CN110331592A - A kind of biological enzyme real silk fabric flame-retardant finishing method - Google Patents

A kind of biological enzyme real silk fabric flame-retardant finishing method Download PDF

Info

Publication number
CN110331592A
CN110331592A CN201910427433.8A CN201910427433A CN110331592A CN 110331592 A CN110331592 A CN 110331592A CN 201910427433 A CN201910427433 A CN 201910427433A CN 110331592 A CN110331592 A CN 110331592A
Authority
CN
China
Prior art keywords
fabric
biological enzyme
agent
real silk
finishing method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910427433.8A
Other languages
Chinese (zh)
Inventor
董家春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Wanzhuo Textile Co Ltd
Original Assignee
Suzhou Wanzhuo Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Wanzhuo Textile Co Ltd filed Critical Suzhou Wanzhuo Textile Co Ltd
Priority to CN201910427433.8A priority Critical patent/CN110331592A/en
Publication of CN110331592A publication Critical patent/CN110331592A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of biological enzyme real silk fabric flame-retardant finishing methods, include the following steps: S1, pretreatment: fabric being impregnated in pretreating agent, 40-50 DEG C for the treatment of temperature, handle time 30-60min, and warm water cleaning is used in taking-up；S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 60-70 DEG C for the treatment of temperature, handles time 80-120min, warm water cleaning is used in taking-up；The present invention is handled fabric using biological enzyme, impurity on fabric is sufficiently decomposed, in the case where not influencing fabric performance itself and feel, the associativity of finishing agent and fabric is improved, to improve the anti-flammability of fabric, and passes through addition antibacterial agent, so that fabric has antibiotic property, compared to traditional handicraft, treatment effeciency is improved, it is less to arrange the pollution that process generates.

Description

A kind of biological enzyme real silk fabric flame-retardant finishing method
Technical field
The present invention relates to textile technology field, specifically a kind of biological enzyme real silk fabric flame-retardant finishing method.
Background technique
Silk refers generally to silk, including mulberry silk, tussah silk, ricinus silk, cassava silkwormsilk etc..Silk is referred to as " fiber Queen ", with its favor of the unique glamour by people through the ages.Biological enzyme is generated by living cells with catalytic action Organic matter, most of is protein, and also having few part is RNA.The manufacture of biological enzyme and application field are gradually expanded, biology Application of the enzyme in textile industry is also ripe day by day, by being mainly used for the desizing of cotton fabric and the degumming of silk in the past, until present Extensive use in each field of textile dyeing and finishing embodies superiority of the biological enzyme in Dyeing & Finishing Industry.Real silk fabric is due to resistance Combustion property is bad, needs to carry out flame-proof treatment often to enhance anti-flammability, but traditional flame-proof finishing process is easy to cocoon fiber Damage is generated, influences the feel of product, finishing effect is poor, and washability is bad.
Summary of the invention
The purpose of the present invention is to provide a kind of biological enzyme real silk fabric flame-retardant finishing methods, to solve above-mentioned background skill The problem of being proposed in art.
To achieve the above object, the invention provides the following technical scheme:
A kind of biological enzyme real silk fabric flame-retardant finishing method, includes the following steps:
S1, pretreatment: fabric is impregnated in pretreating agent, 40-50 DEG C for the treatment of temperature, is handled time 30-60min, is taken Warm water cleaning is used out；
S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 60-70 DEG C for the treatment of temperature, handles time 80- Warm water cleaning is used in 120min, taking-up；
S3, arrangement: fabric is immersed in finishing agent, is padded processing, 20-40 DEG C for the treatment of temperature, is handled time 60-80min, Liquid carrying rate 60-70%；
S4, baking: fabric is sent into drying box, first preliminary drying 2-3min under the conditions of 90-100 DEG C, then at 120-140 DEG C Under the conditions of bake 2-4min；
S5, washing: fabric being soaked with warm water, is then soaped, then cold water is washed 2-4 times, constant temperature forming machine is sent into, in 30- Drying and shaping under the conditions of 50 DEG C.
As a further solution of the present invention: pretreating agent described in step S1 is trimethylolpropane, sodium hypophosphite, sun Ion softening agent, nonshrink aqua mixed solution.
As a further solution of the present invention: the nonshrink aqua is polyethylene terephthalate, polyethylene glycol, shell are poly- Sugared mixed solution.
As a further solution of the present invention: biological enzyme additive described in step S2 includes cellulase, amylase, paint Enzyme, bleeding agent and surfactant.
As a further solution of the present invention: the bleeding agent is fatty alcohol polyoxyethylene ether, sodium alkyl benzene sulfonate, alkyl Any one of phenol polyethenoxy ether, the surfactant are polysorbate and Tea Saponin mixed solution.
As a further solution of the present invention: finishing agent described in step S3 includes fire retardant, antibacterial agent, dispersing agent, hydroxyl Propyl methocel and eucalyptus oil.
As a further solution of the present invention: the fire retardant is tributyl phosphate, in triphenyl phosphate, tributyl phosphate It is any.
As a further solution of the present invention: the antibacterial agent is Chinese juniper oil, argy wormwood, catechin mixed solution.
Compared with prior art, the beneficial effects of the present invention are:
The present invention is handled fabric using biological enzyme, the impurity on fabric is sufficiently decomposed, in not shadow In the case where ringing fabric performance itself and feel, the associativity of finishing agent and fabric is improved, to improve the fire-retardant of fabric Property, and by addition antibacterial agent, so that fabric has antibiotic property, traditional handicraft is compared, improves treatment effeciency, process is arranged and produces Raw pollution is less.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects It encloses.
Embodiment one:
A kind of biological enzyme real silk fabric flame-retardant finishing method, includes the following steps:
S1, pretreatment: fabric is impregnated in pretreating agent, 40 DEG C for the treatment of temperature, handles time 60min, is taken out with temperature Water is cleaned；
S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 60 DEG C for the treatment of temperature, is handled time 120min, is taken Warm water cleaning is used out；
S3, arrangement: fabric is immersed in finishing agent, is padded processing, 20 DEG C for the treatment of temperature, is handled time 80min, liquid carrying rate 70%；
S4, baking: fabric is sent into drying box, first preliminary drying 3min under the conditions of 90 DEG C, then bakes under the conditions of 120 DEG C 4min；
S5, washing: fabric being soaked with warm water, is then soaped, then cold water is washed 4 times, constant temperature forming machine is sent into, in 30 DEG C of items Drying and shaping under part.
Pretreating agent described in step S1 is trimethylolpropane, sodium hypophosphite, cationic softener, the mixing of nonshrink aqua Solution.
The nonshrink aqua is polyethylene terephthalate, polyethylene glycol, chitosan mixed solution.
Biological enzyme additive described in step S2 includes cellulase, amylase, laccase, bleeding agent and surfactant.
The bleeding agent is fatty alcohol polyoxyethylene ether, and the surfactant is that polysorbate and Tea Saponin mixing are molten Liquid.
Finishing agent described in step S3 includes fire retardant, antibacterial agent, dispersing agent, hydroxypropyl methyl cellulose and eucalyptus oil.
The fire retardant is tributyl phosphate.
The antibacterial agent is Chinese juniper oil, argy wormwood, catechin mixed solution.
Embodiment two:
A kind of biological enzyme real silk fabric flame-retardant finishing method, includes the following steps:
S1, pretreatment: fabric is impregnated in pretreating agent, 45 DEG C for the treatment of temperature, handles time 45min, is taken out with temperature Water is cleaned；
S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 65 DEG C for the treatment of temperature, is handled time 100min, is taken Warm water cleaning is used out；
S3, arrangement: fabric is immersed in finishing agent, is padded processing, 30 DEG C for the treatment of temperature, is handled time 70min, liquid carrying rate 65%；
S4, baking: fabric is sent into drying box, first preliminary drying 2.5min under the conditions of 95 DEG C, then dries under the conditions of 130 DEG C Roast 3min；
S5, washing: fabric being soaked with warm water, is then soaped, then cold water is washed 3 times, constant temperature forming machine is sent into, in 40 DEG C of items Drying and shaping under part.
Pretreating agent described in step S1 is trimethylolpropane, sodium hypophosphite, cationic softener, the mixing of nonshrink aqua Solution.
The nonshrink aqua is polyethylene terephthalate, polyethylene glycol, chitosan mixed solution.
Biological enzyme additive described in step S2 includes cellulase, amylase, laccase, bleeding agent and surfactant.
The bleeding agent is sodium alkyl benzene sulfonate, and the surfactant is polysorbate and Tea Saponin mixed solution.
Finishing agent described in step S3 includes fire retardant, antibacterial agent, dispersing agent, hydroxypropyl methyl cellulose and eucalyptus oil.
The fire retardant is triphenyl phosphate.
The antibacterial agent is Chinese juniper oil, argy wormwood, catechin mixed solution.
Embodiment three:
A kind of biological enzyme real silk fabric flame-retardant finishing method, includes the following steps:
S1, pretreatment: fabric is impregnated in pretreating agent, 50 DEG C for the treatment of temperature, handles time 30min, is taken out with temperature Water is cleaned；
S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 70 DEG C for the treatment of temperature, is handled time 80min, is taken Warm water cleaning is used out；
S3, arrangement: fabric is immersed in finishing agent, is padded processing, 40 DEG C for the treatment of temperature, is handled time 60min, liquid carrying rate 60%；
S4, baking: fabric is sent into drying box, first preliminary drying 2min under the conditions of 100 DEG C, then dries under the conditions of 140 DEG C Roast 2min；
S5, washing: fabric being soaked with warm water, is then soaped, then cold water is washed 2 times, constant temperature forming machine is sent into, in 50 DEG C of items Drying and shaping under part.
Pretreating agent described in step S1 is trimethylolpropane, sodium hypophosphite, cationic softener, the mixing of nonshrink aqua Solution.
The nonshrink aqua is polyethylene terephthalate, polyethylene glycol, chitosan mixed solution.
Biological enzyme additive described in step S2 includes cellulase, amylase, laccase, bleeding agent and surfactant.
The bleeding agent is alkyl phenol polyoxyethylene ether, and the surfactant is that polysorbate and Tea Saponin mixing are molten Liquid.
Finishing agent described in step S3 includes fire retardant, antibacterial agent, dispersing agent, hydroxypropyl methyl cellulose and eucalyptus oil.
The fire retardant is tributyl phosphate.
The antibacterial agent is Chinese juniper oil, argy wormwood, catechin mixed solution.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims Variation is included within the present invention.

Claims (8)

1. a kind of biological enzyme real silk fabric flame-retardant finishing method, which comprises the steps of:
S1, pretreatment: fabric is impregnated in pretreating agent, 40-50 DEG C for the treatment of temperature, is handled time 30-60min, is taken out and use Warm water cleaning；
S2, bioenzyme washing: fabric is impregnated in biological enzyme additive, 60-70 DEG C for the treatment of temperature, handles time 80-120min, Taking-up warm water cleaning；
S3, arrangement: fabric is immersed in finishing agent, is padded processing, 20-40 DEG C for the treatment of temperature, is handled time 60-80min, band liquid Rate 60-70%；
S4, baking: fabric is sent into drying box, first preliminary drying 2-3min under the conditions of 90-100 DEG C, then in 120-140 DEG C of condition Lower baking 2-4min；
S5, washing: fabric being soaked with warm water, is then soaped, then cold water is washed 2-4 times, constant temperature forming machine is sent into, at 30-50 DEG C Under the conditions of drying and shaping.
2. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 1, which is characterized in that in step S1 The pretreating agent is trimethylolpropane, sodium hypophosphite, cationic softener, nonshrink aqua mixed solution.
3. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 2, which is characterized in that described nonshrink Aqua is polyethylene terephthalate, polyethylene glycol, chitosan mixed solution.
4. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 1, which is characterized in that in step S2 The biological enzyme additive includes cellulase, amylase, laccase, bleeding agent and surfactant.
5. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 4, which is characterized in that the infiltration Agent is any one of fatty alcohol polyoxyethylene ether, sodium alkyl benzene sulfonate, alkyl phenol polyoxyethylene ether, and the surfactant is Polysorbate and Tea Saponin mixed solution.
6. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 1, which is characterized in that in step S3 The finishing agent includes fire retardant, antibacterial agent, dispersing agent, hydroxypropyl methyl cellulose and eucalyptus oil.
7. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 6, which is characterized in that described fire-retardant Agent is any one of tributyl phosphate, triphenyl phosphate, tributyl phosphate.
8. a kind of biological enzyme real silk fabric flame-retardant finishing method according to claim 6, which is characterized in that the antibacterial Agent is Chinese juniper oil, argy wormwood, catechin mixed solution.
CN201910427433.8A 2019-05-22 2019-05-22 A kind of biological enzyme real silk fabric flame-retardant finishing method Pending CN110331592A (en)