CN110283649A - A kind of oil composition for front shock absorber of motorcycle and preparation method thereof - Google Patents
A kind of oil composition for front shock absorber of motorcycle and preparation method thereof Download PDFInfo
- Publication number
- CN110283649A CN110283649A CN201910603225.9A CN201910603225A CN110283649A CN 110283649 A CN110283649 A CN 110283649A CN 201910603225 A CN201910603225 A CN 201910603225A CN 110283649 A CN110283649 A CN 110283649A
- Authority
- CN
- China
- Prior art keywords
- oil
- motorcycle
- composition
- pour
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is the Oil mixture for improving the service life and control stability of motorcycle the present invention relates to a kind of oil composition for front shock absorber of motorcycle and preparation method thereof.It is of the invention by using oil based on highly viscous hydrocrackates and the solvent-refined oil of medium viscosity proportion, in conjunction with nanometer and ceramic anti-wear agent, solve the problems, such as that viscosity-temperature characteristics existing for common two end number mixing mineral oil and cryogenic property are undesirable in current motorcycle shock-absorber oil, the special selection of antiwear additive and antioxidant is especially squeezed various additives component simultaneously, shear stability, lubricity and the antioxygen rustless property for improving lubricating oil can satisfy front damper of motorcycle oil indices requirement.
Description
Technical field
It is the use longevity for improving motorcycle the present invention relates to a kind of oil composition for front shock absorber of motorcycle and preparation method thereof
The Oil mixture of life and control stability.
Background technique
Since the manufacturing technology of modern motorcycle develops, the traveling field of motorcycle is excessive, and road severity increases, and causes
Requirement to damper and its oil product is also higher, for shock absorber fluid, in the viscosity-temperature characteristics of oil product, low temperature flow, rubber phase
The requirement of capacitive, oxidation stability and abrasion resistance is higher and higher.In order to mitigate and decay motorcycle in the process of moving because
The uneven impact and vibration being subject to of road, guarantee driving ride comfort and comfort, improve motorcycle service life and
The stability of manipulation is provided with dampening arrangement on motorcycle.
Motorcycle shock-absorber oil requires viscosity appropriateness, and viscous warm nature is good, and cryogenic property is good, thus just to the selection of base oil
Higher requirement is proposed, but China's front damper of motorcycle oil is mostly simple two end number mixing mineral oil, viscosity-temperature characteristics at present
It is extremely undesirable with cryogenic property, even if remaining difficult usually (40 DEG C of working environment that meet motorcycle vibration absorber after addition additive
To -40 DEG C).
Summary of the invention
Above-mentioned in order to overcome the shortcomings of, present invention topic provides a kind of oil composition for front shock absorber of motorcycle and its preparation side
Method.
The technical solution that the present invention uses is as follows:
A kind of oil composition for front shock absorber of motorcycle,
Its raw material components is calculated by per kilogram raw material, and composition and content are as follows:
700~1050g of lubricating base oils,
10~40g of nano antiwear agent,
5~10g of antioxidant,
10~20g of pour-point depressant,
0.0004~0.001g of anti-foaming agent
The lubricating base oils are the mixture that solvent-refined oil and hydrocrackates form；
The solvent-refined oil is MVIS150BS or MVIS150；
The hydrocrackates are VHVI H300 or HVIW H60；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B group
At mixture；
The antioxidant is the mixture that 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551 is formed；
The pour-point depressant is the mixing that polyalphaolefin T803B and polymethacrylates Viscoplex 8-310 is formed
Object；
The anti-foaming agent is methyl-silicone oil T901.
A kind of oil composition for front shock absorber of motorcycle, raw material components are calculated by per kilogram raw material, are formed as follows:
Lubricating base oils 800.1585g,
Ceramic anti-wear agent 25g,
Antioxidant 10g,
Pour-point depressant 30g,
Anti-foaming agent 0.0005g,
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrogen being added to split
Carburetion is the mixture of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are VHVI H300；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B,
It is in mass ratio sulphur phosphorus brothers alcohol radical zinc salt T204: the isooctyl acid sulphur phosphatide octadecylamine T308B mixture formed for 1:1；
The antioxidant be 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio i.e. 2,6-
Di-tert-butyl p-cresol T501: the benzotriazole derivative T551 mixture formed for 5:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, is in mass ratio
Polyalphaolefin T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
A kind of oil composition for front shock absorber of motorcycle, raw material components are calculated by per kilogram raw material, are formed as follows:
Lubricating base oils 560g
Nano antiwear agent 10g
Pour-point depressant 19.9995g
Anti-foaming agent 0.0005g
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrogen being added to split
Carburetion is the composition of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are HVIW H60；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B,
It is in mass ratio sulphur phosphorus brothers alcohol radical zinc salt T204: the isooctyl acid sulphur phosphatide octadecylamine T308B mixture formed for 2:1；
The antioxidant be 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio i.e. 2,6-
Di-tert-butyl p-cresol T501: the benzotriazole derivative T551 mixture formed for 4:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, is in mass ratio
Polyalphaolefin T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert in proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), 75~85 DEG C are warming up to, control speed of agitator is after 300~400r/min stirs 4h, to add extreme-pressure anti-wear
Agent and antioxidant, it is 300~400r/min that speed of agitator is controlled at 50~60 DEG C, stirs 4h, is filtered to get a kind of motorcycle
Front damper fluid composition.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), 60~75 DEG C are warming up to, control speed of agitator is after 200~300r/min stirs 3h, to add extreme-pressure anti-wear
Agent and antioxidant, it is 200~300r/min that speed of agitator is controlled at 40~50 DEG C, stirs 3h, is filtered to get a kind of motorcycle
Front damper fluid composition.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert, and be added
Stabilizer；
(2), 60~75 DEG C are warming up to, control speed of agitator is after 200~300r/min stirs 3h, after stablizing 32 minutes again
3h is stirred, extreme pressure anti-wear additives and antioxidant are added, it is 200~300r/min, stirring that speed of agitator is controlled at 30~40 DEG C
Filtering is after 3h to get a kind of oil composition for front shock absorber of motorcycle.
Beneficial effects of the present invention:
It is of the invention by using oil based on highly viscous hydrocrackates and the solvent-refined oil of medium viscosity proportion,
In conjunction with nanometer and ceramic anti-wear agent, solves and glue temperature in current motorcycle shock-absorber oil existing for common two end number mixing mineral oil
Characteristic and the undesirable problem of cryogenic property, while antiwear additive and antioxidant are especially squeezed to various additives component
Special selection, improve shear stability, lubricity and the antioxygen rustless property of lubricating oil, subtract before can satisfy motorcycle
Shake the requirement of device oil indices.
Specific embodiment
For a better understanding of the present invention, the present invention is further described below by embodiment, but is not intended to limit this hair
It is bright.
The technical solution that the present invention uses is as follows:
A kind of oil composition for front shock absorber of motorcycle,
Its raw material components is calculated by per kilogram raw material, and composition and content are as follows:
700~1050g of lubricating base oils,
10~40g of nano antiwear agent,
5~10g of antioxidant,
10~20g of pour-point depressant,
0.0004~0.001g of anti-foaming agent
The lubricating base oils are the mixture that solvent-refined oil and hydrocrackates form；
The solvent-refined oil is MVIS150BS or MVIS150；
The hydrocrackates are VHVI H300 or HVIW H60；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B group
At mixture；
The antioxidant is the mixture that 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551 is formed；
The pour-point depressant is the mixing that polyalphaolefin T803B and polymethacrylates Viscoplex 8-310 is formed
Object；
The anti-foaming agent is methyl-silicone oil T901.
A kind of oil composition for front shock absorber of motorcycle, raw material components are calculated by per kilogram raw material, are formed as follows:
Lubricating base oils 800.1585g,
Ceramic anti-wear agent 25g,
Antioxidant 10g,
Pour-point depressant 30g,
Anti-foaming agent 0.0005g,
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrogen being added to split
Carburetion is the mixture of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are VHVI H300；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B,
It is in mass ratio sulphur phosphorus brothers alcohol radical zinc salt T204: the isooctyl acid sulphur phosphatide octadecylamine T308B mixture formed for 1:1；
The antioxidant be 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio i.e. 2,6-
Di-tert-butyl p-cresol T501: the benzotriazole derivative T551 mixture formed for 5:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, is in mass ratio
Polyalphaolefin T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
A kind of oil composition for front shock absorber of motorcycle, raw material components are calculated by per kilogram raw material, are formed as follows:
Lubricating base oils 560g
Nano antiwear agent 10g
Pour-point depressant 19.9995g
Anti-foaming agent 0.0005g
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrogen being added to split
Carburetion is the composition of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are HVIW H60；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B,
It is in mass ratio sulphur phosphorus brothers alcohol radical zinc salt T204: the isooctyl acid sulphur phosphatide octadecylamine T308B mixture formed for 2:1；
The antioxidant be 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio i.e. 2,6-
Di-tert-butyl p-cresol T501: the benzotriazole derivative T551 mixture formed for 4:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, is in mass ratio
Polyalphaolefin T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert in proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), 75~85 DEG C are warming up to, control speed of agitator is after 300~400r/min stirs 4h, to add extreme-pressure anti-wear
Agent and antioxidant, it is 300~400r/min that speed of agitator is controlled at 50~60 DEG C, stirs 4h, is filtered to get a kind of motorcycle
Front damper fluid composition.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), 60~75 DEG C are warming up to, control speed of agitator is after 200~300r/min stirs 3h, to add extreme-pressure anti-wear
Agent and antioxidant, it is 200~300r/min that speed of agitator is controlled at 40~50 DEG C, stirs 3h, is filtered to get a kind of motorcycle
Front damper fluid composition.
A kind of preparation method of oil composition for front shock absorber of motorcycle, preparation step are as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert, and be added
Stabilizer；
(2), 60~75 DEG C are warming up to, control speed of agitator is after 200~300r/min stirs 3h, after stablizing 32 minutes again
3h is stirred, extreme pressure anti-wear additives and antioxidant are added, it is 200~300r/min, stirring that speed of agitator is controlled at 30~40 DEG C
Filtering is after 3h to get a kind of oil composition for front shock absorber of motorcycle.
In order to evaluate the performance of oil composition for front shock absorber of motorcycle of the invention, the testing standard of performance and test institute
Instrument model information see the table below.
| Test item | Test reference standard | Instrument model |
| Kinematic viscosity | GB/T265 | DSL-007A |
| Oxidation stability | SH/T0193 | SH/T0193 |
| Copper strip test | GB/T5096 | M305465 |
| Anti-foaming property test | GB/T12579 | DSL-031 |
| Bearing capacity | GB/T3142 | MQ-12-EP |
| Liquid-phase corrosion test | GB/T11143 | SHXS-3 |
| Abrasion resistance test | SH/T0189 | MRS-1J |
The information of various raw materials used in the present invention see the table below.
| Material name | Code name |
| Solvent-refined oil | MVIS150BS |
| Solvent-refined oil | MVIS150 |
| Hydrocrackates | VHVIH300 |
| Hydrocrackates | HVIWH60 |
| Sulphur phosphorus brothers alcohol radical zinc salt | T205 |
| Ten amine of isooctyl acid sulphur phosphatide | T308 |
| 2,6-di-tert-butyl p-cresol | T501 |
| Benzotriazole analog derivative | T551 |
| Poly- a alkene | T803B |
| Polymethacrylates | Viscoplex8-310 |
| Methyl-silicone oil | T901 |
Above said content is only the basic explanation under present inventive concept, and is appointed made by technical solution according to the present invention
What equivalent transformation, is within the scope of protection of the invention.
Claims (6)
1. a kind of oil composition for front shock absorber of motorcycle, it is characterised in that:
Its raw material components is calculated by per kilogram raw material, and composition and content are as follows:
700~1050g of lubricating base oils,
10~40g of nano antiwear agent,
5~10g of antioxidant,
10~20g of pour-point depressant,
0.0004~0.001g of anti-foaming agent
The lubricating base oils are the mixture that solvent-refined oil and hydrocrackates form；
The solvent-refined oil is MVIS150BS or MVIS150；
The hydrocrackates are VHVI H300 or HVIW H60；
The extreme pressure anti-wear additives are what sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B was formed
Mixture；
The antioxidant is the mixture that 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551 is formed；
The pour-point depressant is the mixture that polyalphaolefin T803B and polymethacrylates Viscoplex 8-310 is formed；
The anti-foaming agent is methyl-silicone oil T901.
2. a kind of oil composition for front shock absorber of motorcycle described in claim 1, it is characterised in that: its raw material components presses per kilogram
Raw material calculates, and forms as follows:
Lubricating base oils 800.1585g,
Ceramic anti-wear agent 25g,
Antioxidant 10g,
Pour-point depressant 30g,
Anti-foaming agent 0.0005g,
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrocrackates
For the mixture of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are VHVI H300；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B, by matter
Amount is the mixture of 1:1 composition than i.e. sulphur phosphorus brothers alcohol radical zinc salt T204: isooctyl acid sulphur phosphatide octadecylamine T308B；
The antioxidant is 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio bis- uncle of i.e. 2,6-
Butyl paracresol T501: the benzotriazole derivative T551 mixture formed for 5:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, α alkene i.e. poly- in mass ratio
Hydrocarbon T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
3. a kind of oil composition for front shock absorber of motorcycle described in claim 1, it is characterised in that: its raw material components presses per kilogram
Raw material calculates, and forms as follows:
Lubricating base oils 560g
Nano antiwear agent 10g
Pour-point depressant 19.9995g
Anti-foaming agent 0.0005g
The lubricating base oils are solvent-refined oil and hydrocrackates, in mass ratio i.e. solvent-refined oil: hydrocrackates
For the composition of 2:3 composition；
The solvent-refined oil is MVIS150BS；
The hydrocrackates are HVIW H60；
The extreme pressure anti-wear additives are sulphur phosphorus brothers alcohol radical zinc salt T204 and isooctyl acid sulphur phosphatide octadecylamine T308B, by matter
Amount is the mixture of 2:1 composition than i.e. sulphur phosphorus brothers alcohol radical zinc salt T204: isooctyl acid sulphur phosphatide octadecylamine T308B；
The antioxidant is 2,6-di-tert-butyl p-cresol T501 and benzotriazole derivative T551, in mass ratio bis- uncle of i.e. 2,6-
Butyl paracresol T501: the benzotriazole derivative T551 mixture formed for 4:1；
The pour-point depressant is polyalphaolefin T803B and polymethacrylates Viscoplex 8-310, α alkene i.e. poly- in mass ratio
Hydrocarbon T803B: the polymethacrylates Viscoplex 8-310 mixture formed for 1:1；
The anti-foaming agent is methyl-silicone oil T901.
4. a kind of preparation method of oil composition for front shock absorber of motorcycle described in claim 1-3 any claim, special
Sign is: preparation step is as follows:
(1), each component in base oil is subjected to mix and convert in proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), be warming up to 75~85 DEG C, control speed of agitator be after 300~400r/min stirs 4h add extreme pressure anti-wear additives and
Antioxidant, it is 300~400r/min that speed of agitator is controlled at 50~60 DEG C, stirs 4h, is filtered to get subtracting before a kind of motorcycle
Shake device fluid composition.
5. a kind of preparation method of oil composition for front shock absorber of motorcycle described in claim 1-3 any claim, special
Sign is: preparation step is as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert；
(2), be warming up to 60~75 DEG C, control speed of agitator be after 200~300r/min stirs 3h add extreme pressure anti-wear additives and
Antioxidant, it is 200~300r/min that speed of agitator is controlled at 40~50 DEG C, stirs 3h, is filtered to get subtracting before a kind of motorcycle
Shake device fluid composition.
6. a kind of preparation method of oil composition for front shock absorber of motorcycle described in claim 1-3 any claim, special
Sign is: preparation step is as follows:
(1), each component in base oil is subjected to mix and convert by equal proportion, anti-foaming agent and pour-point depressant is added after mix and convert, and stabilization is added
Agent；
(2), 60~75 DEG C are warming up to, control speed of agitator is after 200~300r/min stirs 3h, to be stirred for after stablizing 32 minutes
3h adds extreme pressure anti-wear additives and antioxidant, and it is 200~300r/min that speed of agitator is controlled at 30~40 DEG C, after stirring 3h
Filtering is to get a kind of oil composition for front shock absorber of motorcycle.