CN110408258A - Coating and preparation method thereof, the cated cooker of tool and preparation method thereof - Google Patents
Coating and preparation method thereof, the cated cooker of tool and preparation method thereof Download PDFInfo
- Publication number
- CN110408258A CN110408258A CN201910719595.9A CN201910719595A CN110408258A CN 110408258 A CN110408258 A CN 110408258A CN 201910719595 A CN201910719595 A CN 201910719595A CN 110408258 A CN110408258 A CN 110408258A
- Authority
- CN
- China
- Prior art keywords
- cooker
- coating
- preparation
- blank
- cated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses coating and preparation method thereof, the cated cooker of tool and preparation method thereof, and the constituent of the coating includes cannabis oil.When carrying out vegetable cutting culinary art, the cannabis oil of rich in nutrition content can penetrate into vegetable cook from cooker coating, can not only increase one of flavor for vegetable, but also can supplement vegetable nutriment, a person sponging on an aristocrat is enable to have the vegetable of more delicious more nutrition；Gaps in market has been filled up, vast market prospect is possessed.
Description
Technical field
The present invention relates to cooker technical field more particularly to coating and preparation method thereof, the cated cooker of tool and its systems
Preparation Method.
Background technique
Cooker in kitchen includes but is not limited to pot body, pot cover, slice, spoon, cutter, knife rest and dishes, currently, big portion
Divide on cooker and be designed with coating, but existing coating is often from raising cooker wearability, resistance to soiling, non-stick, heat-resisting quantity
Etc. be designed, it is cooker that these coatings, which act on main body,.Till now, there are no any cooker coating be from
It is designed in terms of supplement vegetable nutriment, this is gaps in market.
Summary of the invention
The technical problems to be solved by the present invention are: provide a kind of coating and preparation method thereof, the cated cooker of tool and
Preparation method, the coating which forms on cooker can supplement the nutriment of vegetable.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention one are as follows: coating, its components include hemps
Oil.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention two are as follows: the preparation method of coating prepares base
Material；Cannabis oil is added in the preparation process of base-material and stirs, alternatively, cannabis oil is added in the base-material completed to preparation and stirs
It mixes.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention three are as follows: have cated cooker, the cooker
The coating formed by forming the coating that cost includes cannabis oil.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention four are as follows: have the preparation side of cated cooker
Method,
Cleaning: cooker blank is cleaned, is then dried；
Coating: including on the surface of the cooker blank of the coating coating of cannabis oil after cleaning by constituent；
Solidify: by the paint solidification on the surface of cooker blank, forming coating.
The beneficial effects of the present invention are: cook is when carrying out vegetable cutting culinary art, the cannabis oil meeting of rich in nutrition content
It is penetrated into vegetable from cooker coating, one of flavor can not only be increased for vegetable, but also vegetable nutriment can be supplemented, made
A person sponging on an aristocrat can have the vegetable of more delicious more nutrition；Gaps in market has been filled up, vast market prospect is possessed.
Specific embodiment
To explain the technical content, the achieved purpose and the effect of the present invention in detail, it is explained below in conjunction with embodiment.
Cannabis oil includes hemp-seed oil and CBD oil etc., and hemp-seed oil originates from cannabis seeds, and it is edible to be mainly used for auxotype
Oil and skin care item are added as nutritional ingredient, CBD oil mainly extracts from floral leaf and the stem of cannabis plants, is mainly used for medical treatment.
Cannabis oil (hemp oil) can be used for describing any and all oil extracted from any part of industrial hemp, including industrial hemp
Stem, flower and seed of plant etc..Although cannabis oil includes CBD oil, one usually is described using this term of cannabis oil in the industry
The widely used nutritional oil for being known as hemp-seed oil of kind.Hemp-seed oil (hemp seed oil) is by cold press cannabis plants
Auxotype made of seed eats cooking oil, it has dark color to limpid light green color and natural mild nut taste, is suitable for
Salad and sauce.Hemp-seed oil is described generally as " super food ", contains important nutritional ingredient, including amino acid, fiber
Element, Omega-3 and Omega-6 fatty acid and a series of important vitamin and minerals.
The most critical design of the present invention is: the very high cannabis oil of nutritive value is doped in the coating of cooker, kitchen
When using cooker, the cannabis oil in coating can be sustained in vegetable teacher, to supplement the nutriment of vegetable.
Coating, its components include cannabis oils.
The preparation method of coating, prepares base-material；Cannabis oil is added in the preparation process of base-material and stirs, alternatively, to system
Cannabis oil is added in the standby base-material completed and stirs.
Has cated cooker, the coating of the cooker is formed by forming the coating that cost includes cannabis oil.
As can be seen from the above description, the beneficial effects of the present invention are: cook is when carrying out vegetable cutting culinary art, nutritional ingredient
Cannabis oil abundant can penetrate into vegetable from cooker coating, can not only increase one of flavor for vegetable, but also can supplement
Vegetable nutriment enables a person sponging on an aristocrat to have the vegetable of more delicious more nutrition；Gaps in market is filled up, before possessing wide market
Scape.
Further, the cooker is pot body, pot cover, slice, spoon, cutter, knife rest or dishes.
Seen from the above description, the type of cooker is varied.
Further, the coating is non-sticking lining, hydrophobic oleophobic coating, scratch-resistant coating, high-temperaure coating and resistant
One of coating is a variety of.
Seen from the above description, the type of coating is varied.
Further, the material of the cooker is glass, stainless steel, aluminium alloy or cast iron.
Seen from the above description, the material of cooker is varied.
Have the preparation method of cated cooker,
Cleaning: cooker blank is cleaned, is then dried；
Coating: including on the surface of the cooker blank of the coating coating of cannabis oil after cleaning by constituent；
Solidify: by the paint solidification on the surface of cooker blank, forming coating.
Seen from the above description, has the preparation process of cated cooker simply, conveniently.
Further, further include step before the cleaning, degreasing washing: cooker blank is subjected to ungrease treatment, then
Washing.
Seen from the above description, degreasing washing can remove cooker surface greasy dirt, to improve post-coatings coating effect.
It further, further include step, surface active: by the surface active of cooker blank after the degreasing washing.
Seen from the above description, surface activation process can be improved post-coatings coating effect.
Further, further include step after degreasing washing, surface roughness processing: to the surface of cooker blank into
Row polishing.
Seen from the above description, surface roughness processing can be improved post-coatings coating effect.
Embodiment one
The embodiment of the present invention one are as follows: coating, its components include cannabis oils.The coating is non-stick pan coating, dredges
One of water oleophobic coating, mar-proof coating, high-temperature resistant coating and antifouling paint are a variety of.
The present embodiment also provides a kind of preparation method of coating, prepares base-material；Hemp is added in the preparation process of base-material
Oil simultaneously stirs, alternatively, cannabis oil is added in the base-material completed to preparation and stirs.The base-material is chosen as existing cooker coating and applies
Material, in other words, the optional non-stick pan coating in the prior art of base-material, hydrophobic oleophobic coating, mar-proof coating, high-temperature resistant coating
With one of antifouling paint or a variety of.
Embodiment two
The embodiment of the present invention two are as follows: have cated cooker, the coating of the cooker includes big by forming cost
The coating of sesame oil is formed.
The cooker is pot body, pot cover, slice, spoon, cutter, knife rest or dishes.Preferably, the cooker is pot
Body.
The coating is one in non-sticking lining, hydrophobic oleophobic coating, scratch-resistant coating, high-temperaure coating and resistant coating
Kind is a variety of.
The material of the cooker is glass, stainless steel, aluminium alloy or cast iron.
The present embodiment also provides a kind of preparation method for having cated cooker,
Cleaning: cooker blank is cleaned, is then dried；
Coating: including on the surface of the cooker blank of the coating coating of cannabis oil after cleaning by constituent；
Solidify: by the paint solidification on the surface of cooker blank, forming coating.
Further, further include step before the cleaning, degreasing washing: cooker blank is subjected to ungrease treatment, then
Washing.
It optionally, further include step, surface active: by the surface active of cooker blank after the degreasing washing.
Optionally, further include step after the degreasing washing, surface roughness processing: the surface of cooker blank is carried out
Polishing.
Embodiment three
The embodiment of the present invention three are as follows: a kind of preparation method of the cooker with non-sticking lining includes the following steps: to cook a meal
Have blank and carry out ungrease treatment, the greasy dirt of cooker blank surface is removed, specifically, the cooker blank is immersed in alkaline solution
Middle carry out ungrease treatment, the temperature of the ungrease treatment are 45~55 DEG C, and the time is 4~6min.It can be added in alkaline solution
Surfactant with cleaning function, concentration can be arranged according to specific needs.
Cooker blank after ungrease treatment is subjected to first wash, removes the remaining alkaline solution of cooker blank surface.
The temperature of the first wash is 20~30 DEG C, and the time is 2~4min.
Cooker blank after first wash is activated, to increase the electric conductivity of cooker surface, to mention
The high subsequent adhesive force for carrying out electrophoretic coating when ability cathode electrophoresis.It is carried out specifically, the cooker blank is immersed in activating solution
It is activated, the temperature of the activation processing is 20~30 DEG C, and the time is 9~11min.It can be added in activating solution a certain amount of
Acidic materials, such as hydrochloric acid etc..
Second wash is carried out to the cooker blank after activation processing, to remove the remaining activating solution of cooker blank surface.
Specifically, the temperature of the second wash is 20~30 DEG C, the time is 2~4min.
Cooker blank after second wash is immersed in water-soluble cathode electrophoresis dope and constitutes electrolytic circuit, makes institute
The surface for stating cooker blank forms electrophoretic coating.Cathode electrophoresis dope dissociates the resin ion of electrification in aqueous solution, these
The resin particle of electrification is together with the pigment particles electrophoresis adsorbed by resin ion to cooker blank surface and loses charge shape
At electrophoretic coating.The temperature for forming the electrophoretic coating is 20~30 DEG C, and the time is 2~4min.
Third time washing is carried out to the cooker blank for being formed with electrophoretic coating, to remove the remaining painting of cooker blank surface
Material, can first spray washing, then soaking and water washing.The temperature of the third time washing is 20~30 DEG C, and the time is 2~4min.
Cooker blank after washing to third time carries out drying and processing, and cooker blank is put into oven, the electricity of reinforced surface
Swimming coating, and dry the moisture on surface.The temperature of the drying and processing is 140~160 DEG C, and the time is 40~60min.
The cooker blank for being formed with electrophoretic coating is sprayed, the surface of the electrophoretic coating is formed and transparent does not glue
Coating.Wherein, the constituent of coating used in spraying includes cannabis oil.Cooking a meal with non-sticking lining provided in this embodiment
The preparation method of tool, non-sticking lining will not cover the lines of cooker blank itself, and cooker blank can also be made to retain original gold
Belong to texture, and electrophoretic coating is strong in the adhesive force of cooker blank surface, can extend the service life of cooker.
The embodiment of the present invention four are as follows:
A kind of preparation method of the cooker with non-sticking lining, with embodiment three the difference is that:
The temperature of the ungrease treatment is 50 DEG C, time 5min；The temperature of the first wash is 25 DEG C, and the time is
3min；The temperature of the activation processing is 25 DEG C, time 10min；The temperature of the second wash is 25 DEG C, and the time is
3min；The temperature for forming the electrophoretic coating is 25 DEG C, time 3min；The temperature of the third time washing is 25 DEG C, the time
For 3min；The temperature of the drying and processing is 150 DEG C, time 50min.
The embodiment of the present invention five are as follows:
A kind of preparation method of the cooker with non-sticking lining, with embodiment three the difference is that:
The temperature of the ungrease treatment is 45 DEG C, time 6min；The temperature of the first wash is 30 DEG C, and the time is
2min；The temperature of the activation processing is 30 DEG C, time 9min；The temperature of the second wash is 30 DEG C, and the time is
2min；The temperature for forming the electrophoretic coating is 30 DEG C, time 2min；The temperature of the third time washing is 30 DEG C, the time
For 2min；The temperature of the drying and processing is 160 DEG C, time 40min.
The embodiment of the present invention six are as follows:
A kind of preparation method of the cooker with non-sticking lining, with embodiment three the difference is that:
The temperature of the ungrease treatment is 5 DEG C, time 4min；The temperature of the first wash is 20 DEG C, and the time is
4min；The temperature of the activation processing is 20 DEG C, time 11min；The temperature of the second wash is 20 DEG C, and the time is
4min；The temperature for forming the electrophoretic coating is 20 DEG C, time 4min；The temperature of the third time washing is 20 DEG C, the time
For 4min；The temperature of the drying and processing is 140 DEG C, time 60min.
The cooker coating layer thickness that embodiment three to embodiment six is prepared is respectively less than 10 microns, will not cover cooker base
The lines and color of part itself are clear that cooker blank surface especially for the cooker blank after wire drawing process
Texture.
Measure of merit
Adhesion property test, test result are carried out respectively to the coating for the cooker that embodiment three to embodiment six is prepared
Show the adhesive force between the adhesive force and non-sticking lining and electrophoretic coating between electrophoretic coating and cooker blank of the invention
Much larger than the adhesive force between traditional non-sticking lining and cooker blank.
The embodiment of the present invention seven are as follows:
A kind of preparation method of the iron cooker with non-sticking lining includes the following steps: first to be suspended to cooker blank
On automatic bracing wire hanger, guarantee not falling off, then cooker blank is immersed in degreasing tank to (liquid includes following weight in oil groove
The component of part: 75 parts of clear water, 15 parts of degreasing agents and 10 parts of degreasing powders), oil removing is carried out, the oil removing time is 12-15 minutes.
Cooker blank enters Rinsing Area, clear water washing time is after coming out in degreasing tank after being sprayed with clear water
8-10 minutes.
Cooker blank enters table tune slot after coming out from Rinsing Area, and (liquid includes the component of following parts by weight in table tune slot: 95
Part clear water and 10 parts of tables are adjusted), it is 5-8 minutes between table timing.
Cooker blank from table tune slot come out after enter Phosphating Slot (liquid includes the component of following parts by weight in Phosphating Slot:
75 parts of clear water, 15 portions of bonderites and 10 parts of promotors), phosphating time is 20-25 minutes.
It is again introduced into Rinsing Area processing after the completion of cooker blank phosphatization, then is sprayed with clear water, it is desirable that cooker blank table
Face is printed without grease stain, without liquid medicine.
After reaching requirement, cooker blank is put into oven drying, drying temperature is 150 DEG C -180 DEG C, 20-30 minutes, is cooked a meal
Have blank pre-processing to complete.
The cooker blank that pre-processing is completed is hung to automatic spraying bracing wire hanger, and cooker blank go to dedusting area into
Row dedusting, cleaning.
Cleaning complete back guy by cooker blank be transported to automatic spraying machine carry out first time spraying, about 3-5 minutes, then
Some dead angles of cooker blank are sprayed by hand, complete spray treatment, the constituent for spraying coating used includes hemp
Oil.
The cooker blank that spraying is completed is put into 280 DEG C of -300 DEG C of ovens and toasts, the time be 25-30 minutes to get
Finished product.
The embodiment of the present invention eight are as follows:
A kind of preparation method of the aluminium cooking utensils with non-sticking lining includes the following steps: first to be suspended to cooker blank
On automatic bracing wire hanger, guarantee not falling off, then cooker blank is immersed in degreasing tank to (liquid includes following weight in oil groove
The component of part: 70 parts of clear water, 15 parts of degreasing agents and 10 parts of degreasing powders), oil removing is carried out, the oil removing time is 8-10 minutes.
1. number clear water zone is transported it into after the completion of the cleaning of cooker blank, cooker blank is rinsed with high-pressure pump clear water, then will
Cooker blank transports 2. number clear water zone, rinses cooker blank with high-pressure pump clear water again.
After the completion of cooker blank rinses, 150 DEG C of -180 DEG C of ovens drying are put it into, drying time is 12-15 minutes,
Ask cooker blank surface without greasy dirt, water stain-free.
The cooker blank of drying is put into automatic sand shaker, is surface-treated with (60#-80#) Brown Alundum, makes cooker base
There is harsh feeling on part surface, without greasy dirt.
The cooker blank for completing surface polishing is placed into cleaning bracing wire, and is delivered to high-pressure hydraulic pump and is rinsed, is rushed
Wash surface dirt.
Cooker blank is placed on automatic spraying coating line after the completion of flushing, automatic spraying coating line by cooker blank be sent into 100 DEG C-
120 DEG C of preheating chambers.
Coating spraying is carried out to the cooker blank after the completion of preheating, the constituent that coating sprays coating used includes hemp
Oil.
The cooker blank that spraying is completed is put into 250 DEG C of -280 DEG C of ovens, is toasted 20-25 minutes.
Cooker blank reverse side is processed by shot blasting after the completion of baking.
Oil spout processing is carried out to cooker blank reverse side after the completion of polishing.
The cooker blank that oil spout is completed is put into 280 DEG C -300 DEG C, baking time is 20-25 minutes, after the completion finished product packet
Dress.
In conclusion coating provided by the invention and preparation method thereof, the cated cooker of tool and preparation method thereof, not only
One of flavor can be increased for vegetable, but also vegetable nutriment can be supplemented, a person sponging on an aristocrat is enable to have more delicious more nutrition
Vegetable；Gaps in market has been filled up, vast market prospect is possessed.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalents made by bright description are applied directly or indirectly in relevant technical field, are similarly included in this hair
In bright scope of patent protection.
Claims (10)
1. coating, it is characterised in that: its components include cannabis oils.
2. the preparation method of coating described in claim 1, it is characterised in that:
Prepare base-material；
Cannabis oil is added in the preparation process of base-material and stirs, alternatively, cannabis oil is added in the base-material completed to preparation and stirs
It mixes.
3. having cated cooker, it is characterised in that: the coating of the cooker is formed by coating described in claim 1.
4. the cated cooker of tool according to claim 3, it is characterised in that: the cooker be pot body, pot cover, slice,
Spoon, cutter, knife rest or dishes.
5. the cated cooker of tool according to claim 3, it is characterised in that: the coating is non-sticking lining, hydrophobic dredges
One of oil coating, scratch-resistant coating, high-temperaure coating and resistant coating are a variety of.
6. the cated cooker of tool according to claim 3, it is characterised in that: the material of the cooker is glass, stainless
Steel, aluminium alloy or cast iron.
7. having the preparation method of cated cooker, it is characterised in that:
Cleaning: cooker blank is cleaned, is then dried；
Coating: will be on the surface of the cooker blank of the coating of coating described in claim 1 after cleaning；
Solidify: by the paint solidification on the surface of cooker blank, forming coating.
8. the preparation method of the cated cooker of tool according to claim 7, it is characterised in that: also wrapped before the cleaning
Step is included, degreasing washing: cooker blank being subjected to ungrease treatment, is then washed.
9. the preparation method of the cated cooker of tool according to claim 8, it is characterised in that: after the degreasing washing
It further include step, surface active: by the surface active of cooker blank.
10. the preparation method of the cated cooker of tool according to claim 8, it is characterised in that: the degreasing washes it
After further include step, surface roughness processing: polish the surface of cooker blank.