CN110305715A - A kind of stainless steel drawing oil and preparation method thereof - Google Patents
A kind of stainless steel drawing oil and preparation method thereof Download PDFInfo
- Publication number
- CN110305715A CN110305715A CN201810420457.6A CN201810420457A CN110305715A CN 110305715 A CN110305715 A CN 110305715A CN 201810420457 A CN201810420457 A CN 201810420457A CN 110305715 A CN110305715 A CN 110305715A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel drawing
- drawing oil
- chlorinated paraffin
- tackifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stainless steel drawing oils, it is characterized in that, the formula of the stainless steel drawing oil includes at least following composition: the mass fraction of mineral oil, chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition is as follows: mineral oil 5-15%；Chlorinated paraffin 30-40%；Sulfurized lard 20-30%；Calcium mahogany sulfonate 3-5%；Oiliness improver 5-10%；Extreme-pressure anti-friction additive 3-5%；Tackifier 5-7%.The drawing oil has preparation method simple, the good feature of function and effect.
Description
Technical field
The present invention relates to building wall board fields, and in particular to a kind of stainless steel drawing oil and preparation method thereof.
Background technique
It is that one kind aims at the highly difficult stretching of hard steel plate, punch forming and slab punching that stainless steel, which draws and dials oily (stainless steel drawing oil),
It cuts, sawing sheet and tube-drawing and the high film strength lubricating oil that sets.With high viscosity, high film strength and high extreme pressure etc. are special
Property.It can effectively prevent mold and product garland and sintering, reduce the abrasion of mold, improve product quality and extend the service life of mold
The characteristics of, and in the processing for being widely used in stainless steel kitchenware, stainless steel products, stainless steel work-piece etc..However the prior art
In, stainless steel, which is drawn, dials the generally existing following problems of oiliness energy: the abrasion resistance under high pressure is poor, and the wear intensity of tool and mould is big；Add
It will appear excessive erosion problem during work high pressure-temperature, influence the quality of product, surface smoothness is poor.
Chinese patent CN201510196573.0 discloses a kind of stainless steel drawing group oil, and stainless steel drawing oil of the invention is matched
Mineral oil addition two generation of 2- ethylhexyl trbasic zinc phosphate, the olefine sulfide oleate of the certain scientific formula of Fang Caiyong are used as efficient
Extreme-pressure anti-friction additive provides efficient extreme pressure and antiwear behavior for high speed, the drawing process of high draft, effectively lowers and add
The abrasion of tool and mould, prolongs the service life；Excessive erosion in process is solved the problems, such as with calcium mahogany sulfonate simultaneously, and is improved
Surface smoothness of the stainless steel material after drawing.
But drawing oil preparation method is complicated in the prior art, while being formulated relatively conventional, corresponding effect is more general,
The formula that especially above-mentioned patent refers to, the part cost of raw material is high, and cost performance is low.
Summary of the invention
The purpose of the present invention is to provide a kind of stainless steel drawing oils and preparation method thereof.
To achieve the above object, the invention provides the following technical scheme:
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 5-15%；
Chlorinated paraffin 30-40%；
Sulfurized lard 20-30%；
Calcium mahogany sulfonate 3-5%；
Oiliness improver 5-10%；
Extreme-pressure anti-friction additive 3-5%；
Tackifier 5-7%.
Stainless steel drawing oil according to an embodiment of the invention can be further arranged in the stainless steel drawing oil respectively at
The mass fraction of part is as follows:
Mineral oil 15%；
Chlorinated paraffin 30%；
Sulfurized lard 28%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
The stainless steel drawing oil of another embodiment can be further arranged in the stainless steel drawing oil respectively according to the present invention
The mass fraction of composition is as follows:
Mineral oil 15%；
Chlorinated paraffin 38%；
Sulfurized lard 20%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
The stainless steel drawing oil of another embodiment can be further arranged to the chlorinated paraffin using chlorine according to the present invention
Fossil waxes 52.
It includes purification that the stainless steel drawing oil of another embodiment, which can be further arranged to the oiliness improver, according to the present invention
Lard or the mixing of pentaerythritol oleate alternative one or the two, and the control of the two mixing mass ratio is in 1:(2-5).
The stainless steel drawing oil of another embodiment can be further arranged to the extreme-pressure anti-friction additive according to the present invention
Using sulfide isobutene.
The stainless steel drawing oil of another embodiment can be further arranged to the tackifier using second third according to the present invention
Copolymer T614.
Another object of the present invention be a kind of preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 500-600r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 30-40 DEG C, mixing speed control is canned after 400-500r/min, cooling and standings.
Another object of the present invention be a kind of preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 30-40 DEG C, mixing time control is controlled in 30min, mixing speed in 450- for temperature control
500r/min, it is canned after cooling and standings.
Compared with prior art, beneficial effects of the present invention are as follows:
Stainless steel drawing oil of the invention increases various auxiliary agents using the mineral oil of formula design, wherein chlorinated paraffin 52, vulcanization
Lard, for sulfide isobutene as efficient extreme-pressure anti-friction additive, coefficient of friction is low, and the drawing for high speed, high draft adds
Work process provides efficient extreme pressure and antiwear behavior, effectively lowers the abrasion of processing mold, prolongs the service life；And prepared lard or
Pentaerythritol oleate increases lubrication property as oiliness improver, so that drawing oil has boundary lubrication characteristic；Tackifier (second third
Copolymer T614) adhesiveness that increases oil product, make this product with more lubricity；It is solved with calcium mahogany sulfonate in process
In excessive erosion problem, and improve surface smoothness of the stainless steel material after drawing.Mineral oil can use white oil or non-
Machinery oil is marked, appropriate to add to adjust dilute thickness of this product, adaptation is brushed by hand or immersion way；
Meanwhile in stainless steel drawing oil preparation method of the invention, simplest method is directly to mix each ingredient in formula
Stirring is closed, standing is canned can to obtain final products, without excessive operation, save time cost；Of course for raising product
Function and effect, can using two-step method stir, i.e., first handle mineral oil, chlorinated paraffin, sulfurized lard, then by various auxiliary agents
It is canned that addition futher stirs standing to be cooled.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil includes at least following composition: mineral
Oil, chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, respectively
The mass fraction of composition is as follows:
Mineral oil 5-15%；
Chlorinated paraffin 30-40%；
Sulfurized lard 20-30%；
Calcium mahogany sulfonate 3-5%；
Oiliness improver 5-10%；
Extreme-pressure anti-friction additive 3-5%；
Tackifier 5-7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:(2-5).The extreme-pressure anti-friction additive is using vulcanization
Isobutene.The tackifier use ethylene-propylene copolymer T614.
Another object of the present invention be a kind of preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 500-600r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 30-40 DEG C, mixing speed control is canned after 400-500r/min, cooling and standings.
Another object of the present invention be a kind of preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 30-40 DEG C, mixing time control is controlled in 30min, mixing speed in 450- for temperature control
500r/min, it is canned after cooling and standings.
Embodiment 1
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 15%；
Chlorinated paraffin 30%；
Sulfurized lard 28%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:(2-5).The extreme-pressure anti-friction additive is using vulcanization
Isobutene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 550r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 40 DEG C, mixing speed control is canned after 500r/min, cooling and standings.
Embodiment 2
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 15%；
Chlorinated paraffin 30%；
Sulfurized lard 28%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:2.The extreme-pressure anti-friction additive is using vulcanization isobutyl
Alkene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 35 DEG C, mixing time control is controlled in 30min, mixing speed in 450r/ for temperature control
Min, it is canned after cooling and standings.
Embodiment 3
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 15%；
Chlorinated paraffin 38%；
Sulfurized lard 20%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:5.The extreme-pressure anti-friction additive is using vulcanization isobutyl
Alkene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 600r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 40 DEG C, mixing speed control is canned after 450r/min, cooling and standings.
Embodiment 4
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 15%；
Chlorinated paraffin 38%；
Sulfurized lard 20%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:5.The extreme-pressure anti-friction additive is using vulcanization isobutyl
Alkene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 40 DEG C, mixing time control is controlled in 30min, mixing speed in 450r/ for temperature control
Min, it is canned after cooling and standings.
Embodiment 5
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 10%；
Chlorinated paraffin 40%；
Sulfurized lard 23%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:3.The extreme-pressure anti-friction additive is using vulcanization isobutyl
Alkene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 580r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 35 DEG C, mixing speed control is canned after 450r/min, cooling and standings.
Embodiment 6
A kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil is including at least following composition: mineral oil,
Chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, each composition
Mass fraction it is as follows:
Mineral oil 10%；
Chlorinated paraffin 40%；
Sulfurized lard 23%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
Wherein the chlorinated paraffin uses chlorinated paraffin 52.The oiliness improver includes prepared lard or pentaerythritol oleate
Alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:3.The extreme-pressure anti-friction additive is using vulcanization isobutyl
Alkene.The tackifier use ethylene-propylene copolymer T614.
The preparation method of stainless steel drawing oil the following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 30 DEG C, mixing time control is controlled in 30min, mixing speed in 450r/ for temperature control
Min, it is canned after cooling and standings.
The stainless steel drawing oil for being formulated and preparing according to embodiment 1 to 6 carries out performance detection, finds the performance of embodiment 1
It is best.Wherein at 208 DEG C, ASTM 2783 carries out PB in four-ball test and is the temperature of ASTM D92 progress flash-point (opening)
1320N, PD 7934N.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of stainless steel drawing oil, which is characterized in that the formula of the stainless steel drawing oil includes at least following composition: mineral
Oil, chlorinated paraffin, sulfurized lard, prepared lard, pentaerythritol oleate, sulfide isobutene, calcium mahogany sulfonate, tackifier, respectively
The mass fraction of composition is as follows:
Mineral oil 5-15%；
Chlorinated paraffin 30-40%；
Sulfurized lard 20-30%；
Calcium mahogany sulfonate 3-5%；
Oiliness improver 5-10%；
Extreme-pressure anti-friction additive 3-5%；
Tackifier 5-7%.
2. a kind of stainless steel drawing oil according to claim 1, which is characterized in that each composition in the stainless steel drawing oil
Mass fraction is as follows:
Mineral oil 15%；
Chlorinated paraffin 30%；
Sulfurized lard 28%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
3. a kind of stainless steel drawing oil according to claim 1, which is characterized in that each composition in the stainless steel drawing oil
Mass fraction is as follows:
Mineral oil 15%；
Chlorinated paraffin 38%；
Sulfurized lard 20%；
Calcium mahogany sulfonate 5%；
Oiliness improver 10%；
Extreme-pressure anti-friction additive 5%；
Tackifier 7%.
4. a kind of stainless steel drawing oil according to any one of claims 1 to 3, which is characterized in that the chlorinated paraffin is adopted
With chlorinated paraffin 52.
5. a kind of stainless steel drawing oil according to claim 4, which is characterized in that the oiliness improver include prepared lard or
Pentaerythritol oleate alternative one or the two mixing, and the control of the two mixing mass ratio is in 1:(2-5).
6. a kind of stainless steel drawing oil according to claim 5, which is characterized in that the extreme-pressure anti-friction additive uses sulphur
Change isobutene.
7. a kind of stainless steel drawing oil according to claim 6, which is characterized in that the tackifier use ethylene-propylene copolymer
T614。
8. a kind of stainless steel drawing oil according to claim 7, which is characterized in that the preparation method of the stainless steel drawing oil
The following steps are included:
S1, mineral oil, chlorinated paraffin, sulfurized lard are taken respectively according to recipe ratio, be placed in agitating device, stirred under room temperature
10min, mixing speed are controlled in 500-600r/min；
S2, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-friction additive, tackifier are taken to be placed in S1 step respectively according to recipe ratio
In agitating device, 20min is stirred at 30-40 DEG C, mixing speed control is canned after 400-500r/min, cooling and standings.
A kind of stainless steel drawing oil according to claim 7, which is characterized in that the preparation method packet of the stainless steel drawing oil
Include following steps:
S1, mineral oil, chlorinated paraffin, sulfurized lard, calcium mahogany sulfonate, oiliness improver, extreme-pressure anti-wear is taken to add respectively according to recipe ratio
Agent, tackifier is added to be placed in agitating device together；
S2, starting agitating device, at 30-40 DEG C, mixing time control is controlled in 30min, mixing speed in 450- for temperature control
500r/min, it is canned after cooling and standings.