CN110317542A - 环保uv型oca光学胶 - Google Patents
环保uv型oca光学胶 Download PDFInfo
- Publication number
- CN110317542A CN110317542A CN201910575411.6A CN201910575411A CN110317542A CN 110317542 A CN110317542 A CN 110317542A CN 201910575411 A CN201910575411 A CN 201910575411A CN 110317542 A CN110317542 A CN 110317542A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic acid
- box
- type
- optical cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保UV型OCA光学胶，包括UV型特种丙烯酸脂压敏胶层和分别位于其两侧的PET离型膜，UV型特种丙烯酸脂压敏胶的具体成分包括丙烯酸3‑5份、丙烯酸羟乙酯10‑20份，丙烯酸丁酯10‑20份，丙烯酸异辛酯50‑60份，甲基丙烯酸异辛酯10‑20份，光引发剂2，4，6‑三苯基甲酰基‑二苯基氧化膦0.2‑1份，1‑羟基环己基苯基丙酮0.2‑1份，活性稀释剂季戊四醇三丙烯酸酯0.2‑0.5份，聚乙二醇（200）二甲基丙烯酸酯0.2‑0.5份以及增感剂0.2‑0.5份。UV型特种丙烯酸脂压敏胶是通过光聚合的方式制成，具有高透光、无需后段固化、胶结强度高、无溶剂挥发、环境友好的特点。
Description
技术领域
本发明涉及光学胶制备技术领域，具体是涉及一种环保UV型OCA光学胶。
背景技术
OCA（Optically Clear Adhesive）光学透明胶是用于胶结透明光学元件（如镜头等）的特种粘胶剂。要求具有无色透明、光透过率在90%以上、胶结强度良好、可在室温或中温下固化、固化收缩小等特点。OCA光学胶是触摸屏的重要原材料之一，是将光学亚克力胶做成无基材，然后在上下底层再各贴合一层离型薄膜制备而成，是一种无基体材料的双面贴合胶。简而言之，OCA就是具有光学透性的特种无基材的双面胶。
现有的OCA光学胶主要由溶剂型丙烯酸酯压敏胶制成，溶剂型的压敏胶在涂布工艺环节会有大量的溶剂挥发造成环境污染，这一现象不符合当今的环保趋势，与国家的未来发展方向相违背，同时，溶剂型的丙烯酸酯压敏胶存在后端熟化的问题，造成额外的生产成本压力。
同时， OCA光学胶成品在运输的过程中容易因碰撞、挤压和震动等问题造成变形和压伤等不良现象，难以保证OCA的品质。
发明内容
本发明的目的在于解决现有技术中存在的不足，通过改变聚合的方式聚合出环保UV型OCA光学胶，不仅无溶剂挥发，且不需要额外的熟化时间，做到了对环境友好、降低生产成本并提高生产效率的目的，且通过设计一种防撞包装盒避免了运输过程对良品率的不良影响。
本发明的技术方案为：环保UV型OCA光学胶，包括UV型特种丙烯酸脂压敏胶层和分别位于其两侧的PET离型膜，UV型特种丙烯酸脂压敏胶的具体成分包括丙烯酸3-5份、丙烯酸羟乙酯10-20份，丙烯酸丁酯10-20份，丙烯酸异辛酯50-60份，甲基丙烯酸异辛酯10-20份和光引发剂2，4，6-三苯基甲酰基-二苯基氧化膦 0.2-1份，1-羟基环己基苯基丙酮0.2-1份和活性稀释剂季戊四醇三丙烯酸酯0.2-0.5份、聚乙二醇（200）二甲基丙烯酸酯0.2-0.5份以及增感剂0.2-0.5份。
所述环保UV型OCA光学胶的制备方法为：
1. UV型特种丙烯酸脂压敏胶的聚合：将3-5份丙烯酸、10-20份丙烯酸羟乙酯，10-20份丙烯酸丁酯，50-60份丙烯酸异辛酯，10-20份甲基丙烯酸异辛酯和0.2-1份光引发剂2，4，6-三苯基甲酰基-二苯基氧化膦，0.2-1份1-羟基环己基苯基丙酮依次加入透明玻璃反应釜中，搅拌均匀，通氮气，防止氧阻聚，用350 nm的LED紫外光进行照射，照射至其黏度达到3000-5000 mpa·s时关闭光源；
2. 将步骤1制得的UV型特种丙烯酸脂压敏胶加入0.2-0.5份活性稀释剂季戊四醇三丙烯酸酯、0.2-0.5份聚乙二醇（200）二甲基丙烯酸酯以及0.2-0.5份增感剂后搅拌均匀并涂布在两层PET离型薄膜之间；
3. 再次经过LED灯光源照射，UV光固化在波长300～400 nm的光下进行，固化时间为1-5min，UV辐射剂量为500～1000 mJ/cm2，制成成品环保UV型丙烯酸酯压敏胶；
4. 将OCA光学胶切割成标准的片状结构并水平叠放进防撞包装盒中。
进一步地，所述防撞包装盒包括长方体状的外盒和内盒，外盒和内盒均由盒体和顶盖两部分组成且外盒和内盒均为掀盖设计，在内盒的六个外表面上均设有格状的防撞缓冲栅栏，在内盒内部以四条挡边围合形成OCA胶的放置工位，且四条挡边的边沿不连接形成四个过渡空位。
进一步地，在每个过渡空位处设有一个直角形的压板，所述压板的其中一条直角边的自由端底部设有一根连接杆，所述连接杆底部与内盒的盒体底面可转动连接，在连接杆上靠近压板的一端设有一段可伸缩段。
进一步地，所述内盒置于外盒中后，内盒外表面上的防撞缓冲栅栏的外侧与内盒的相应内侧面相互接触，避免内盒在外盒内晃动。
本发明的有益效果为：
本发明通过采用光聚合的方式制成UV型特种丙烯酸酯树脂，具有高透光、无需后段固化、胶结强度高、无溶剂挥发、环境友好的特点，成功解决长期以来溶剂对环境的污染，且一次固化制成成品，无需和传统制备工艺一样进行后段熟化，节省生产步骤，极大的降低生产成本；利用本发明公开的防撞包装盒进行OCA胶的包装运输可显著缓解运输过程中受到的震动、挤压等不良状况，降低OCA胶的损毁率，保证产品品质。
附图说明
图1为本发明制备的环保UV型OCA光学胶的结构图；
图2为本发明公开的防撞包装盒的外盒的结构示意图；
图3为本发明公开的防撞包装盒的内盒的结构示意图；
图4为本发明公开的防撞包装盒的外盒的盒体的结构示意图；
图5为本发明公开的防撞包装盒的内部结构示意图；
图6为本发明公开的防撞包装盒内压板的结构示意图；
其中，01-PET离型膜，02-UV型特种丙烯酸脂压敏胶层；
1-外盒，2-内盒，3-防撞缓冲栅栏，4-挡边，5-压板，6-连接杆，7-可伸缩段，8-OCA胶。
具体实施方式
以下实施例进一步说明本发明的内容，但不应理解为对本发明的限制。在不背离本发明实质的情况下，对本发明方法、步骤或条件所作的修改和替换，均属于本发明的范围。
实施例一
一种环保UV型OCA光学胶的制备方法
1. UV型特种丙烯酸脂压敏胶的聚合：将3份丙烯酸、15份丙烯酸羟乙酯，10份丙烯酸丁酯，52份丙烯酸异辛酯，14份甲基丙烯酸异辛酯和0.4份光引发剂2，4，6-三苯基甲酰基-二苯基氧化膦，0.2份1-羟基环己基苯基丙酮依次加入透明玻璃反应釜中，搅拌均匀，通氮气，防止氧阻聚，用350 nm的LED紫外光进行照射，照射至其黏度达到3000-5000 mpa·s时关闭光源；
2. 将步骤1制得的UV型特种丙烯酸脂压敏胶加入0.2份活性稀释剂季戊四醇三丙烯酸酯0.2份聚乙二醇（200）二甲基丙烯酸酯以及0.2份增感剂后搅拌均匀并涂布在两层PET离型薄膜之间；
3. 再次经过LED灯光源照射，UV光固化在波长300～400 nm的光下进行，固化时间为3min，UV辐射剂量为500～1000 mJ/cm2，制成成品环保UV型丙烯酸酯压敏胶；
4. 将OCA光学胶切割成标准的片状结构并水平叠放进防撞包装盒中。
实施例二
一种环保UV型OCA光学胶的制备方法
1. UV型特种丙烯酸脂压敏胶的聚合：将4份丙烯酸、13份丙烯酸羟乙酯，12份丙烯酸丁酯，50份丙烯酸异辛酯，12份甲基丙烯酸异辛酯和0.5份光引发剂2，4，6-三苯基甲酰基-二苯基氧化膦，0.4份1-羟基环己基苯基丙酮依次加入透明玻璃反应釜中，搅拌均匀，通氮气，防止氧阻聚，用350 nm的LED紫外光进行照射，照射至其黏度达到3000-5000 mpa·s时关闭光源；
2. 将步骤1制得的UV型特种丙烯酸脂压敏胶加入0.3份活性稀释剂季戊四醇三丙烯酸酯0.3份聚乙二醇（200）二甲基丙烯酸酯以及0.3份增感剂后搅拌均匀并涂布在两层PET离型薄膜之间；
3. 再次经过LED灯光源照射，UV光固化在波长300～400 nm的光下进行，固化时间为2min，UV辐射剂量为500～1000 mJ/cm2，制成成品环保UV型丙烯酸酯压敏胶；
4. 将OCA光学胶切割成标准的片状结构并水平叠放进防撞包装盒中。
为了保证产品品质，避免OCA胶在运输过程中发生损伤，本发明制备的OCA胶最终放入特别设计的防撞包装盒中进行运输，所述防撞包装盒包括长方体状的外盒1和内盒2，外盒1和内盒2均由盒体和顶盖两部分组成且外盒1和内盒2均为掀盖设计，在内盒2的六个外表面上均设有格状的防撞缓冲栅栏3，防撞缓冲栅栏3可对内盒2盒体起到保护作用，缓冲运输过程中盒体受到的撞击、震动等不良状况，在内盒2内部以四条挡边4围合形成OCA胶8的放置工位且四条挡边4的边沿不连接形成四个过渡空位，在运输过程中，OCA胶8的四角位置最易因受到挤压等不良状况而产生变形，过渡空位有一个留空缓冲的作用，避免硬物与OCA胶的四角直接接触，即使盒体四角受到一定程度的挤压也因与OCA胶8间存在一定距离而不会影响OCA胶8，过渡空位的设置也可方便盒中OCA胶8的拿取。
在每个过渡空位处设有一个直角形的压板5，所述压板5的其中一条直角边的自由端底部设有一根连接杆6，所述连接杆6底部与内盒2的盒体底面可转动连接，在连接杆6上靠近压板5的一端设有一段可伸缩段7，在生产单位包装出厂前，首先是将数片OCA胶8依次叠放在放置工位内，此时压板5处于放置工位外侧，当装盒完成后，将压板5向OCA胶8方向转动使其压住OCA胶8的相应直角边，利用可伸缩段7使压板5下降紧压在OCA胶的边角顶部，这样即使在运输过程中盒体受到撞击震动，OCA胶8也能始终保持稳定，不会跳出放置工位或发生OCA胶之间相互碰撞的情况，边角处不易产生卷曲变形，出售使用后因不存在运输问题时压板5可始终转动至放置工位外侧，不必压住OCA胶8，这样也方便拿取。
所述内盒2置于外盒1中后，内盒2外表面上的防撞缓冲栅栏3的外侧与内盒1的相应内侧面相互接触，避免内盒2在外盒1内晃动，在内盒2外部设计一层外盒1，一方面可以起到加强防撞缓冲的作用，另一方面是因为内盒2的外表面为不平整的格栅状，导致装箱时堆叠困难，容易影响包装盒的平稳性。
以上显示和描述了本发明的基本原理、主要特征及优点。但是以上所述仅为本发明的具体实施例，本发明的技术特征并不局限于此，任何本领域的技术人员在不脱离本发明的技术方案下得出的其他实施方式均应涵盖在本发明的专利范围之中。
Claims (5)
1. 一种环保UV型OCA光学胶，其特征在于，包括UV型特种丙烯酸脂压敏胶层和分别位于其两侧的PET离型膜，UV型特种丙烯酸脂压敏胶的具体成分包括丙烯酸3-5份、丙烯酸羟乙酯10-20份，丙烯酸丁酯10-20份，丙烯酸异辛酯50-60份，甲基丙烯酸异辛酯10-20份，光引发剂2，4，6-三苯基甲酰基-二苯基氧化膦 0.2-1份，1-羟基环己基苯基丙酮0.2-1份，活性稀释剂季戊四醇三丙烯酸酯0.2-0.5份，聚乙二醇（200）二甲基丙烯酸酯0.2-0.5份以及增感剂0.2-0.5份。
2.如权利要求1所述的环保UV型OCA光学胶的制备方法，其特征在于，具体的制备步骤为：
1）UV型特种丙烯酸脂压敏胶的聚合：将3-5份丙烯酸、10-20份丙烯酸羟乙酯，10-20份丙烯酸丁酯，50-60份丙烯酸异辛酯，10-20份甲基丙烯酸异辛酯，0.2-1份光引发剂和0.2-1份1-羟基环己基苯基丙酮依次加入透明玻璃反应釜中，搅拌均匀，通氮气，防止氧阻聚，用350 nm的LED紫外光进行照射，照射至其黏度达到3000-5000 mpa·s时关闭光源；
2）将步骤1制得的UV型特种丙烯酸脂压敏胶加入0.2-0.5份活性稀释剂季戊四醇三丙烯酸酯，0.2-0.5份聚乙二醇（200）二甲基丙烯酸酯以及0.2-0.5份增感剂后搅拌均匀并涂布在两层PET离型薄膜之间；
3）再次经过LED灯光源照射，UV光固化在波长300～400 nm的光下进行，固化时间为1-5min，UV辐射剂量为500～1000 mJ/cm2，制成成品环保UV型OCA光学胶；
4）将OCA光学胶切割成标准的片状结构并水平叠放进防撞包装盒中。
3.如权利要求2所述的环保UV型OCA光学胶的制备方法，其特征在于，所述防撞包装盒包括长方体状的外盒（1）和内盒（2），外盒（1）和内盒（2）均由盒体和顶盖两部分组成，且外盒（1）和内盒（2）均为掀盖设计，在内盒（2）的六个外表面上均设有格状的防撞缓冲栅栏（3），在内盒（2）内部以四条挡边（4）围合形成OCA胶的放置工位且四条挡边（4）的边沿不连接形成四个过渡空位。
4.如权利要求3所述的环保UV型OCA光学胶的制备方法，其特征在于，在每个过渡空位处设有一个直角形的压板（5），所述压板（5）的其中一条直角边的自由端底部设有一根连接杆（6），所述连接杆（6）底部与内盒（2）的盒体底面可转动连接，在连接杆（6）上靠近压板（5）的一端设有一段可伸缩段（7）。
5.如权利要求3所述的环保UV型OCA光学胶的制备方法，其特征在于，所述内盒（2）置于外盒（1）中后，内盒（2）外表面上的防撞缓冲栅栏（3）的外侧与内盒（1）的相应内侧面相互接触。