CN110408440B - 一种用于蒸汽锅炉的节能添加剂及其应用 - Google Patents
一种用于蒸汽锅炉的节能添加剂及其应用 Download PDFInfo
- Publication number
- CN110408440B CN110408440B CN201910671691.0A CN201910671691A CN110408440B CN 110408440 B CN110408440 B CN 110408440B CN 201910671691 A CN201910671691 A CN 201910671691A CN 110408440 B CN110408440 B CN 110408440B
- Authority
- CN
- China
- Prior art keywords
- polyoxyethylene polyoxypropylene
- parts
- ether
- additive
- boiler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于蒸汽锅炉的节能添加剂及其应用，该添加剂包括以下重量份组分，高级烷醇1‑40份、高碳醇脂肪酸酯0‑40份、聚氧乙烯聚氧丙烯烷基醚0‑40份、聚氧乙烯聚氧丙烯脂肪酸酯0‑40份、糖脂1‑40份、聚氧乙烯聚氧丙烯硅氧烷0‑40份、氟碳聚氧乙烯聚氧丙烯醚0‑40份。与现有技术相比，本发明添加剂可有效降低水分子间的范德华力，降低锅炉水的表面张力，提高锅炉内水的蒸发效率，从而达到提高相同工况条件下锅炉的产气率，降低单位产量能耗；且添加剂的pH＝6‑8，对锅炉无腐蚀、无不良影响，在蒸汽锅炉原生产条件不变的状况下，按蒸汽锅炉內水质量的0.10‑0.15％添加本发明之节能添加剂，可比原不加添加剂的状态节约5‑15％的燃料。
Description
技术领域
本发明涉及公用工程领域，尤其是涉及一种用于蒸汽锅炉的节能添加剂及其应用。
背景技术
目前，我国室内供暖，工业加热的主要热源为蒸汽锅炉生产的高温蒸汽，每年消耗掉大量的天然气，燃料油和煤炭，产生的二氧化碳和有毒有害气体对大气和水土环境造成严重污染，因此国家大力体提倡减少化石燃料的使用。
现有的节能措施是通过对蒸汽锅炉的技术改造，使用燃料用节能添加剂等节能技术以减少煤炭，燃油以及天然气使用，运行成本高，节能效率有限。
因此，探索新的高效节能模式对于减少化石燃料的使用，节能降耗，减少环境污染具有重大的现实意义。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种可有效降低水的表面张力，提高水的蒸发效率，降低单位产气量的能源消耗，从而节约能源的用于蒸汽锅炉的节能添加剂及其应用。
本发明的目的可以通过以下技术方案来实现：
一种用于蒸汽锅炉的节能添加剂，其特征在于，该添加剂包括以下重量份组分，高级烷醇1-40份、高碳醇脂肪酸酯0-40份、聚氧乙烯聚氧丙烯烷基醚0-40份、聚氧乙烯聚氧丙烯脂肪酸酯0-40份、糖脂1-40份、聚氧乙烯聚氧丙烯硅氧烷0-40份、氟碳聚氧乙烯聚氧丙烯醚0-40份。
进一步地，所述的高级烷醇，有如下分子式：
CH3(CH2)n2OH或CH3(CH2)n2CH[CH3(CH2)m2]OH
式中：n2＝8-18，m2＝0-18；包括辛醇、葵醇，月桂醇，辛基十二醇,棕榈醇,硬脂醇中的一种或多种；
进一步地，所述的高碳醇脂肪酸酯有如下分子式：
CH3(CH2)n3OCO(CH2)m3CH3
式中：n3＝8-18，m3＝8-18；包括月桂醇硬脂酸酯、十四碳醇硬脂酸酯或棕榈醇硬脂酸酯中的一种或多种；
进一步地，所述的聚氧乙烯聚氧丙烯烷基醚有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x4(-CH2CH3-CH2-O-)y4-(CH2)n4CH3
式中：n4＝3-17，x4＝1-20，y4＝0-20；包括聚氧乙烯聚氧丙烯丁基醚，聚氧乙烯聚氧丙烯己基醚，聚氧乙烯聚氧丙烯乙基己基醚，聚氧乙烯聚氧丙烯壬基醚，聚氧乙烯聚氧丙烯月桂醚中的一种或多种；
进一步地，所述的聚氧乙烯聚氧丙烯脂肪酸酯有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x5(-CH2CH3-CH2-O-)y5OCO(CH2)n5CH3
式中：n5＝7-17，x5＝1-20，y5＝0-20；包括聚氧乙烯聚氧丙烯月桂酸酯、聚氧乙烯聚氧丙烯棕榈酸酯或聚氧乙烯聚氧丙烯硬脂酸酯中的一种或几种；
进一步地，所述的糖脂包括内酯型槐糖脂、酸型槐糖脂中的一种或两种，有如下分子式。
进一步地，所述的聚氧乙烯聚氧丙烯硅氧烷有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x7(-CH2CH3-CH2-O-)y7Sin7(OCH3)m7
式中：n7＝1-8，m7＝2n7+1，x7＝1-20，y7＝0-20；包括聚氧乙烯聚氧丙烯一硅氧烷、聚氧乙烯聚氧丙烯二硅氧烷，聚氧乙烯聚氧丙烯三硅氧烷，聚氧乙烯聚氧丙烯四硅氧烷，聚氧乙烯聚氧丙烯六硅氧烷，聚氧乙烯聚氧丙烯八硅氧烷中的一种或几种；
进一步地，所述的氟碳聚氧乙烯聚氧丙烯醚有如下分子式：
CH3CH2-O-(-CH2-CH2-O-)x8(-CH2CH3-CH2-O-)y8Cn8Fm8
式中：n8＝4-18，m8＝2n8+1，x8＝1-20，y8＝0-20；包括全氟丁基聚氧乙烯聚氧丙烯醚，全氟戊基聚氧乙烯聚氧丙烯醚，全氟己基聚氧乙烯聚氧丙烯醚和全氟乙基己基聚氧乙烯聚氧丙烯醚中的一种或几种；
优选地，该添加剂包括以下重量份组分，高级烷醇1～40份、优选1-20份；高碳醇脂肪酸酯1～40份、优选1-20份；聚氧乙烯聚氧丙烯烷基醚1～40份、优选1-20份；聚氧乙烯聚氧丙烯脂肪酸酯1～40份、优选1-20份，糖脂1～40份、优选1-20份；聚氧乙烯聚氧丙烯硅氧烷1～40份、优选1-20份；氟碳聚氧乙烯聚氧丙烯醚1～40份、优选1-20份。
上述用于蒸汽锅炉的节能添加剂通过常规方法混合制得：将各组分按照重量份含量分别称量后，常温搅拌混合均匀即得添加剂产品。
一种用于蒸汽锅炉的节能添加剂的应用，该添加剂按水质量的0.10-0.15％加于蒸汽锅炉内的水中。
与现有技术相比，本发明具有以下优点：
(1)可有效降低水分子间的范德华力，降低锅炉水的表面张力，提高锅炉内水的蒸发效率，从而达到提高相同工况条件下锅炉的产气率，降低单位产量能耗；
(2)添加剂的pH＝6-8，对锅炉无腐蚀、无不良影响，在蒸汽锅炉原生产条件不变的状况下，按蒸汽锅炉內水质量的0.10-0.15％添加本发明之节能添加剂，可比原不加添加剂的状态节约5-15％的燃料。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
下面各实施例中采用的添加剂原料的用量如无特别说明按重量份计：
实施例1
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①内酯型槐糖脂30份，其分子式为：
②全氟丁基聚氧乙烯(20)醚5份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)19C4F9
③正辛醇20份，其分子式为：
CH3(CH2)7OH
④聚氧乙烯(10)聚氧丙烯(10)月桂酸酯10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10CO(CH2)10CH3
⑤聚氧乙烯(10)聚氧丙烯(10)三硅氧烷25份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si3(OCH3)7
⑥聚氧乙烯聚氧丙烯月桂醚10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)11CH3
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某化工厂2吨燃煤蒸汽锅炉，向锅炉水中加入2公斤添加剂，锅炉原工况条件不变，运行一个月，平均节约燃煤12.6％。
实施例2
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①聚氧乙烯(10)聚氧丙烯(10)己基醚15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)5CH3
②葵醇15份，其分子式为：
CH3(CH2)9OH
③月桂醇硬脂酸酯15份，其分子式为：
CH3(CH2)11OCO(CH2)16CH3
④酸型槐糖脂20份，其分子式为：
⑤聚氧乙烯(10)聚氧丙烯(10)二硅氧烷25份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si2(OCH3)5
⑥棕榈醇10份，其分子式为：
CH3(CH2)15OH
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，将该添加剂应用于某印染厂5吨燃气蒸汽锅炉，向锅炉水中加入5公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油9.8％。
实施例3
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①全氟乙基己基聚氧乙烯醚(20)10份，其分子式为：
CH3CH2-O-(-CH2-CH2-O-)19C8F17
②月桂醇10份，其分子式为：
CH3(CH2)11OH
③聚氧乙烯(10)聚氧丙烯(10)硬脂酸酯10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10OCO(CH2)16CH3
④聚氧乙烯(10)聚氧丙烯(10)四硅氧烷35份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si4(OCH3)9
⑤槐糖脂20份，其分子式同实施例1。
⑥辛基十二醇15份，其分子式为：
CH3(CH2)10CH[CH3(CH2)7]OH
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某木材加工厂2.5吨燃油蒸汽锅炉，向锅炉水中加入2.5公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油7.8％。
实施例4
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①全氟己基聚氧乙烯醚(20)10份，其分子式为：
CH3CH2-O-(-CH2-CH2-O-)19C6F13
②葵醇20份，其分子式为：
CH3(CH2)9OH
③内酯型槐糖脂25份，其分子式同实施例1：
④聚氧乙烯聚氧丙烯硬脂酸酯10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10OCO(CH2)16CH3
⑤聚氧乙烯(10)聚氧丙烯(10)丁基醚10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)3CH3
⑥聚氧乙烯(10)聚氧丙烯(10)六硅氧烷25份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si6(OCH3)13
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某精密铸造厂2.5吨燃油蒸汽锅炉，向锅炉水中加入2.5公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油13.2％。
实施例5
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①全氟丁基聚氧乙烯(20)醚15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)19C4F9
②槐糖脂20份，其分子式同实施例2
③聚氧乙烯(10)聚氧丙烯(10)三硅氧烷15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si3(OCH3)7
④聚氧乙烯(10)聚氧丙烯(10)壬基醚15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)8CH3
⑤聚氧乙烯(10)聚氧丙烯(10)二硅氧烷15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si2(OCH3)5
⑥硬脂醇20份，其分子式为：
CH3(CH2)17OH
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某供热厂5吨燃油蒸汽锅炉，向锅炉水中加入5公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油12.5％。
实施例6
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①全氟戊基聚氧乙烯醚(20)10份，其分子式为：
CH3CH2-O-(-CH2-CH2-O-)19C5F11
②聚氧乙烯聚氧丙烯棕榈酸酯10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10CO(CH2)14CH3
③内酯型槐糖脂30份，其分子式同实施例1
④聚氧乙烯(10)聚氧丙烯(10)八硅氧烷15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si8(OCH3)17
⑤辛基十二醇20份，其分子式为：
CH3(CH2)10CH[CH3(CH2)7]OH
⑥聚氧乙烯(10)聚氧丙烯(10)一硅氧烷15份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si(OCH3)3
将上述6种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于造纸厂3吨燃油蒸汽锅炉，向锅炉水中加入3公斤节能添加剂，锅炉原工况条件不变，运行3个月，平均节约燃油10.7％。
实施例7
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①正葵醇10份，其分子式为：
CH3(CH2)9OH
②槐糖脂30份，其分子式同实施例2
③聚氧乙烯(10)聚氧丙烯(10)壬基醚5份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)3CH3
④全氟乙基己基聚氧乙烯醚5份，其分子式为：
CH3CH2-O-(-CH2-CH2-O-)19C8F17
⑤聚氧乙烯(10)聚氧丙烯(10)二硅氧烷10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si2(OCH3)5
⑥辛基十二醇20份，其分子式为：
CH3(CH2)10CH[CH3(CH2)7]OH
⑦聚氧乙烯(10)聚氧丙烯(10)三硅氧烷20份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si3(OCH3)7
将上述7种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某钢铁厂5吨燃油蒸汽锅炉，向锅炉水中加入5公斤节能添加剂，锅炉原工况条件不变，运行1.5个月，平均节约燃油11.2％。
实施例8
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①月桂醇15份，其分子式为：
CH3(CH2)11OH
②槐糖脂15份，其分子式同实施例1
③辛基十二醇15份，其分子式为：
CH3(CH2)10CH[CH3(CH2)7]OH
④月桂醇硬脂酸酯5份，其分子式为：
CH3(CH2)11OCO(CH2)16CH3
⑤聚氧乙烯聚氧丙烯硬脂酸酯5份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10OCO(CH2)16CH3
⑥聚氧乙烯(10)聚氧丙烯(10)己基醚5份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)5CH3
⑦聚氧乙烯(10)聚氧丙烯(10)三硅氧烷35份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si3(OCH3)7
将上述7种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某木材加工厂5吨燃油蒸汽锅炉，向锅炉水中加入5公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油15％。
实施例9
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
①全氟己基聚氧乙烯醚(20)10份，其分子式为：
CH3CH2-O-(-CH2-CH2-O-)19C6F13
②辛基十二醇20份，其分子式为：
CH3(CH2)10CH[CH3(CH2)7]OH
③内酯型槐糖脂20份，其分子式同实施例1
④棕榈醇硬脂酸酯5份，其分子式为：
CH3(CH2)15OCO(CH2)16CH3
⑤聚氧乙烯聚氧丙烯硬脂酸酯5份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10OCO(CH2)16CH3
⑥聚氧乙烯(10)聚氧丙烯(10)乙基己基醚10份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10(CH2)7CH3
⑦聚氧乙烯(10)聚氧丙烯(10)三硅氧烷30份，其分子式为：
CH3-CH2-O-(-CH2-CH2-O-)9(-CH2CH3-CH2-O-)10Si3(OCH3)7
将上述7种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂应用于某精密铸造厂2吨燃油蒸汽锅炉，向锅炉水中加入3公斤节能添加剂，锅炉原工况条件不变，运行2个月，平均节约燃油5％。
实施例10
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分，辛醇1份、内酯型槐糖脂1份，聚氧乙烯(10)聚氧丙烯(10)三硅氧烷1份。
将3种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂按水质量的0.12％加于某油脂加工厂的燃油蒸汽锅炉内，锅炉原工况条件不变，运行2个月，平均节约燃油5％。
实施例11
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分，葵醇1份、酸型槐糖脂1份，聚氧乙烯(10)聚氧丙烯(10)二硅氧烷1份。
将3种组分按重量份称量后混合均匀，即得添加剂产品，该添加剂按水质量的0.15％加于某化工厂的燃油蒸汽锅炉内，锅炉原工况条件不变，运行2个月，平均节约燃油15％。
实施例12
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
高级烷醇20份：由辛醇，葵醇，月桂醇按质量比1:1:1混合而成；
高碳醇脂肪酸酯5份：由月桂醇硬脂酸酯，十四碳醇硬脂酸酯，棕榈醇硬脂酸酯按质量比1:1:1混合而成；
聚氧乙烯聚氧丙烯烷基醚10份：由聚氧乙烯聚氧丙烯丁基醚，聚氧乙烯聚氧丙烯己基醚，聚氧乙烯聚氧丙烯乙基己基醚按质量比1:1:1混合而成；
聚氧乙烯聚氧丙烯脂肪酸酯5份：由聚氧乙烯聚氧丙烯月桂酸酯，聚氧乙烯聚氧丙烯棕榈酸酯，聚氧乙烯聚氧丙烯硬脂酸酯按质量比1:1:1混合而成；
糖脂25份：由内酯型槐糖脂、酸型槐糖脂按质量比1:1混合而成；
聚氧乙烯聚氧丙烯硅氧烷30份：聚氧乙烯聚氧丙烯一硅氧烷，聚氧乙烯聚氧丙烯二硅氧烷，聚氧乙烯聚氧丙烯三硅氧烷按质量比1:1:1混合而成；
氟碳聚氧乙烯聚氧丙烯醚5份：由全氟丁基聚氧乙烯聚氧丙烯醚，全氟己基聚氧乙烯聚氧丙烯醚，全氟乙基己基聚氧乙烯聚氧丙烯醚按质量比1:1:1混合而成；
将上述各组分按重量份称量后混合均匀，即得添加剂产品，该添加剂按水质量的0.1％加于某粮油加工厂的燃油蒸汽锅炉内，锅炉原工况条件不变，运行2个月，平均节约燃油15％。
实施例13
一种用于蒸汽锅炉的节能添加剂，该添加剂包括以下重量份组分：
高级烷醇40份：由辛醇，葵醇，月桂醇按质量比1:0.1:0.1混合而成；
高碳醇脂肪酸酯40份：由月桂醇硬脂酸酯，十四碳醇硬脂酸酯，棕榈醇硬脂酸酯按质量比1:0.1:0.1混合而成；
聚氧乙烯聚氧丙烯烷基醚40份：由聚氧乙烯聚氧丙烯丁基醚，聚氧乙烯聚氧丙烯己基醚，聚氧乙烯聚氧丙烯乙基己基醚按质量比1:0.1:0.1混合而成；
聚氧乙烯聚氧丙烯脂肪酸酯40份：由聚氧乙烯聚氧丙烯月桂酸酯，聚氧乙烯聚氧丙烯棕榈酸酯，聚氧乙烯聚氧丙烯硬脂酸酯按质量比1:0.1:0.1混合而成；
糖脂40份：由内酯型槐糖脂、酸型槐糖脂按质量比1:0.1混合而成；
聚氧乙烯聚氧丙烯硅氧烷40份：聚氧乙烯聚氧丙烯一硅氧烷，聚氧乙烯聚氧丙烯二硅氧烷，聚氧乙烯聚氧丙烯三硅氧烷按质量比1:0.1:0.1混合而成；
氟碳聚氧乙烯聚氧丙烯醚40份：由全氟丁基聚氧乙烯聚氧丙烯醚，全氟己基聚氧乙烯聚氧丙烯醚，全氟乙基己基聚氧乙烯聚氧丙烯醚按质量比1:0.1:0.1混合而成；
将上述各组分按重量份称量后混合均匀，即得添加剂产品，该添加剂按水质量的0.10％加于某化纤厂的燃油蒸汽锅炉内，锅炉原工况条件不变，运行2个月，平均节约燃油15％。
以上实施例仅用于说明本发明技术方案，并非是对本发明的限制，本技术领域的普通技术人员在本发明的实质范围内所做的改变、替代、修饰、简化均为等效的变换，都不脱离本发明的宗旨，也应属于本发明的权利要求保护范围。
Claims (4)
1.一种用于蒸汽锅炉的节能添加剂，其特征在于，该添加剂包括以下重量份组分，高级烷醇1-40份、高碳醇脂肪酸酯1-20份、聚氧乙烯聚氧丙烯烷基醚1-20份、聚氧乙烯聚氧丙烯脂肪酸酯1-20份、糖脂1-20份、聚氧乙烯聚氧丙烯硅氧烷1-20份、氟碳聚氧乙烯聚氧丙烯醚1-20份；
所述的高级烷醇有如下分子式：
CH3(CH2)n2 CH2OH，CH3(CH2)n2 CH [CH3(CH2)m2]OH
式中：n2=8-18，m2=0-18；
所述的高碳醇脂肪酸酯有如下分子式：
CH3(CH2)n3OCO(CH2)m3CH3
式中：n3=8-18，m3=8-18；
所述的聚氧乙烯聚氧丙烯烷基醚有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x4(-CH2CH3-CH2-O-)y4-(CH2)n4CH3
式中：n4=3-18，x4=1-20，y4=0-20；
所述的聚氧乙烯聚氧丙烯脂肪酸酯有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x5(-CH2CH3-CH2-O-)y5OCO(CH2)n5CH3
式中：n5=7-17，x5=1-20，y5=0-20；
所述的聚氧乙烯聚氧丙烯硅氧烷有如下分子式：
CH3-CH2-O-(-CH2-CH2-O-)x7(-CH2CH3-CH2-O-)y7Sin7(OCH3)m7
式中：n7=1-8，m7=2n7+1，x7=1-20，y7=0-20；
所述的氟碳聚氧乙烯聚氧丙烯醚有如下分子式：
CH3CH2-O-(-CH2-CH2-O-)x8(-CH2CH3-CH2-O-)y8Cn8Fm8
式中：n8=4-18，m8=2n8+1，x8=1-20，y8=0-20。
2.根据权利要求1所述的一种用于蒸汽锅炉的节能添加剂，其特征在于，所述的糖脂包括内酯型槐糖脂或酸型槐糖脂有如下分子式：
3.根据权利要求1所述的一种用于蒸汽锅炉的节能添加剂，其特征在于，
所述的高级烷醇包括葵醇，月桂醇，棕榈醇，硬脂醇中的一种或几种；
所述的高碳醇脂肪酸酯包括月桂醇硬脂酸酯，十四碳醇硬脂酸酯，棕榈醇硬脂酸酯中的一种或多种；
所述的聚氧乙烯聚氧丙烯烷基醚包括聚氧乙烯聚氧丙烯丁基醚，聚氧乙烯聚氧丙烯己基醚，聚氧乙烯聚氧丙烯乙基己基醚，聚氧乙烯聚氧丙烯壬基醚，聚氧乙烯聚氧丙烯月桂醚中的一种或多种；
所述聚氧乙烯聚氧丙烯脂肪酸酯包括聚氧乙烯聚氧丙烯月桂酸酯，聚氧乙烯聚氧丙烯棕榈酸酯，聚氧乙烯聚氧丙烯硬脂酸酯中的一种或几种；
所述的糖脂包括内酯型槐糖脂、酸型槐糖脂中的一种或两种；
所述聚氧乙烯聚氧丙烯硅氧烷包括聚氧乙烯聚氧丙烯一硅氧烷，聚氧乙烯聚氧丙烯二硅氧烷，聚氧乙烯聚氧丙烯三硅氧烷，聚氧乙烯聚氧丙烯四硅氧烷，聚氧乙烯聚氧丙烯六硅氧烷，聚氧乙烯聚氧丙烯八硅氧烷中的一种或几种；
所述氟碳聚氧乙烯醚包括全氟丁基聚氧乙烯聚氧丙烯醚，全氟戊基聚氧乙烯聚氧丙烯醚，全氟己基聚氧乙烯聚氧丙烯醚，全氟乙基己基聚氧乙烯聚氧丙烯醚中的一种或几种。
4.一种如权利要求1所述的用于蒸汽锅炉的节能添加剂的应用，其特征在于，该添加剂按蒸汽锅炉内水质量的0.10-0.15%加于蒸汽锅炉内的水中。