CN110158350A - A kind of environment-friendly type cigarette case package transfer paper - Google Patents
A kind of environment-friendly type cigarette case package transfer paper Download PDFInfo
- Publication number
- CN110158350A CN110158350A CN201810255204.8A CN201810255204A CN110158350A CN 110158350 A CN110158350 A CN 110158350A CN 201810255204 A CN201810255204 A CN 201810255204A CN 110158350 A CN110158350 A CN 110158350A
- Authority
- CN
- China
- Prior art keywords
- paper
- parts
- layer
- center
- internal lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of environment-friendly type cigarette case package transfer paper, including transfer paper ontology, the transfer paper ontology includes center paper layer, and on centrally disposed one surface of paper layer and the first fixed internal lining paper is bonded with center paper layer, and be arranged on the first internal lining paper surface and be bonded fixed first with the first internal lining paper and shifts aluminium layer；Another surface of the center paper layer, which is provided with, is bonded the second fixed internal lining paper with center paper layer, and be arranged on the second internal lining paper surface and be bonded fixed second with the second internal lining paper and shifts aluminium layer；The inside of the center paper layer is additionally provided with one layer of web；The transfer paper successively covers the first internal lining paper, the first transfer aluminium layer, the second internal lining paper and the second transfer aluminium layer by two surfaces on the paper layer of center, and transfer paper obtained can be made to have excellent mechanical strength and thermal stability, can be used as tobacco package paper.
Description
Technical field
The present invention relates to a kind of environment-friendly type cigarette case package transfer papers.
Background technique
Cigarette package is an important component of production of cigarettes, is last procedure of entire production process.?
In production of cigarettes, circulation and the overall process of consumption, the superiority and inferiority of packaging material is to maintenance cigarette product quality, promotion sale, guidance
Consume important role.For relatively other commodity, to certain particularity that requires of cigarette packaging material, such as:
There cannot be peculiar smell, answer non-toxic to humans, should have certain moisture resistance and insulating etc..
Cigarette is to be combined with each other by aluminium foil and internal lining paper by adhesive with transfer paper, and effect is primarily used to wrap up
Cigarette in cigarette case, and Conservation environment needed for maintaining cigarette, keep cigarette moisture, cigarette flavor component is delayed to scatter and disappear.With
The development of tobacco business, the continuous improvement of scientific and technological level, more stringent requirements are proposed for use of the cigarette enterprise to transfer paper.And show
Some transfer papers when in use, are easy to be torn by user, are detached from cigarette case, the plume in cigarette case is caused to be exposed to air for a long time
In, it is easy to absorb the moisture in air, influences the quality of cigarette, furthermore, existing transfer paper is easily deformed at high temperature, unfavorable
In tobacco package, therefore, existing transfer paper has that mechanical strength is low and thermal stability is low.
Summary of the invention
In view of this, that it is an object of the present invention to provide a kind of is good with excellent mechanical strength and thermal stability, can make
For the transfer paper of tobacco package paper.
In order to solve the above-mentioned technical problem, the technical scheme is that
A kind of environment-friendly type cigarette case package transfer paper, including transfer paper ontology, the transfer paper ontology include center paper layer,
And on centrally disposed one surface of paper layer and the first fixed internal lining paper is bonded with center paper layer, and be arranged in the first liner
First transfer aluminium layer on paper surface and that fixation is bonded with the first internal lining paper；Another surface of the center paper layer is provided with
The second fixed internal lining paper is bonded with center paper layer, and be arranged on the second internal lining paper surface and be bonded with the second internal lining paper
The second fixed transfer aluminium layer.
Further, two surfaces of the center paper layer are set in sawtooth installing.
Further, the web is by shredded coconut meat web.
Further, first internal lining paper is provided with first for engaging with center paper layer with center paper layer joint place
Sawtooth portion.
Further, second internal lining paper is provided with second for engaging with center paper layer with center paper layer joint place
Sawtooth portion.
Further, the center paper layer is made of the material of following weight: 50-60 parts of bleached cotton starch, bleaching
40-48 parts of reed pulp, 30-40 parts of latex, 30-42 parts of starch, 11-17 parts of sodium carboxymethylcellulose, 9-15 parts of sodium tripolyphosphate, coke
8-12 parts of sodium phosphate, 10-16 parts of ammonium hydroxide, 5-9 parts of aluminium silicate wool, 11-15 parts of alumina powder, 14-20 parts of cellulose acetate resin,
12-15 parts of polypropylene wax, 6-8 parts of titanate coupling agent, 5-7 parts of PPE wet strength agent and 10-14 parts of antibacterial agent.
Further, the antibacterial agent is the mixing of one or more of chitin, mustard, castor oil and horseradish
Object.
Another technical problem to be solved by the invention be provide it is a kind of pressure resistance without picking center paper layer preparation method, including
Following steps:
1) it takes 50-60 parts and bleached reed pulp 40-48 parts of bleached cotton starch to be put into pulper, is run at high speed by pulper,
Bleached cotton starch and bleached reed pulp are beaten, mixed serum is made, then pours into mixed serum obtained in steam stove, then
It is heated to 300-380 DEG C, so that slurries boil, it is spare；
2) 11-17 parts of sodium carboxymethylcellulose, 9-15 parts of sodium tripolyphosphate and 8-12 parts of sodium pyrophosphate is taken to be added to step
1) in slurries made from, slurries ferment by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate fluffy, be enhanced
Then slurries obtained are washed and starched machine by pressurized screen and vacuum and carry out washing and screening, obtain concentration by the pliability of pulp fibers
It is spare for the cleaning slurries of 20-28%；
3) take 30-40 parts of latex, 14-20 parts of cellulose acetate resin and 12-15 parts of polypropylene wax be put into reaction kettle plus
Hot 20-30min makes its temperature reach 260-300 DEG C, while starting the blender in reaction kettle and being stirred with the speed of 40-50r/pm
35-40min is mixed, so that after high-temperature fusion, mixed glue solution is made in latex, cellulose acetate resin and polypropylene wax
4) take 30-42 parts of starch, 5-9 parts of aluminium silicate wool and 11-15 parts of the alumina powder sieves using 50 mesh to grinding institute
The powder obtained is screened, and the powder of 50 mesh or more is isolated, and filler is made, then filler obtained is added in agitator,
Water is added by weight the ratio of 3:4, then starts blender and is mixed above-mentioned material with water with the revolving speed of 55r/min, be made
Filler slurries, it is spare；
5) by filler slurries and titanium made from glue made from step 2) cleaning slurries obtained, step 3 and step 4)
6-8 parts of acid esters coupling agent, 5-7 parts of PPE wet strength agent and 10-14 parts of antibacterial agent are transferred in agitator, then will by blender
It is equal with the revolving speed stirring of 25r/min to clean slurries, glue and filler slurries and titanate coupling agent, PPE wet strength agent and antibacterial agent
It is even, body paper slurries are made, are then held with boiler, and be heated to 200-230 DEG C, the retrogradation so that body paper slurries are heated then will
Body paper slurries obtained pour into pressure cooker, and are 55KPa by the pressure set of pressure cooker, then by paper pulp raw material in setting
It is heated to 210-250 DEG C in pressure, so that body paper slurries are reacted with ingredients at high temperature, enhances the function of body paper slurries,
It is spare；
6) 10-16 parts of ammonium hydroxide are taken to be added in body paper slurries made from step 5), by ammonium hydroxide by bubble in body paper slurries
Removal, it is spare；
7) body paper slurries made from step 6) are subjected to copy paper, are scooped up paper pulp by scooping slurry, and by control scoop slurry with
The frequency for swinging 24 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out and reach thickness
The requirement of uniform good toughness, is then squeezed the copy paper on gauze by extruder, so that the moisture in copy paper squeezes out
And form, last copy paper after extruding be placed into the low temperature in low temp dryer with 12-26 DEG C dried to get.
The technology of the present invention effect major embodiment is in the following areas: the transfer paper by two surfaces on the paper layer of center successively
The first internal lining paper, the first transfer aluminium layer, the second internal lining paper and the second transfer aluminium layer are covered, transfer paper obtained can be made to have excellent
Good mechanical strength and thermal stability, can be used as tobacco package paper；In addition, center paper layer is with bleached cotton starch and bleached reed pulp
As main fibrous material, depigmentation is bleached and washed and starched by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate
And impurity, mix the filler as made from latex, starch, aluminium silicate wool and alumina powder and cellulose acetate resin and poly- third
Alkene wax is improved the toughness of center obtained paper layer, finally ammonium hydroxide is combined to defoam, titanate esters by melting glue obtained
Coupling agent, PPE wet strength agent and antibacterial agent further increase the excellent performance of center paper layer, are applicable in its transfer paper obtained more
In tobacco package.
Detailed description of the invention
Fig. 1 is a kind of cross-sectional view of environment-friendly type cigarette case package transfer paper of the present invention；
Fig. 2 is the structure chart of web.
Specific embodiment
Below in conjunction with attached drawing, a specific embodiment of the invention is described in further detail, so that technical solution of the present invention is more
It should be readily appreciated that and grasp.
In embodiment, it is to be understood that term " centre ", "upper", "lower", " top ", " right side ", " left end ", " on
Side ", " back side ", " middle part ", etc. instructions orientation or positional relationship be based on the orientation or positional relationship shown in the drawings, be only for
Convenient for the description present invention, rather than the device or element of indication or suggestion meaning must have a particular orientation, with specific
Orientation construction and operation, therefore be not considered as limiting the invention.
Embodiment 1
A kind of environment-friendly type cigarette case package transfer paper, as shown in Figs. 1-2, including transfer paper ontology 1, the transfer paper ontology
1 includes on 11 1 surface of center paper layer 11 and centrally disposed paper layer and is fixed with center paper layer 1 by shifting glue laminating
The first internal lining paper 12, and be arranged on 12 surface of the first internal lining paper and it is solid by transfer glue laminating with the first internal lining paper 12
The first fixed transfer aluminium layer 13；First internal lining paper 12 is provided with 11 joint place of center paper layer for nibbling with center paper layer 11
The the first sawtooth portion 121 closed.Another surface of the center paper layer 11 is provided with solid by transfer glue laminating with center paper layer 11
The second fixed internal lining paper 14, and be arranged on 14 surface of the second internal lining paper and with the second internal lining paper 14 by transfer glue laminating
The second fixed transfer aluminium layer 15；Second internal lining paper 14 and 11 joint place of center paper layer be provided with for center paper layer 11
Second sawtooth portion 141 of engagement.The inside of the center paper layer 11 is additionally provided with one layer of web 111.In this experimental example, institute
It is set in sawtooth installing on two surfaces for stating center paper layer 11.The web 111 is by shredded coconut meat web.
The center paper layer 11 is made of the material of following weight: 60 parts of bleached cotton starch, 40 parts of bleached reed pulp, cream
30 parts of glue, 30 parts of starch, sodium carboxymethylcellulose 11, sodium tripolyphosphate 9,8 parts of sodium pyrophosphate, ammonium hydroxide 10, aluminium silicate wool 5, oxygen
Change 11 parts of aluminium powder, 14 parts of cellulose acetate resin, 12 parts of polypropylene wax, 6 parts of titanate coupling agent, 5 parts of PPE wet strength agent and antibacterial
Agent 10.
A kind of preparation method of the pressure resistance without picking center paper layer, comprising the following steps:
1) it takes 60 parts and 40 parts of bleached reed pulp of bleached cotton starch to be put into pulper, is run at high speed, will be bleached by pulper
Cotton pulp and bleached reed pulp are beaten, and mixed serum is made, then pours into steam stove mixed serum obtained, is then heated to
300 DEG C, so that slurries boil, it is spare；
2) 11 parts of sodium carboxymethylcellulose, 9 parts of sodium tripolyphosphate and 8 parts of sodium pyrophosphate is taken to be added to step 1) slurry obtained
In liquid, slurries ferment by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate fluffy, enhance pulp fibers
Pliability, then by slurries obtained by pressurized screen and vacuum wash and starch machine carry out washing and screening, obtain concentration be 20% it is clear
Clean slurries, it is spare；
3) it takes 30 parts of latex, 14 parts of cellulose acetate resin and 12 parts of polypropylene wax to be put into reaction kettle and heats 20in, make
Its temperature reaches 260 DEG C, while starting the blender in reaction kettle and stirring 35min with the speed of 40r/pm, so that latex, acetic acid
Mixed glue solution is made after high-temperature fusion in celluosic resin and polypropylene wax
4) take 30 parts of starch, 5 parts of aluminium silicate wool and 11 parts of the alumina powder sieves using 50 mesh to the resulting powder of grinding
It is screened, the powder of 50 mesh or more is isolated, filler is made, then filler obtained is added in agitator, by weight
The ratio of 3:4 adds water, then starts blender and is mixed above-mentioned material with water with the revolving speed of 55r/min, filler slurries are made,
It is spare；
5) by filler slurries and titanium made from glue made from step 2) cleaning slurries obtained, step 3 and step 4)
6 parts of acid esters coupling agent, 5 parts of PPE wet strength agent and antibacterial agent 10 are transferred in agitator, then by blender will clean slurries,
Glue and filler slurries are stirred evenly with titanate coupling agent, PPE wet strength agent and antibacterial agent with the revolving speed of 25r/min, and original is made
Then pulp liquor is held with boiler, and be heated to 200 DEG C, the retrogradation so that body paper slurries are heated, then by body paper slurries obtained
It pours into pressure cooker, and is 55KPa by the pressure set of pressure cooker, be then heated to paper pulp raw material in the pressure of setting
210 DEG C, so that body paper slurries are reacted with ingredients at high temperature, enhance the function of body paper slurries, it is spare；
6) it takes 10 parts of ammonium hydroxide to be added in body paper slurries made from step 5), is removed bubble in body paper slurries by ammonium hydroxide
It removes, it is spare；
7) body paper slurries made from step 6) are subjected to copy paper, are scooped up paper pulp by scooping slurry, and by control scoop slurry with
The frequency for swinging 24 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out and reach thickness
The requirement of uniform good toughness, is then squeezed the copy paper on gauze by extruder, so that the moisture in copy paper squeezes out
And form, last copy paper after extruding be placed into low temp dryer with 12 DEG C of low temperature dried to get.
In the present embodiment.The antibacterial agent is chitin.
Embodiment 2
A kind of environment-friendly type cigarette case package transfer paper, as shown in Figs. 1-2, including transfer paper ontology 1, the transfer paper ontology
1 includes on 11 1 surface of center paper layer 11 and centrally disposed paper layer and is fixed with center paper layer 1 by shifting glue laminating
The first internal lining paper 12, and be arranged on 12 surface of the first internal lining paper and it is solid by transfer glue laminating with the first internal lining paper 12
The first fixed transfer aluminium layer 13；First internal lining paper 12 is provided with 11 joint place of center paper layer for nibbling with center paper layer 11
The the first sawtooth portion 121 closed.Another surface of the center paper layer 11 is provided with solid by transfer glue laminating with center paper layer 11
The second fixed internal lining paper 14, and be arranged on 14 surface of the second internal lining paper and with the second internal lining paper 14 by transfer glue laminating
The second fixed transfer aluminium layer 15；Second internal lining paper 14 and 11 joint place of center paper layer be provided with for center paper layer 11
Second sawtooth portion 141 of engagement.The inside of the center paper layer 11 is additionally provided with one layer of web 111.In this experimental example, institute
It is set in sawtooth installing on two surfaces for stating center paper layer 11.The web 111 is by shredded coconut meat web.
The center paper layer 11 is made of the material of following weight: 50 parts of bleached cotton starch, 48 parts of bleached reed pulp, cream
40 parts of glue, 42 parts of starch, 17 parts of sodium carboxymethylcellulose, 15 parts of sodium tripolyphosphate, 12 parts of sodium pyrophosphate, 16 parts of ammonium hydroxide, silicic acid
9 parts of aluminum wool, 15 parts of alumina powder, 20 parts of cellulose acetate resin, 15 parts of polypropylene wax, 8 parts of titanate coupling agent, PPE are wet strong
7 parts and 14 parts of antibacterial agent of agent.
A kind of preparation method of the pressure resistance without picking center paper layer, comprising the following steps:
1) it takes 50 parts and 48 parts of bleached reed pulp of bleached cotton starch to be put into pulper, is run at high speed, will be bleached by pulper
Cotton pulp and bleached reed pulp are beaten, and mixed serum is made, then pours into steam stove mixed serum obtained, is then heated to
380 DEG C, so that slurries boil, it is spare；
2) 17 parts of sodium carboxymethylcellulose, 15 parts of sodium tripolyphosphate and 12 parts of sodium pyrophosphate is taken to be added to step 1) obtained
In slurries, slurries ferment by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate fluffy, enhances pulp fibers
Pliability, slurries obtained are then washed and starched into machine by pressurized screen and vacuum and carry out washing and screening, obtaining concentration is 28%
Slurries are cleaned, it is spare；
3) it takes 40 parts of latex, 20 parts of cellulose acetate resin and 15 parts of polypropylene wax to be put into reaction kettle and heats 30min, make
Its temperature reaches 300 DEG C, while starting the blender in reaction kettle and stirring 40min with the speed of 50r/pm, so that latex, acetic acid
Mixed glue solution is made after high-temperature fusion in celluosic resin and polypropylene wax
4) take 42 parts of starch, 9 parts of aluminium silicate wool and 15 parts of the alumina powder sieves using 50 mesh to the resulting powder of grinding
It is screened, the powder of 50 mesh or more is isolated, filler is made, then filler obtained is added in agitator, by weight
The ratio of 3:4 adds water, then starts blender and is mixed above-mentioned material with water with the revolving speed of 55r/min, filler slurries are made,
It is spare；
5) by filler slurries and titanium made from glue made from step 2) cleaning slurries obtained, step 3 and step 4)
8 parts of acid esters coupling agent, 7 parts of PPE wet strength agent and 14 parts of antibacterial agent are transferred in agitator, are then starched cleaning by blender
Liquid, glue and filler slurries are stirred evenly with titanate coupling agent, PPE wet strength agent and antibacterial agent with the revolving speed of 25r/min, are made
Body paper slurries, are then held with boiler, and are heated to 230 DEG C, and the retrogradation so that body paper slurries are heated then starches body paper obtained
Liquid pours into pressure cooker, and is 55KPa by the pressure set of pressure cooker, is then heated to paper pulp raw material in the pressure of setting
250 DEG C, so that body paper slurries are reacted with ingredients at high temperature, enhance the function of body paper slurries, it is spare；
6) it takes 16 parts of ammonium hydroxide to be added in body paper slurries made from step 5), is removed bubble in body paper slurries by ammonium hydroxide
It removes, it is spare；
7) body paper slurries made from step 6) are subjected to copy paper, are scooped up paper pulp by scooping slurry, and by control scoop slurry with
The frequency for swinging 24 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out and reach thickness
The requirement of uniform good toughness, is then squeezed the copy paper on gauze by extruder, so that the moisture in copy paper squeezes out
And form, last copy paper after extruding be placed into low temp dryer with 26 DEG C of low temperature dried to get.
In the present embodiment.The antibacterial agent is mustard, castor oil and the mixture of horseradish.
Embodiment 3
A kind of environment-friendly type cigarette case package transfer paper, as shown in Figs. 1-2, including transfer paper ontology 1, the transfer paper ontology
1 includes on 11 1 surface of center paper layer 11 and centrally disposed paper layer and is fixed with center paper layer 1 by shifting glue laminating
The first internal lining paper 12, and be arranged on 12 surface of the first internal lining paper and it is solid by transfer glue laminating with the first internal lining paper 12
The first fixed transfer aluminium layer 13；First internal lining paper 12 is provided with 11 joint place of center paper layer for nibbling with center paper layer 11
The the first sawtooth portion 121 closed.Another surface of the center paper layer 11 is provided with solid by transfer glue laminating with center paper layer 11
The second fixed internal lining paper 14, and be arranged on 14 surface of the second internal lining paper and with the second internal lining paper 14 by transfer glue laminating
The second fixed transfer aluminium layer 15；Second internal lining paper 14 and 11 joint place of center paper layer be provided with for center paper layer 11
Second sawtooth portion 141 of engagement.The inside of the center paper layer 11 is additionally provided with one layer of web 111.In this experimental example, institute
It is set in sawtooth installing on two surfaces for stating center paper layer 11.The web 111 is by shredded coconut meat web.
The center paper layer 11 is made of the material of following weight: 55 parts of bleached cotton starch, 44 parts of bleached reed pulp, cream
35 parts of glue, 36 parts of starch, 14 parts of sodium carboxymethylcellulose, 12 parts of sodium tripolyphosphate, 10 parts of sodium pyrophosphate, ammonium hydroxide 13, alumina silicate
7 parts of cotton, 13 parts of alumina powder, 17 parts of cellulose acetate resin, 13.5 parts of polypropylene wax, 7 parts of titanate coupling agent, PPE are wet strong
6 parts and 12 parts of antibacterial agent of agent.
A kind of preparation method of the pressure resistance without picking center paper layer, comprising the following steps:
1) it takes 55 parts and 44 parts of bleached reed pulp of bleached cotton starch to be put into pulper, is run at high speed, will be bleached by pulper
Cotton pulp and bleached reed pulp are beaten, and mixed serum is made, then pours into steam stove mixed serum obtained, is then heated to
340 DEG C, so that slurries boil, it is spare；
2) 14 parts of sodium carboxymethylcellulose, 12 parts of sodium tripolyphosphate and 10 parts of sodium pyrophosphate is taken to be added to step 1) obtained
In slurries, slurries ferment by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate fluffy, enhances pulp fibers
Pliability, slurries obtained are then washed and starched into machine by pressurized screen and vacuum and carry out washing and screening, obtaining concentration is 24%
Slurries are cleaned, it is spare；
3) it takes 35 parts of latex, 17 parts of cellulose acetate resin and 13.5 parts of polypropylene wax to be put into reaction kettle and heats 25min,
So that its temperature is reached 280 DEG C, while starting the blender in reaction kettle and 37min is stirred with the speed of 45r/pm, so that latex, vinegar
Mixed glue solution is made after high-temperature fusion in acid cellulose resin and polypropylene wax
4) take 36 parts of starch, 7 parts of aluminium silicate wool and 13 parts of the alumina powder sieves using 50 mesh to the resulting powder of grinding
It is screened, the powder of 50 mesh or more is isolated, filler is made, then filler obtained is added in agitator, by weight
The ratio of 3:4 adds water, then starts blender and is mixed above-mentioned material with water with the revolving speed of 55r/min, filler slurries are made,
It is spare；
5) by filler slurries and titanium made from glue made from step 2) cleaning slurries obtained, step 3 and step 4)
7 parts of acid esters coupling agent, 6 parts of PPE wet strength agent and 12 parts of antibacterial agent are transferred in agitator, are then starched cleaning by blender
Liquid, glue and filler slurries are stirred evenly with titanate coupling agent, PPE wet strength agent and antibacterial agent with the revolving speed of 25r/min, are made
Body paper slurries, are then held with boiler, and are heated to 215 DEG C, and the retrogradation so that body paper slurries are heated then starches body paper obtained
Liquid pours into pressure cooker, and is 55KPa by the pressure set of pressure cooker, is then heated to paper pulp raw material in the pressure of setting
230 DEG C, so that body paper slurries are reacted with ingredients at high temperature, enhance the function of body paper slurries, it is spare；
6) it takes 13 parts of ammonium hydroxide to be added in body paper slurries made from step 5), is removed bubble in body paper slurries by ammonium hydroxide
It removes, it is spare；
7) body paper slurries made from step 6) are subjected to copy paper, are scooped up paper pulp by scooping slurry, and by control scoop slurry with
The frequency for swinging 24 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out and reach thickness
The requirement of uniform good toughness, is then squeezed the copy paper on gauze by extruder, so that the moisture in copy paper squeezes out
And form, last copy paper after extruding be placed into low temp dryer with 19 DEG C of low temperature dried to get.
In the present embodiment.The antibacterial agent is chitin, mustard, castor oil and the mixture of horseradish.
Experimental example
Following table is the technical indicator of the center paper layer of the application:
According to the data of upper table, center paper layer of the invention is compared with paper layer, and records data.
Experimental products: it using center paper layer as a control group one made from starch mixing wood skin slurry, is mixed using latex
The control group two the most of center paper layer made from wood skin slurry, the center paper layer of the application is as experimental group, and insides in three groups
Layer compares, and records specific value, as shown in the table:
In conjunction with upper table, compare control group one, control group two and experimental group, center paper layer of the invention as experimental group,
Measured data are superior to control group one and control group two, therefore, compared to than control group one and control group two, in the application
Transfer paper made from insides layer has excellent mechanical strength and thermal stability.
Therefore, above-mentioned preparation method and preparation is being combined to be formulated center obtained paper layer, so that manufactured transfer paper is more
It is suitable as tobacco package paper.
The technology of the present invention effect major embodiment is in the following areas: the transfer paper by two surfaces on the paper layer of center successively
The first internal lining paper, the first transfer aluminium layer, the second internal lining paper and the second transfer aluminium layer are covered, transfer paper obtained can be made to have excellent
Good mechanical strength and thermal stability, can be used as tobacco package paper；In addition, center paper layer is with bleached cotton starch and bleached reed pulp
As main fibrous material, depigmentation is bleached and washed and starched by sodium carboxymethylcellulose, sodium tripolyphosphate and sodium pyrophosphate
And impurity, mix the filler as made from latex, starch, aluminium silicate wool and alumina powder and cellulose acetate resin and poly- third
Alkene wax is improved the toughness of center obtained paper layer, finally ammonium hydroxide is combined to defoam, titanate esters by melting glue obtained
Coupling agent, PPE wet strength agent and antibacterial agent further increase the excellent performance of center paper layer, are applicable in its transfer paper obtained more
In tobacco package.
Certainly, above is representative instance of the invention, and in addition to this, the present invention can also have other a variety of specific implementations
Mode, all technical solutions formed using equivalent substitution or equivalent transformation, is all fallen within the scope of protection of present invention.
Claims (7)
1. a kind of environment-friendly type cigarette case package transfer paper, including transfer paper ontology, it is characterised in that: the transfer paper ontology includes
The first internal lining paper on one surface of center paper layer and centrally disposed paper layer and that fixation is bonded with center paper layer, and setting exist
First transfer aluminium layer on first internal lining paper surface and that fixation is bonded with the first internal lining paper；Another table of the center paper layer
Face, which is provided with, is bonded the second fixed internal lining paper with center paper layer, and be arranged on the second internal lining paper surface and with second in
The second fixed transfer aluminium layer of lining paper fitting.
2. a kind of environment-friendly type cigarette case package transfer paper as described in claim 1, it is characterised in that: the two of the center paper layer
It is set in sawtooth installing on surface.
3. a kind of environment-friendly type cigarette case package transfer paper as described in claim 1, it is characterised in that: the web is by shredded coconut meat
Web.
4. a kind of environment-friendly type cigarette case package transfer paper as described in claim 1, it is characterised in that: first internal lining paper with
Center paper layer joint place is provided with the first sawtooth portion for engaging with center paper layer.
5. a kind of environment-friendly type cigarette case package transfer paper as described in claim 1, it is characterised in that: second internal lining paper with
Center paper layer joint place is provided with the second sawtooth portion for engaging with center paper layer.
6. a kind of environment-friendly type cigarette case package transfer paper as described in claim 1, it is characterised in that: the center paper layer by with
The material of lower weight is made: 50-60 parts of bleached cotton starch, 40-48 parts of bleached reed pulp, 30-40 parts of latex, starch 30-42
Part, 11-17 parts of sodium carboxymethylcellulose, 9-15 parts of sodium tripolyphosphate, 8-12 parts of sodium pyrophosphate, 10-16 parts of ammonium hydroxide, aluminium silicate wool
5-9 parts, 11-15 parts of alumina powder, 14-20 parts of cellulose acetate resin, 12-15 parts of polypropylene wax, titanate coupling agent 6-8
Part, 5-7 parts of PPE wet strength agent and 10-14 parts of antibacterial agent.
7. a kind of environment-friendly type cigarette case package transfer paper as claimed in claim 6, it is characterised in that: the antibacterial agent is crust
The mixture of one or more of element, mustard, castor oil and horseradish.