CN110241322A - 一种再生铝合金精炼剂 - Google Patents

一种再生铝合金精炼剂 Download PDF

Info

Publication number
CN110241322A
CN110241322A CN201910564841.8A CN201910564841A CN110241322A CN 110241322 A CN110241322 A CN 110241322A CN 201910564841 A CN201910564841 A CN 201910564841A CN 110241322 A CN110241322 A CN 110241322A
Authority
CN
China
Prior art keywords
parts
refining agent
weight
naf
kcl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910564841.8A
Other languages
English (en)
Inventor
王启
王赟
姜俊旗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Shunbo Aluminum Alloy Co Ltd
Original Assignee
Guangdong Shunbo Aluminum Alloy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Shunbo Aluminum Alloy Co Ltd filed Critical Guangdong Shunbo Aluminum Alloy Co Ltd
Priority to CN201910564841.8A priority Critical patent/CN110241322A/zh
Publication of CN110241322A publication Critical patent/CN110241322A/zh
Pending legal-status Critical Current

Abstract

一种铝合金精炼剂，其各成份按重量比计如下：NaCl 30～40份，KCl 30～35份，MgCl220～25份，NaF 20～25份，Na3AlF610～15份，CaF22～5份。精炼剂按重量配好后，混合并加水搅拌，几天后流化床干燥、破碎、再干燥脱水，真空封装。本发明制备工艺简单，便于规模化生产。可充分去除熔体中的氧化物夹杂，除渣率可达到90％以上。

Description

一种再生铝合金精炼剂
技术领域：
本发明涉及一种铝合金精炼剂，尤其是涉及一种再生铝合金精炼剂。
背景技术：
铝合金冶炼过程时，熔解于熔体中的精炼剂能够通过物理的、化学的或物理化学的相互作用，从熔体中除去金属杂质，氧化物及其它氧化物夹杂等。精炼剂的除杂能力是由精炼剂对熔体中的氧化物夹杂的吸附、溶解作用以及精炼剂与熔体中杂质之间的化学作用决定的。精炼剂和夹杂物之间的界面张力越小，精炼剂的吸附作用越好，除杂作用越强。
发明内容：
本发明目的在于提供一种再生铝合金精炼剂大大提高铝合金产品精炼效率和效果。
本发明的技术方案是这样实现的：
一种再生铝合金精炼剂，其成份按重量份计如下：NaCl 30～40份，KCl 30～35份，MgCl2 20～25份，NaF 20～25份，Na3AlF6 10～15份， CaF2 2～5份。
进一步，按照重量份计：NaCl 40份，KCl 35份，MgCl2 20份，NaF 20份，Na3AlF6 10份， CaF2 5份。
进一步，按照重量份计：NaCl 32份，KCl 32份， MgCl2 22份，NaF 22份，Na3AlF6 12份， CaF2 3份。
进一步，按照重量份计：NaCl 35份，KCl 30份，MgCl2 25份，NaF 25份，Na3AlF6 15份， CaF2 2份。
进一步，所述的一种再生铝合金精炼剂制备包括以下步骤：
精炼剂按重量配好后，混合并加水搅拌，几天后流化床干燥、破碎、再干燥脱水，真空封装。
MgCl2：降低熔点，降低吸潮；
本发明制备工艺简单，便于规模化生产。可充分去除熔体中的氧化物夹杂，除渣率可达到90％以上。
具体实施方式：
实例1
一种再生铝合金精炼剂，按重量份计如下：
NaCl 40份，KCl 35份，MgCl2 20份，NaF 20份，Na3AlF6 10份， CaF2 5份。
进一步，所述的一种再生铝合金精炼剂制备包括以下步骤：
精炼剂按重量配好后，混合并加水搅拌，几天后流化床干燥、破碎、再干燥脱水，真空封装。
实例2
一种再生铝合金精炼剂，按重量份计如下：
NaCl 32份，KCl 32份， MgCl2 22份，NaF 22份，Na3AlF6 12份， CaF2 3份。
进一步，所述的一种再生铝合金精炼剂制备包括以下步骤：
精炼剂按重量配好后，混合并加水搅拌，几天后流化床干燥、破碎、再干燥脱水，真空封装。
实例3
一种再生铝合金精炼剂，按重量份计如下：
NaCl 35份，KCl 30份，MgCl2 25份，NaF 25份，Na3AlF6 15份， CaF2 2份。
进一步，所述的一种再生铝合金精炼剂制备包括以下步骤：
精炼剂按重量配好后，混合并加水搅拌，几天后流化床干燥、破碎、再干燥脱水，真空封装。
以上所描述的实施例是本发明一部分实施例，而不是全部的实施例。本发明的实施例的详细描述并非旨在限制要求保护的本发明的范围，而是仅仅表示本发明的选定实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。

Claims (5)

1. 一种铝合金精炼剂，其特征在于：各成份按重量份计如下：NaCl 30～40份，KCl 30～35份，MgCl2 20～25份，NaF 20～25份，Na3AlF6 10～15份， CaF2 2～5份。
2.根据权利要求1所述的铝合金精炼剂，其特征在于：所述铝合金精炼剂，其组分按重量份计为： NaCl 40份，KCl 35份，MgCl2 20份，NaF 20份，Na3AlF6 10份，CaF2 5份。
3.根据权利要求1所述的一种铝合金精炼剂，其特征在于：所述各组分按重量份计计为：NaCl 32份，KCl 32份， MgCl2 22份，NaF 22份，Na3AlF6 12份， CaF2 3份。
4.根据权利要求1所述的一种铝合金精炼剂，其特征在于：所述各组分按重量份计计为：NaCl 35份，KCl 30份，MgCl2 25份，NaF 25份，Na3AlF6 15份， CaF2 2份。
5.根据权利要求1～4中任一项所述的一种铝合金精炼剂的制备方法，包括以下步骤：
精炼剂按重量配好后，混合并加水搅拌，24小时后流化床干燥、破碎、再干燥脱水，真空封装。
CN201910564841.8A 2019-06-27 2019-06-27 一种再生铝合金精炼剂 Pending CN110241322A (zh)