CN110359282A - A kind of wicking function ameliorative way of viscose glue class fabric - Google Patents
A kind of wicking function ameliorative way of viscose glue class fabric Download PDFInfo
- Publication number
- CN110359282A CN110359282A CN201910589613.6A CN201910589613A CN110359282A CN 110359282 A CN110359282 A CN 110359282A CN 201910589613 A CN201910589613 A CN 201910589613A CN 110359282 A CN110359282 A CN 110359282A
- Authority
- CN
- China
- Prior art keywords
- viscose glue
- glue class
- class fabric
- ameliorative way
- wicking function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to fabric processing technology fields, more particularly to a kind of wicking function ameliorative way of viscose glue class fabric, include the following steps: A1, viscose glue class fabric is placed in Special Finishing liquid handles, the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer, and the solution of the anionic aryl sulfonic acid ester polymer accounts for the 2-4% of Special Finishing liquid total weight.For the present invention by using the mode of converse thought, anionic aryl sulfonic acid ester polymer fills up gap between fabric tissue as crosslinking agent, solves the problems, such as that moisture caused by gap is excessive climbs difficult weak tendency, 100g/m2Viscose glue class fabric can achieve under AATCC 197-2013 testing standard 15 ± 1cm/30min wicking requirement, have the function of super wicking.
Description
Technical field
The present invention relates to fabric processing technology fields, and in particular to a kind of wicking function ameliorative way of viscose glue class fabric.
Background technique
With the development of economy, people require the indices of clothes higher and higher, refer in face of instantly stringent test
Mark requires, in addition the particularity (bright and clean, the special skin-core structure of fiber surface) and ultra-thin dry goods sheet of viscose glue fibre structure itself
Body structure problem causes the dry goods to handle (such as nonionic surfactant, such as wetting agent, bleeding agent by conventional hydrophilic
Deng) moisture climbs extremely difficult under standard test condition, it is extremely difficult to existing index request, so to use other processing sides
Formula reaches super wicking function.
Summary of the invention
In order to overcome shortcoming and defect existing in the prior art, the purpose of the present invention is to provide a kind of viscose glue class fabrics
Wicking function ameliorative way.
The purpose of the invention is achieved by the following technical solution:
A kind of wicking function ameliorative way of viscose glue class fabric, include the following steps: A1, viscose glue class fabric is placed in it is special
It is handled in finishing fluid, the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer, the anion
The solution of type aryl sulfonic acid ester polymer accounts for the 2-4% of Special Finishing liquid total weight.
By using the mode of converse thought, anionic aryl sulfonic acid ester polymer fills up fabric group as crosslinking agent
A gap is knitted, solves the problems, such as that moisture caused by gap is excessive climbs difficult weak tendency, 100g/m2Viscose glue class fabric in AATCC
The wicking requirement that can achieve 15 ± 1cm/30min under 197-2013 testing standard, has the function of super wicking.
Wherein, the solution of the anionic aryl sulfonic acid ester polymer is Nylofixan HF liq.Nylofixan
HF liq comprising following composition:
This is a kind of high-effect color fixing agent with agent, can be used for all nylon fibers and its cotton-spinning fabric, after dyeing, stamp
Post-processing use, can be improved fabric every color fastness performance.Applicant has found during accidentally, this is used with agent
In the post-processing of viscose glue class fabric, film layer appropriate can be formed in fiber surface, fill up gap between fabric tissue, solve seam
Moisture caused by gap is excessive climbs difficult weak tendency problem, to greatly improve the wicking function of viscose glue class fabric.
Wherein, the treatment temperature of the step A1 is 50-70 DEG C, and the processing time is 10-30min.Item is crosslinked by optimization
Part can be certain crosslinking degree but the channel of moisture conveying will not be blocked because of excessive crosslinking.
Wherein, further include step A2 after the step A1: viscose glue class fabric being placed in feel treatment fluid and is padded,
The bleeding agent of hydrophilic hand feel finishing agent and 0.5-1.5g/L in the feel inorganic agent including 10-30g/L.The reasonable parent of cooperation
Water finishing technique can guarantee the original hydrophilicity of fabric and soft feel, thus guaranteeing original style and performance (color
Fastness, feel, hydrophily etc.) on the basis of solve viscose glue class it is ultra-thin knitting fabric wicking feature dissatisfaction status.
Wherein, the hydrophilic hand feel finishing agent is 2,3- epoxypropyltrimethylchloride chloride.
Wherein, in the step A2, the pick-up padded is 70-90%.Optimizing the pick-up parameter padded can make to knit
Object is more fluffy under physical mechanical effect, can also promote the absorbability and conveying capacity of moisture to a certain extent.
Wherein, further include step A0 before the step A1: viscose glue class fabric is successively carried out at oil removal treatment and dyeing
Reason.Preferably, oil removal treatment is to carry out oil removing twice to viscose glue class fabric using the degreaser of 0.6-1.0g/L, when each oil removing
Between be 10-20min；The temperature of dyeing processing is 60-80 DEG C, and the processing time is 30-60min.It can guarantee fabric well
Fastness properties.
Wherein, the grammes per square metre is 50-120g/m2.It such as can be 50g/m2、55g/m2、62g/m2、74g/m2、81g/
m2、92g/m2、95g/m2、100g/m2、107g/m2、115g/m2、120g/m2Deng the wicking function of those viscose glue class fabrics is not
It can be handled by conventional hydrophilic and reach higher standard.
Wherein, the viscose glue class fabric includes the viscose rayon of 25-100wt%.Such as can be 25wt%, 32wt%,
37wt%, 45wt%, 51wt%, 55wt%, 58wt%, 64wt%, 77wt%, 84wt%, 88wt%, 93wt%, 100wt%
Deng can be adjusted based on business demand.
Wherein, the viscose glue class fabric includes the Modal fibre of 45-75wt% and the viscose rayon of 25-55wt%.Not
Dai Er fiber is a kind of staple fibre, and the good flexibility and excellent hygroscopicity that itself has can improve fabric
Can, at the same can also wicking function ameliorative way through the invention reach preferable wicking function.
Wherein, the viscose glue class fabric includes the viscose rayon and 10wt% of the Modal fibre of 58wt%, 32wt%
Spandex fibre.The elasticity of fabric can be improved in the participation of spandex fibre, meets industry demand, is using the face in the present invention
Material carries out embodiment, but wicking function ameliorative way of the invention is also applicable to the viscose rayon of 25-100wt%, and
And it can achieve apparent improvement.
The beneficial effects of the present invention are: mode of the present invention by using converse thought, anionic aromatic yl sulphonate
Polymer fills up gap between fabric tissue as crosslinking agent, solves the problems, such as that moisture caused by gap is excessive climbs difficult weak tendency,
100g/m2Viscose glue class fabric can achieve under AATCC 197-2013 testing standard 15 ± 1cm/30min wicking requirement,
Has the function of super wicking.Cooperate simultaneously it is specific after whole processing hydrophilic finiss technique and dry, specific rear whole hydrophilic treated
It can guarantee the original hydrophilicity of fabric and soft feel, and specifically drying mode can be such that fabric makees in physical mechanical
It is more fluffy under, the absorbability and conveying capacity of moisture can be also promoted to a certain extent.
Specific embodiment
For the ease of the understanding of those skilled in the art, below with reference to embodiment, the present invention is further illustrated, real
The content that the mode of applying refers to not is limitation of the invention.
Embodiment 1
A kind of wicking function ameliorative way of viscose glue class fabric, include the following steps: A1, viscose glue class fabric is placed in it is special
It is handled in finishing fluid, the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer, the anion
The solution of type aryl sulfonic acid ester polymer accounts for the 3% of Special Finishing liquid total weight, remaining is water.
Wherein, the solution of the anionic aryl sulfonic acid ester polymer is Nylofixan HF liq.
Wherein, the treatment temperature of the step A1 is 60 DEG C, and the processing time is 20min.
Wherein, further include step A2 after the step A1: viscose glue class fabric being placed in feel treatment fluid and is padded,
The bleeding agent of hydrophilic hand feel finishing agent and 1g/L in the feel inorganic agent including 20g/L.
Wherein, the hydrophilic hand feel finishing agent is 2,3- epoxypropyltrimethylchloride chloride.
Wherein, in the step A2, the pick-up padded is 80%.
Wherein, further include step A0 before the step A1: viscose glue class fabric is successively carried out at oil removal treatment and dyeing
Reason.Oil removal treatment is to carry out oil removing twice to viscose glue class fabric using the degreaser of 0.8g/L, and each oil removing time is 15min；
The temperature of dyeing processing is 70 DEG C, and the processing time is 45min.
Wherein, the grammes per square metre of the viscose glue class fabric is 100g/m2。
Embodiment 2
A kind of wicking function ameliorative way of viscose glue class fabric, include the following steps: A1, viscose glue class fabric is placed in it is special
It is handled in finishing fluid, the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer, the anion
The solution of type aryl sulfonic acid ester polymer accounts for the 2% of Special Finishing liquid total weight, remaining is water.
Wherein, the solution of the anionic aryl sulfonic acid ester polymer is Nylofixan HF liq.
Wherein, the treatment temperature of the step A1 is 50 DEG C, and the processing time is 30min.
Wherein, further include step A2 after the step A1: viscose glue class fabric being placed in feel treatment fluid and is padded,
The bleeding agent of hydrophilic hand feel finishing agent and 0.5g/L in the feel inorganic agent including 10g/L.
Wherein, the hydrophilic hand feel finishing agent is 2,3- epoxypropyltrimethylchloride chloride.
Wherein, in the step A2, the pick-up padded is 70%.
Wherein, further include step A0 before the step A1: viscose glue class fabric is successively carried out at oil removal treatment and dyeing
Reason.Preferably, oil removal treatment is to carry out oil removing twice to viscose glue class fabric using the degreaser of 0.6g/L, and each oil removing time is
20min；The temperature of dyeing processing is 60 DEG C, and the processing time is 60min.
Wherein, the grammes per square metre of the viscose glue class fabric is 100g/m2。
Embodiment 3
A kind of wicking function ameliorative way of viscose glue class fabric, include the following steps: A1, viscose glue class fabric is placed in it is special
It is handled in finishing fluid, the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer, the anion
The solution of type aryl sulfonic acid ester polymer accounts for the 4% of Special Finishing liquid total weight, remaining is water.
Wherein, the solution of the anionic aryl sulfonic acid ester polymer is Nylofixan HF liq.
Wherein, the treatment temperature of the step A1 is 70 DEG C, and the processing time is 10min.
Wherein, further include step A2 after the step A1: viscose glue class fabric being placed in feel treatment fluid and is padded,
The bleeding agent of hydrophilic hand feel finishing agent and 1.5g/L in the feel inorganic agent including 30g/L.
Wherein, the hydrophilic hand feel finishing agent is 2,3- epoxypropyltrimethylchloride chloride.
Wherein, in the step A2, the pick-up padded is 90%.
Wherein, further include step A0 before the step A1: viscose glue class fabric is successively carried out at oil removal treatment and dyeing
Reason.Preferably, oil removal treatment is to carry out oil removing twice to viscose glue class fabric using the degreaser of 1.0g/L, and each oil removing time is
10min；The temperature of dyeing processing is 80 DEG C, and the processing time is 30min.
Wherein, the grammes per square metre of the viscose glue class fabric is 100g/m2。
Comparative example 1
This comparative example the difference from embodiment 1 is that: step A1 is handled using polyether type polyester hydrophilic finishing agent.
Comparative example 2
This comparative example the difference from embodiment 1 is that: step A1 is handled using polysiloxane-based hydrophilic finishing agent.
Comparative example 3
This comparative example the difference from embodiment 1 is that: step A1 use polyurethanes hydrophilic finishing agent.
Testing surface, embodiment 1-3 and comparative example 1-3 are greatly improved to the hydrophily of fabric, but in AATCC
Under 197-2013 testing standard, test condition be it is fixed, humidity is fixed as 65%, and temperature is fixed as 20 DEG C ± 1 DEG C, embodiment
The fabric of 1-3 can achieve the test index of 15 ± 1cm/30min, but comparative example 1-3 can only achieve the survey of 11 ± 1cm/30min
Try index.
Above-described embodiment is the preferable implementation of the present invention, and in addition to this, the present invention can be realized with other way,
Do not depart under the premise of present inventive concept it is any obviously replace it is within the scope of the present invention.
Claims (10)
1. a kind of wicking function ameliorative way of viscose glue class fabric, characterized by the following steps: A1, by viscose glue class face
Material, which is placed in Special Finishing liquid, to be handled, and the Special Finishing liquid includes the solution of anionic aryl sulfonic acid ester polymer,
The solution of the anionic aryl sulfonic acid ester polymer accounts for the 2-4% of Special Finishing liquid total weight.
2. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: it is described yin from
The solution of subtype aryl sulfonic acid ester polymer is Nylofixan HF liq.
3. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: the step
The treatment temperature of A1 is 50-70 DEG C, and the processing time is 10-30min.
4. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: the step
Further include step A2 after A1: viscose glue class fabric being placed in feel treatment fluid and is padded, includes in the feel inorganic agent
The bleeding agent of hydrophilic the hand feel finishing agent and 0.5-1.5g/L of 10-30g/L.
5. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 4, it is characterised in that: described hydrophilic
Hand feel finishing agent is 2,3- epoxypropyltrimethylchloride chloride.
6. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 4, it is characterised in that: the step
In A2, the pick-up padded is 70-90%.
7. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: the step
Further include step A0 before A1: viscose glue class fabric being successively subjected to oil removal treatment and dyeing is handled.
8. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: the viscose glue
The grammes per square metre of class fabric is 50-120g/m2。
9. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 1, it is characterised in that: the viscose glue
Class fabric includes the viscose rayon of 25-100wt%.
10. a kind of wicking function ameliorative way of viscose glue class fabric according to claim 9, it is characterised in that: described viscous
Glue class fabric includes the Modal fibre of 45-75wt% and the viscose rayon of 25-55wt%.