CN110194682A - A kind of process of preparing of water-soluble solid siliceous fertilizer - Google Patents
A kind of process of preparing of water-soluble solid siliceous fertilizer Download PDFInfo
- Publication number
- CN110194682A CN110194682A CN201910531755.7A CN201910531755A CN110194682A CN 110194682 A CN110194682 A CN 110194682A CN 201910531755 A CN201910531755 A CN 201910531755A CN 110194682 A CN110194682 A CN 110194682A
- Authority
- CN
- China
- Prior art keywords
- siliceous fertilizer
- water
- preparing
- activator
- soluble solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of process of preparing of water-soluble solid siliceous fertilizer.The present invention is to be added to be suitable for and suitable activator in silica flour sandy plain material, roasted at 600-900 DEG C after mixing, be cooling, after grinding to obtain the final product;The activator is one or more of sodium hydroxide, potassium hydroxide, calcium carbonate, calcium oxide, calcium hydroxide;The mass ratio of the activator and quartz powder is 0.45~0.6.It is raw material present invention employs natural cheap quartz sand, realize the activation of silica, compared with the technique of original siliceous fertilizer, reduce energy consumption, reduces the economic cost in preparation process, Product Activity silicone content is more than 20%, obtained siliceous fertilizer has water solubility, and obtained to be formulated directly into liquid silicon fertilizer, the siliceous fertilizer of production can realize the passivation of heavy metal, have high economic benefit and environmental benefit.
Description
Technical field
The present invention relates to a kind of Solid/liquid two purpose fertilizer and preparation method thereof, specifically a kind of water-soluble solid siliceous fertilizer
Preparation method, the solid siliceous fertilizer can be mixed with a certain proportion of water, and liquid silicon fertilizer is made, and be used for foliage-spray.
Background technique
Silicon plays an important role in the mineral matter nutritional of plant.Studies have shown that element silicon can improve the anti-of crop
Sick ability, improves crop drought resistance lodging tolerance and raising crop salinity and alkalinity resistance etc. at reduction heavy metallic poison.Practical application table
Bright, silicon and nitrogen, phosphorus, potassium scientific matching are applied, and can just play the effect of high yield.Studies have shown that increasing production of rice can be made by applying siliceous fertilizer
7.6%~18.2%, make sugarcane production-increasing 27~36.4%, soybean yield-increasing 5.6~11.8%.
Silicon is the element of the second abundance on the earth, but most silicon are difficult to be absorbed by plants, only when silicon is with molecular state
Or could be efficiently used by plant after ionic state dissolution, referred to as " effective silicon ".
China's anthropogenic soil generally lacks silicon, and south is seriously in the north.Foreign literature is recorded, and can give state SiO in soil2Contain
Measuring < 130mg/kg is to lack silicon, and it is effective to apply silicon.Data shows that China is that southern subtropical zone has 70% or so soil to lack
Silicon, available silicon content is general only in 80-120mg/kg, and Alluvial deposit soil from Yangtze River and lacustrine deposits rice soil available silicon content are in 200mg/
Kg or more.
Some siliceous fertilizers are prepared at present with industrial silicate-containing slag, such as steel slag, but its dissolution is slowly, and fertilizer efficiency is lower;Or with
Quartz sand with soda ash is levigate mix thoroughly after in 1300~1400 DEG C of meltings preparations, this method energy consumption is very high, to equipment requirement
It is very high;Also useful silicon-containing solid waste, if prepared by flyash and activator, though this method turns waste into wealth, its is potential
The harm such as heavy metal pollution cannot ignore.
Summary of the invention
The object of the present invention is to provide a kind of process of preparing of safe quick-acting water-soluble solid siliceous fertilizer, use natural
Cheap quartz sand is raw material, realizes the activation of silica, and more than 20%, obtained siliceous fertilizer has Product Activity silicone content
Have water solubility, and it is obtained be formulated directly into liquid silicon fertilizer, the siliceous fertilizer of production can realize the passivation of heavy metal.
A kind of process of preparing of water-soluble solid siliceous fertilizer, including processing method below and step:
1) quartz sand is milled to 120 mesh or more with the broken machine of electromagnetic powder, quartz powder is made, it is spare;
2) quartz powder and activator are added in crucible according to the mass ratio of 0.1~1.2:1, are sufficiently stirred, are made
Stock;
3) it will stock up and be put into Muffle kiln roasting 30-150 minutes that are preheated to 100-1100 DEG C, take out cold in drier
But 30-40 minutes, it is produced above that 120 mesh are ground to.
Furthermore, in step 1), the content of silica needs >=90% in quartz sand.
Furthermore, in step 2), the activator is sodium hydroxide, potassium hydroxide, calcium carbonate, calcium oxide, hydrogen-oxygen
Change one of calcium or a variety of.
Furthermore, in step 2), the mass ratio of the activator and quartz powder is 0.1~1.2:1.
Furthermore, in step 2), the mass ratio of the activator and quartz powder is 0.45-0.55:1.
Furthermore, in step 2), based on sodium hydroxide, can mix with other activators makes the activator
With when other activators are added, the ratio of sodium hydroxide need to be more than or equal to 80%, and the ratio of other activators, which is not done, strictly to be wanted
It asks.
Furthermore, in step 3), maturing temperature is 100-1100 DEG C, and calcining time is 30-150 minutes;Muffle furnace
Assigned temperature need to be preheated to.
Furthermore, in step 3), the temperature of the calcination process is 600-900 DEG C, and calcining time is 60 minutes.
Furthermore, in step 3), after the completion of roasting, take out immediately be put into drier it is cooling, cooling time 30-
40 minutes;It needs to be ground to 120 mesh or more after cooling.
In addition, the present invention also provides water-soluble solid silicon made from a kind of preparation process of above-mentioned water-soluble solid siliceous fertilizer
Fertilizer.
By above-mentioned technical proposal, the invention has the following beneficial effects:
1) preparation process of the invention is simple, active silicon concentration reaches 20% or more in short production cycle, product, meets
" NY/T 797-2004 siliceous fertilizer " standard is conducive to plant absorption and utilizes, to achieve the purpose that increasing both production and income;
2) traditional siliceous fertilizer production technology need to be heated to 1300 DEG C -1400 DEG C, and energy consumption is very high, also high to equipment requirement, we
Method need to only roast at 600 DEG C -900 DEG C, and allow continuous production;
3) raw material quartz sand of the invention, potassium feldspar, diatomite etc. are from a wealth of sources, and utilization is at low cost, can when producing siliceous fertilizer
To gather materials on the spot, transportation cost is low, solves huge caused by China's siliceous fertilizer is produced because of reasons such as raw material, technique, energy consumption and equipment
Notch;
4) siliceous fertilizer produced by the invention, can will be prepared by the present invention when needing to carry out foliage-spray due to good water solubility
Siliceous fertilizer and water use after being mixed in a certain ratio uniformly;
5) siliceous fertilizer produced by the invention has good passivation effect to heavy metal, can mitigate heavy metal after application to crop
Persecution.
Specific embodiment
The invention discloses a kind of preparation processes of water soluble quick-acting solid siliceous fertilizer.The present invention is in silica flour sandy plain material
Be added and be suitable for and suitable activator, roasted at 600-900 DEG C after mixing, be cooling, after grinding to obtain the final product.The activator
For one or more of sodium hydroxide, potassium hydroxide, calcium carbonate, calcium oxide, calcium hydroxide;The activator and quartz powder
Mass ratio be 0.45~0.6.
A kind of preparation process of water soluble quick-acting siliceous fertilizer, including processing method below and step:
1) quartz sand is milled to 120 mesh or more with the broken machine of electromagnetic powder, quartz powder is made, it is spare;
2) quartz powder and activator are added in crucible according to the mass ratio of 0.1~1.2:1, are sufficiently stirred, are made
Stock;
3) it will stock up and be put into Muffle kiln roasting 30-150 minutes that are preheated to 100-1100 DEG C, take out cold in drier
But 30-40 minutes, it is produced above that 120 mesh are ground to.
Below by way of specific preferred embodiment combination effete test embodiment, invention is further described in detail, but the present invention
It is not limited in embodiment below.
The unit of following parts by weight can be g or kg.
Embodiment 1
A kind of preparation process of water-soluble solid siliceous fertilizer, including processing method below and step:
1) 120 mesh or more will be crushed to the broken machine of electromagnetic powder after 1000 parts of quartz sands dryings, be prepared into quartz powder, it is standby
With;
2) 100 parts of quartz powders are put into crucible, 45 parts of activator of sodium hydroxide is added, quartz powder and activation
Agent mixes well;
3) treated that mixture is put into is preheating to Muffle kiln roasting 1 hour of 600 DEG C for step 2), is fetched within 1 hour
It is 30 minutes cooling in drier, 120 mesh are ground to, the quick-acting siliceous fertilizers that available silicon content is greater than 20% can be obtained.
Embodiment 2
A kind of preparation process of water-soluble solid siliceous fertilizer, including processing method below and step:
1) 120 mesh or more will be crushed to the broken machine of electromagnetic powder after 1000 parts of quartz sands dryings, be prepared into quartz powder, it is standby
With;
2) 100 parts of quartz powders are put into crucible, 38 parts of sodium hydroxides of activator and 7 parts of potassium hydroxide are added, stone
English powder is mixed well with activator;
3) treated that mixture is put into is preheating to Muffle kiln roasting 1 hour of 700 DEG C for step 2), is fetched within 1 hour
It is 30 minutes cooling in drier, 120 mesh are ground to, the quick-acting siliceous fertilizers that available silicon content is greater than 20% can be obtained.
Embodiment 3
A kind of preparation process of water-soluble solid siliceous fertilizer, including processing method below and step:
1) 200 mesh or more will be crushed to the broken machine of electromagnetic powder after 1000 parts of quartz sands dryings, be prepared into quartz powder, it is standby
With;
2) 100 parts of quartz powders are put into crucible, 40 parts of sodium hydroxides of activator and 10 parts of calcium carbonate is added, quartz
Powder is mixed well with activator;
3) treated that mixture is put into is preheating to Muffle kiln roasting 1 hour of 900 DEG C for step 2), is fetched within 1 hour
It is 30 minutes cooling in drier, 200 mesh are ground to, the quick-acting siliceous fertilizers that available silicon content is greater than 20% can be obtained.
Embodiment 4
A kind of preparation process of water-soluble solid siliceous fertilizer, including processing method below and step:
1) 200 mesh or more will be crushed to the broken machine of electromagnetic powder after 1000 parts of quartz sands dryings, be prepared into quartz powder, it is standby
With;
2) 100 parts of quartz powders are put into crucible, 40 parts of sodium hydroxides of activator and 5 parts of calcium oxide is added, quartz
Powder is mixed well with activator;
3) treated that mixture is put into is preheating to Muffle kiln roasting 1 hour of 900 DEG C for step 2), is fetched within 1 hour
It is 30 minutes cooling in drier, 200 mesh are ground to, the quick-acting siliceous fertilizers that available silicon content is greater than 20% can be obtained.
Embodiment 5
A kind of preparation process of water-soluble solid siliceous fertilizer, including processing method below and step:
1) 200 mesh or more will be crushed to the broken machine of electromagnetic powder after 1000 parts of quartz sands dryings, be prepared into quartz powder, it is standby
With;
2) 100 parts of quartz powders are put into crucible, 40 parts of sodium hydroxides of activator and 6 parts of calcium hydroxides are added, stone
English powder is mixed well with activator;
3) treated that mixture is put into is preheating to Muffle kiln roasting 1 hour of 900 DEG C for step 2), is fetched within 1 hour
It is 30 minutes cooling in drier, 200 mesh are ground to, the quick-acting siliceous fertilizers that available silicon content is greater than 20% can be obtained.
It is individually below the Application Example and compliance test result test example of the siliceous fertilizer product of above-described embodiment 1-5.
Application Example 1
Laboratory potted plant experiment plants pakchoi, and 2kg farmland soil is added into the flowerpot that specification is 190*140*170mm
Earth, experimental group apply the solid siliceous fertilizer of millesimal embodiment 1, plant pakchoi after mixing, and control group does not apply, often
3, basin, a water is respectively poured sooner or later daily, cultivates 35 days and gathers in, compared with the control group potting for being not added with solid siliceous fertilizer, pakchoi
Fresh weight increases by 13.65%.
Application Example 2
Laboratory potted plant experiment plants pakchoi, and 2kg copper ion is added into the flowerpot that specification is 190*140*170mm and contains
Amount is the agricultural land soil of 1000mg/kg, and experimental group applies the solid siliceous fertilizer of 2/1000ths embodiment 2, plants after mixing
Pakchoi, control group do not apply, 3, every basin, respectively pour a water sooner or later daily, cultivate 35 days and gather in, and are not added with solid siliceous fertilizer
Control group potting compare, pakchoi fresh weight increase by 59.17%.
Application Example 3
1 part of quick-acting siliceous fertilizers made in embodiment 3 is added into 700 parts of water, available activity silicone content is greater than
The liquid silicon fertilizer of 310mg/L.The liquid silicon fertilizer is used directly for foliage-spray, the flowerpot for being 190*140*170mm to specification
Middle addition 2kg agricultural land soil, 3, every basin respectively pour a water sooner or later daily, spray an aforesaid liquid silicon within experimental group every 7-10 days
Fertilizer, each every basin spray 3ml, cultivate 35 days and gather in, compared with the control group, can increase production 18.74%.
Effete test embodiment
1 activated silica measurement experiment of test example
The present invention evaluates the performance of product using following analysis and measuring method:
The measurement of activated silica:
0.1g siliceous fertilizer is weighed in 250mL triangular flask, the 0.025mol/L citric acid of 100mL is added, shakes up, is being returned
1h is shaken under rotation oscillator 150r/min, filters, is measured with Silicon Molybdenum Blue Spectrophotometry immediately.
1) it is 21.99% that 1 solid siliceous fertilizer of embodiment, which measures active silicone content,.
2) it is 21.56% that 2 solid siliceous fertilizer of embodiment, which measures active silicone content,.
3) it is 21.13% that 3 solid siliceous fertilizer of embodiment, which measures active silicone content,.
4) it is 20.54% that 4 solid siliceous fertilizer of embodiment, which measures active silicone content,.
5) it is 20.38% that 5 solid siliceous fertilizer of embodiment, which measures active silicone content,.
The experiment of 2 solid silicon rich water dissolubility of test example
The present invention evaluates the water soluble characteristic of product using following analysis and measuring method:
The measurement of activated silica: weighing 0.1g siliceous fertilizer in 250mL triangular flask, and 100mL ultrapure water is added, shakes up,
1h is shaken under cyclotron oscillation device 150r/min, filters, is measured with Silicon Molybdenum Blue Spectrophotometry immediately.
1) it is 21.87% that 1 solid siliceous fertilizer of embodiment, which measures active silicone content,.
2) it is 21.32% that 2 solid siliceous fertilizer of embodiment, which measures active silicone content,.
3) it is 20.85% that 3 solid siliceous fertilizer of embodiment, which measures active silicone content,.
4) it is 20.77% that 4 solid siliceous fertilizer of embodiment, which measures active silicone content,.
5) it is 20.16% that 5 solid siliceous fertilizer of embodiment, which measures active silicone content,.
Passivation of the quick-acting siliceous fertilizers of test example 3 to bivalent cupric ion
1) the quick-acting siliceous fertilizers in 0.02g embodiment 2 are added into 100mgL 50mg/L copper ion solution, 30 after mixing
DEG C, water-bath is shaken 2 hours under 100RPM, copper ion removal rate reaches 97.89%.
2) the quick-acting siliceous fertilizers in 0.15g embodiment 2 are added into 100mgL 300mg/L copper ion solution, 30 after mixing
DEG C, water-bath is shaken 2 hours under 100RPM, copper ion removal rate reaches 97.29%.
3) the quick-acting siliceous fertilizers in 0.4g embodiment 2 are added into 100mgL 1000mg/L copper ion solution, 30 after mixing
DEG C, water-bath is shaken 2 hours under 100RPM, copper ion removal rate reaches 99.96%.
In conclusion being raw material present invention employs natural cheap quartz sand, the activation of silica is realized, with original
There is the technique of siliceous fertilizer to compare, reduce energy consumption, reduce the economic cost in preparation process, Product Activity silicone content is more than
20%, obtained siliceous fertilizer has water solubility, and it is obtained be formulated directly into liquid silicon fertilizer, the siliceous fertilizer of production can realize a huge sum of money
The passivation of category, has high economic benefit and environmental benefit.
The above described is only a preferred embodiment of the present invention, be not intended to limit the present invention in any form, therefore
Without departing from the technical solutions of the present invention, to the above embodiments according to the technical essence of the invention any simply to repair
Change, equivalent variations and modification, all of which are still within the scope of the technical scheme of the invention.
Claims (10)
1. a kind of process of preparing of water-soluble solid siliceous fertilizer, which is characterized in that including processing method below and step:
1) quartz sand is milled to 120 mesh or more with the broken machine of electromagnetic powder, quartz powder is made, it is spare;
2) quartz powder and activator are added in crucible according to the mass ratio of 0.1~1.2:1, are sufficiently stirred, stock is made;
3) it will stock up and be put into Muffle kiln roasting 30-150 minutes that are preheated to 100-1100 DEG C, take out cooling in drier
30-40 minutes, it is produced above to be ground to 120 mesh.
2. the process of preparing of water-soluble solid siliceous fertilizer according to claim 1, it is characterised in that: in step 1),
The content of silica needs >=90% in quartz sand.
3. the process of preparing of water-soluble solid siliceous fertilizer according to claim 1, it is characterised in that: in step 2),
The activator is one of sodium hydroxide, potassium hydroxide, calcium carbonate, calcium oxide, calcium hydroxide or a variety of.
4. the process of preparing of water-soluble solid siliceous fertilizer according to claim 1, it is characterised in that: in step 2),
The mass ratio of the activator and quartz powder is 0.1~1.2:1.
5. the process of preparing of water soluble quick-acting siliceous fertilizer according to claim 4, it is characterised in that: in step 2),
The mass ratio of the activator and quartz powder is 0.45-0.55:1.
6. the process of preparing of water-soluble solid siliceous fertilizer according to claim 1, it is characterised in that: in step 2),
The activator can be used in mixed way based on sodium hydroxide with other activators, when other activators are added, sodium hydroxide
Ratio need to be more than or equal to 80%, the ratio of other activators is not strict with.
7. the process of preparing of water soluble quick-acting siliceous fertilizer according to claim 1, it is characterised in that: in step 3),
Maturing temperature is 100-1100 DEG C, and calcining time is 30-150 minutes;Muffle furnace need to be preheated to assigned temperature.
8. the process of preparing of water-soluble solid siliceous fertilizer according to claim 7, it is characterised in that: in step 3),
The temperature of the calcination process is 600-900 DEG C, and calcining time is 60 minutes.
9. the process of preparing of water-soluble solid siliceous fertilizer according to claim 1, it is characterised in that: in step 3),
It after the completion of roasting, takes out be put into cooling in drier immediately, cooling time is 30-40 minutes;Need to be ground to after cooling 120 mesh with
On.
10. water-soluble solid siliceous fertilizer made from the preparation process of water-soluble solid siliceous fertilizer of any of claims 1-9.