CN110181914A - A kind of multimedia projector foam strip and preparation method thereof - Google Patents
A kind of multimedia projector foam strip and preparation method thereof Download PDFInfo
- Publication number
- CN110181914A CN110181914A CN201910468893.5A CN201910468893A CN110181914A CN 110181914 A CN110181914 A CN 110181914A CN 201910468893 A CN201910468893 A CN 201910468893A CN 110181914 A CN110181914 A CN 110181914A
- Authority
- CN
- China
- Prior art keywords
- parts
- antistatic layer
- layer
- foam strip
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to multimedia accessory preparation technical fields, specifically provide a kind of multimedia projector foam strip and preparation method thereof, gained foam strip is bonded using three-decker, successively includes the first antistatic layer, electric eliminating layer and the second antistatic layer linked by viscose glue;First antistatic layer and the second antistatic layer are mixed by modified O-phthalic ester and other components, and the antistatic property of general sponge is improved, and in the case where guaranteeing high-antistatic effect, still have good leakproofness effect.
Description
Technical field
The present invention relates to multimedia projector preparation technical fields, and in particular to a kind of multimedia projector foam strip and
Preparation method.
Background technique
With our social progress, scientific and technological development, the popularization and application of multimedia overhead projector technology, people are to multimedia throwing
The requirement of shadow instrument is also higher and higher, mostly uses foam strip to be sealed on projector, although existing foam strip sealing effect is good,
But antistatic effect is poor, is easy to produce electrostatic, and projector is caused job failure occur.Sponge is a kind of porous material, is had good
Good elasticity, plays sealing effect, but the antistatic effect of sponge is poor, when being electrified for a long time, is easy absorption dust, shadow
Ring normal use.A kind of antistatic sponge is urgently developed, is met in the case of projector is electrified for a long time, the antistatic spy of foam strip
Property.
Summary of the invention
In view of the deficiencies of the prior art, the purpose of the present invention is to provide a kind of multimedia projector foam strip and its systems
Preparation Method, the foam strip plasticity is good, and antistatic effect is strong, low in cost.
A kind of multimedia projector foam strip, successively include by viscose glue link the first antistatic layer, electric eliminating layer with
Second antistatic layer;First antistatic layer and the second antistatic layer are mixed by following component according to parts by weight to be made
At: 48-60 parts of sodium polyacrylate, 0.05-0.08 parts of nitrocellulose, 18-23 parts of aluminium hydroxide, changes 5-10 parts of butyl rubber
5-10 parts of phthalic acid ester of property, 1-5 parts of castor oil, 1-3 parts of copper oxide, 1-2 parts of calcium naphthenate, 1-1.8 parts of epoxychloropropane,
23-48 parts of banana slag, 1-3 parts of age resister;The modified phthalic acid ester is by phthalic acid ester, dopamine solution, titanium
Sour barium mixes;The electric eliminating layer includes following component according to parts by weight: 1-3 parts of triethylene diamine, polyethylene glycol
50-75 parts, 8-12 parts of acid polyethylene sodium, 1-4 parts of castor oil, 3-7 parts of water.
It is that first antistatic layer and the second antistatic layer are by following component according to parts by weight as improved
It is mixed: 58 parts of sodium polyacrylate, 8 parts of butyl rubber, 0.07 part of nitrocellulose, 20 parts of aluminium hydroxide, modified adjacent benzene two
It is 7 parts of formic acid esters, 2 parts of castor oil, 2 parts of copper oxide, 1.2 parts of calcium naphthenate, 1.2 parts of epoxychloropropane, 32 parts of banana slag, anti-aging
2 parts of agent.
It is that phthalic acid ester in the modified phthalic acid ester, dopamine solution, barium titanate rub as improved
You are than being 3-5:1:1-3.
It is that the electric eliminating layer includes following component according to parts by weight: 2 parts of triethylene diamine, poly- second as improved
68 parts of glycol, 10 parts of acid polyethylene sodium, 3 parts of castor oil, 5 parts of water.
The preparation method of above-mentioned multimedia projector foam strip, comprising the following steps:
Step 1, weigh component used in the first antistatic layer, electric eliminating layer and the second antistatic layer, and conventionally into
Row preparation;
Step 2, one layer of viscose glue is painted on the two sides of electric eliminating layer, then sticks the first antistatic layer and the second antistatic layer, constant temperature
Drying is to get foam strip.
It is that the viscose glue selects silicon rubber as improved.
The utility model has the advantages that
Compared with prior art, the present invention provides a kind of multimedia projector foam strip and preparation method thereof, gained foams
Item is bonded using three-decker, and first antistatic layer and the second antistatic layer pass through modified O-phthalic ester and its
His component mixes, and improves the antistatic effect of general sponge, but still retains high rebound effect, and electric eliminating layer has good
Good energy storage effect, electrostatic of the respite projector because of the generation that works long hours.
Specific embodiment
The present invention is further described in detail below by specific embodiment.
Embodiment 1
A kind of multimedia projector foam strip successively includes the first antistatic layer, the electric eliminating layer and second linked by viscose glue
Antistatic layer;First antistatic layer and the second antistatic layer are mixed by following component according to parts by weight: poly-
Acrylic acid receives 48 parts, 5 parts of butyl rubber, 0.05 part of nitrocellulose, 18 parts of aluminium hydroxide, modified 5 parts of phthalic acid ester, castor
1-5 parts of sesame oil, 1 part of copper oxide, 1 part of calcium naphthenate, 1 part of epoxychloropropane, 23 parts of banana slag, 1 part of age resister;The modification
Phthalic acid ester is mixed by phthalic acid ester, dopamine solution, barium titanate;The electric eliminating layer include it is following by weight
The component of number meter: 1 part of triethylene diamine, 50 parts of polyethylene glycol, 8 parts of acid polyethylene sodium, 1 part of castor oil, 3 parts of water.
Phthalic acid ester, dopamine solution, the molar ratio of barium titanate are 3:1:1 in the modified phthalic acid ester.
The preparation method of above-mentioned multimedia projector foam strip, comprising the following steps:
Step 1, weigh component used in the first antistatic layer, electric eliminating layer and the second antistatic layer, and conventionally into
Row preparation;
Step 2, one layer of silicon rubber is painted on the two sides of electric eliminating layer, then sticks the first antistatic layer and the second antistatic layer, it is permanent
Temperature is dry to get foam strip.
It is detected according to the foam strip that national standard prepares existing single layer sponge and embodiment 1, the foam of embodiment 1
Antistatic effect improves 15%, and rebound degree reaches 100%, and 120 DEG C, aging process 48 hours under relative humidity 80RH, rebound
For rate 98%, antistatic effect is still higher by 12%.
Embodiment 2
A kind of multimedia projector foam strip successively includes the first antistatic layer, the electric eliminating layer and second linked by viscose glue
Antistatic layer;First antistatic layer and the second antistatic layer are mixed by following component according to parts by weight: poly-
Acrylic acid receives 58 parts, 8 parts of butyl rubber, 0.07 part of nitrocellulose, 20 parts of aluminium hydroxide, modified 7 parts of phthalic acid ester, castor
2 parts of sesame oil, 2 parts of copper oxide, 1.2 parts of calcium naphthenate, 1.2 parts of epoxychloropropane, 32 parts of banana slag, 2 parts of age resister;It is described to change
Property phthalic acid ester is mixed by phthalic acid ester, dopamine solution, barium titanate;The electric eliminating layer includes below by weight
Measure the component of number meter: 2 parts of triethylene diamine, 68 parts of polyethylene glycol, 10 parts of acid polyethylene sodium, 3 parts of castor oil, 5 parts of water.
Phthalic acid ester, dopamine solution, the molar ratio of barium titanate are 4:1:2 in the modified phthalic acid ester.
The preparation method of above-mentioned multimedia projector foam strip, comprising the following steps:
Step 1, weigh component used in the first antistatic layer, electric eliminating layer and the second antistatic layer, and conventionally into
Row preparation;
Step 2, one layer of silicon rubber is painted on the two sides of electric eliminating layer, then sticks the first antistatic layer and the second antistatic layer, it is permanent
Temperature is dry to get foam strip.
It is detected according to the foam strip that national standard prepares existing single layer sponge and embodiment 2, the foam of embodiment 2
Antistatic effect improves 21%, and rebound degree reaches 100%, and 120 DEG C, aging process 48 hours under relative humidity 80RH, rebound
For rate 99.5%, antistatic effect is still higher by 18%.
Embodiment 3
A kind of multimedia projector foam strip successively includes the first antistatic layer, the electric eliminating layer and second linked by viscose glue
Antistatic layer;First antistatic layer and the second antistatic layer are mixed by following component according to parts by weight: poly-
Acrylic acid receive 60 parts, 10 parts of butyl rubber, 0.08 part of nitrocellulose, 23 parts of aluminium hydroxide, modified 10 parts of phthalic acid ester,
5 parts of castor oil, 3 parts of copper oxide, 2 parts of calcium naphthenate, 1.8 parts of epoxychloropropane, 48 parts of banana slag, 3 parts of age resister;It is described to change
Property phthalic acid ester is mixed by phthalic acid ester, dopamine solution, barium titanate;The electric eliminating layer includes below by weight
Measure the component of number meter: 3 parts of triethylene diamine, 75 parts of polyethylene glycol, 12 parts of acid polyethylene sodium, 4 parts of castor oil, 7 parts of water.
Phthalic acid ester, dopamine solution, the molar ratio of barium titanate are 5:1:3 in the modified phthalic acid ester.
The preparation method of above-mentioned multimedia projector foam strip, comprising the following steps:
Step 1, weigh component used in the first antistatic layer, electric eliminating layer and the second antistatic layer, and conventionally into
Row preparation;
Step 2, one layer of silicon rubber is painted on the two sides of electric eliminating layer, then sticks the first antistatic layer and the second antistatic layer, it is permanent
Temperature is dry to get foam strip.
It is detected according to the foam strip that national standard prepares existing single layer sponge and embodiment 3, the foam of embodiment 3
Antistatic effect improves 18%, and rebound degree reaches 100%, and 120 DEG C, aging process 48 hours under relative humidity 80RH, rebound
For rate 98.2%, antistatic effect is still higher by 12%.
In conclusion foam strip of the present invention is arranged using layer structure, in such a way that antistatic layer encases electric eliminating layer, to the greatest extent
Accumulation of energy more than possible has rebound effect well, and anti-aging, therefore has a good application prospect.
The foregoing is only a preferred embodiment of the present invention, the scope of protection of the present invention is not limited to this, it is any ripe
Know those skilled in the art within the technical scope of the present disclosure, the letter for the technical solution that can be become apparent to
Altered or equivalence replacement are fallen within the protection scope of the present invention.
Claims (6)
1. a kind of multimedia projector foam strip, which is characterized in that successively include by viscose glue link the first antistatic layer,
Electric eliminating layer and the second antistatic layer;First antistatic layer and the second antistatic layer are by following component according to parts by weight
It is mixed: 48-60 parts of sodium polyacrylate, 5-10 parts of butyl rubber, 0.05-0.08 parts of nitrocellulose, aluminium hydroxide 18-23
Part, modified phthalic acid ester 5-10 parts, 1-5 parts of castor oil, 1-3 parts of copper oxide, 1-2 parts of calcium naphthenate, epoxychloropropane 1-
1.8 parts, 23-48 parts of banana slag, 1-3 parts of age resister;The modified phthalic acid ester is molten by phthalic acid ester, dopamine
Liquid, barium titanate mix;The electric eliminating layer includes following component according to parts by weight: 1-3 parts of triethylene diamine, poly- second
50-75 parts of glycol, 8-12 parts of acid polyethylene sodium, 1-4 parts of castor oil, 3-7 parts of water.
2. multimedia projector foam strip according to claim 1, which is characterized in that first antistatic layer and
Two antistatic layers are mixed by following component according to parts by weight: 58 parts of sodium polyacrylate, 8 parts of butyl rubber, nitric acid
0.07 part of cellulose, 20 parts of aluminium hydroxide, modified 7 parts of phthalic acid ester, 2 parts of castor oil, 2 parts of copper oxide, calcium naphthenate 1.2
Part, 1.2 parts of epoxychloropropane, 32 parts of banana slag, 2 parts of age resister.
3. multimedia projector foam strip according to claim 1, which is characterized in that the modified phthalic acid ester
Middle phthalic acid ester, dopamine solution, the molar ratio of barium titanate are 3-5:1:1-3.
4. multimedia projector foam strip according to claim 1, which is characterized in that the electric eliminating layer includes pressing below
The component of parts by weight meter: 2 parts of triethylene diamine, 68 parts of polyethylene glycol, 10 parts of acid polyethylene sodium, 3 parts of castor oil, 5 parts of water.
5. the preparation method based on multimedia projector foam strip described in claim 1, which is characterized in that including following step
It is rapid: step 1, to weigh component used in the first antistatic layer, electric eliminating layer and the second antistatic layer, and conventionally carry out
Preparation;One layer of silicon rubber is painted on the two sides of electric eliminating layer, then sticks the first antistatic layer and the second antistatic layer, constant temperature is dry
It is dry to get foam strip.
6. the preparation method of multimedia projector foam strip according to claim 5, which is characterized in that the viscose glue choosing
Use silicon rubber.