CN110409185A - A kind of mosquito-proof type fabric of waterproof and preparation method thereof - Google Patents
A kind of mosquito-proof type fabric of waterproof and preparation method thereof Download PDFInfo
- Publication number
- CN110409185A CN110409185A CN201810400692.7A CN201810400692A CN110409185A CN 110409185 A CN110409185 A CN 110409185A CN 201810400692 A CN201810400692 A CN 201810400692A CN 110409185 A CN110409185 A CN 110409185A
- Authority
- CN
- China
- Prior art keywords
- mosquito
- waterproof
- proof
- parts
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of mosquito-proof type fabrics of waterproof, fabric is attached to by the mosquito-proof coating of waterproof to obtain later through dry, the mosquito-proof coating of waterproof by following mass parts material composition: 50~150 parts of adhesive, 1~7.5 part of thickener, 5~25 parts of insect-proof agent, 2~15 parts of waterproofing agent, 0.5~2.5 part of surfactant, 3~10 parts of sustained release agent；The insect-proof agent is the combination of one or both of Metadelphene, Permethrin, and the waterproofing agent is selected from one of metal soap, paraffin class and organic silicon.The invention also discloses a kind of preparation methods of the mosquito-proof type fabric of waterproof.The mosquito-proof type fabric of waterproof in the present invention not only has the mosquito-proof effect of preferable waterproof, but also have the characteristics that environmental protection, it is efficient, have broad application prospects.
Description
Technical field
The present invention relates to fabric arts, more particularly to mosquito-proof type fabric of a kind of waterproof and preparation method thereof.
Background technique
With the development of human sciences' technology, the improvement of people's living standards, outdoor sports increase, and to health and
The attention of environmental protection, to fabric, there has also been new requirements, i.e., focus on fabric beauty and it is comfortable while, environmental protection to fabric
More stringent requirements are proposed for the functions such as property and wholesomeness.Therefore, novel and multifunctional fabric will become an important new industry
It draws attention.And has and eliminate peculiar smell, prevents from bacteria breed, reduces the pathogenetic anti-mosquito function fabric of skin infection to be its development
One of trend.
Medical research, which shows bite by mosquitos not only, can cause the red and swollen and scratchy of human skin, or propagate the diseases such as malaria
One of the main channel of disease.Moreover, summer mosquito breeds extensively, many people are often by mosquito bite, and gently then surprise is itched unbearably, it is heavy then
Infectious disease, brings many puzzlements to people's normal life, work, outdoor sports, if it is long-acting mosquito-proof to have kind of fabric to have
The function of mosquito repellent, will reduce mosquito to we live bring interference.Therefore, exploitation has the novel fabric of long-acting anti-mosquito function
With dress-goods with pre- mosquito proof bite and virus infection be very urgent.
For this reason, it is necessary to be able to solve in view of the above-mentioned problems, propose a kind of mosquito-proof type fabric of waterproof and preparation method thereof
Problems of the prior art.
Summary of the invention
It is in the prior art to overcome the purpose of the present invention is to provide mosquito-proof type fabric of a kind of waterproof and preparation method thereof
It is insufficient.
To achieve the above object, the invention provides the following technical scheme:
A kind of mosquito-proof type fabric of waterproof is attached to fabric by the mosquito-proof coating of waterproof and obtains later through dry, and the waterproof is anti-
Mosquito coating by following mass parts material composition: 50~150 parts of adhesive, 1~7.5 part of thickener, 5~25 parts of insect-proof agent, prevent
2~15 parts of aqua, 0.5~2.5 part of surfactant, 3~10 parts of sustained release agent；The insect-proof agent is Metadelphene, in Permethrin
One or two kinds of combinations, the waterproofing agent are selected from one of metal soap, paraffin class and organic silicon.
Preferably, described adhesive is selected from aliphatic polyurethane binders, aromatic urethane adhesives, polyacrylate
One of adhesive is a variety of.
Preferably, the thickener is acrylic thickener.
Preferably, the surfactant be Tween-80, Tween-60, Tween-40, Tween-20, Span-80,
One of Span-60, Span-40, Span-20 or more than one combination.
Preferably, the sustained release agent is polyacrylic resin or polyvinylpyrrolidone.
The present invention also provides a kind of preparation methods of the mosquito-proof type fabric of waterproof, include the following steps:
(1) 1~7.5 part of thickener is added into 50~150 parts of adhesives, stirs 20~30min, is uniformly mixed it,
5~25 parts of insect-proof agents, 2~15 parts of waterproofing agents are added, 20~30min is stirred, finally adds 0.5~2.5 part of surface-active
Agent, 3~10 parts of sustained release agents stir 20~30min, obtain the mosquito-proof slurry of waterproof；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in
80~100 DEG C bake 1~2min, finally bake 40~50s at 120~150 DEG C, obtain the mosquito-proof type fabric of waterproof.
Compared with the prior art, the advantages of the present invention are as follows: the mosquito-proof type fabric of waterproof in the present invention not only has preferably
The mosquito-proof effect of waterproof, but also have the characteristics that environmental protection, it is efficient, have broad application prospects.
Specific embodiment
The present invention is described further by the following example: according to following embodiments, the present invention may be better understood.
However, as it will be easily appreciated by one skilled in the art that specific material ratio, process conditions and its result described in embodiment are only used
In illustrating the present invention, without the present invention described in detail in claims should will not be limited.
The present invention discloses a kind of mosquito-proof type fabric of waterproof, is attached to fabric by the mosquito-proof coating of waterproof and obtains later through dry,
The mosquito-proof coating of waterproof by following mass parts material composition: 50~150 parts of adhesive, 1~7.5 part of thickener, insect-proof agent 5
~25 parts, 2~15 parts of waterproofing agent, 0.5~2.5 part of surfactant, 3~10 parts of sustained release agent；The insect-proof agent is Metadelphene, chlorine
The combination of one or both of pyrethroids, the waterproofing agent are selected from one of metal soap, paraffin class and organic silicon.
Invention additionally discloses a kind of preparation methods of the mosquito-proof type fabric of waterproof, include the following steps:
(1) 1~7.5 part of thickener is added into 50~150 parts of adhesives, stirs 20~30min, is uniformly mixed it,
5~25 parts of insect-proof agents, 2~15 parts of waterproofing agents are added, 20~30min is stirred, finally adds 0.5~2.5 part of surface-active
Agent, 3~10 parts of sustained release agents stir 20~30min, obtain the mosquito-proof slurry of waterproof；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in
80~100 DEG C bake 1~2min, finally bake 40~50s at 120~150 DEG C, obtain the mosquito-proof type fabric of waterproof.
Wherein, it is viscous to be selected from aliphatic polyurethane binders, aromatic urethane adhesives, polyacrylate for described adhesive
One of mixture is a variety of.
Wherein, the thickener is acrylic thickener.
Wherein, the surfactant be Tween-80, Tween-60, Tween-40, Tween-20, Span-80,
One of Span-60, Span-40, Span-20 or more than one combination.
Wherein, the sustained release agent is polyacrylic resin or polyvinylpyrrolidone.
Following preparation methods that the mosquito-proof type fabric of the waterproof in the present invention is illustrated with specifically embodiment.
Embodiment 1
(1) 1 part of thickener is added into 50 parts of adhesives, stirs 20min, is uniformly mixed it, is added 5 parts of insect prevention
20min is stirred in agent, 2 parts of waterproofing agents, finally adds 0.5 part of surfactant, 3 parts of sustained release agents, is stirred 20min, is obtained waterproof
Mosquito-proof slurry；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in
80 DEG C bake 1~2min, finally bake 40~50s at 120 DEG C, obtain the mosquito-proof type fabric of waterproof.
Embodiment 2
(1) 5 parts of thickeners are added into 100 parts of adhesives, stir 25min, are uniformly mixed it, are added 15 parts of insect prevention
25min is stirred in agent, 10 parts of waterproofing agents, finally adds 1.5 parts of surfactants, 6 parts of sustained release agents, is stirred 25min, is prevented
The mosquito-proof slurry of water；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in
90 DEG C bake 1~2min, finally bake 40~50s at 135 DEG C, obtain the mosquito-proof type fabric of waterproof.
Embodiment 3
(1) 7.5 parts of thickeners are added into 150 parts of adhesives, stir 30min, are uniformly mixed it, are added 25 parts and are prevented
30min is stirred in worm agent, 15 parts of waterproofing agents, finally adds 2.5 parts of surfactants, 10 parts of sustained release agents, is stirred 30min, is obtained
The mosquito-proof slurry of waterproof；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in
100 DEG C bake 1~2min, finally bake 40~50s at 150 DEG C, obtain the mosquito-proof type fabric of waterproof.
The mosquito-proof type fabric of waterproof in the present invention not only has the mosquito-proof effect of preferable waterproof, but also has environmental protection, height
The characteristics of effect, has broad application prospects.
Finally, it is to be noted that, the terms "include", "comprise" or its any other variant be intended to it is non-exclusive
Property include so that include a series of elements process, method, article or equipment not only include those elements, but also
Further include other elements that are not explicitly listed, or further include for this process, method, article or equipment it is intrinsic
Element.
Claims (6)
1. a kind of mosquito-proof type fabric of waterproof is attached to fabric by the mosquito-proof coating of waterproof and obtains later through dry, which is characterized in that institute
The mosquito-proof coating of waterproof is stated by the material composition of following mass parts: 50~150 parts of adhesive, 1~7.5 part of thickener, insect-proof agent 5~
25 parts, 2~15 parts of waterproofing agent, 0.5~2.5 part of surfactant, 3~10 parts of sustained release agent；The insect-proof agent is Metadelphene, chlorine chrysanthemum
The combination of one or both of ester, the waterproofing agent are selected from one of metal soap, paraffin class and organic silicon.
2. the mosquito-proof type fabric of waterproof according to claim 1, which is characterized in that described adhesive is selected from aliphatic polyurethane
One of adhesive, aromatic urethane adhesives, palyacrylate binder are a variety of.
3. the mosquito-proof type fabric of waterproof according to claim 1, which is characterized in that the thickener is acrylic thickener.
4. the mosquito-proof type fabric of waterproof according to claim 1, which is characterized in that the surfactant is Tween-
80, one of Tween-60, Tween-40, Tween-20, Span-80, Span-60, Span-40, Span-20 or a kind of with
On combination.
5. the mosquito-proof type fabric of waterproof according to claim 1, which is characterized in that the sustained release agent be polyacrylic resin or
Polyvinylpyrrolidone.
6. a kind of preparation method of the mosquito-proof type fabric of waterproof according to claim 1, which is characterized in that including walking as follows
It is rapid:
(1) 1~7.5 part of thickener is added into 50~150 parts of adhesives, stirs 20~30min, is uniformly mixed it, then plus
Enter 5~25 parts of insect-proof agents, 2~15 parts of waterproofing agents, stirs 20~30min, finally add 0.5~2.5 part of surfactant, 3
~10 parts of sustained release agents stir 20~30min, obtain the mosquito-proof slurry of waterproof；
(2) fabric is subjected to alkali cleaning, except starching, drying, then the mosquito-proof slurry of above-mentioned waterproof is coated in the surface of fabric, in 80~
100 DEG C bake 1~2min, finally bake 40~50s at 120~150 DEG C, obtain the mosquito-proof type fabric of waterproof.