CN110184741A - A kind of banana fiber mask substrate and preparation method thereof - Google Patents
A kind of banana fiber mask substrate and preparation method thereof Download PDFInfo
- Publication number
- CN110184741A CN110184741A CN201910390014.1A CN201910390014A CN110184741A CN 110184741 A CN110184741 A CN 110184741A CN 201910390014 A CN201910390014 A CN 201910390014A CN 110184741 A CN110184741 A CN 110184741A
- Authority
- CN
- China
- Prior art keywords
- banana
- mask substrate
- parts
- banana fiber
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of banana fiber mask substrates and preparation method thereof, are related to facial mask cloth manufacturing field.It is characterized in that: a kind of banana fiber mask substrate, the component including following parts by weight: banana fiber: 20~40 parts；Alginate fibre: 50~80 parts；Viscose rayon: 20~60 parts；Tencel fiber: 20~60 parts；Biology cellulose:, making main body by using banana fiber, and form biology cellulose by 50~100 parts, so that manufactured mask substrate has high water absorbing capacity, humectant, highly-breathable and good patch skin.
Description
Technical field
The present invention relates to facial mask cloth manufacturing fields, more specifically, it relates to a kind of banana fiber mask substrate and its system
Preparation Method.
Background technique
As the improvement of people's living standards, ladies increasingly pay close attention to skin care, makeup problem；Wherein, facial mask is important
Skin care, whitening articles.The principle of facial mask skin care is temporarily isolating outside air and dirt exactly using the time for being covered on face
Dye, improves skin temperature, and the pore expansion of skin promotes sweat gland secretion and metabolism, increase the oxygen content of skin, facial mask
Be conducive to skin and exclude the product of epidermal cell metabolism and the oil substances of accumulation, the facial mask liquid and moisture in facial mask are seeped
In the cuticula for entering skin epidermis, skin becomes soft, increases elasticity.
Facial mask cloth relatively common at present is mostly non-woven fabrics facial mask, and the most common facial mask cloth type, advantage are exactly in the market
The troublesome operation for simplifying mantle, make things convenient for customers nursing of being in, and price is human-oriented, but non-woven fabrics mask substrate disadvantage is also very bright
It is aobvious, the only carrier of Essence bad with skin affinity；And water absorption rate is lower, once moisture in mask substrate with
Time evaporation, the liquor strength in facial mask liquid increase, osmotic pressure increases, and leads to the phenomenon that " back suction " occur.
It is, therefore, desirable to provide a kind of new scheme solves the above problems.
Summary of the invention
In view of the deficienciess of the prior art, the purpose of the present invention one is to provide a kind of banana fiber mask substrate, lead to
It crosses using banana fiber as main body, so that manufactured mask substrate has high water absorbing capacity, humectant, highly-breathable and well
Patch skin.
To achieve the above object one, the present invention provides the following technical scheme that
A kind of banana fiber mask substrate, the component including following parts by weight:
Banana fiber: 20~40 parts；
Alginate fibre: 50~80 parts；
Viscose rayon: 20~60 parts；
Tencel fiber: 20~60 parts；
Biology cellulose: 50~100 parts.
By using above-mentioned technical proposal, the mask substrate in the present invention is used based on banana fiber, and it is fine that banana is made
Dimension mask substrate has the characteristics that natural environmental-protective, and banana fiber mask substrate material without being dyed for yellowish colored appearance
Matter ensure that top penetrating patch skin, in use, facial mask is close to skin, guarantee the good using effect of facial mask, furthermore high
There is bored acne phenomenon in the skin that gas can avoid user, guarantees " eupnea " of skin；Protein, rouge are rich in banana skin
The several kinds of mineral elements such as fat, sugar and K, Ca, Mg, S, Fe, Zn, furthermore banana skin is rich in tryptophan, vitamin B6, blood abundant
Clear element, may make skin become to moisten it is smooth, it is to skin because dry and being chapped from the cold for generating also has some improvement.
Further preferably, the extraction process of the banana fiber are as follows:
Banana is cut off into banana stem and banana head obtains banana skin, banana fiber extract equipment is sent into after banana skin is cleaned, passes through
It smashs to pieces and is separated by filtration, obtain banana fiber.
Further preferably, the alginate fibre includes sodium alginate and calcium alginate.
By using above-mentioned technical proposal, alginate fibre has good biocompatibility, is used in mask substrate, makes
Obtaining face-mask material will not cause allergic reaction, so as to be suitable for wider crowd.
Further preferably, the percentage composition of the sodium alginate and calcium alginate ratio is 1:(6~10).
It by using above-mentioned technical proposal, is mixed using sodium alginate and calcium alginate, Sodium/Calcium ion occurs in water and hands over
It changes, to form fluffy and high water absorption face-mask material.
Further preferably, the biology cellulose is made by fermentation medium and gluconacetobacter.
By using above-mentioned technical proposal, facial mask uses the time between 15~20min, during which inevitably occurs
The case where moisture evaporation, mask substrate dries out, by using biology cellulose, the ability with stronger vapor water barriers makes
Moisture can be lockked by obtaining mask substrate, its evaporation rate be reduced, to improve moisturizing rate and skin effect.
Further preferably, the fermentation medium includes glucose 5w/v%, peptone 0.5w/v%, yeast extract
0.5w/v%, citric acid 0.1w/v%, disodium hydrogen phosphate 0.2w/v%, potassium dihydrogen phosphate 0.1w/v%.
Further preferably, the pH=6.0 of the fermentation medium, cultivation temperature are 30 DEG C.
The purpose of the present invention two is to provide a kind of preparation method of banana fiber mask substrate, using this method preparation
Banana fiber mask substrate has high water absorbing capacity, humectant, highly-breathable and good patch skin.
To achieve the above object two, the present invention provides the following technical scheme that
A kind of preparation method of the banana fiber mask substrate according to purpose one, which is characterized in that the banana fiber
The preparation process flow of mask substrate are as follows: fiber feeds intake → shredding combing → lapping → spun lacing → dried disinfecting → fermented and cultured →
Examine coiled → punching → finished product
By using above-mentioned technical proposal, after face mask substrate material is made in banana fiber, biological fiber is formed on face mask substrate material
Plain gel mould obtains banana fiber mask substrate, compared to commercially available common non-woven fabric facial mask, there is preferably patch skin, and
There are more preferably water holding capacity and lower moisture-vapor transmission.
Further preferably, fermented incubation time is 5 days.
In conclusion compared with prior art, the invention has the following advantages:
(1) banana fiber is used in mask substrate, unique softness property brings good comfortable patch skin sense of touch to skin,
Excellent water absorption character, assigns the ability that film cloth absorbs more Essences, and the highly-breathable of mask substrate can avoid user
Skin there is bored acne phenomenon, guarantee " eupnea " of skin, furthermore unique lines of ingenuity technique, further enhances film
The stealthy effect of cloth；
(2) in banana skin rich in the several kinds of mineral elements such as protein, fat, sugar and K, Ca, Mg, S, Fe, Zn, furthermore banana skin
Rich in tryptophan, vitamin B6, thrombocytin abundant, it may make skin to become to moisten smooth, skin generated because of dry
Be chapped from the cold and also have some improvement；
(3) by using biology cellulose, one layer of biological cellulose gel film is formed on face mask substrate material, it is general compared to commercially available
Logical non-woven fabrics facial mask has preferably patch skin, and has more preferably water holding capacity and lower moisture-vapor transmission.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
With reference to the accompanying drawings and examples, the present invention will be described in detail.It is worth noting that wherein being not specified specific
Condition person, lower according to conventional conditions or manufacturer's recommended conditions to carry out, reagents or instruments used without specified manufacturer,
For the conventional products that can be obtained by commercially available purchase.
Embodiment 1: a kind of banana fiber mask substrate, each component and its corresponding parts by weight are as shown in table 1, and pass through
Following preparation step obtains:
Fiber feeds intake → and shredding combing → lapping → spun lacing → dried disinfecting → fermented and cultured → inspection is coiled → punching → finished product；
The wherein technological parameter of carding machine are as follows: go out net spee 60m/min, net quantitative 20g/m out2, net spee 40m/min out；
Lapping uses horizontal lay-up net, technological parameter are as follows: entrance velocity 50m/min, muzzle velocity 13m/min, 4 layers of the number of plies；
Spun lacing distance in spun lacing step is 15mm；
Dried disinfecting is to sterilize 30min under ultraviolet light；
It is cultivated 5 days in the insulating box that fermented and cultured is 30 DEG C；
Wherein alginate fibre includes percentage composition than the sodium alginate and calcium alginate for 1:6.
Embodiment 2-6: a kind of banana fiber mask substrate, difference from example 1 is that, each component and its corresponding
Parts by weight it is as shown in table 1.
Each component and its parts by weight in 1 embodiment 1-6 of table
Embodiment 7: a kind of banana fiber mask substrate, difference from example 1 is that:
Wherein alginate fibre includes percentage composition than the sodium alginate and calcium alginate for 1:8；
Remaining is same as Example 1.
Embodiment 8: a kind of banana fiber mask substrate, difference from example 1 is that:
Wherein alginate fibre includes percentage composition than the sodium alginate and calcium alginate for 1:10；
Remaining is same as Example 1.
Comparative example 1: a kind of mask substrate, difference from example 1 is that, the component including following parts by weight:
50 parts of alginate fibres；
20 parts of viscose rayons；
20 parts of tencel fibers；
Biology cellulose；
And step acquisition is prepared by the following procedure:
Fiber feeds intake → and shredding combing → lapping → spun lacing → dried disinfecting → fermented and cultured → inspection is coiled → punching → finished product；
The wherein technological parameter of carding machine are as follows: go out net spee 60m/min, net quantitative 20g/m out2, net spee 40m/min out；
Lapping uses horizontal lay-up net, technological parameter are as follows: entrance velocity 50m/min, muzzle velocity 13m/min, 4 layers of the number of plies；
Spun lacing distance in spun lacing step is 15mm；
Dried disinfecting is to sterilize 30min under ultraviolet light；
It is cultivated 5 days in the insulating box that fermented and cultured is 30 DEG C；
Wherein alginate fibre includes percentage composition than the sodium alginate and calcium alginate for 1:6.
Comparative example 2: a kind of mask substrate, difference from example 1 is that, the component including following parts by weight:
20 parts of banana fibers；
50 parts of alginate fibres；
20 parts of viscose rayons；
20 parts of tencel fibers；
And step acquisition is prepared by the following procedure:
Fiber feeds intake → and shredding combing → lapping → spun lacing → dried disinfecting → inspection is coiled → punching → finished product；
The wherein technological parameter of carding machine are as follows: go out net spee 60m/min, net quantitative 20g/m out2, net spee 40m/min out；
Lapping uses horizontal lay-up net, technological parameter are as follows: entrance velocity 50m/min, muzzle velocity 13m/min, 4 layers of the number of plies；
Spun lacing distance in spun lacing step is 15mm；
Wherein alginate fibre includes percentage composition than the sodium alginate and calcium alginate for 1:6.
Performance test
Mask substrate and commercially available two made from banana fiber mask substrate, comparative example 1-2 is made not to embodiment 1-8 respectively
Same mask substrate is tested for the property；
Test method
Air penetrability: according to GB/T 5453-1997, using the full-automatic Permeability gauge of YG461H type, pressure 100MPa, test area
20cm2；
Water absorption rate: according to EDANA standard, weighing 5g dry fibers, be totally submerged in distilled water and take out after 60s, claims after hanging 120s
Weight in wet base is taken, water absorption rate is calculated；
Penetrability: according to GB/T 24218.3-20110, using W3/060 moisture-vapor transmission test macro.
Test result is included in following table 2, by table test data it is found that air penetrability and water absorption rate: comparative example 1, two
Commercially available mask substrate is relatively poor；Moisture-vapor transmission and patch skin: comparative example 2, two commercially available mask substrate are relatively poor, say
Banana fiber mask substrate made from bright inventive formulation and technique has high air penetrability, high water absorbing capacity, low-moisture permeability and good
Patch skin.
2 the performance test results of table
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-described embodiment,
All technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
For those of ordinary skill, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (9)
1. a kind of banana fiber mask substrate, which is characterized in that the component including following parts by weight:
Banana fiber: 20~40 parts；
Alginate fibre: 50~80 parts；
Viscose rayon: 20~60 parts；
Tencel fiber: 20~60 parts；
Biology cellulose: 50~100 parts.
2. banana fiber mask substrate according to claim 1, which is characterized in that the extraction process of the banana fiber
Are as follows:
Banana is cut off into banana stem and banana head obtains banana skin, banana fiber extract equipment is sent into after banana skin is cleaned, passes through
It smashs to pieces and is separated by filtration, obtain banana fiber.
3. banana fiber mask substrate according to claim 1, which is characterized in that the alginate fibre includes sodium alginate
And calcium alginate.
4. banana fiber mask substrate according to claim 3, which is characterized in that the sodium alginate and calcium alginate
Percentage composition ratio is 1:(6~10).
5. banana fiber mask substrate according to claim 1, which is characterized in that the biology cellulose is by fermented and cultured
Base and gluconacetobacter are made.
6. banana fiber mask substrate according to claim 5, which is characterized in that the fermentation medium includes glucose
5w/v%, peptone 0.5w/v%, yeast extract 0.5w/v%, citric acid 0.1w/v%, disodium hydrogen phosphate 0.2w/v%, potassium dihydrogen phosphate
0.1w/v%。
7. banana fiber mask substrate according to claim 6, which is characterized in that the pH of the fermentation medium=
6.0, cultivation temperature is 30 DEG C.
8. a kind of preparation method of banana fiber mask substrate described in any one of -7 according to claim 1, which is characterized in that
The preparation process flow of the banana fiber mask substrate are as follows: fiber feeds intake → shredding combing → lapping → spun lacing → dried disinfecting
→ fermented and cultured → inspection is coiled → punching → finished product.
9. the preparation method of banana cellulose mask substrate according to claim 7, which is characterized in that fermented incubation time
It is 5 days.