CN110342867A - Anion ecological health preserving room - Google Patents
Anion ecological health preserving room Download PDFInfo
- Publication number
- CN110342867A CN110342867A CN201910765098.2A CN201910765098A CN110342867A CN 110342867 A CN110342867 A CN 110342867A CN 201910765098 A CN201910765098 A CN 201910765098A CN 110342867 A CN110342867 A CN 110342867A
- Authority
- CN
- China
- Prior art keywords
- anion
- plate
- parts
- carbon fiber
- wallboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses anion ecological health preserving rooms, including anion plate, the anion plate is based on parts by weight, including the following raw material: 50.0-60.0 parts of diatomite, 13.0-16.0 parts of limestone, 12.0-16.0 parts of cement, 3.5-4.0 parts of perlite, 4.5-5.5 parts of wood fibre, 7.5-8.0 parts of nanoscale negative ion powder.The present invention simulates the natural conditions of Bama area, is applied to anion ecological health preserving room by certain negative ion plate, and may be implemented to be transformed oneself residence can build similar to Bama area living environment, realizes ecological health-care healthcare function.
Description
Technical field
The present invention relates to environmentally friendly technical field of finishing materials, and in particular to anion ecological health preserving room.
Background technique
The living habit of human health and people, living environment are closely connected.It is well known that Guangxi Zhuang Autonomous Region bar
Horse autonomous county is famous Changshou village, negative oxygen ion (the > 5000ions/cm containing high concentration in local air3), in sunlight
75% far infrared wavelength is at 8-14 μm；Its specific natural environment is conducive to enhance human metabolism, improves microcirculation, improves
Body immunity attracts a large amount of populations to pour in also at " secret to longevity " of bar horse people.
However the region area of bar horse is limited, can not carry therefore how excessive external colonization personnel it is specific simulate its
Natural conditions so that it is those skilled in the art's urgent need to resolve that people can enjoy the health environment similar to bar horse at home
The problem of.
Summary of the invention
In view of this, anion plate is applied to anion ecological health preserving room by the present invention, class can be built in oneself residence
It is similar to Bama area living environment, realizes that ecological health-care healthcare function, the anion plate can make to generate high concentration in room air
Negative oxygen ion (ten thousand ions/cm of 2.5-7.83), and discharge far infrared.
To achieve the goals above, the present invention adopts the following technical scheme:
Anion plate, based on parts by weight, including the following raw material: 50.0-60.0 parts of diatomite, limestone 13.0-16.0
Part, 12.0-16.0 parts of cement, 3.5-4.0 parts of perlite, 4.5-5.5 parts of wood fibre, 7.5-8.0 parts of nanoscale negative ion powder.
Anion plate, based on parts by weight, including the following raw material: 55.6 parts of diatomite, 14.3 parts of limestone, cement 13.5
Part, 3.8 parts of perlite, 5.0 parts of wood fibre, 7.8 parts of nanoscale negative ion powder.
Preferably, diatomite crosses 80-100 mesh；Limestone crushed 80-100 mesh；Cement crosses 200-300 mesh；It is precious
Zhu Yan crushed 80-100 mesh；Wood fibre length is 0.5-3mm；Nanoscale negative ion powder partial size is less than 100nm.
On the one hand the selection of above-mentioned raw materials and its dosage, parameter ensure that the intensity of anion plate, on the other hand guarantee shape
At anion plate can quickly induce a large amount of generations of negative oxygen ion in air.
Preferably, nanoscale negative ion powder includes tourmaline powder and monazite powder, further includes medical stone powder and opal
One or both of powder.
The preparation method of anion plate, includes the following steps:
(1) ingredient: weighing each raw material, spare；
(2) it stirs: each raw material is mixed, the water of raw material total amount 1/4-1/3 weight is added, stirs into slurry；
(3) making sheet: slurry is poured into mold, places 20-40min at 300-350 DEG C；
(4) one-step solidification: 35-40 DEG C of placement 24-30h；
(5) it demoulds；
(6) secondary curing: 35-40 DEG C of placement 48-60h；
(7) it cuts.
Solidified twice after making sheet, plate face intensity can be made more preferably, thickness is more evenly accurate.
Preferably, mixing speed 40-50r/min, mixing time 8-10min in step (2).
Anion ecological health preserving room, including furred ceiling, enclosure wall and floor offer air inlet on furred ceiling, and at air inlet
Air purifying and temperature regulating device is installed；It is equipped with carbon fiber electrothermal plate on enclosure wall, is equipped with anion on the outside of carbon fiber electrothermal plate
Wallboard；Enclosure wall bottom is equipped with air exhausting device；
The anion plate that anion wallboard uses the above method to be prepared；Floor is prepared negative using the above method
Ion plate is laid.
Carbon fiber electrothermal plate heating can emit 8-14 μm of far infrared, and anion wallboard is in the temperature of carbon fiber electrothermal plate
Under the influence of quickly induce negative oxygen ion and discharge far infrared, and then make indoor formation high-concentration negative oxygen ion (2.5-7.8 ten thousand
ions/cm3) environment.
Carbon fiber electrothermal plate heating will cause room temperature raising, and the hot environment of short time can accelerate blood circulation, make
Each position muscle of whole body is entirely relaxed, but high temperature is not suitable for children, old man and hypertension, cardiac, and it is long when
Between high temperature health can be adversely affected.Therefore, air purifying and temperature regulating device, i.e. temperature adjustable are set at air inlet
Air purifier can adjust air themperature while for the air-supply of anion ecological health preserving room, and then meet different users couple
The demand of temperature.
Enclosure wall bottom is equipped with air exhausting device, and cooperation air purifying and temperature regulating device is updated room air, Jin Erbao
Room air circulation is demonstrate,proved, user is avoided to generate sultry discomfort.
Preferably, anion plate thickness is 3-7mm.
Preferably, expose part carbon fiber electrothermal plate when anion wallboard is layed on the outside of carbon fiber electrothermal plate, favorably
In the release of far infrared.
Preferably, hole is opened up on anion wallboard, exposes part carbon fiber electrothermal plate；And/or muti-piece anion
Wallboard, which is alternatively arranged, to be layed on the outside of carbon fiber electrothermal plate.
Preferably, it is provided with the decorative panel with air hole on the outside of anion wallboard, be conducive to while neat and artistic remote
The release of infrared ray and negative oxygen ion.
It can be seen via above technical scheme that compared with prior art, the present invention according to the natural conditions of Bama area into
Row simulation, is obtained anion plate, oneself residence is transformed into similar to Bama area living environment using the anion plate
Anion ecological health preserving room is, it can be achieved that ecological health-care healthcare function.
Detailed description of the invention
Fig. 1 show the structural schematic diagram of anion ecological health preserving room.
Fig. 2 show carbon fiber electrothermal plate, anion wall board mounting structure schematic diagram.
Fig. 3 show carbon fiber electrothermal plate, anion wall board mounting structure side room figure.
Detailed description of the invention: 1. furred ceilings；101. air inlet；2. enclosure wall；3. floor；4. air purifying and temperature regulating device；5. carbon fiber
Electric hot plate；6. anion wallboard；601. hole；7. decorative panel；8. air exhausting device；9. bracket；901. crossbeam；902. stringer；
903. vacancy；10. card slot；11. fixed plate；12. fixture block.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
Anion plate, every 100g raw material are as follows: diatomite 55.6g, limestone 14.3g, cement 13.5g, perlite 3.8g,
Wood fibre 5.0g, nanoscale negative ion powder 7.8g.Tourmaline powder, monazite powder, medical stone powder in nanoscale negative ion powder
It is 4:6:1:1 with albumen mountain flour weight ratio.
Wherein, diatomite sieves with 100 mesh sieve；Limestone crushed 80 meshes；Cement crosses 200 meshes；Perlite crushed 80
Mesh；Wood fibre length is 0.5-3mm；Nanoscale negative ion powder partial size about 40nm.
The preparation method of above-mentioned anion plate, includes the following steps:
(1) ingredient: weighing each raw material, spare；
(2) it stirs: each raw material is mixed, the water of 1/4 weight of raw material total amount is added, 50r/min stirs 8min, starched
Material；
(3) making sheet: slurry is poured into mold (die depth decision plate thickness), places 40min at 300 DEG C；
(4) one-step solidification: the mold for filling plate is sent into solidification workshop, 40 DEG C are placed for 24 hours；
(5) it demoulds: will be demoulded by the plate of one-step solidification；
(6) plate after demoulding secondary curing: is sent into solidification workshop, 38 DEG C of placement 48h；
(7) the anion plate of correspondingly-sized is cut into according to use demand.
Embodiment 2
Anion plate, every 100g raw material are as follows: diatomite 58.5g, limestone 13.5g, cement 12.0g, perlite 3.5g,
Wood fibre 4.5g, nanoscale negative ion powder 8.0g.Tourmaline powder, monazite powder and medical stone powder in nanoscale negative ion powder
Weight ratio is 2:3:1.
Wherein, diatomite crosses 80 meshes；Limestone crushing sieves with 100 mesh sieve；Cement crosses 300 meshes；Perlite crushed 100
Mesh；Wood fibre length is 0.5-3mm；Nanoscale negative ion powder partial size about 40nm.
The preparation method of above-mentioned anion plate, includes the following steps:
(1) ingredient: weighing each raw material, spare；
(2) it stirs: each raw material is mixed, the water of 1/3 weight of raw material total amount is added, 40r/min stirs 10min, starched
Material；
(3) making sheet: slurry is poured into mold, places 20min at 350 DEG C；
(4) mold for filling plate one-step solidification: is sent into solidification workshop, 38 DEG C of placement 28h；
(5) it demoulds: will be demoulded by the plate of one-step solidification；
(6) plate after demoulding secondary curing: is sent into solidification workshop, 35 DEG C of placement 54h；
(7) the anion plate of correspondingly-sized is cut into according to use demand.
Embodiment 3
Anion plate, every 100g raw material are as follows: diatomite 52.5g, limestone 15.2g, cement 15.0g, perlite 4.0g,
Wood fibre 5.5g, nanoscale negative ion powder 7.8g.Tourmaline powder, monazite powder and albumen mountain flour in nanoscale negative ion powder
Weight ratio is 2:3:1.
Wherein, diatomite crosses 90 meshes；Limestone crushed 90 meshes；Cement crosses 250 meshes；Perlite crushed 90 mesh
Sieve；Wood fibre length is 0.5-3mm；Nanoscale negative ion powder partial size about 40nm.
The preparation method of above-mentioned anion plate, includes the following steps:
(1) ingredient: weighing each raw material, spare；
(2) it stirs: each raw material is mixed, the water of 1/4 weight of raw material total amount is added, 40r/min stirs 8min, starched
Material；
(3) making sheet: slurry is poured into mold, places 30min at 320 DEG C；
(4) mold for filling plate one-step solidification: is sent into solidification workshop, 35 DEG C of placement 30h；
(5) it demoulds: will be demoulded by the plate of one-step solidification；
(6) plate after demoulding secondary curing: is sent into solidification workshop, 35 DEG C of placement 60h；
(7) the anion board house of correspondingly-sized is cut into according to use demand.
Embodiment 4
As shown in Figure 1, anion ecological health preserving room, including furred ceiling 1, enclosure wall 2 and floor 3, air inlet is offered on furred ceiling 1
101, and air purifying and temperature regulating device 4 is installed at air inlet 101；Carbon fiber electrothermal plate 5, carbon fiber are equipped on enclosure wall 2
It is equipped with anion wallboard 6 on the outside of electric hot plate 5, the decorative panel 7 with air hole is provided on the outside of anion wallboard 6；2 bottom of enclosure wall
Portion is equipped with air exhausting device 8；Anion wallboard 6 is the anion plate for preparing in embodiment 1,2 or 3, floor 3 using embodiment 1,
The anion plate prepared in 2 or 3 is laid with.
Embodiment 5
On the basis of embodiment 4, in order to facilitate the dismounting and change of carbon fiber electrothermal plate 5 and anion wallboard 6, it is laid with carbon
The first mounting bracket 9 on enclosure wall 2 before fiber electric heating plate 5, as Figure 2-3, bracket 9 is by staggered crossbeam 901 and stringer 902
It constitutes, forms the vacancy 903 for placing carbon fiber electrothermal plate 5 and anion wallboard 6, carbon fiber between crossbeam 901 and stringer 902
Dimension electric hot plate 5 and anion wallboard 6 are sequentially placed at vacancy 903, and one end on crossbeam 901 and stringer 902 away from enclosure wall 2 is equal
Several card slots 10 are offered, each 10 two sides of card slot respectively pass through shaft and are connected with a fixed plate 11.
The fixture block 12 being correspondingly arranged with card slot 10 is fixed on decorative panel 7.When fixture block 12 is arranged in card slot 10, decorative panel
7, close to fixed plate 11, make the fitting of fixed plate 11 fix anion wallboard 6.
Carbon fiber electrothermal plate 5 or anion wallboard 6 are such as needed to change, decorative panel 7 can be directly pulled, make fixture block 12 from card slot 10
Interior abjection rotates fixed plate 11, that is, can be taken off anion wall plate 6 and carbon fiber electrothermal plate 5.
Hole 601 is opened up on anion wallboard 6, and muti-piece anion wallboard 6 is alternatively arranged and is layed in carbon fiber electrically
5 outside of hot plate, is conducive to the transmitting of far infrared.
In use, carbon fiber electrothermal plate 5 can be powered, it is heated to 40-60 DEG C, and time opening air purifying and temperature regulating fills
4 and air exhausting device 8 are set, adjust room temperature according to demand.
Embodiment 6
Anion ecological health preserving room in embodiment 5 is laid with the anion plate of embodiment 1-3 preparation respectively, respectively as reality
Test a group 1-3, anion ecological health preserving room area (floor laying area) about 20m2, floor 3 uses 5mm thickness anion plate；Bear from
Sub- wallboard 6 is laid with area about 16m2, thickness about 5mm.It is laid with after completing 3d using this happy air negative oxgyen ion detector of Depew
DP8800PRO measures negative oxygen ion in air；Carbon fiber electrothermal plate 5 is powered, is heated to 45 DEG C, and opens air cleaning tune
Warm device 4 (28 DEG C) and air exhausting device 8 measure air using this happy air negative oxgyen ion detector DP8800PRO of Depew after 2h
Middle negative oxygen ion.Simultaneously setting do not repack into anion ecological health preserving room control group 1 (be not laid with carbon fiber electrothermal plate 5, bear from
Sub- wallboard 6, floor 3), it is not laid with the control group 2 (remaining is with experimental group 1) of carbon fiber electrothermal plate, with the replacement of commercially available anion plate
The control group 3 of 1 anion plate of experimental group (remaining is with experimental group 1).
The experimental result of releasing negative oxygen ion amount is as shown in table 1 in air in anion ecological health preserving room 3d.
Releasing negative oxygen ion amount in air in 1 anion ecological health preserving room 3d of table
The general principles defined herein can without departing from the spirit or scope of the present invention, in other realities
It applies in example and realizes.Therefore, the present invention is not intended to be limited to embodiment illustrated herein, and be to fit to it is disclosed herein
Principle and the consistent widest scope of features of novelty.
Claims (10)
1. anion plate, which is characterized in that based on parts by weight, including the following raw material: 50.0-60.0 parts of diatomite, limestone
13.0-16.0 parts, 12.0-16.0 parts of cement, 3.5-4.0 parts of perlite, 4.5-5.5 parts of wood fibre, nanoscale negative ion powder
7.5-8.0 part.
2. anion plate, which is characterized in that based on parts by weight, including the following raw material: 55.6 parts of diatomite, limestone 14.3
Part, 13.5 parts of cement, 3.8 parts of perlite, 5.0 parts of wood fibre, 7.8 parts of nanoscale negative ion powder.
3. anion plate described in any one of -2 according to claim 1, which is characterized in that the diatomite crosses 80-100 mesh
Sieve；The limestone crushed 80-100 mesh；The cement crosses 200-300 mesh；The perlite crushed 80-100 mesh
Sieve；The wood fibre length is 0.5-3mm；The nanoscale negative ion powder partial size is less than 100nm.
4. the preparation method of anion plate, which comprises the steps of:
(1) ingredient: anion plate according to any one of claim 1-3 weighs each raw material, spare；
(2) it stirs: each raw material is mixed, the water of raw material total amount 1/4-1/3 weight is added, stirs into slurry；
(3) making sheet: slurry is poured into mold, places 20-40min at 300-350 DEG C；
(4) one-step solidification: 35-40 DEG C of placement 24-30h；
(5) it demoulds；
(6) secondary curing: 35-40 DEG C of placement 48-60h；
(7) it cuts.
5. the preparation method of anion plate according to claim 4, which is characterized in that mixing speed in the step (2)
40-50r/min, mixing time 8-10min.
6. anion ecological health preserving room, including furred ceiling, enclosure wall and floor, which is characterized in that
Air inlet is offered on the furred ceiling, and air purifying and temperature regulating device is installed at air inlet；
It is equipped with carbon fiber electrothermal plate on the enclosure wall, is equipped with anion wallboard on the outside of the carbon fiber electrothermal plate；It is described to enclose
Wall bottom is equipped with air exhausting device；
The anion plate that the anion wallboard is prepared using any one of claim 4-5；The floor uses right
It is required that the anion plate that any one of 4-5 is prepared is laid.
7. anion ecological health preserving room according to claim 6, which is characterized in that the anion plate thickness is 3-7mm.
8. anion ecological health preserving room according to claim 6, which is characterized in that the anion wallboard is layed in described
Expose part carbon fiber electrothermal plate when on the outside of carbon fiber electrothermal plate.
9. anion ecological health preserving room according to claim 8, which is characterized in that
Hole is opened up on the anion wallboard, exposes part carbon fiber electrothermal plate；
And/or anion wallboard described in muti-piece is alternatively arranged and is layed on the outside of the carbon fiber electrothermal plate.
10. anion ecological health preserving room according to claim 6, which is characterized in that setting on the outside of the anion wallboard
There is the decorative panel with air hole.