CN110170796A - A kind of melting welding renovation technique remanufacturing automotive wheel - Google Patents
A kind of melting welding renovation technique remanufacturing automotive wheel Download PDFInfo
- Publication number
- CN110170796A CN110170796A CN201910609709.4A CN201910609709A CN110170796A CN 110170796 A CN110170796 A CN 110170796A CN 201910609709 A CN201910609709 A CN 201910609709A CN 110170796 A CN110170796 A CN 110170796A
- Authority
- CN
- China
- Prior art keywords
- wheel
- melting welding
- repairing
- temperature
- renovation technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of melting welding renovation technique for remanufacturing automotive wheel, the melting welding renovation technique includes following operating procedure: step 1, screening: carrying out internal carrying out flaw detection to wheel；Step 2, cleaning；Step 3, selection: according to wheel material and damage position, material is selected；Step 4, melting welding: using Surface Welding at High Temperature repairing method, until fusion completely；Step 5, room temperature；Step 6, polishing: it polishes wheel repairing position, until surfacing is without salient point burr；Step 7, cleaning: it is cleaned using deionized water direct-injection repairing position；Step 8, drying: it is toasted under high temperature dustfree environment；Step 9, low temperature are placed: the wheel after soldering being placed in low temperature dustfree environment 20 minutes, low-temperature shrink soldering position；Step 10, room temperature；Step 11, detection.The present invention overcomes prior art disadvantage, and firmness is strong, and technological operation is simple and practical, high-efficient.
Description
Technical field
The present invention relates to wheel recovery technique field, in particular to a kind of melting welding renovation techniques for remanufacturing automotive wheel.
Background technique
Wheel is the major part of automobile, it is desirable that its intensity height, impact resistance, it is wear-resistant, cannot have any defect, otherwise
Threat to life property safety, is repaired to wheel in the prior art, and conventional wheel injury repair is filled out using powder of lacquer putty for use on
It fills, not high with wheel degrees of fusion, firmness is low；Conventional repair technology simultaneously is directly sprayed after drying putty, and putty has
Water imbibition, easily leads to that spraying effect is bad, and existing technical problem is all urgently improved.
Summary of the invention
The technical problem to be solved by the present invention is to overcome prior art disadvantage, provide and a kind of remanufacture the molten of automotive wheel
Renovation technique is welded, firmness is strong, and technological operation is simple and practical, high-efficient.
In order to solve the above technical problems, technical solution provided by the invention are as follows: a kind of melting welding for remanufacturing automotive wheel is repaired
It returns to work skill, the melting welding renovation technique includes following operating procedure:
Step 1, screening: carrying out internal carrying out flaw detection to wheel, avoids wheel from occurring internal impaired；
Step 2, cleaning: oil removing, decontamination, dust removal process are integrally carried out to wheel；
Step 3, selection: according to wheel material and damage position, the suitable material repaired is selected；
Step 4, melting welding: using Surface Welding at High Temperature repairing method, until wheel damage position is merged completely with patching material, from
And guarantee repairing firmness；
Step 5, room temperature: by the wheel room temperature after fusion welding repair, until the cooling of soldering position finishes；
Step 6, polishing: polishing to wheel repairing position, until the repairing smooth no salient point burr of surface of position；
Step 7, cleaning: it is cleaned using deionized water direct-injection repairing position, guarantees that wheel hub remanufactures the rear free from dust flaw
Defect；
Step 8, drying: it is toasted under 45-55 degree high temperature dustfree environment；
Step 9, low temperature are placed: the wheel after soldering being placed in low temperature dustfree environment 20 minutes, low-temperature shrink soldering
Position；
Step 10, room temperature；
Step 11, detection, repair and complete.
As an improvement, baking time is 10-15 minutes in the step 8.
As an improvement, low temperature is -5 degree or less in the step 9.
The present invention has the advantage that 1, conventional wheel injury repair, is filled using powder of lacquer putty for use on, with wheel degrees of fusion
Not high, firmness is low, this patent technique uses welding technology, ensure that the repairing firmness of wheel；
2, conventional repair technology is directly sprayed after drying putty, and putty has water imbibition, easily leads to spraying effect not
Good, this patent is intersected using high/low temperature places, and guarantees that soldering is thorough, increases firmness；
3, patented technology uses deionized water straight spraying cleaning, guarantees that wheel hub remanufactures rear free from dust flaw；
4, patented technology uses height greenhouse conveyer belt, improves production efficiency.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments.
The present invention in the specific implementation, a kind of melting welding renovation technique remanufacturing automotive wheel, the melting welding renovation technique
Including following operating procedure:
Step 1, screening: carrying out internal carrying out flaw detection to wheel, avoids wheel from occurring internal impaired；
Step 2, cleaning: oil removing, decontamination, dust removal process are integrally carried out to wheel；
Step 3, selection: according to wheel material and damage position, the suitable material repaired is selected；
Step 4, melting welding: using Surface Welding at High Temperature repairing method, until wheel damage position is merged completely with patching material, from
And guarantee repairing firmness；
Step 5, room temperature: by the wheel room temperature after fusion welding repair, until the cooling of soldering position finishes；
Step 6, polishing: polishing to wheel repairing position, until the repairing smooth no salient point burr of surface of position；
Step 7, cleaning: it is cleaned using deionized water direct-injection repairing position, guarantees that wheel hub remanufactures the rear free from dust flaw
Defect；
Step 8, drying: being toasted under 45-55 degree high temperature dustfree environment, and baking time is 10-15 minutes；
Step 9, low temperature are placed: the wheel after soldering being placed in the degree of low temperature -5 or less, 20 minutes in dustfree environment, low temperature
Shrink soldering position；
Step 10, room temperature；
Step 11, detection, repair and complete.
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, fall within the scope of the claimed invention without departing from theon the basis of the spirit of the present invention.
Claims (3)
1. a kind of melting welding renovation technique for remanufacturing automotive wheel, which is characterized in that the melting welding renovation technique includes following behaviour
Make step:
Step 1, screening: carrying out internal carrying out flaw detection to wheel, avoids wheel from occurring internal impaired；
Step 2, cleaning: oil removing, decontamination, dust removal process are integrally carried out to wheel；
Step 3, selection: according to wheel material and damage position, the suitable material repaired is selected；
Step 4, melting welding: using Surface Welding at High Temperature repairing method, until wheel damage position is merged completely with patching material, to protect
Card repairing firmness；
Step 5, room temperature: by the wheel room temperature after fusion welding repair, until the cooling of soldering position finishes；
Step 6, polishing: polishing to wheel repairing position, until the repairing smooth no salient point burr of surface of position；
Step 7, cleaning: it is cleaned using deionized water direct-injection repairing position, guarantees that wheel hub remanufactures rear free from dust flaw；
Step 8, drying: it is toasted under 45-55 degree high temperature dustfree environment；
Step 9, low temperature are placed: the wheel after soldering being placed in low temperature dustfree environment 20 minutes, low-temperature shrink soldering position；
Step 10, room temperature；
Step 11, detection, repair and complete.
2. a kind of melting welding renovation technique for remanufacturing automotive wheel according to claim 1, it is characterised in that: the step
Baking time is 10-15 minutes in 8.
3. a kind of melting welding renovation technique for remanufacturing automotive wheel according to claim 1, it is characterised in that: the step
Low temperature is -5 degree or less in 9.