CN110294943A - A kind of unmade way bitumen regenerant and its preparation method and application - Google Patents
A kind of unmade way bitumen regenerant and its preparation method and application Download PDFInfo
- Publication number
- CN110294943A CN110294943A CN201910651085.2A CN201910651085A CN110294943A CN 110294943 A CN110294943 A CN 110294943A CN 201910651085 A CN201910651085 A CN 201910651085A CN 110294943 A CN110294943 A CN 110294943A
- Authority
- CN
- China
- Prior art keywords
- oil
- agent
- bitumen regenerant
- grease
- unmade way
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of road technical fields more particularly to a kind of unmade way bitumen regenerant and its preparation method and application.By mass percentage, the regenerative agent includes following components: recycling grease 60-80%, lightweight oil 5-15%, plasticizer 5-10%, bleeding agent 2-5%, stabilizer 2-5%, age resister 2-5%.The present invention is one kind to recycle grease environment-friendly type composite regenerant as main component, recycles the utilization of grease, the material cost of regenerative agent can be significantly reduced, have significant economic benefit.Meanwhile the present invention provides a kind of approach for recycling grease resource recycling, so that the solid waste for realizing waste asphalt mixture utilizes and the regeneration of recycling grease, for environmental protection, resource-effective are of great significance.Regenerative agent preparation method of the present invention and required equipment are simple, easy to operate, and technological parameter is convenient for control;Time etc. is added without strict control in use process.
Description
Technical field
The present invention relates to field of road technical fields, specifically, be related to a kind of unmade way bitumen regenerant and its
Preparation method and application.
Background technique
It is only intended to increase understanding of the overall background of the invention for information disclosed in background of invention, without
It is existing well known to persons skilled in the art so to be considered as recognizing or imply that information composition has become in any form
Technology.
Ended for the end of the year 2018, China's highway mileage open to traffic breaks through 130,000 kilometers, occupies first place in the world.China's highway
95% the above are bituminous pavement, being widely applied and using with High Grade Bitumen Pavement, cracking, track, pit slot and pine
The different kinds of roads disease problem such as scattered gradually shows, and the maintenance and maintenance of bituminous pavement are the pressing issues faced at present.According to state
Family's highway development plan, the highway for having 6000-7000km is needed overhaul every year, will generated every year on average close by China
4000000 tons of waste asphalt mixture, wherein 5% is pitch, about 95% is mineral aggregate.Largely discarded asphalt not only accounts for
With a large amount of arable land, surrounding enviroment are polluted, and are a kind of great wastings of resources.Meanwhile Highway Maintenance maintenance needs
It consumes a large amount of pitch, gather materials, the non-renewable resources such as miberal powder.It, not only can be with if waste asphalt mixture can efficiently use
Alleviate Milled asphalt materials and store up bring environmental pressure, and can be reduced the consumption to non-renewable resources, significantly reduces construction
Cost has apparent economic benefit and social benefit.
Waste asphalt mixture gradually aging during prolonged use, microcosmic point show as fragrant fragrant content drop
Low, asphalt content improves, and macroscopic aspect shows as pitch and becomes fragile, is hardened, and leads to bituminous pavement military service reduced performance, causes more
Kind disease.So-called regeneration is exactly that a certain amount of regenerative agent is added into waste asphalt or waste asphalt mixture, adjusts aging drip
Four green component ratios, restore the Sol-gel type colloform texture of pitch, the viscoelasticity of aged asphalt are enable to be restored, from
And guarantee the military service performance of reclaimed asphalt mixture.Currently, common unmade way bitumen regenerant is rich in the light of fragrant sweet smell
Matter oil and plasticizer etc. reconcile by a certain percentage, although present inventors believe that this kind of regenerative agent can restore aging
Four groups of pitch be grouped as with viscoelasticity energy, but the light components in regenerative agent are readily volatilized, lead to reclaimed asphalt mixture
Rate of ageing is fast, and long service performance not can guarantee.Meanwhile the application of a large amount of lightweight oils and plasticizer cause regenerative agent at
This is higher, to limit the regeneration of waste asphalt mixture.
Summary of the invention
In view of the above problems, the present invention is intended to provide a kind of unmade way bitumen regenerant and preparation method thereof and
Using.Of the invention makees bitumen regenerant as main component to recycle grease material, can effectively restore the glutinous of aged asphalt
Elastic energy, can be with large-scale application in the production of hot in-plant reclaimed asphalt mixture, the regeneration of existing road pitch is effectively reduced
The production cost of agent.
An object of the present disclosure: a kind of unmade way bitumen regenerant is provided.
Second purpose of the invention: a kind of preparation method of unmade way bitumen regenerant is provided.
Third purpose of the present invention: the application of the unmade way bitumen regenerant is provided.
For achieving the above object, the invention discloses following technical proposals:
Firstly, the present invention discloses a kind of unmade way bitumen regenerant, by mass percentage, including following components: it returns
Receive grease 60-80%, lightweight oil 5-15%, plasticizer 5-10%, bleeding agent 2-5%, stabilizer 2-5%, age resister 2-
5%.
As further technical solution, the recycling grease includes: waste used oil, food waste oil, any in rubber oil
One or more of combinations, a combination thereof ratio can be adjusted arbitrarily.The recycling grease is mainly used for supplement pitch to be damaged because of aging
The low molecular weight fragrance of mistake point, makes four component ratios of aged asphalt be restored to normal level, while improving the colloid knot of pitch
Structure, and play the effect of collaboration improvement aged asphalt rheological property.
As further technical solution, the recycling grease is gone using the techniques such as heating, cooling, filtering are preceding first passed around
Except solid residue, the moisture etc. in recycling grease, to improve its stability of material and intermiscibility.
As further technical solution, the light oil point include: furfural extract oil, aromatic naphtha, naphthenic base extraction oil,
Intermediate base extraction oil, in any one or the combination of several of them in m- naphthenic base extraction oil.
As further technical solution, the plasticizer is phthalate, terephthalic acid ester, liquid fourth
One or more of combinations of benzene rubber.Plasticizer is mainly used for restoring the ductility of regeneration asphalt, improves the low temperature of regeneration asphalt
Cracking resistance.
As further technical solution, the bleeding agent includes: polyethylene glycol, fatty alcohol, alkyl phenol polyoxyethylene ether
In any one or two kinds, be mainly used for improving regenerative agent to the dissolution diffusion of aged asphalt, improve regenerative agent with
The fusion speed of aged asphalt.
As further technical solution, the stabilizer include: silane coupling agent, it is stearic any one or two
Kind, it is mainly used for improving the thermal stability of regenerative agent, prevents the isolation of different component.
As further technical solution, the age resister is any one or two kinds of montmorillonite, hydrotalcite, master
It is used to improve the anti-aging property of regeneration asphalt.
As further technical solution, the unmade way bitumen regenerant further includes other auxiliary agents etc..
Secondly, the present invention discloses a kind of preparation method of unmade way bitumen regenerant, include the following steps:
(1) heating stirring after mixing the recycling grease with lightweight oil obtains regenerative agent basis oil;
(2) the plasticizer, bleeding agent and stabilizer are added in the oil of Xiang Suoshu regenerative agent basis, continues heating stirring,
Obtain environment-friendly type regeneration agent precursor liquid;
(3) it is sheared after addition age resister in Xiang Suoshu environment-friendly type regeneration agent precursor liquid compound again to get environment-friendly type
Raw agent.
As further technical solution, in step (1), the heating stirring are as follows: stir 5- under the conditions of 100-120 DEG C
10 minutes.
As further technical solution, in step (2), the heating stirring are as follows: stir 5- under the conditions of 100-120 DEG C
10 minutes.
As further technical solution, in step (3), the technique of the shearing are as follows: sheared under the conditions of 120-130 DEG C
15-30 minutes, shear velocity 500rpm-1000rpm.
Finally, the present invention discloses application of the unmade way bitumen regenerant in field of road.
Compared with prior art, the present invention achieve it is following the utility model has the advantages that
(1) present invention is one kind to recycle grease environment-friendly type unmade way bitumen regenerant as main component, oil recovery
The material cost of regenerative agent can be significantly reduced in the utilization of rouge, has significant economic benefit.Meanwhile the present invention provides one
The approach of kind recycling grease resource recycling, so that the solid waste for realizing waste asphalt mixture utilizes and recycle grease
Regeneration for environmental protection, resource-effective is of great significance.
(2) unmade way bitumen regenerant provided by the invention, basic oil to supplement lacked in aged asphalt it is light
Matter component generates certain diluting effect to it, makes its more easily sliding intermolecular under external force, effectively reduces aging
The hardness of pitch;To reach soft pitch and restore the result of Rheological Property of Asphalt.
(3) regenerative agent preparation method of the present invention and required equipment are simple, easy to operate, and technological parameter is convenient for control;Make
Time etc. is added with strict control is not necessarily in the process.
Specific embodiment
It is noted that following detailed description is all illustrative, it is intended to provide further instruction to the present invention.Unless another
It indicates, all technical and scientific terms used herein has usual with general technical staff of the technical field of the invention
The identical meanings of understanding.
It should be noted that term used herein above is merely to describe specific embodiment, and be not intended to restricted root
According to exemplary embodiments of the present invention.Such as, used herein, unless the context clearly indicates otherwise, otherwise singular shape
Formula is also intended to include plural form, additionally, it should be understood that, when in the present specification using term "comprising" and/or " packet
Include " when, indicate existing characteristics, step, operation, device, component and/or their combination.
As previously mentioned, current some unmade way bitumen regenerants still have that cost is excessively high a series of to ask
Topic.Therefore, the invention proposes one kind to recycle grease material waste asphalt reclaiming agent as main component, is used for pitch milling
The recycling and reusing of material can effectively restore the viscoelasticity energy of aged asphalt, improve the military service performance of reclaimed asphalt mixture;It is existing
The present invention is further illustrated in conjunction with specific embodiment.
In the following example, the waste used oil is from Jinan flood along full-sized car repair shop;The food waste oil from
Shandong University's restaurant kitchen, the waste rubber oil inspire confidence in profit up to Chemical Co., Ltd. from Shandong.In addition, the waste used oil makes
Solid residue therein, moisture etc. successively are removed by the techniques such as heating, cooling, filtering with preceding, to improve its material settling out
Property and intermiscibility.
Embodiment 1
A kind of preparation method of unmade way bitumen regenerant, includes the following steps:
(1) by mass percentage, following raw material: waste used oil 70%, aromatic naphtha 12%, two fourth of phthalic acid is weighed
Ester 7%, polyethylene glycol 5%, silane coupling agent 3%, montmorillonite 3%;
(2) waste used oil is mixed with aromatic hydrocarbons oil, is stirred 8 minutes under the conditions of 120 DEG C, obtains environment-friendly type regeneration
Agent basis oil;
(3) the plasticizer dibutyl phthalate, the poly- second two of bleeding agent are added in the oil of Xiang Suoshu regenerative agent basis
Pure and mild stabilizer silane coupling agent, continuation are stirred 10 minutes under the conditions of 110 DEG C, obtain environment-friendly type regeneration agent precursor liquid;
(4) montmorillonite is added in Xiang Suoshu environment-friendly type regeneration agent precursor liquid, is cut under the conditions of 110 DEG C using high-speed shearing machine
It cuts 20 minutes, shear velocity 800rpm finally obtains environment-friendly type composite regenerant.
Embodiment 2
A kind of preparation method of unmade way bitumen regenerant, includes the following steps:
(1) by mass percentage, weigh following raw material: food waste oil 75%, aromatic naphtha 10%, liquid butadiene-styrene rubber 5%,
Polyethylene glycol 5%, silane coupling agent 2%, hydrotalcite 3%;
(2) the food waste oil is mixed with aromatic hydrocarbons oil, is stirred 10 minutes under the conditions of 100 DEG C, obtains environment-friendly type regeneration
Agent basis oil;
(3) in the oil of Xiang Suoshu regenerative agent basis be added the plasticizer liquid butadiene-styrene rubber, bleeding agent polyethylene glycol and
Stabilizer silane coupling agent, continuation are stirred 5 minutes under the conditions of 100 DEG C, obtain environment-friendly type regeneration agent precursor liquid;
(4) age resister is added in Xiang Suoshu environment-friendly type regeneration agent precursor liquid, using high-speed shearing machine under the conditions of 130 DEG C
Shearing 30 minutes, shear velocity 1000rpm finally obtains environment-friendly type composite regenerant.
Embodiment 3
A kind of preparation method of unmade way bitumen regenerant, includes the following steps:
(1) by mass percentage, following raw material: waste used oil 75%, aromatic naphtha 8%, liquid butadiene-styrene rubber is weighed
5%, fatty alcohol 4%, stearic acid 4%, montmorillonite 4%;
(2) waste used oil is mixed with aromatic naphtha, is stirred 5 minutes under the conditions of 120 DEG C, obtains environment-friendly type regeneration agent
Basic oil;
(3) the plasticizer liquid butadiene-styrene rubber, bleeding agent fatty alcohol and steady are added in the oil of Xiang Suoshu regenerative agent basis
Determine agent stearic acid, continuation is stirred 5 minutes under the conditions of 120 DEG C, obtains environment-friendly type regeneration agent precursor liquid;
(4) montmorillonite is added in Xiang Suoshu environment-friendly type regeneration agent precursor liquid, is cut under the conditions of 120 DEG C using high-speed shearing machine
It cuts 15 minutes, shear velocity 500rpm finally obtains environment-friendly type composite regenerant.
Embodiment 4
A kind of preparation method of unmade way bitumen regenerant, includes the following steps:
(1) by mass percentage, following raw material: rubber oil 75%, aromatic naphtha 12%, dibutyl phthalate is weighed
7%, polyethylene glycol 5%, silane coupling agent 3%, montmorillonite 3%;
(2) rubber oil is mixed with aromatic hydrocarbons oil, is stirred 8 minutes under the conditions of 115 DEG C, obtains environment-friendly type regeneration agent
Basic oil;
(3) the plasticizer dibutyl phthalate, the poly- second two of bleeding agent are added in the oil of Xiang Suoshu regenerative agent basis
Pure and mild stabilizer silane coupling agent, continuation are stirred 6 minutes under the conditions of 115 DEG C, obtain environment-friendly type regeneration agent precursor liquid;
(4) montmorillonite is added in Xiang Suoshu environment-friendly type regeneration agent precursor liquid, is cut under the conditions of 125 DEG C using high-speed shearing machine
It cuts 25 minutes, shear velocity 900rpm finally obtains environment-friendly type composite regenerant.
Test example 1
A kind of preparation method of unmade way bitumen regenerant, with embodiment 1, difference is: described in being substituted with aromatic naphtha
The basic oil of recycling grease in basic oil, the i.e. regenerative agent is only lightweight oil rather than recycling grease.
Test example 2
A kind of preparation method of unmade way bitumen regenerant, with embodiment 1, difference is: the increasing in the regenerative agent
Modeling agent is replaced by waste used oil.
Test example 3
A kind of unmade way bitumen regenerant, the component of the regenerative agent are only waste used oil.
Performance test:
1, performance detection is carried out to regenerative agent prepared in embodiment 1-4 and test example 1-3, is main control with viscosity
Index determines that the optimum mix amount is 10%, studies the regeneration effect of each regenerative agent under the optimum mix amount;Wherein:
(1) regeneration effect of regeneration asphalt and reclaimed asphalt mixture evaluation analysis environment-friendly type regeneration agent is prepared;Regeneration drip
See Table 1 for details for green conventional performance index.
Table 1
Test index | Needle penetration (0.1mm) | Softening point (DEG C) | 10 DEG C of ductilities (cm) |
Matrix pitch | 68.3 | 48.2 | 40.1 |
Aged asphalt | 28.5 | 63.5 | 0 |
Embodiment 1 | 67.9 | 48.5 | 49.5 |
Embodiment 2 | 68.7 | 47.9 | 42 |
Embodiment 3 | 68.2 | 48.6 | 46 |
Embodiment 4 | 67.9 | 49 | 52 |
Test example 1 | 68 | 46.1 | 51.8 |
Test example 2 | 66.5 | 49.1 | 28 |
Test example 3 | 62 | 53.4 | 22.6 |
(2) aged asphalt used in regeneration effect evaluation test is Shandong 70# matrix pitch according to " highway engineering pitch
And Asphalt Mixture Experiment regulation " T 0610-2011 in (JTG E20-2011): " asphalt rotating thin-film heat run " preparation
Aged asphalt.See Table 2 for details for regenerative agent basic performance testing result.
Table 2
It can be seen that regenerative agent viscosity prepared by the present invention in 108-125mPa from the testing inspection result of table 1 and table 2
Between s, it is more advantageous to during reclamation of old material and is uniformly merged with waste asphalt and waste asphalt mixture.Embodiment 1-4
In have to recycle environment-friendly type regeneration agent that grease is basic oil preparation compared to traditional light oil regenerative agent it is preferably anti-
Ageing properties.
In addition, energy will be old for the regenerative agent prepared in 1-4 of the embodiment of the present invention from 1 regeneration asphalt Performance Analysis of table
Change pitch and is restored to matrix pitch level.The addition of plasticizer shows the ductility of regeneration asphalt it can be seen from test example 2-3
Writing improves, this is because plasticizer can act at aged asphalt large fragment DNA ligation, macromolecular dispersion and solvation are promoted again
The flexibility and ductility of raw pitch.
(3) the environment-friendly type regeneration agent prepared in the present invention is applicable in high additive, low-dosage waste asphalt mixture.To survey
Regenerative agent prepared by the present invention is tried to the power of regeneration of waste asphalt mixture, mixture performance test uses 20%, 60%
Waste asphalt mixture volume simultaneously adds embodiment 1-2 and comparative example 1 in the present invention according to the optimum mix amount of regenerating waste asphalt
The regenerative agent of middle preparation prepares reclaimed asphalt mixture and carries out analysis of experiments;See Table 3 for details for the performance indicator of reclaimed asphalt mixture.
Table 3
From table 3 it can be seen that the dynamic stability of reclaimed asphalt mixture is all larger than specification and wants in embodiment 1-2, test example 1
800 times/the mm asked.From the point of view of comparing three kinds of reclaimed asphalt mixtures, the reclaimed asphalt mixture embodiment under identical old material volume
The dynamic stability of 1-2 is slightly below reclaimed asphalt mixture test example 1, illustrates the Rut resistance of reclaimed asphalt mixture test example 1
Ability is preferable, but also illustrates that the regeneration effect of waste asphalt mixture in test example 1 is poor simultaneously.Old material volume is 20% He
Reclaimed asphalt mixture immersion residual stability when 60% is able to satisfy the immersion residual of plain asphalt mixture as defined in specification
Stability is greater than 80% requirement.And the immersion residual stability of mixture in embodiment, freeze-thaw split intensity ratio compared to
Reclaimed asphalt mixture in test example wants high, illustrates the regeneration effect to regenerative agent in embodiment to reclaimed asphalt mixture
It is better than regenerative agent in test example.
2, embodiment 1 and comparative example 1 in the present invention are chosen and prepares regenerative agent progress cost analysis, in which:
(1) 1 cost analysis of embodiment: 700 yuan/ton of waste used oil, 3600 yuan/ton of aromatic naphtha, dibutyl phthalate
8000 yuan/ton, 10800 yuan/ton of polyethylene glycol, 20000 yuan/ton of silane coupling agent, 8500 yuan/ton of montmorillonite.
According to above-mentioned price, one ton of regenerative agent cost are as follows: 0.75 × 700+0.12 × 3600+0.07 × 8000+0.05 ×
10800+0.03 × 20000+0.03 × 8500=2912 yuan/ton.
(2) 1 cost analysis of comparative example: one ton of regenerative agent cost are as follows: 0.87 × 3600+0.07 × 8000+0.05 × 10800
+ 0.03 × 20000+0.03 × 8500=5087 yuan/ton.
According to the above analysis, price, regeneration effect and production technology, the regeneration prepared in the embodiment of the present invention are comprehensively considered
Agent has higher cost performance and promotional value compared with common regenerative agent.
The above description is only a preferred embodiment of the present invention, is not intended to restrict the invention, for those skilled in the art
For member, the invention may be variously modified and varied.All within the spirits and principles of the present invention, it is made it is any modification,
Equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of unmade way bitumen regenerant, which is characterized in that by mass percentage, including following components: recycling grease
60-80%, lightweight oil 5-15%, plasticizer 5-10%, bleeding agent 2-5%, stabilizer 2-5%, age resister 2-5%.
2. unmade way bitumen regenerant as described in claim 1, which is characterized in that the recycling grease includes: waste and old machine
Any one or the combination of several of them in oily, food waste oil, rubber oil.
3. unmade way bitumen regenerant as described in claim 1, which is characterized in that the light oil point includes: that furfural is taken out
Fuel-displaced, aromatic naphtha, naphthenic base extraction oil, intermediate base extraction oil, in any one or a few group in m- naphthenic base extraction oil
It closes;
Preferably, the plasticizer is phthalate, terephthalic acid ester, the one or more of liquid butadiene-styrene rubber
Combination.
4. unmade way bitumen regenerant as described in claim 1, which is characterized in that the bleeding agent include: polyethylene glycol,
Any one in fatty alcohol, alkyl phenol polyoxyethylene ether or two kinds.
5. unmade way bitumen regenerant as described in claim 1, which is characterized in that the stabilizer includes: silane coupled
Agent, stearic any one or two kinds.
6. unmade way bitumen regenerant as described in claim 1, which is characterized in that the age resister is montmorillonite, water
Any one or two kinds of talcum.
7. unmade way bitumen regenerant as claimed in any one of claims 1 to 6, which is characterized in that the recycling grease uses
Before first pass around heating, cooling, filtering removal oil recovery rouge in solid residue, moisture.
8. a kind of preparation method of unmade way bitumen regenerant, which comprises the steps of:
(1) by mass percentage, following components is weighed: recycling grease 60-80%, lightweight oil 5-15%, plasticizer 5-
10%, bleeding agent 2-5%, stabilizer 2-5%, age resister 2-5%, it is spare;
(2) heating stirring after mixing recycling grease described in step (1) with lightweight oil, obtains regenerative agent basis oil;
(3) plasticizer, bleeding agent and stabilizer described in step (1) are added in the oil of Xiang Suoshu regenerative agent basis, continues to heat
Stirring, obtains environment-friendly type regeneration agent precursor liquid;
(4) it is sheared after age resister described in step (1) being added in Xiang Suoshu environment-friendly type regeneration agent precursor liquid to get environmental protection
Type composite regenerant.
9. the preparation method of unmade way bitumen regenerant as claimed in claim 8, which is characterized in that described in step (1)
Heating stirring are as follows: stirred 5-10 minutes under the conditions of 100-120 DEG C;
Preferably, in step (2), the heating stirring are as follows: stirred 5-10 minutes under the conditions of 100-120 DEG C;
Preferably, in step (3), the technique of the shearing are as follows: sheared 15-30 minutes under the conditions of 120-130 DEG C, shear velocity
500rpm-1000rpm。
10. such as the described in any item unmade way bitumen regenerants of claim 1-7 and/or square as claimed in claim 8 or 9
The application of method and its regenerative agent of preparation in field of road.