 120 DEG C are heated to the speed of 1 DEG C/s.
Embodiment 3
A kind of paper urine pad with deodorization functions, including liquid-permeable layer, absorbed layer and the bottom that from top to bottom successively lamination is arranged
Layer, the liquid-permeable layer include polyethylene, polyethylene wax and starch, the absorbed layer include coconut carbon, copper sulphate, superfine silica gel powder,
Diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, the bottom are liquid-tight material.
Specifically, the polyethylene accounts for 105 parts by weight, and the polyethylene wax accounts for 3 parts by weight, described in the liquid-permeable layer
Starch accounts for 6 parts by weight, and in the absorbed layer, the coconut carbon accounts for 7 parts by weight, and the copper sulphate accounts for 14 parts by weight, the micro mist
Silica gel accounts for 25 parts, and the diatomite accounts for 11 parts by weight, and the sodium citrate accounts for 3 parts by weight, and the ivy extract accounts for 9 weight
Part, the Time of Fluff Slurry accounts for 140 parts by weight, and the water-absorbing resin accounts for 32 parts by weight.
Further, the preparation process of the liquid-permeable layer are as follows:
(1) polyethylene and the polyethylene wax mixing for taking molten condition, stir evenly, obtain transparent liquid mixture；
(2) the 1/3 transparent liquid mixture is taken, starch is added in Xiang Suoshu transparent liquid mixture, is uniformly mixed, it is cooling, it obtains
Transparent liquid cooled material；
(3) the transparent liquid cooled material is placed in warm water and will be impregnated 1.3 hours, taking-up is again heated to melting, and remaining
Liquid mixture mixing, cooling, aperture obtains the liquid-permeable layer.
In addition, the preparation process of the absorbed layer are as follows:
(1) coconut carbon, copper sulphate, superfine silica gel powder and diatomite are taken, is ground, adds water and stirs uniformly, mixing must be absorbed
Object；
(2) 110 DEG C are heated to the absorption mixture, constant temperature is kept for 1 hour, obtains heating mixture；
(3) sodium citrate and ivy extract are taken, grind, add water and stir uniformly, using bacillus subtilis into
Row fermentation, obtains fermentation liquid；
(4) absorption is heated and is uniformly mixed under mixture, fermentation liquid, Time of Fluff Slurry and water-absorbing resin room temperature, is pressed into
Type obtains absorbed layer.
Specifically, described add water and stir in uniform step, described plus water quality be it is described absorb mixture 60~
80%.
Preferably, described the step of being heated to 105 DEG C to the absorption mixture, includes:
(1) 30 DEG C are heated to the speed of 2 DEG C/s；
(2) 75 DEG C are heated to the speed of 5 DEG C/s；
(3) 105 DEG C are heated to the speed of 1 DEG C/s.
Reference examples 1
This reference examples and embodiment 3 are almost the same, the difference is that:
In this reference examples, the liquid-permeable layer only includes polyethylene and polyethylene wax.
Reference examples 2
This reference examples and embodiment 3 are almost the same, the difference is that:
The absorbed layer only includes Time of Fluff Slurry and water-absorbing resin.
Reference examples 3
This reference examples and embodiment 3 are almost the same, the difference is that:
The absorbed layer only includes coconut carbon, superfine silica gel powder, diatomite, Time of Fluff Slurry and water-absorbing resin.
Reference examples 4
This reference examples and embodiment 3 are almost the same, the difference is that:
The absorbed layer include 60 parts by weight of nano-silicon dioxide hollow sphere, 25 parts of superfine silica gel powder, 11 parts by weight of diatomite,
32 parts by weight of 140 parts by weight of Time of Fluff Slurry and water-absorbing resin.
Reference examples 5
This reference examples and embodiment 3 are almost the same, the difference is that:
This reference examples does not ferment to the mixture of sodium citrate and ivy extract.
Reference examples 6
This reference examples and embodiment 3 are almost the same, the difference is that:
This reference examples uses 10 DEG C/s to be heated to 105 DEG C to mixture is absorbed.
10 parts of sample of paper urine pad are taken obtained by above-described embodiment and reference examples, is surveyed using ZRD-1000 electronic type flexibility analyzer
Determine pliability, ammonia removal rate is measured using sodium hypochlorite-salicylic acid spectrophotometry, using ammonium alcohol polyvinyl phosphate absorption-Asia
Methyl blue colorimetric method for determining hydrogen sulfide removal rate evaluates deodorizing effect with ammonia removal rate and hydrogen sulfide removal rate, and removal rate is higher,
Deodorizing effect is better, and water absorption rate is calculated after sample is impregnated in water, and results are averaged is shown in Table 1.
Table 1
Please refer to table 1, comparative example 1, embodiment 2 and embodiment 3, it is known that using the scheme of the application obtain compared with
Good effect, wherein be embodiment 3 effect it is best, it is believed that it is most preferred embodiment；
Comparative example 3, reference examples 1 and reference examples 2, it is known that, traditional paper made according to reference examples 1 and reference examples 2
Diaper its respectively in pliability and deodorizing effect much worse than embodiment 3；
Comparative example 3, reference examples 3 and reference examples 4, it is known that, about the component of absorbed layer, only using embodiment 3
Group timesharing can be only achieved most preferably；
Comparative example 3, reference examples 5 and reference examples 6, it is known that, giving up fermentation and segmentally heating can drop to a certain extent
The deodorizing effect of low paper urine pad.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example
Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not
Centainly refer to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be any
One or more embodiment or examples in can be combined in any suitable manner.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
Limitations on the scope of the patent of the present invention therefore cannot be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to guarantor of the invention
Protect range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (8)
1. a kind of paper urine pad with deodorization functions, including successively liquid-permeable layer, absorbed layer and the bottom of lamination setting from top to bottom,
It is characterized in that, the liquid-permeable layer includes polyethylene, polyethylene wax and starch, the absorbed layer includes coconut carbon, copper sulphate, micro-
Powder silica gel, diatomite, sodium citrate, ivy extract, Time of Fluff Slurry and water-absorbing resin, the bottom are liquid-tight material.
2. the paper urine pad according to claim 1 with deodorization functions, which is characterized in that described poly- in the liquid-permeable layer
Ethylene accounts for 100~120 parts by weight, and the polyethylene wax accounts for 2~5 parts by weight, and the starch accounts for 5~10 parts by weight.
3. the paper urine pad according to claim 1 with deodorization functions, which is characterized in that in the absorbed layer, the coconut palm
Shell carbon accounts for 5~8 parts by weight, and the copper sulphate accounts for 10~15 parts by weight, and the superfine silica gel powder accounts for 25~30 parts, and the diatomite accounts for
10~15 parts by weight, the sodium citrate account for 3~8 parts by weight, and the ivy extract accounts for 8~12 parts by weight, the villus
Slurry accounts for 120~140 parts by weight, and the water-absorbing resin accounts for 30~40 parts by weight.
4. the paper urine pad according to claim 1 or 2 with deodorization functions, which is characterized in that the preparation of the liquid-permeable layer
Process are as follows:
Polyethylene and the polyethylene wax mixing for taking molten condition, stir evenly, obtain transparent liquid mixture；
The 1/3 transparent liquid mixture is taken, starch is added in Xiang Suoshu transparent liquid mixture, is uniformly mixed, it is cooling, it is cooling to obtain transparent liquid
Object；
The transparent liquid cooled material is placed in warm water and is impregnated 1~2 hour, is taken out, is again heated to melting, is mixed with remaining transparent liquid
Object mixing, cooling, aperture obtains the liquid-permeable layer.
5. the paper urine pad according to claim 1 or 3 with deodorization functions, which is characterized in that the preparation of the absorbed layer
Process are as follows:
The coconut carbon, copper sulphate, superfine silica gel powder and diatomite are taken, is ground, adds water and stirs uniformly, obtains absorption mixture；
100~120 DEG C are heated to the absorption mixture, constant temperature is kept for 1~2 hour, obtains heating mixture；
The sodium citrate and ivy extract are taken, is ground, is added water and stirred uniformly, fermentation obtains fermentation liquid；
The absorption is heated and is uniformly mixed under mixture, fermentation liquid, Time of Fluff Slurry and water-absorbing resin room temperature, compression moulding must inhale
Receive layer.
6. the paper urine pad according to claim 5 with deodorization functions, which is characterized in that described to add water and stir uniform step
In rapid, described plus water quality is the 60~80% of the absorption mixture.
7. the paper urine pad according to claim 5 with deodorization functions, which is characterized in that described to the absorption mixture
The step of being heated to 100~120 DEG C include:
30~40 DEG C are heated to the speed of 2 DEG C/s；
70~80 DEG C are heated to the speed of 5 DEG C/s；
100~120 DEG C are heated to the speed of 1 DEG C/s.
8. the paper urine pad according to claim 5 with deodorization functions, which is characterized in that the fermentation uses withered grass gemma
Bacillus.