CN110194864A - 驱蟑螂的聚烯烃组合物、驱蟑螂的聚烯烃材料及制备方法与应用、家电部件及产品和胶带 - Google Patents
驱蟑螂的聚烯烃组合物、驱蟑螂的聚烯烃材料及制备方法与应用、家电部件及产品和胶带 Download PDFInfo
- Publication number
- CN110194864A CN110194864A CN201910139078.4A CN201910139078A CN110194864A CN 110194864 A CN110194864 A CN 110194864A CN 201910139078 A CN201910139078 A CN 201910139078A CN 110194864 A CN110194864 A CN 110194864A
- Authority
- CN
- China
- Prior art keywords
- parts
- cockroach
- weight
- polyolefin
- repellent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及驱蟑螂材料领域,公开了驱蟑螂的聚烯烃组合物、驱蟑螂的聚烯烃材料及制备方法与应用、家电部件及产品和胶带。该组合物包括:复配驱虫剂0.1‑3重量份、聚烯烃树脂100重量份、稳定剂2‑4重量份、抗氧剂1‑3重量份、碳酸钙5‑10重量份、相容剂0.5‑2重量份和润滑剂1‑2重量份;其中,所述复配驱虫剂包括薄荷脑、香精和驱虫植物提取物。本发明提供的聚烯烃材料具有本征的驱蟑螂作用,可以提供长效且易加工的实现家用电器驱蟑螂的效果。
Description
技术领域
本发明涉及驱蟑螂材料领域,具体涉及驱蟑螂的聚烯烃组合物、由该组合物制备而得的驱蟑螂的聚烯烃材料及制备方法与应用,含有所述驱蟑螂的聚烯烃材料的家电部件、家电产品和胶带。
背景技术
蟑螂(Cockroach)往往泛指“蜚蠊目”(Blattodea)的杂食性昆虫,以现代生物学分类,蟑螂约有4000种,其中数十种被认为是害虫。家具中常见的的蟑螂有:美洲蟑螂、澳洲蟑螂、德国小蠊、亚洲姬蠊等。蟑螂穿梭与人类、食物和垃圾之间,可能传播多种疾病的病原体,如:大肠杆菌、肠病毒、沙门氏菌、链球菌、钩虫、鼠疫杆菌等。对人们的身体健康产生极大的威胁。
人类厨房是蟑螂最常活动的地点。厨房中潮湿、温暖、阴暗的角落是蟑螂最喜爱的栖息之地。家用电器,如电饭煲、电压力锅、电磁炉等,具有散热装置。散热装置主要由风机和散热孔(格栅)组成。散热孔(格栅)背后的封闭部空间是蟑螂藏身的最佳之地,蟑螂可从散热通道进入小家电的内部空间繁殖和生存。蟑螂进入电器内部不仅存在健康风险,还容易造成电路短路、诱发火灾等安全事故。
现有的驱蟑螂技术可分为物理和化学两种。物理驱虫法主要通过声波、电磁波、光、电等手段达到驱除蟑螂的目的,此方法长期效果差,蟑螂适应后装置失效,且将物理驱虫装置安装在小家电中成为一大难点。化学驱虫法采用杀虫剂、除虫菊酯、樟脑等对蟑螂起到有效的杀灭和驱除作用,但缺点是有毒性或者有很大的刺激性气味,不适用于小型家用电器。
目前,家用电器,尤其是厨房用电器的蟑螂驱除,需要解决的主要问题是长效性、安全性和可制造性。
发明内容
本发明的目的是为了如何实现家用电器驱除蟑螂的长效性、安全性和可制造性,提供了驱蟑螂的聚烯烃组合物、驱蟑螂的聚烯烃材料及制备方法与应用、家电部件及产品和胶带,该聚烯烃组合物将聚烯烃改性与生物无毒驱蟑螂试剂结合,制备具有本征驱蟑螂的高分子材料或者母粒,能够在不改变家电产品结构和工艺的前提下达到有效驱避蟑螂的效果。
为了实现上述目的,本发明第一方面提供一种驱蟑螂的聚烯烃组合物,该组合物包括:
复配驱虫剂0.1-3重量份、聚烯烃树脂100重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份;其中,所述复配驱虫剂包括薄荷脑、香精和驱虫植物提取物。
优选地,所述复配驱虫剂中,薄荷脑、香精和驱虫植物提取物的重量比为1:(1-2):(1-3)。
优选地,所述香精为水蒸汽蒸馏得到的水果香精和/或花香香精,优选为柠檬香精和/或茉莉花香精。
优选地,所述驱虫植物提取物为通过二氧化碳超临界萃取从菊花和/或香草提取的混合物。
优选地,所述驱虫植物提取物的25℃密度为0.92-0.98g/cm3,所述驱虫植物提取物的20℃折射率为1.4-1.6。
优选地,所述聚烯烃树脂为高密度聚乙烯、低密度聚乙烯、均聚聚丙烯、共聚聚丙烯、乙烯-醋酸乙烯酯共聚物中的一种或多种。
优选地,所述抗氧剂选自四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、三(2,4-二叔丁基苯基)亚磷酸酯中的一种或多种。
优选地,所述的润滑剂为硬脂酸、硬脂酸钙、乙撑双硬脂酸酯、季戊四醇硬脂酸酯、聚乙烯蜡、聚丙烯蜡中的一种或多种。
优选地,所述稳定剂为紫外线吸收剂和/或光稳定剂。
优选地,所述相容剂为马来酸酐或甲基丙烯酸缩水甘油酯与聚丙烯的接枝共聚物,所述相容剂的接枝率为0.6-1.2%,所述相容剂2.16kg载荷下190℃的熔融指数为20-40g/10min。
本发明第二方面提供一种驱蟑螂的聚烯烃材料的制备方法,包括:
S1:将聚烯烃树脂100重量份、复配驱虫剂0.1-3重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份加入高速混合机,充分混合10-20min;
S2:将步骤S1得到的混合物进行混炼加工,加工温度为150℃-220℃;
S3:将步骤S2加工得到的产物进行造粒。
本发明第三方面提供一种本发明的方法制得的驱蟑螂的聚烯烃材料。
本发明第四方面提供一种本发明提供的驱蟑螂的聚烯烃材料在家电产品或家电部件中的应用。
本发明第五方面提供一种家电部件,该家电部件由本发明的驱蟑螂的聚烯烃材料成型而得。
本发明第六方面提供一种家电产品,该家电产品包括由本发明的驱蟑螂的聚烯烃材料制得的部件或本发明的家电部件。
本发明第七方面提供一种防蟑螂胶带,包括由本发明的驱蟑螂的聚烯烃材料加工成型而得的薄膜。
优选地,所述胶带还包括在所述薄膜上设置的胶粘层和设置在所述胶粘层上的保护层。
通过上述技术方案,本发明采用特定的来自生物基质的驱虫成分,与特定的聚烯烃进行组合,通过共混复合方法得到具有本征驱蟑螂效果的聚烯烃材料。制备的驱蟑螂聚烯烃材料安全、环保、无毒。本发明提供的聚烯烃材料具有本征的驱蟑螂作用,可以提供长效且易加工的实现家用电器驱蟑螂的效果。
本发明提供的驱蟑螂的聚烯烃材料具备良好的加工性能,可以进一步适用各种热塑加工成型方法(挤出成型、注塑成型、热压成型),兼具良好的力学性能,适合于加工成各种需要的家电部件,以及家电产品;还可以是防蟑螂胶带。
具体实施方式
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值,这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说,各个范围的端点值之间、各个范围的端点值和单独的点值之间,以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围,这些数值范围应被视为在本文中具体公开。
本发明第一方面提供一种驱蟑螂的聚烯烃组合物,该组合物包括:
复配驱虫剂0.1-3重量份、聚烯烃树脂100重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份;其中,所述复配驱虫剂包括薄荷脑、香精和驱虫植物提取物。
本发明中,为了能够与聚烯烃树脂相结合实现提供驱蟑螂的效果,所述聚烯烃组合物中包括的复配驱虫剂为天然生物质提取物,不仅可以很好地与聚烯烃组合物相复配,而且可以提供进一步制得的驱蟑螂的聚烯烃材料具有安全、环保、无毒的效果。优选地,薄荷脑可以是通过二氧化碳超临界萃取从植物薄荷的叶和茎中提取的混合物。薄荷脑为已知物质,可以商购获得。例如,南京绿洋生物科技有限公司的天然薄荷脑、江西泰诚天然香料有限公司的天然萃取薄荷脑、广州南嘉化工科技有限公司的天然薄荷脑。
本发明中,所述香精也来自生物质。优选地,所述香精为水蒸汽蒸馏得到的水果香精和/或花香香精,优选为柠檬香精和/或茉莉花香精。所述香精为已知物质,可以商购获得。例如,江西泰诚天然香料有限公司的柠檬香精和蒸馏萃取茉莉精油。
本发明中,所述驱虫植物提取物来自生物质。优选地,所述驱虫植物提取物为通过二氧化碳超临界萃取从菊花和/或香草提取的混合物。优选地,所述驱虫植物提取物的25℃密度为0.92-0.98g/cm3,所述驱虫植物提取物的20℃折射率为1.4-1.6。本发明中更优选地,所述驱虫植物提取物为通过二氧化碳超临界萃取从菊花和/或香草的叶或茎中提取出的混合物,其中主要的有效组分可以包括除虫菊酯、瓜菊酯、茉莉菊酯、香兰素、香草酸、肉桂酸等。优选地,所述驱虫植物提取物中,主要有效组分的总含量为10-20重量%。二氧化碳超临界萃取的条件可以是温度为32℃-40℃,压力为7-7.5MPa。
本发明的所述复配驱虫剂中,薄荷脑、香精和驱虫植物提取物相匹配,提供更好的驱蟑螂的长效性。优选地,所述复配驱虫剂中,薄荷脑、香精和驱虫植物提取物的重量比为1:(1-2):(1-3)。
本发明中,选用上述复配驱虫剂,在上述组成下可以保证所述复配驱虫剂与聚烯烃树脂的相容性,能够实现聚烯烃材料具有驱蟑螂的特性,且具有长效性。而不使用上述组分组合以及各组分间的用量关系时,则不能实现制得具有驱蟑螂功效的聚烯烃材料,无法用于家电部件或家电产品的制备。
本发明中,可以选取聚烯烃树脂以能够与所述复配驱虫剂进行复配,获得具有长效驱蟑螂效果的聚烯烃材料且适于家电部件或家电产品的制备。优选地,所述聚烯烃树脂为高密度聚乙烯、低密度聚乙烯、均聚聚丙烯、共聚聚丙烯、乙烯-醋酸乙烯酯共聚物中的一种或多种。上述聚烯烃树脂可以进一步优选,例如高密度聚乙烯可以是密度为0.95-0.97g/cm3,2.16kg载荷下190℃的熔融指数为4-8g/10min。低密度聚乙烯可以是密度为0.88-0.92g/cm3,2.16kg载荷下190℃的熔融指数为15-30g/10min。均聚聚丙烯可以是密度为0.89-0.92g/cm3,2.16kg载荷下190℃的熔融指数为4-10g/10min。共聚聚丙烯可以是密度为0.89-0.92g/cm3,2.16kg载荷下190℃的熔融指数为10-20g/10min。乙烯-醋酸乙烯酯共聚物(EVA)可以是密度为0.93-0.95g/cm3,2.16kg载荷下190℃的熔融指数为6-8g/10min,醋酸乙烯含量为15-28重量%。上述聚烯烃树脂的密度可以按照GB1033标准测定。熔融指数可以按照GB3682标准测定。上述聚烯烃树脂均为已知物质,可以商购获得。例如,高密度聚乙烯为燕山石化6380M(密度为0.95g/cm3,2.16kg载荷下190℃的熔融指数为6.2g/10min)。低密度聚乙烯为韩国现代XL505(密度为0.88g/cm3,2.16kg载荷下190℃的熔融指数为15.6g/10min)。均聚聚丙烯为上海石化S1003(密度为0.905g/cm3,2.16kg载荷下190℃的熔融指数为5.3g/10min)、巴塞尔PP1605(密度为0.9g/cm3,2.16kg载荷下190℃的熔融指数为5.1g/10min)。共聚聚丙烯为上海石化F850EBA(密度为0.89g/cm3,2.16kg载荷下190℃的熔融指数为10.5g/10min)、台塑6535A(密度为0.90g/cm3,2.16kg载荷下190℃的熔融指数为11g/10min)。EVA为美国西湖EF526AA(密度为0.93g/cm3,2.16kg载荷下190℃的熔融指数为7.6g/10min,醋酸乙烯含量为16重量%)。
本发明中,使用所述聚烯烃树脂可以根据应用家电产品的需求选用。可以是上述树脂中的一种,或者是两种。当选用两种上述树脂时,优选两种树脂之间的重量比为(10-90):(90-10),且两种树脂的总量为100重量份。
本发明提供的所述驱蟑螂的聚烯烃组合物中,可以添加的抗氧剂起到防止进一步制得的聚烯烃材料老化,满足家电部件或家电产品的制备即可。优选地,所述抗氧剂选自四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、三(2,4-二叔丁基苯基)亚磷酸酯中的一种或多种。
本发明中,所述润滑剂可以提供制备聚烯烃材料好的加工性。优选地,所述润滑剂为硬脂酸、硬脂酸钙、乙撑双硬脂酸酯、季戊四醇硬脂酸酯、聚乙烯蜡、聚丙烯蜡中的一种或多种。聚乙烯蜡、聚丙烯蜡可以是本领域常规使用的用作润滑剂的物质。可以商购获得,例如,聚乙烯蜡为霍尼韦尔AC6A。聚丙烯蜡为广州川聚化工5108C。
本发明提供的所述驱蟑螂的聚烯烃组合物包括的所述稳定剂可以提供进一步制得的聚烯烃材料的耐光老化性即可。优选地,所述稳定剂为紫外线吸收剂和/或光稳定剂。紫外线吸收剂和/或光稳定剂均可以为本领域常规使用的聚烯烃加工助剂,可以商购获得。例如,巴斯夫的光稳定剂770或UV-531。
本发明提供的所述驱蟑螂的聚烯烃组合物包括的所述相容剂可以有助于提高聚烯烃树脂与复配驱虫剂的相容性,满足家电部件或家电产品的制备即可,优选地,所述相容剂为马来酸酐或甲基丙烯酸缩水甘油酯与聚丙烯的接枝共聚物,所述相容剂的接枝率为0.6-1.2%,所述相容剂在2.16kg载荷下190℃的熔融指数为20-40g/10min。所述相容剂是已知物质,可以商购获得。例如,巴塞尔公司的PO-1015(马来酸酐与聚丙烯的接枝物,接枝率为1.2%,2.16kg载荷下190℃的熔融指数约为32g/10min)。
本发明提供的驱蟑螂的聚烯烃组合物,特别选用上述组分以及限定的用量,可以实现进一步制得的驱蟑螂的聚烯烃材料产生良好的驱防蟑螂的效果。
本发明第二方面提供一种驱蟑螂的聚烯烃材料的制备方法,包括:
S1:将聚烯烃树脂100重量份、复配驱虫剂0.1-3重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份加入高速混合机,充分混合10-20min;
S2:将步骤S1得到的混合物进行混炼加工,加工温度为150℃-220℃;
S3:将步骤S2加工得到的产物进行造粒。
步骤S2中所述混炼加工的方法不限,可以是双螺杆挤出机混炼、单螺杆挤出机混炼或混炼机混炼。加工条件适合聚烯烃的加工也不损伤所述复配驱虫剂的性能。
所述聚烯烃树脂、复配驱虫剂、稳定剂、抗氧剂、碳酸钙、相容剂和润滑剂如上所述,不再赘述。
本发明第三方面提供一种本发明的方法制得的驱蟑螂的聚烯烃材料。
本发明中,得到的驱蟑螂的聚烯烃材料可以具有长效的驱蟑螂效果。优选地,所述驱蟑螂的聚烯烃材料可以具有300天以上的良好的驱蟑螂效果。
本发明第四方面提供一种本发明提供的驱蟑螂的聚烯烃材料在家电产品或家电部件中的应用。
本发明中,优选地,所述家电产品为电磁炉、电饭煲、电压力锅中的至少一种。更优选所述驱蟑螂的聚烯烃材料不用于可能与食品接触的部件。可以是,所述家电部件为底座、风机扇叶、风机支架、出风口的部分或全部。
本发明第五方面提供一种家电部件,该家电部件由本发明的驱蟑螂的聚烯烃材料成型而得。
本发明中还可以通过将本发明第一方面提供的驱蟑螂的聚烯烃组合物制备为所述复配驱虫剂含量为8-15重量%的母粒(可以通过如上所述的混合、混炼和造粒得到);然后在进一步的所述成型时,将所述母粒和聚烯烃树脂(与所述母粒中的聚烯烃树脂相同)混合均匀后直接进行注塑成型加工。得到的家电部件中,所述复配驱虫剂含量满足0.08-2.7重量%,优选为0.08-1.8重量%即可。
本发明第六方面提供一种家电产品,该家电产品包括由本发明的驱蟑螂的聚烯烃材料制得的部件或本发明的家电部件。
本发明第七方面提供一种防蟑螂胶带,包括由本发明的驱蟑螂的聚烯烃材料加工成型而得的薄膜。
优选地,所述胶带还包括在所述薄膜上设置的胶粘层和设置在所述胶粘层上的保护层。
所述薄膜可以是厚度为0.2-0.5mm。胶粘层可以为实现所述薄膜与所述保护层粘合的胶粘剂组成,所述胶粘剂可以选自丙烯酸类胶粘剂、有机硅类胶粘剂或聚氨酯类胶粘剂,为本领域常规使用的胶粘剂,可以商购获得。所述胶粘层的厚度可以为0.02-0.08mm。所述保护层可以为由牛皮纸制成的膜,厚度可以为0.08-0.16mm。所述防蟑螂胶带,可以是在所述薄膜的一面或两面设置所述胶粘层和保护层。所述防蟑螂胶带可以粘贴在家电的部件上,达到防止蟑螂进入的目的。还可以粘贴在厨房墙壁或橱柜等蟑螂经常出入的区域,达到区域性防蟑螂的效果。
以下将通过实施例对本发明进行详细描述。
以下实施例和对比例中使用的原料如下:
薄荷脑,南京绿洋生物科技有限公司的天然薄荷脑、江西泰诚天然香料有限公司的天然萃取薄荷脑、广州南嘉化工科技有限公司的天然薄荷脑。
香精,江西泰诚天然香料有限公司的柠檬香精、蒸馏萃取茉莉精油。
均聚聚丙烯:上海石化S1003(密度为0.905g/cm3,2.16kg载荷下190℃的熔融指数为5.3g/10min);
共聚聚丙烯:上海石化F850EBA(密度为0.89g/cm3,2.16kg载荷下190℃的熔融指数为10.5g/10min);
高密度聚乙烯:燕山石化6380M(密度为0.95g/cm3,2.16kg载荷下190℃的熔融指数为6.2g/10min);
低密度聚乙烯:韩国现代XL505(密度为0.88g/cm3,2.16kg载荷下190℃的熔融指数为15.6g/10min);
稳定剂,巴斯夫的光稳定剂770或UV-531;
相容剂,巴塞尔PO-1015;
抗氧剂,巴斯夫的抗氧剂1010或168;
润滑剂:硬脂酸,东马棕榈工业VA-1810;
聚乙烯蜡:霍尼韦尔AC6A;
聚丙烯蜡:广州川聚化工5108C。
以下实施例和对比例制得的聚烯烃材料的性能测试按照以下方法进行:
拉伸强度按照GB/T1040;
悬臂梁缺口冲击强度按照GB/T1843;
密度按照GB1033;
熔融指数按照GB3682,2.16kg载荷下190℃。
制备例
驱虫植物提取物的制备。
将菊花和/或香草的叶或茎进行二氧化碳超临界萃取,条件包括温度约为36℃,压力约为7.2MPa,得到驱虫植物提取物。
驱虫植物提取物的主要有效组分包括除虫菊酯、瓜菊酯、茉莉菊酯、香兰素、香草酸、肉桂酸等,主要有效组分的总含量约为18重量%;驱虫植物提取物的25℃密度约为0.96g/cm3,20℃的折射率约为1.5。
以下份均为重量份。
实施例1
(1)按照表1的用量配制驱蟑螂的聚烯烃组合物:
复配驱虫剂(南京绿洋生物科技有限公司的天然薄荷脑;江西泰诚天然香料有限公司的柠檬香精;驱虫植物提取物(制备例制得))0.1份、均聚PP(上海石化S1003)80份、共聚PP(上海石化F850EBA)20份、稳定剂(巴斯夫UV-531)2.0份、抗氧剂(巴斯夫抗氧剂1010)1.0份、碳酸钙5份,相容剂(巴塞尔PO-1015)0.5份、润滑剂(硬脂酸(VA-1810):聚丙烯蜡(5108C)=1:1)1.0份。
其中复配驱虫剂包括:薄荷脑、香精、驱虫植物提取物,按照1:1:1的重量配比混合。
(2)将上述各组分原料混合后,加入高速混合机,充分混合约10min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为200℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒;
将上述驱蟑螂聚丙烯通过注塑成型为电磁炉底座。进行相关测试,结果见表2。
实施例2
(1)按照表1的用量配制驱蟑螂的聚烯烃组合物:
复配驱虫剂(江西泰诚天然香料有限公司的天然萃取薄荷脑;蒸馏萃取茉莉精油;驱虫植物提取物(制备例制得))2.0份、共聚PP(上海石化F850EBA)80份、均聚PP(上海石化S1003)20份、稳定剂(巴斯夫光稳定剂770)3份、抗氧剂(巴斯夫抗氧剂168)2份、碳酸钙8份,相容剂(巴塞尔PO-1015)1份、润滑剂(硬脂酸(VA-1810):聚丙烯蜡(5108C)=1:1)1.5份。
其中复配驱虫剂包括:薄荷脑、香精、驱虫植物提取物,按照1:1.5:2.0的重量配比混合。
(2)将上述各组分原料混合后,加入高速混合机,充分混合约20min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为180℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒;
将上述驱蟑螂聚丙烯通过注塑成型为电饭煲底座。进行相关测试,结果见表2。
实施例3
(1)按照表1的用量配制驱蟑螂的聚烯烃组合物:
复配驱虫剂(广州南嘉化工科技有限公司的天然薄荷脑;江西泰诚天然香料有限公司的柠檬香精;驱虫植物提取物(制备例制得))3.0份、LDPE(韩国现代XL505)100份、稳定剂(巴斯夫UV-531)4份、抗氧剂(巴斯夫抗氧剂1010)3份、碳酸钙10份,相容剂(巴塞尔PO-1015)2.0份、润滑剂(硬脂酸(VA-1810):聚乙烯蜡(霍尼韦尔AC6A)=1:1)2.0份。
其中复配驱虫剂包括:薄荷脑、香精、驱虫植物提取物,按照1:2:3的重量配比混合。
制备方法如下:
(2)将上述各组分原料混合后,加入高速混合机,充分混合约16min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为160℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒;
将上述驱蟑螂低密度聚乙烯通过吹塑成膜,得到驱蟑螂低密度聚乙烯薄膜。进行相关测试,结果见表2。
实施例4
按照实施例1的方法,不同的是,复配驱虫剂按照1:0.5:1的重量配比混合,替换复配驱虫剂按照1:1:1的重量配比混合。
制得驱蟑螂聚丙烯。进行相关测试,结果见表2。
实施例5
按照实施例1的方法,不同的是,复配驱虫剂按照1:1:4的重量配比混合,替换复配驱虫剂按照1:1:1的重量配比混合。
制得驱蟑螂聚丙烯。进行相关测试,结果见表2。
实施例6
(1)按照表1的用量配制驱蟑螂的聚烯烃组合物:
复配驱虫剂(江西泰诚天然香料有限公司的天然萃取薄荷脑;蒸馏萃取茉莉精油;驱虫植物提取物(制备例制得))2份、共聚PP(上海石化F850EBA)4份、均聚PP(上海石化S1003)1份、稳定剂(巴斯夫光稳定剂770)3份、抗氧剂(巴斯夫抗氧剂168)2份、碳酸钙8份,相容剂(巴塞尔PO-1015)1份、润滑剂(硬脂酸(VA-1810):聚丙烯蜡(5108C)=1:1)1.5份。
其中复配驱虫剂包括:薄荷脑、香精、驱虫植物提取物,按照1:1:1的重量配比混合。
(2)将上述各组分原料混合后,加入高速混合机,充分混合约20min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为180℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒得到复配驱虫剂含量为8.9重量%的母粒;
将上述母粒加上共聚PP(上海石化F850EBA)76份、均聚PP(上海石化S1003)19份进行加工成型为薄膜(共聚PP(上海石化F850EBA)共计80份、均聚PP(上海石化S1003)共计20份;其中,相对于100份聚烯烃树脂,复配驱虫剂投料量为2份,复配驱虫剂含量为1.7重量%),厚度为0.4mm;在薄膜上涂覆丙烯酸类胶粘剂,形成厚度为0.05mm的胶粘层;再在胶粘层上通过覆膜机将牛皮纸复合形成保护层(厚度为0.08mm),得到驱蟑螂胶带。进行相关测试,结果见表2。
实施例7
(1)按照表1的用量配制驱蟑螂的聚烯烃组合物:
复配驱虫剂(广州南嘉化工科技有限公司的天然薄荷脑;江西泰诚天然香料有限公司的柠檬香精;驱虫植物提取物(制备例制得))3.0份、LDPE(韩国现代XL505)3份、稳定剂(巴斯夫UV-531)4份、抗氧剂(巴斯夫抗氧剂1010)3份、碳酸钙10份,相容剂(巴塞尔PO-1015)2.0份、润滑剂(硬脂酸(VA-1810):聚乙烯蜡(霍尼韦尔AC6A)=1:1)2.0份。
其中复配驱虫剂包括:薄荷脑、香精、驱虫植物提取物,按照1:2:3的重量配比混合。
制备方法如下:
(2)将上述各组分原料混合后,加入高速混合机,充分混合约16min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为160℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒得到复配驱虫剂含量为12.5重量%的母粒;
将上述母粒加上LDPE(韩国现代XL505)97份通过吹塑成膜,得到厚度为0.5mm的薄膜,其中,相对于100份LDPE,复配驱虫剂投料量为3份,复配驱虫剂含量为2.5重量%);在薄膜上涂覆丙烯酸类胶粘剂,形成厚度为0.08mm的胶粘层;再在胶粘层上通过覆膜机方法将牛皮纸形成保护层(厚度为0.16mm),得到驱蟑螂胶带。进行相关测试,结果见表2。
对比例1
(1)按照表1的用量配制聚烯烃组合物:
共聚PP(上海石化F850EBA)80份、均聚PP(上海石化S1003)20份、稳定剂(巴斯夫770)3份、抗氧剂(巴斯夫抗氧剂168)2份、碳酸钙8份,相容剂(巴塞尔PO-1015)1份、润滑剂(硬脂酸(VA-1810):聚丙烯蜡(5108C)=1:1)1.5份。
(2)将上述各组分原料混合后,加入高速混合机,充分混合约20min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为180℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒;
将上述驱蟑螂聚丙烯通过注塑成型为电磁炉底座。进行相关测试,结果见表2。
对比例2
(1)按照表1的用量配制聚烯烃组合物:
复配驱虫剂(江西泰诚天然香料有限公司的柠檬香精;驱虫植物提取物(制备例制得))0.1份、均聚PP(上海石化S1003)80份、共聚PP(上海石化F850EBA)20份、稳定剂(巴斯夫UV-531)2.0份、抗氧剂(巴斯夫抗氧剂1010)1.0份、碳酸钙5份,相容剂(巴塞尔PO-1015)0.5份、润滑剂(硬脂酸(VA-1810):聚丙烯蜡(5108C)=1:1)1.0份。
其中复配驱虫剂包括:香精、驱虫植物提取物,按照1:1的重量配比混合。
(2)将上述各组分原料混合后,加入高速混合机,充分混合约10min,取出静置1h备用;
将上述混合物通过双螺杆挤出热塑加工,加工温度控制约为200℃;
将上述热塑加工得到的驱蟑螂聚丙烯材料用造粒机造粒;
将上述驱蟑螂聚丙烯通过注塑成型为电磁炉底座。进行相关测试,结果见表2。
对比例3
按照实施例1的方法,不同的是,复配驱虫剂4份替换复配驱虫剂0.1份。
制得电磁炉底座进行相关测试结果见表2。
表1
组分(重量份) | 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 |
均聚PP | 80 | 20 | - | 20 | 80 |
共聚PP | 20 | 80 | - | 80 | 20 |
LDPE | - | - | 100 | - | - |
稳定剂 | 2.0 | 3 | 4.0 | 3 | 2.0 |
抗氧剂 | 1.0 | 2 | 3 | 2 | 1.0 |
碳酸钙 | 5 | 8 | 10 | 8 | 5 |
相容剂 | 0.5 | 1.0 | 2.0 | 1.0 | 0.5 |
润滑剂 | 1.0 | 1.5 | 2.0 | 1.5 | 1.0 |
复配驱虫剂# | 0.1 | 2 | 3.0 | - | - |
复配驱虫剂## | - | - | - | - | 0.1 |
注:#包括:薄荷脑、香精、驱虫植物提取物;
##包括:香精、驱虫植物提取物。
表1(续)
注:*复配驱虫剂按照1:0.5:1的重量配比混合
**复配驱虫剂按照1:1:4的重量配比混合
***复配驱虫剂按照1:1:1的重量配比混合
****复配驱虫剂按照1:2:3的重量配比混合
实施例6中先用4份共聚PP和1份均聚PP制备母粒;
实施例7中先用3份LDPE制备母粒。
表2
注:1驱蟑螂效果测试方法:将实施例、对比例制得的家电部件或聚烯烃材料放入环境模拟测试装置,放入10只蟑螂,观察一天内蟑螂进入家电部件所占空间的数量,以此判断驱蟑螂效果。没有进入为优良,1只进入为良好,2只以上进入为差;
2将实施例、对比例制得的家电部件或聚烯烃材料在25℃、0.1MPa、相对湿度50%的条件下放置一定天数(100、200、300、400天)后再按照驱蟑螂效果测试方法进行测试,评价驱蟑螂效果的优、良、差。当评价为差时,即认为失去长效性,确定对应的测试天数为失效时间,表示长效性。
表2(续)
由实施例、对比例和表2的结果可以看出,采用本发明的驱蟑螂的聚烯烃组合物可以得到具有本征驱蟑螂的聚烯烃材料,并应用于厨房家电、防蟑螂胶带可以提供良好、且长效的驱蟑螂效果。提供的复配驱虫剂中,薄荷脑、香精和驱虫植物提取物的重量比合适可以提供更好的驱蟑螂效果且具有更好的长效性。
对比例1-3中,复配驱虫剂的组成不符合本发明的组合物,不能提供驱蟑螂效果。
以上详细描述了本发明的优选实施方式,但是,本发明并不限于此。在本发明的技术构思范围内,可以对本发明的技术方案进行多种简单变型,包括各个技术特征以任何其它的合适方式进行组合,这些简单变型和组合同样应当视为本发明所公开的内容,均属于本发明的保护范围。
Claims (13)
1.一种驱蟑螂的聚烯烃组合物,该组合物包括:
聚烯烃树脂100重量份、复配驱虫剂0.1-3重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份;其中,
所述复配驱虫剂包括薄荷脑、香精和驱虫植物提取物。
2.根据权利要求1所述的组合物,其中,所述复配驱虫剂中,薄荷脑、香精和驱虫植物提取物的重量比为1:(1-2):(1-3)。
3.根据权利要求1或2所述的组合物,其中,所述香精为水蒸汽蒸馏得到的水果香精和/或花香香精,优选为柠檬香精和/或茉莉花香精。
4.根据权利要求1或2所述的组合物,其中,所述驱虫植物提取物为通过二氧化碳超临界萃取从菊花和/或香草提取的混合物;优选地,所述驱虫植物提取物的25℃密度为0.92-0.98g/cm3,所述驱虫植物提取物的20℃折射率为1.4-1.6。
5.根据权利要求1所述的组合物,其中,所述聚烯烃树脂为高密度聚乙烯、低密度聚乙烯、均聚聚丙烯、共聚聚丙烯、乙烯-醋酸乙烯酯共聚物中的一种或多种。
6.根据权利要求1所述的组合物,其中,所述抗氧剂选自四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、三(2,4-二叔丁基苯基)亚磷酸酯中的一种或多种。
7.根据权利要求1所述的组合物,其中,所述润滑剂为硬脂酸、硬脂酸钙、乙撑双硬脂酸酯、季戊四醇硬脂酸酯、聚乙烯蜡、聚丙烯蜡中的一种或多种;
优选地,所述稳定剂为紫外线吸收剂和/或光稳定剂;
优选地,所述相容剂为马来酸酐或甲基丙烯酸缩水甘油酯与聚丙烯的接枝共聚物,所述相容剂的接枝率为0.6-1.2%,所述相容剂2.16kg载荷下190℃的熔融指数为20-40g/10min。
8.一种驱蟑螂的聚烯烃材料的制备方法,包括:
S1:将聚烯烃树脂100重量份、复配驱虫剂0.1-3重量份、稳定剂2-4重量份、抗氧剂1-3重量份、碳酸钙5-10重量份、相容剂0.5-2重量份和润滑剂1-2重量份加入高速混合机,充分混合10-20min;
S2:将步骤S1得到的混合物进行混炼加工,加工温度为150℃-220℃;
S3:将步骤S2加工得到的产物进行造粒。
9.一种权利要求8所述的方法制得的驱蟑螂的聚烯烃材料。
10.一种权利要求9所述的驱蟑螂的聚烯烃材料在家电产品或家电部件中的应用。
11.一种家电部件,该家电部件由权利要求9所述的驱蟑螂的聚烯烃材料成型而得。
12.一种家电产品,该家电产品包括由权利要求9所述的驱蟑螂的聚烯烃材料制得的部件或权利要求11所述的家电部件。
13.一种防蟑螂胶带,包括由权利要求9所述的驱蟑螂的聚烯烃材料加工成型而得的薄膜;优选地,所述胶带还包括在所述薄膜上设置的胶粘层和设置在所述胶粘层上的保护层。