CN104997248A - Hollowed-out character jewelry making method - Google Patents
Hollowed-out character jewelry making method Download PDFInfo
- Publication number
- CN104997248A CN104997248A CN201510294280.6A CN201510294280A CN104997248A CN 104997248 A CN104997248 A CN 104997248A CN 201510294280 A CN201510294280 A CN 201510294280A CN 104997248 A CN104997248 A CN 104997248A
- Authority
- CN
- China
- Prior art keywords
- wax
- plastotype
- casting
- silver
- chinese
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a hollowed-out character jewelry making method. The method includes the steps of 1, designing and platemaking, 2, mould opening, 3, wax injection, 4, moulding, 5, casting, 6, grinding and 7, polishing. The moulding step includes the steps that 1, wax pieces required to be shaped are put into warm water at the temperature of 40 DEG C to 50 DEG C, and the wax pieces are slightly held between the fingers to make different kinds of lines after being taken out of the warm water; 2, the primarily-formed plastic piece is put into cold water to be cooled so as to make the form of the plastic piece be fixed; 3, different wax block pieces are formed by welding the qualified wax pieces and put on a wax core, a wax tree is formed, and Chinese characters are adopted to serve as a shaping structure. Products obtained through the hollowed-out character jewelry making method can be made into diversified three-dimensional frames, the diversity of the Chinese traditional characters in the design concept is improved, and the extensive and profound Chinese culture and variety and plasticity of the Chinese culture are carried forward; meanwhile, attractive appearance and practical value of the modern product design and manufacturing are achieved by highlighting the Chinese characters.
Description
Technical field
The present invention relates to jewelry manufacture process application technical field, especially relate to a kind of hollow out word jewelry manufacture method.
Background technology
Jewellery, as the ornament be worn on the person.Literal sense only refers to the ornament worn on head, now makes a general reference the earrings, necklace, ring, bracelet etc. that process with precious metal, jewel etc.Jewellery, generally in order to decorate human body, also have the meaning such as performance social status, display wealth.
Chinese characters, that Chinese characters reach the development of thousands of years and the historical process of differentiation, according to the time sequencing of development, the Qin, Chinese music, the Chinese, Tang's word in period, Song, first era, bright, clear word, China modern word and contemporary Chinese word etc. in the past substantially can be divided into.China is a multi-ethnic country.In the long years from ancient times to modern age, people of all nationalities create the superior text culture of motherland jointly.
Present stage is in jewellery industry, the jewellery that the design of existing product Chinese characters is made, majority is on the basis in plane or light face, add single or multiple plane word, with technologies such as engraving, cutting, etchings, be made into the jewellery of some Chinese characters by assembly, this kind of product mostly is plane, stiff, dull, third dimension is poor.
Summary of the invention
For the deficiency that above-mentioned prior art exists, the object of this invention is to provide a kind of hollow out word jewelry manufacture method.
To achieve these goals, the technical solution adopted in the present invention is:
A kind of hollow out word jewelry manufacture method: comprise step one, design, plate-making; Step 2, die sinking; Step 3, casting; Step 4, plastotype; Step 5, casting; Step 6, grinding; Step 7, polishing.
In above-described step one, first through the drawing of the novel unique texture of computer design, then make stencil plate by fully automatic forming machine, through casting, processing, the accurate silver-colored version of the standard one by one that completes.
In step 2: silver-colored version step one made copies as glued membrane; Completed by four steps, the silver-colored version of S1. special (purpose) rubber filling parcel; S2. put into film laminator to heat, pressurization, shaping; S3. cut open glued membrane, take out silver-colored version; S4. glued membrane is processed.
In step 3: S1. rubber alloy film; S2. casting; S3. open glued membrane, get wax; S4. wax part is checked;
In step 4: S1., the wax part needing plastotype, puts into the warm water of 40 ~ 50 degree gently, then take out with have gentle hands light pinch out various lines; S2. the plastic of first one-step forming, put into cold water and allow it cool, its form is fixed; S3. by qualified wax part by being welded to form different wax stone sheets, then be placed on wax core, form wax tree.
In step 5: wax tree is inserted in steel cylinder by S1.; S2. steel cylinder is put into moulding machine; S3. stir gypsum, vacuumize; S4. calcium plaster is injected; S5. numbering is left standstill; S6. roaster roasting is put into after dewaxing; S7. roasting plaster mold is inserted in casting machine and cast; S8. taken out by the plaster mold of having cast, quick-fried water also flushes out clean silver tree.
In step 6: S1. files the mouth of a river, mill inner ring; S2. shaping, amount refers to enclose; S3. beat flying saucer, be bulldozed.
In step 7: S1. car flying saucer; S2. inner ring is thrown; S3. fiber crops wheel is thrown; S4. hacking brush; S5. step wheel is thrown.
In above-described step 4, the wax part of described plastotype adopts hollow out Chinese characters as the plastotype structure of wax stone, and this plastotype wax part is placed on temperature is soak in the warm water of 45 degree, the textured wax part of the band pinched out is placed in cold water treats that form is fixed, and this twice step repeats to complete for 3 ~ 4 times.
In above-described step 7, the metal surface after polishing without any impurity, sand hole or scar.
After adopting technique scheme, the present invention is compared to the prior art advantageously: this hollow out word jewelry manufacture method, different Chinese characters are utilized to arrange, the three-dimensional object of different shape is made in combination, form can be the various personage birds and beasts of various animal, plant, flower, bird, insect, personage, scenery with hills and waters, dragon and phoenix or other folks of china legends, again with different expensive metals, make jewellery product.Product of the present invention can be made into into the three-dimensional price of diversity, in raising Chinese tradition word diversity in the design concepts, the extensive knowledge and profound scholarship of carry forward Chinese culture, polytropy and plasticity.Outstanding Chinese characters also can take attractive in appearance and practical value out of on new detection technology and making simultaneously.
Accompanying drawing explanation
Below in conjunction with drawings and Examples, the present invention is further described:
Fig. 1 is overall flow figure of the present invention;
Fig. 2 and Fig. 3 is hollow-out word body structure schematic diagram of the present invention;
Fig. 4 is plastotype structural representation of the present invention.
Detailed description of the invention
The following stated is only preferred embodiment of the present invention, does not therefore limit protection scope of the present invention.
Embodiment, is shown in Fig. 1.
As shown in Figure 1, a kind of hollow out word jewelry manufacture method: comprise step one, design, plate-making; Step 2, die sinking; Step 3, casting; Step 4, plastotype; Step 5, casting; Step 6, grinding; Step 7, polishing.
In above-described step one, first through the drawing of the novel unique texture of computer design, then make stencil plate by fully automatic forming machine, through casting, processing, the accurate silver-colored version of the standard one by one that completes.
In step 2: silver-colored version step one made copies as glued membrane; Completed by four steps, the silver-colored version of S1. special (purpose) rubber filling parcel; S2. put into film laminator to heat, pressurization, shaping; S3. cut open glued membrane, take out silver-colored version; S4. glued membrane is processed.
In step 3: utilize glued membrane by wax injector, the wax of liquid state to be injected cooling forming in rubber pattern under the influence of air pressure; S1. rubber alloy film; S2. casting; S3. open glued membrane, get wax; S4. wax part is checked;
In step 4: due to the wax part of just having worked it out entirely for solid form, the various forms oneself wanted can be moulded by this technique, make it more lively, improve sight.More be added with artistic feeling, third dimension.S1. the wax part needing plastotype, put into the warm water of 40 ~ 50 degree gently, then take out with have gentle hands light pinch out various lines; S2. the plastic of first one-step forming, put into cold water and allow it cool, its form is fixed; S3. by qualified wax part by being welded to form different wax stone sheets, then be placed on wax core, form wax tree.
In step 5: cream mould is inserted in casting machine and cast; S8. taken out by the plaster mold of having cast, quick-fried water also flushes out clean silver tree; S1. wax tree is inserted in steel cylinder; S2. steel cylinder is put into moulding machine; S3. stir gypsum, vacuumize; S4. calcium plaster is injected; S5. numbering is left standstill; S6. roaster roasting is put into after dewaxing; S7. roasting plaster mold is inserted in casting machine and cast; S8. taken out by the plaster mold of having cast, quick-fried water also flushes out clean silver tree.
In step 6: the process of grinding is by the entirety of product or local, is corrected or shaping by milling tool, till being worked into flat smooth, makes whole product svelteness floriation even, symmetrical; S1. the mouth of a river is filed, mill inner ring; S2. shaping, amount refers to enclose; S3. beat flying saucer, be bulldozed.
In step 7: polishing is taken turns by the cloth of High Rotation Speed, under the effect of buffing wax, make metal surface produce high heat, to reach the effect of ironing light, or carry out polishing by jewellery instrument (agate pressure) the steel system of rolling.Through the product of polishing, light is as new.Can not there be any impurity metal surface, sand hole or scar; S1. car flying saucer; S2. inner ring is thrown; S3. fiber crops wheel is thrown; S4. hacking brush; S5. step wheel is thrown.
In above-described step 4, the wax part of described plastotype adopts hollow out Chinese characters as the plastotype structure of wax stone, and this plastotype wax part is placed on temperature is soak in the warm water of 45 degree, the textured wax part of the band pinched out is placed in cold water treats that form is fixed, and this twice step repeats to complete for 3 ~ 4 times.
In above-described step 7, the metal surface after polishing without any impurity, sand hole or scar.
In sum, drawn by computer software, design multiple hollow out Chinese characters (numerous, simplified), then carry out and connect; Modify from the initial finished product that is designed into through the processing that a lot of is meticulous, yarn dialled by the jewelry product of pieces beautiful skirt of raising, to the greatest extent in elegance, also just no longer mysterious.
The above is only better embodiment of the present invention, therefore all equivalences done according to structure, feature and the principle described in patent claim of the present invention change or modify, and are included in patent claim of the present invention.
Claims (4)
1. a hollow out word jewelry manufacture method: comprise step one, design, plate-making; Step 2, die sinking; Step 3, casting; Step 4, plastotype; Step 5, casting; Step 6, grinding; Step 7, polishing; It is characterized in that:
In step one, first through the drawing of the novel unique texture of computer design, then make stencil plate by fully automatic forming machine, through casting, processing, the accurate silver-colored version of the standard one by one that completes;
In step 2: silver-colored version step one made copies as glued membrane; Completed by four steps, the silver-colored version of S2.1 special (purpose) rubber filling parcel; S2.2 puts into film laminator and heats, pressurization, shaping; S2.3 cuts open glued membrane, takes out silver-colored version; S2.4 process glued membrane;
In step 3: S3.1 rubber alloy film; S3.2 casting; S3.3 opens glued membrane, gets wax; S3.4 checks wax part;
In step 4: S4.1, the wax part needing plastotype, puts into the warm water of 40 ~ 50 degree gently, then take out with have gentle hands light pinch out various lines; S4.2, the plastic of first one-step forming, puts into cold water and allows it cool, its form is fixed; By being welded to form your wax stone sheet different after S4.3 screening, by qualified wax part, then being placed on wax core, forming wax tree;
In step 5: wax tree is inserted in steel cylinder by S5.1; Steel cylinder is put into moulding machine by S5.2; S5.3 stirs gypsum, vacuumizes; S5.4 injects calcium plaster; S5.5 leaves standstill numbering; Roaster roasting is put into after S5.6 dewaxing; Roasting plaster mold is inserted in casting machine and is cast by S5.7; The plaster mold of having cast takes out by S5.8, and quick-fried water also flushes out clean silver tree;
In step 6: S6.1 files the mouth of a river, mill inner ring; S6.2 shaping, amount refer to enclose; S6.3 beats flying saucer, is bulldozed;
In step 7: S7.1 car flying saucer; S7.2 throws inner ring; S7.3 throws fiber crops wheel; S7.4 hacking brush; S7.5 throws step wheel.
2. a kind of hollow out word jewelry manufacture method according to claim 1, it is characterized in that: in described step 4 plastotype, it is plastotype structure that solid-state wax stone part plastotype is preferably Chinese characters.
3. a kind of hollow out word jewelry manufacture method according to claim 1, is characterized in that: in step 4, needs the wax part of plastotype, put into the warm water that temperature is preferably 45 degree, then takes out and pinch out various lines with hand; The just plastic of one-step forming, puts into its cooling of cold water, till form is fixing; Above step repeats to complete for 3 ~ 4 times.
4. a kind of hollow out word jewelry manufacture method according to claim 1, is characterized in that: the metal surface after polishing without any impurity, sand hole or scar.