CN110179224A - A kind of cameo incrustation technology - Google Patents
A kind of cameo incrustation technology Download PDFInfo
- Publication number
- CN110179224A CN110179224A CN201910499612.2A CN201910499612A CN110179224A CN 110179224 A CN110179224 A CN 110179224A CN 201910499612 A CN201910499612 A CN 201910499612A CN 110179224 A CN110179224 A CN 110179224A
- Authority
- CN
- China
- Prior art keywords
- wax
- pattern
- foot
- lens reflex
- wammel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cameo incrustation technologies, comprising the following steps: 1) makes wax-pattern: using 3D wax spray, sprays former wax-pattern, is changed into silver-colored version, then silver-colored version note is caused wax-pattern, then produce wax-pattern rabbet and wax pawl by wax injector note；2) polishing diamond: ten single-lens reflex camera bradawls of production and an anti-wammel of foot；3) inlaid diamond: ten single-lens reflex camera bradawls and an anti-wammel of foot are embedded on wax-pattern respectively；4) reverse mould；5) cleaning, drying；6) it polishes: surface polishing is carried out to get finished product to metal framework；Ten single-lens reflex camera melees and the anti-bitellos of foot are embedded on wax-pattern by the present invention, it is formed again with investment wax casting method reverse mould, it is shunk by High-temperature cooling, to reach brill, to be embedded in Jin Tuoshang stronger, it reduces turquoise, fall the phenomenon that stone, the visual effect of the brill of 11 diamonds such as one can be more showed, and production process more saves time.
Description
Technical field
The present invention relates to processing of ornament technical fields, and in particular to a kind of cameo incrustation technology.
Background technique
The prior art is that wax-pattern is first poured in molding by wax injector, is deployed into 18K gold reverse mould out again with foot with thousand pure golds
Back-drilling stone is manually inlayed, and possibly is present in artificial mosaic process and is opened precision when inlaying hole location and be deviated, disadvantage is just
It is to be easy to appear diamond loosening, there is also diamond under serious situation and fall off；The prior art is to utilize sufficient back-drilling stone and utilization
Multiple fixed points fix bradawl and bitellos, and fixed point is more, using being that anti-its refracted light of winding wheel setting of foot is entirely
It is extremely difficult to such as one, 11 each diamonds whole visual effect.
Summary of the invention
For above-mentioned technical deficiency, the object of the present invention is to provide a kind of cameo incrustation technologies, by ten single-lens reflex cameras
Melee and the anti-bitellos of foot are embedded on wax-pattern, then are formed with investment wax casting method reverse mould, are shunk by High-temperature cooling, from
And reach brill to be embedded in Jin Tuoshang stronger, it reduces turquoise, fall the phenomenon that stone, can more show the view that 11 diamonds such as one bore
Feel effect, and production process more saves time.
In order to solve the above technical problems, the present invention adopts the following technical scheme:
A kind of cameo incrustation technology, comprising the following steps:
1) it makes wax-pattern: using 3D wax spray, spray former wax-pattern, changed into silver-colored version, then silver-colored version is infused and causes wax-pattern, then by
Wax injector note produces wax-pattern rabbet and wax pawl；
2) polishing diamond: ten single-lens reflex camera bradawls of production and an anti-wammel of foot；
3) inlaid diamond: ten single-lens reflex camera bradawls and an anti-wammel of foot are embedded on wax-pattern respectively, first will the anti-wammel of foot
It is embedded in the center of wax-pattern, then uniformly inlays ten single-lens reflex camera bradawls around wammel again, allows single-lens reflex camera bradawl that can push down foot anti-big
Bore edge；
4) reverse mould: the good wax tree of wax-pattern kind that will inlay stone is put into reverse mould cup, pours into calcium plaster, waits to be solidified place into
Die reversing machine is warmed to 620-630 DEG C, and deployed 18k gold is then heated up to metal and dissolves into Jinsui River, then Jinsui River is poured into
In reverse mould cup, gold support bath is taken out after cooling, reverse mould process is completed；
5) cleaning, drying: jewellery are cleaned using cleaning solution, are dried after cleaning；
6) it polishes: surface polishing is carried out to get finished product to metal framework.
Preferably, when single-lens reflex camera bradawl is embedded axis to the anti-wammel tilt angle of foot be 15 °.
Preferably, it is along the anti-wammel diametrical direction 0.15mm of foot that single-lens reflex camera bradawl, which pushes down the length at the anti-wammel edge of foot,.
Preferably, the spacing of two neighboring single-lens reflex camera bradawl is 0.1mm.
Preferably, the diameter of wax pawl is 0.6mm.
The beneficial effects of the present invention are: ten single-lens reflex camera melees and the anti-bitellos of foot are embedded on wax-pattern, then
It is formed with investment wax casting method reverse mould, is shunk by High-temperature cooling, to be embedded in Jin Tuoshang stronger to reach brill, reduces pine
Stone falls the phenomenon that stone, can more show the visual effect of the brill of 11 diamonds such as one, and production process more saves time.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with
It obtains other drawings based on these drawings.
Fig. 1 is a kind of structural schematic diagram of the cameo incrustation technology provided in an embodiment of the present invention when implementing.
Description of symbols:
1- wax-pattern, 2- wax pawl, 3- single-lens reflex camera bradawl, 4- anti-wammel enough.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
As shown in Figure 1, a kind of cameo incrustation technology, comprising the following steps:
1) it makes wax-pattern: using 3D wax spray, spray former wax-pattern, changed into silver-colored version, then silver-colored version note is caused into wax-pattern 1, then
Wax-pattern rabbet and wax pawl 2 are produced by wax injector note；
2) polishing diamond: ten single-lens reflex camera bradawls 3 of production and the anti-wammel 4 of a foot；
3) inlaid diamond: ten single-lens reflex camera bradawls 3 and the anti-wammel 4 of a foot are embedded in respectively on wax-pattern 1, first will be sufficient anti-big
4 centers for being embedded in wax-pattern 1 are bored, then ten single-lens reflex camera bradawls 3 is uniformly inlayed around the anti-wammel 4 of foot again, allows single-lens reflex camera bradawl 3 can
Push down anti-4 edge of wammel of foot；
4) reverse mould: the good wax tree of wax-pattern kind that will inlay stone is put into reverse mould cup, pours into calcium plaster, waits to be solidified place into
Die reversing machine is warmed to 620-630 DEG C, and deployed 18k gold is then heated up to metal and dissolves into Jinsui River, then Jinsui River is poured into
In reverse mould cup, gold support bath is taken out after cooling, reverse mould process is completed；
5) cleaning, drying: jewellery are cleaned using cleaning solution, are dried after cleaning；
6) it polishes: surface polishing is carried out to get finished product to metal framework.
Further, when single-lens reflex camera bradawl 3 is embedded axis to anti-4 tilt angle of wammel of foot be 15 °.
Further, it is along the anti-4 diametrical direction 0.15mm of wammel of foot that single-lens reflex camera bradawl 3, which pushes down the length at anti-4 edge of wammel of foot,.
Further, the spacing of two neighboring single-lens reflex camera bradawl 3 is 0.1mm.
Further, the diameter of wax pawl 2 is 0.6mm.
Ten single-lens reflex camera melees and the anti-bitellos of foot are embedded on wax-pattern by this technique, then with investment wax casting method reverse mould
It forms, is shunk by High-temperature cooling, to be embedded in Jin Tuoshang stronger to reach brill, reduces turquoise, falls the phenomenon that stone, more can
The visual effect of the brill of 11 diamonds such as one is showed, and production process more saves time.
Obviously, various changes and modifications can be made to the invention without departing from essence of the invention by those skilled in the art
Mind and range.In this way, if these modifications and changes of the present invention belongs to the range of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to include these modifications and variations.
Claims (5)
1. a kind of cameo incrustation technology, which comprises the following steps:
1) it makes wax-pattern: using 3D wax spray, spray former wax-pattern, changed into silver-colored version, then silver-colored version note is caused into wax-pattern, then by casting
Machine note produces wax-pattern rabbet and wax pawl；
2) polishing diamond: ten single-lens reflex camera bradawls of production and an anti-wammel of foot；
3) inlaid diamond: ten single-lens reflex camera bradawls and an anti-wammel of foot are embedded on wax-pattern respectively, first inlay the anti-wammel of foot
At the center of wax-pattern, ten single-lens reflex camera bradawls are then uniformly inlayed around wammel again, allow single-lens reflex camera bradawl that can push down the anti-wammel side of foot
Edge；
4) reverse mould: the good wax tree of wax-pattern kind that will inlay stone is put into reverse mould cup, pours into calcium plaster, waits to be solidified placing into reverse mould
Machine is warmed to 620-630 DEG C, and deployed 18k gold is then heated up to metal and dissolves into Jinsui River, then reverse mould is poured into Jinsui River
In cup, gold support bath is taken out after cooling, reverse mould process is completed；
5) cleaning, drying: jewellery are cleaned using cleaning solution, are dried after cleaning；
6) it polishes: surface polishing is carried out to get finished product to metal framework.
2. a kind of cameo incrustation technology as described in claim 1, which is characterized in that axis is anti-big to foot when single-lens reflex camera bradawl is embedded
Boring tilt angle is 15 °.
3. a kind of cameo incrustation technology as described in claim 1, which is characterized in that single-lens reflex camera bradawl pushes down the anti-wammel edge of foot
Length is along the anti-wammel diametrical direction 0.15mm of foot.
4. a kind of cameo incrustation technology as described in claim 1, which is characterized in that the spacing of two neighboring single-lens reflex camera bradawl is
0.1mm。
5. a kind of cameo incrustation technology as described in claim 1, which is characterized in that the diameter of wax pawl is 0.6mm.