CN110240826A - A kind of molten ink of PVC decorative paper high-performance alcohol - Google Patents
A kind of molten ink of PVC decorative paper high-performance alcohol Download PDFInfo
- Publication number
- CN110240826A CN110240826A CN201910508340.8A CN201910508340A CN110240826A CN 110240826 A CN110240826 A CN 110240826A CN 201910508340 A CN201910508340 A CN 201910508340A CN 110240826 A CN110240826 A CN 110240826A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- decorative paper
- pvc decorative
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of molten inks of PVC decorative paper high-performance alcohol, pure water including 6-10% parts by weight, the alcohols mixed solvent of 23-27% parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, the acrylic emulsion of 41-45% parts by weight, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the pigment of 11-15% parts by weight, above-mentioned each component parts by weight summation are 100% parts by weight.The molten ink of PVC decorative paper high-performance alcohol of the invention has good rheological performance, fast fixation performance, transmitting transfer performance and good stability.
Description
Technical field
The present invention relates to ink areas, and in particular to a kind of molten ink of PVC decorative paper high-performance alcohol.
Background technique
PVC decorative paper ink is mostly solvent-based ink before this, not only inflammable and explosive, but also odorous big, pollutes the disadvantage of weight.
Therefore under the promotion of environmentally friendly cry, PVC water-borne decorative paper ink inherently becomes the mainstream of PVC decorative paper printing ink.To the greatest extent
Pipe PVC decorative paper ink has environmentally friendly prospect well, but the exploitation due to PVC ink own characteristic to PVC ink brings one
Fixed difficulty, main difficult point are: 1, the drying property problem of aqueous PVC ink;2, PVC ink ink is adjusted, is close to
Even more than traditional ink.Solvent content is lower in PVC ink, and underdry occurs in the PVC ink produced, therefore, works as print
After on to PVC paper, mostly have substantially non-volatile at normal temperature.When PVC ink prints on PVC paper, can not consolidate immediately
On PVC paper, printing show as not doing, need to take indemnifying measure.
Summary of the invention
It is a kind of with good rheological performance, fast fixation performance, transmitting technical problem to be solved by the present invention lies in providing
The molten ink of PVC decorative paper high-performance alcohol of transfer performance and good stability.
In order to solve the above technical problems, a kind of molten ink of PVC decorative paper high-performance alcohol provided by the invention, including 6-10%
The pure water of parts by weight, the alcohols mixed solvent of 23-27% parts by weight, the film forming of the wetting agent of 2% parts by weight, 2% parts by weight help
Agent, the acrylic emulsion of 41-45% parts by weight, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, 11-15%
The organic pigment of parts by weight, above-mentioned each component parts by weight summation are 100% parts by weight.
Preferably, the alcohols mixed solvent is by the ethyl alcohol of 21-25% parts by weight and the low volatility alcohols of 2% parts by weight
Solvent composition.
Preferably, the wetting agent is acetylenic diols compound.
Preferably, the solid content of the acrylic emulsion is 45%.
Preferably, the thickener is the swollen class compound of alkali soluble.
A kind of preparation method of the molten ink of PVC decorative paper high-performance alcohol, includes the following steps:
(1) it premixes: pure water, alcohols mixed solvent, wetting agent, coalescing agent is uniformly mixed, bonding agent is made;
(2) it adds auxiliary material: pigment is added into bonding agent obtained in step (1), be uniformly mixed, mixed slurry is made;
(3) ink is ground: being ground being added on horizontal sand mill in the slurry being uniformly mixed obtained in step (2)
System, grinding distribution are uniform;
(4) grind again: acrylic emulsion, water-borne wax cream, thickener is added in the obtained ink in step (3), grinds
Mill is uniformly dispersed, and the molten ink of PVC decorative paper high-performance alcohol is made.
Beneficial effects of the present invention: the present invention uses alcohols mixed solvent, and evaporation rate is suitable for overcoming traditional PVC water
There is the problem of underdry in ink, has good rheological performance, fast fixation performance, transmitting transfer performance and good stability, especially
It is suitable for the printings of PVC decorative paper.
Specific embodiment
Embodiment 1
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 6% parts by weight, the ethyl alcohol of 25% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 45% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the 15:3 of 15% parts by weight
Phthalocyanine blue pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
Embodiment 2
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 10% parts by weight, the ethyl alcohol of 23% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 45% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the F5RK of 13% parts by weight
Red pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
Embodiment 3
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 8% parts by weight, the ethyl alcohol of 25% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 43% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the 15:3 of 15% parts by weight
Phthalocyanine blue pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
Embodiment 4
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 10% parts by weight, the ethyl alcohol of 21% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 45% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the F5RK of 15% parts by weight
Red pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
Embodiment 5
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 10% parts by weight, the ethyl alcohol of 25% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 41% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the 15:3 of 15% parts by weight
Phthalocyanine blue pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
Embodiment 6
A kind of molten ink of PVC decorative paper high-performance alcohol, the pure water including 10% parts by weight, the ethyl alcohol of 25% parts by weight, 2%
The low volatility alcohols solvent of parts by weight, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, 45% parts by weight are consolidated
Content is 45% acrylic emulsion, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the F5RK of 11% parts by weight
Red pigment.The wetting agent is acetylenic diols compound, and the thickener is the swollen class compound of alkali soluble.
The preparation method of the molten ink of PVC decorative paper high-performance alcohol of above-described embodiment 1- embodiment 6, includes the following steps:
(1) it premixes: pure water, alcohols mixed solvent, wetting agent, coalescing agent is uniformly mixed, bonding agent is made;
(2) it adds auxiliary material: pigment is added into bonding agent obtained in step (1), be uniformly mixed, mixed slurry is made;
(3) ink is ground: being ground being added on horizontal sand mill in the slurry being uniformly mixed obtained in step (2)
System, grinding distribution are uniform;
(4) grind again: acrylic emulsion, water-borne wax cream, thickener is added in the obtained ink in step (3), grinds
Mill is uniformly dispersed, and the molten ink of PVC decorative paper high-performance alcohol is made.
The molten ink technical indicator of PVC decorative paper high-performance alcohol of embodiment 1- embodiment 6 is as shown in the table:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | |
Fineness (μm) | ≤15 | ≤15 | ≤15 | ≤15 | ≤15 | ≤15 |
Sticky (400r) | 9-12 | 8-12 | 8-11 | 9-12 | 7-10 | 8-11 |
Fluidity (25 DEG C, mm) | 32-38mm | 32-38mm | 32-38mm | 32-38mm | 32-38mm | 32-38mm |
It can be seen that the molten ink of PVC decorative paper high-performance alcohol of the invention has good rheological property, fast anchorage
Can, transfer performance and good stability be transmitted, is particularly suitable for the printing of PVC decorative paper.
Above description is exemplary and not limiting.By above description skilled person realizes that originally
Many kinds of change and modification of invention, will also fall within the spirit and scope of the invention.
Claims (6)
1. a kind of molten ink of PVC decorative paper high-performance alcohol, which is characterized in that the pure water including 6-10% parts by weight, 23-27% weight
Measure the alcohols mixed solvent of part, the wetting agent of 2% parts by weight, the coalescing agent of 2% parts by weight, the propylene of 41-45% parts by weight
Yogurt liquid, the waterborne wax emulsion of 1% parts by weight, the thickener of 2% parts by weight, the pigment of 11-15% parts by weight, above-mentioned each component
Parts by weight summation is 100% parts by weight.
2. the molten ink of PVC decorative paper high-performance alcohol according to claim 1, which is characterized in that the alcohols mixed solvent
It is made of the ethyl alcohol of 21-25% parts by weight and the low volatility alcohols solvent of 2% parts by weight.
3. the molten ink of PVC decorative paper high-performance alcohol according to claim 1, which is characterized in that the wetting agent is alkynes two
Alcohol compound.
4. the molten ink of PVC decorative paper high-performance alcohol according to claim 1, which is characterized in that the acrylic emulsion
Solid content is 45%.
5. the molten ink of PVC decorative paper high-performance alcohol according to claim 1, which is characterized in that the thickener is
Alkali soluble is swollen class compound.
6. a kind of preparation method of the molten ink of PVC decorative paper high-performance alcohol as described in claim 1, which is characterized in that including
Following steps:
(1) it premixes: pure water, alcohols mixed solvent, wetting agent, coalescing agent is uniformly mixed, bonding agent is made;
(2) it adds auxiliary material: pigment is added into bonding agent obtained in step (1), be uniformly mixed, mixed slurry is made;
(3) ink is ground: being ground, is ground by being added on horizontal sand mill in the slurry being uniformly mixed obtained in step (2)
Mill is uniformly dispersed;
(4) grind again: acrylic emulsion, water-borne wax cream, thickener, grinding point is added in the obtained ink in step (3)
It dissipates uniformly, the molten ink of PVC decorative paper high-performance alcohol is made.