CN110183920A - A kind of water paint and preparation method thereof that LED lamp scattering is strong - Google Patents
A kind of water paint and preparation method thereof that LED lamp scattering is strong Download PDFInfo
- Publication number
- CN110183920A CN110183920A CN201910530607.3A CN201910530607A CN110183920A CN 110183920 A CN110183920 A CN 110183920A CN 201910530607 A CN201910530607 A CN 201910530607A CN 110183920 A CN110183920 A CN 110183920A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- blender
- slurry
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water paints and preparation method thereof that LED lamp scattering is strong, it is counted by total mass fraction 100%, it includes water-based acrylic resin 25%-30% that it, which is formulated, coloring agent 8%-12%, organic light diffusing agent 24%-30%, ethyl alcohol 18%-27%, water paint auxiliary agent 1%-2%, water 4%-8%, in order to overcome the prior art novel or there is easy depaintings, foaming, non-refractory, there is slight crack, and the disadvantage deficiency that scattering is weak, now propose a kind of water paint and preparation method thereof that LED lamp scattering is strong, to solve, the prior art is novel or there is easy depaintings, foaming, non-refractory, there is slight crack, and the disadvantage that scattering is weak, it is not easy depainting to reach, do not allow to foam, high-temperature corrosion resistance, be not easy to occur slight crack and Scattered power, light transmittance can be up to 85% or more effect.
Description
Technical field
The present invention relates to formulation for coating material and preparation method thereof technical field, in particular to a kind of LED lamp scattering is strong
Water paint and preparation method thereof.
Background technique
The coating coating of most oiliness, oil paint can cause dirt to air in LED light bubble shell currently on the market
Dye, and have very big harm, later with the rapid development of science and technology, corresponding product to the health of production and user
Obtained technological improvement, but the prior art it is novel or there is easy depainting, foaming, non-refractory, there is slight crack, and dissipate
The weak disadvantage of penetrating property.
Summary of the invention
(1) technical problems to be solved
In order to overcome the prior art novel or there is easy depainting, foaming, non-refractory, there is slight crack, and scatter
Property weak disadvantage it is insufficient, it is proposed that a kind of water paint and preparation method thereof that LED lamp scattering is strong, to solve the prior art
It is novel or there is easy depainting, foaming, non-refractory, there is slight crack, and the disadvantage that scattering is weak, do not allow to reach
Easy depainting, do not allow foaming, high-temperature corrosion resistance, be not easy slight crack occur and scattered power, light transmittance can be up to 85% or more effect
Fruit.
(2) technical solution
The present invention is achieved through the following technical solutions: the invention proposes a kind of water paints that LED lamp scattering is strong
And preparation method thereof, it is counted by total mass fraction 100%, formula includes water-based acrylic resin 25%-30%, coloring agent
8%-12%, organic light diffusing agent 24%-30%, ethyl alcohol 18%-27%, water paint auxiliary agent 1%-2%, water 4%-8%；Institute
Stating light diffusing agent main component is titanium dioxide；The water paint auxiliary agent mainly becomes wetting dispersing agent, levelling agent, organic silicon-type
Defoaming agent, resinae adhesion promoter, thixotroping thicken resist sagging auxiliary agent, plasticizer, promotor, insulating compound, fire retardant and resist
Aging agent.
Further, the levelling agent is BD-3232, and levelling agent proportion is 1%-1.5%.
Further, it is mainly deployed using epoxy resin and dyestuff for described dose, dyestuff includes C- R (R-100), orange
It color C-O (O-300), yellow Y-200S, green C-G, C-G-1, G- 400B, blue B-500 and adjusts to white and uses TV-100.
Further, water-based acrylic resin, organic light diffusing agent are deployed into proportion after slurry and are sanded using bedroom
Machine carries out ball milling, and blender is added in the slurry that water-based acrylic resin, the organic light diffusing agent after ball milling are formed and is then pressed
Water, water paint auxiliary agent, coloring agent are added into blender for ratio, stir and obtain slurry to it using blender,
Finally, being stirred ethyl alcohol is added in blender in proportion, slurry is diluted.
Further, the water-based acrylic resin, organic light diffusing agent carry out the time of ball milling using bedroom sand mill
At least 2h.
Further, stirring is added in the slurry that the water-based acrylic resin by after ball milling, organic light diffusing agent are formed
Machine is then added water, water paint auxiliary agent, coloring agent into blender in proportion, is stirred simultaneously using blender to it
The mixing time for obtaining slurry is at least 45min.
It further, is 15min ethyl alcohol is added in blender in the mixing time being stirred in proportion.
(3) beneficial effect
The present invention compared with the existing technology, has the advantages that
In order to overcome the prior art novel or there is easy depainting, foaming, non-refractory, there is slight crack, and scatter
Property weak disadvantage it is insufficient, it is proposed that a kind of water paint and preparation method thereof that LED lamp scattering is strong, to solve the prior art
It is novel or there is easy depainting, foaming, non-refractory, there is slight crack, and the disadvantage that scattering is weak, do not allow to reach
Easy depainting, do not allow foaming, high-temperature corrosion resistance, be not easy slight crack occur and scattered power, light transmittance can be up to 85% or more effect
Fruit.
Specific embodiment
The following examples are further illustrations of the invention, rather than limiting the invention.
Embodiment 1
Water paint of the invention is equipped with according to following component ratio:
(1) 25kg water-based acrylic resin and the organic light diffusing agent of 25kg slurry: are subjected to ball milling using bedroom sand mill
2h is up to uniform；
(2) slurry obtained above-mentioned (1) is added in blender, then sequentially add 8kg water, 2kg water paint auxiliary agent,
12kg coloring agent is added into blender, and 45min or more is sufficiently stirred to it using blender uniformly and obtains slurry；
(3) finally, the ethyl alcohol slurry that (2) are obtained that 18kg is added into blender again to be stirred 15min or more dilute
It releases to obtain the water paint.
Embodiment 2
(1) 2.5kg water-based acrylic resin and the organic light diffusing agent of 2.5kg slurry: are subjected to ball using bedroom sand mill
2h is ground up to uniform；
(2) slurry for obtaining above-mentioned (1) is added in blender, then sequentially adds 0.8kg water, 0.2kg water paint helps
Agent, 1.2kg coloring agent are added into blender, and 45min or more is sufficiently stirred to it using blender uniformly and obtains slurry；
(3) finally, the ethyl alcohol slurry that (2) are obtained that 1.8kg is added into blender again to be stirred 15min or more dilute
It releases to obtain the water paint.
Water paint of the invention is equipped with according to following component ratio:
Embodiment 3
(1) slurry: 12.5kg water-based acrylic resin and the organic light diffusing agent of 12.5kg are carried out using bedroom sand mill
Ball milling 2h is up to uniform；
(2) slurry obtained above-mentioned (1) is added in blender, then sequentially add 4kg water, 1kg water paint auxiliary agent,
6kg coloring agent is added into blender, and 45min or more is sufficiently stirred to it using blender uniformly and obtains slurry；
(3) finally, the ethyl alcohol slurry that (2) are obtained that 9kg is added into blender again to be stirred 15min or more dilute
It releases to obtain the water paint.
Water paint of the invention is equipped with according to following component ratio:
Embodiment 4
Water paint of the invention is equipped with according to following component ratio:
(1) 5kg water-based acrylic resin and the organic light diffusing agent of 5kg slurry: are subjected to ball milling 2h using bedroom sand mill
Up to uniform；
(2) slurry for obtaining above-mentioned (1) is added in blender, then sequentially adds 1.6kg water, 0.4kg water paint helps
Agent, 2.4kg coloring agent are added into blender, and 45min or more is sufficiently stirred to it using blender uniformly and obtains slurry；
(3) finally, the ethyl alcohol slurry that (2) are obtained that 3.6kg is added into blender again to be stirred 15min or more dilute
It releases to obtain the water paint.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
Other implementations being understood that.
Claims (7)
1. a kind of water paint and preparation method thereof that LED lamp scattering is strong, it is characterised in that: press total mass fraction 100%
It counting, formula includes water-based acrylic resin 25%-30%, coloring agent 8%-12%, organic light diffusing agent 24%-30%,
Ethyl alcohol 18%-27%, water paint auxiliary agent 1%-2%, water 4%-8%；The light diffusing agent main component is titanium dioxide；It is described
Water paint auxiliary agent mainly becomes wetting dispersing agent, levelling agent, organic silicon-type defoaming agent, resinae adhesion promoter, thixotroping increasing
Thick resist sagging auxiliary agent, plasticizer, promotor, insulating compound, fire retardant and age resister.
2. one kind according to claim 1, it is characterised in that: the levelling agent is BD-3232, and levelling agent proportion is
1%-1.5%.
3. one kind according to claim 1, it is characterised in that: described dose mainly using epoxy resin and dyestuff allotment and
At dyestuff includes C-R (R-100), orange C-O (O-300), yellow Y-200S, green C-G, C-G-1, G-400B, blue B-
It 500 and adjusts to white and uses TV-100.
4. one kind according to claim 1, it is characterised in that: in proportion by water-based acrylic resin, organic light diffusing agent
It is deployed into after slurry and carries out ball milling using bedroom sand mill, water-based acrylic resin, the organic light diffusing agent after ball milling are formed
Slurry be added blender, then, in proportion into blender be added water, water paint auxiliary agent, coloring agent, using blender to it
Slurry is stirred and obtained, finally, being stirred ethyl alcohol is added in blender in proportion, enables slurry
Dilution.
5. one kind according to claim 4, it is characterised in that: the water-based acrylic resin, organic light diffusing agent utilize
The time that bedroom sand mill carries out ball milling is at least 2h.
6. one kind according to claim 4, it is characterised in that: the water-based acrylic resin by after ball milling, You Jiguang
Blender is added in the slurry that diffusant is formed, and then, water, water paint auxiliary agent, coloring agent is added into blender in proportion, utilizes
Blender, which stirs it and obtains the mixing time of slurry, is at least 45min.
7. one kind according to claim 4, it is characterised in that: be stirred ethyl alcohol is added in blender in proportion
Mixing time be 15min.