CN106758533A - A kind of abrasion-proof stainless steel lining paper and preparation method thereof - Google Patents
A kind of abrasion-proof stainless steel lining paper and preparation method thereof Download PDFInfo
- Publication number
- CN106758533A CN106758533A CN201611144905.1A CN201611144905A CN106758533A CN 106758533 A CN106758533 A CN 106758533A CN 201611144905 A CN201611144905 A CN 201611144905A CN 106758533 A CN106758533 A CN 106758533A
- Authority
- CN
- China
- Prior art keywords
- parts
- stainless steel
- steel lining
- lining paper
- enzyme
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of abrasion-proof stainless steel lining paper, it is made up of the raw material of following weight portion, including 90 160 parts of stainless steel lining paper waste material, 70 90 parts of long fibre sulfate wood pulp, 70 90 parts of softwood pulp, 20 34 parts of silicon disulfide, 33 39 parts of sodium metasilicate, 31 37 parts of potassium silicate, 19 27 parts of alumina silicate, 10 16 parts of silicic acid, 30 40 parts of ceramic powder, 15 19 parts of schmigel, 20 36 parts of polytetrafluoro emulsion, 79 parts of cellulase, 79 parts of hemicellulase, 10 16 parts of pectase, 11 17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9 13 parts of enzyme of acid；This kind of abrasion-proof stainless steel lining paper has the advantages that wear-resisting, intensity is high, tear-resistant and surface is smooth.
Description
Technical field
The present invention relates to a kind of abrasion-proof stainless steel lining paper and preparation method thereof.
Background technology
Stainless steel lining paper is that, in recent years as domestic and international stainless steel industry is greatly developed, progressively matched is protection
Stainless-steel sheet product quality and a kind of new special industrial paper for padding.Stainless steel lining paper is according to stainless steel production technology
Difference can be divided into：High temperature resistant stainless steel lining paper suitable for hot pressing stainless steel plate and suitable for the common stainless of cold rolled stainless steel sheet
Steel lining paper.In July, 2006 learns that the country has been provided with the producer of stainless steel lining paper at present, but is provided not through sci-tech novelty-search
Rust steel lining paper major part is that, from external import, domestic development and production about stainless steel lining paper also has document report, but compare
It is few.Such as a kind of high temperature resistant stainless steel lining paper that Henan Provincial Light Industrial Sciences Inst. develops, Jiangsu Xin great paper industry group is to common
Produced problem has carried out research report in the production technology of stainless steel lining paper and production.
Stainless steel lining paper be in cold rolling high-grade stainless steel steel plate, in coiling process in order to prevent stainless steel plate between
A kind of dedicated paper for rubbing and padding.In stainless-steel sheet production process, because the milling train for running at high speed pulling force aborning
Intensity is big, produces certain frictional force, the smooth of stainless steel product, refraction, brightness is had a huge impact, particularly in volume
After plate, due to temperature, the change of humidity, easily make paper aging, simultaneously because lining paper tensile strength and smoothness etc. are referred mainly to
Mark is nonconforming, and in debatching, often because the phenomenons such as lining paper tear, breakage occur, directly contact is produced between causing steel plate
Friction, influences product quality.Therefore, stainless-steel sheet producer refers to tensile strength, smoothness, cleannes of stainless steel lining paper etc.
Mark requires more and more higher.
Therefore, in sum, there is not wear-resisting, low intensity, be easily torn and surface in existing abrasion-proof stainless steel lining paper
Not enough smooth the problem for causing serious wear.
The content of the invention
In view of this, it is an object of the present invention to provide the abrasion-proof stainless steel that a kind of wear-resisting, intensity is high, tear-resistant and surface is smooth
Lining paper.
In order to solve the above-mentioned technical problem, the technical scheme is that：A kind of abrasion-proof stainless steel lining paper, by following weight
The raw material of part is made, including 90-160 parts of stainless steel lining paper waste material, 70-90 parts of long fibre sulfate wood pulp, softwood pulp 70-90
Part, silicon disulfide 20-34 parts, sodium metasilicate 33-39 parts, potassium silicate 31-37 parts, alumina silicate 19-27 parts, silicic acid 10-16 parts, ceramics
Powder 30-40 parts, schmigel 15-19 parts, 20-36 parts of polytetrafluoro emulsion, cellulase 7-9 parts, hemicellulase 7-9 parts, pectin
Enzyme 10-16 parts, 11-17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9-13 parts of enzyme of acid.
Further, the abrasion-proof stainless steel lining paper is made up of the raw material of following weight portion, including stainless steel lining paper waste material
160 parts, 70 parts of long fibre sulfate wood pulp, 70 parts of softwood pulp, 20 parts of silicon disulfide, 33 parts of sodium metasilicate, 31 parts of potassium silicate, silicon
19 parts of sour aluminium, 10 parts of silicic acid, 30 parts of ceramic powder, 15 parts of schmigel, 20 parts of polytetrafluoro emulsion, 7 parts of cellulase, hemicellulase
7 parts, 10 parts of pectase, 11 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9 parts of enzyme of acid.
Further, the abrasion-proof stainless steel lining paper is made up of the raw material of following weight portion, including stainless steel lining paper waste material
90 parts, 90 parts of long fibre sulfate wood pulp, 90 parts of softwood pulp, 34 parts of silicon disulfide, 39 parts of sodium metasilicate, 37 parts of potassium silicate, silicon
27 parts of sour aluminium, 16 parts of silicic acid, 40 parts of ceramic powder, 19 parts of schmigel, 36 parts of polytetrafluoro emulsion, 9 parts of cellulase, hemicellulase
9 parts, 16 parts of pectase, 17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 13 parts of enzyme of acid.
Further, the abrasion-proof stainless steel lining paper is made up of the raw material of following weight portion, including stainless steel lining paper waste material
125 parts, 80 parts of long fibre sulfate wood pulp, 80 parts of softwood pulp, 27 parts of silicon disulfide, 36 parts of sodium metasilicate, 34 parts of potassium silicate, silicon
23 parts of sour aluminium, 13 parts of silicic acid, 35 parts of ceramic powder, 17 parts of schmigel, 28 parts of polytetrafluoro emulsion, 8 parts of cellulase, hemicellulase
8 parts, 13 parts of pectase, 14 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 11 parts of enzyme of acid.
The invention solves the problems that another technical problem be that a kind of preparation method of abrasion-proof stainless steel lining paper is provided, it is including following
Step：
1) 90-160 parts of stainless steel lining paper waste material is taken as raw material, is crushed by shredder and put into and added water in fermentation vat leaching
Bubble 3-6 hour so that stainless steel lining paper water suction softens, the stainless steel lining paper that then will soften is such as in Bellmer, to stainless steel
Lining paper is bleached, and then washing and starching machine by pressurized screen and vacuum carries out washing and screening, obtains the body paper that concentration is 16~18%
Slurries, it is standby；
2) by step 1) obtained in body paper slurries agitator hold, then add 70-90 parts of long fibre sulfate wood pulp
With softwood pulp 70-90 parts, and start mixer and operated with the rotating speed of 55r/min so that long fibre sulfate wood pulp and needle
Wood pulp is well mixed with body paper slurries, supplements the string of body paper slurries, standby；
3) by step 2) obtained in body paper slurries pour into steam stove, then add 20-36 parts of polytetrafluoro emulsion, cellulase
7-9 parts, hemicellulase 7-9 parts, pectase 10-16 parts, 11-17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside acid enzyme
9-13 parts, stirred with the rotating speed of 45r/min by mixer so that polytetrafluoro emulsion, cellulase, hemicellulase, pectin
Enzyme, poly galactolipin thuja acid enzyme and alpha-galactoside acid enzyme are well mixed with body paper slurries, then cause steam stove by heating
Temperature is increased to 300-380 DEG C so that slurries boil, standby；
4) silicon disulfide 20-34 parts, sodium metasilicate 33-39 parts, potassium silicate 31-37 parts, alumina silicate 19-27 parts, silicic acid 10- are taken
16 parts, ceramic powder 30-40 parts and schmigel 15-19 parts are added in agitator, by weight 1:4 ratio addition water, then
Start mixer to mix above-mentioned material with water with the rotating speed of 65r/min, filler is obtained, it is standby；
5) by step 4) obtained in slurries be added to step 3) in it is obtained cleaning slurries in, then by mixer will starch
Liquid is stirred with mixed pulp with the rotating speed of 35r/min, and body paper slurries are obtained, and obtained body paper slurries are poured into pressure cooker
It is interior, and be 50KPa by the pressure set of pressure cooker, paper pulp raw material is then heated to 170-250 DEG C in the pressure of setting, make
Obtain body paper slurries to be reacted with ingredients at high temperature, strengthen the function of body paper slurries, it is standby；
6) by step 5) obtained in body paper slurries carry out copy paper, paper pulp is scooped up by scooping oar, and by control scoop oar with
The frequency for swinging 30 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out to reach thickness
The requirement of uniform good toughness, is then extruded the copy paper on gauze by extruder so that the moisture extrusion in copy paper
And be molded, the copy paper after finally extruding is placed into low temp dryer is dried with 12-26 DEG C of low temperature, standby；
7) by step 6) obtained in copy paper cut by cutter by specification, obtain final product.
The technology of the present invention effect major embodiment is in the following areas：By with stainless steel lining paper waste material as primary raw material, adding
Long fibre sulfate wood pulp and softwood pulp and combine silicon disulfide, sodium metasilicate, silicon as the string added material of raw material
Sour potassium, alumina silicate, silicic acid, ceramic powder, schmigel, polytetrafluoro emulsion, cellulase, hemicellulase, pectase, poly gala
Glycuronide enzyme and the alpha-galactoside acid material such as enzyme, are obtained with wear-resisting, intensity is high, tear-resistant and the features such as smooth surface
Stainless steel lining paper, can when in use avoid being subject to the extruding and tear of steel plate, simultaneously because surface is smooth, can reduce
The degree of wear of lining paper, and then increase the service life.
Specific embodiment
Embodiment 1
A kind of abrasion-proof stainless steel lining paper, is made up of the raw material of following weight portion, including 160 parts of stainless steel lining paper waste material, length
70 parts of fiber sulfuric acid salt wood pulp, 70 parts of softwood pulp, 20 parts of silicon disulfide, 33 parts of sodium metasilicate, 31 parts of potassium silicate, alumina silicate 19
Part, 10 parts of silicic acid, 30 parts of ceramic powder, 15 parts of schmigel, 20 parts of polytetrafluoro emulsion, 7 parts of cellulase, 7 parts of hemicellulase, fruit
10 parts of glue enzyme, 11 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9 parts of enzyme of acid.
A kind of preparation method of abrasion-proof stainless steel lining paper, comprises the following steps：
1) 160 parts of stainless steel lining paper waste material is taken as raw material, is crushed and is put into by shredder and 3 are soaked in fermentation vat
Hour so that stainless steel lining paper water suction softens, and the stainless steel lining paper that then will soften to stainless steel lining paper as in Bellmer, entered
Row bleaching, then washing and starching machine by pressurized screen and vacuum carries out washing and screening, obtains the body paper slurries that concentration is 16%, standby；
2) by step 1) obtained in body paper slurries agitator hold, then add 70 parts of long fibre sulfate wood pulp and pin
70 parts of leaf wood pulp, and start mixer with the rotating speed running of 55r/min so that long fibre sulfate wood pulp and softwood pulp and original
Pulp liquor is well mixed, and supplements the string of body paper slurries, standby；
3) by step 2) obtained in body paper slurries pour into steam stove, then add 20 parts of polytetrafluoro emulsion, cellulase 7
Part, 7 parts of hemicellulase, 10 parts of pectase, 11 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9 parts of enzyme of acid, by stirring
Machine is stirred with the rotating speed of 45r/min so that polytetrafluoro emulsion, cellulase, hemicellulase, pectase, poly galactoside
Sour enzyme and alpha-galactoside acid enzyme are well mixed with body paper slurries, and the temperature for then causing steam stove by heating is increased to 300
DEG C so that slurries boil, standby；
4) 20 parts of silicon disulfide, 33 parts of sodium metasilicate, 31 parts of potassium silicate, 19 parts of alumina silicate, 10 parts of silicic acid, 30 parts of ceramic powder are taken
15 parts are added in agitator with schmigel, by weight 1:4 ratio addition water, then starts mixer with 65r/min's
Rotating speed mixes above-mentioned material with water, and filler is obtained, standby；
5) by step 4) obtained in slurries be added to step 3) in it is obtained cleaning slurries in, then by mixer will starch
Liquid is stirred with mixed pulp with the rotating speed of 35r/min, and body paper slurries are obtained, and obtained body paper slurries are poured into pressure cooker
It is interior, and be 50KPa by the pressure set of pressure cooker, paper pulp raw material is then heated to 170 DEG C in the pressure of setting so that former
Pulp liquor reacts with ingredients at high temperature, strengthens the function of body paper slurries, standby；
6) by step 5) obtained in body paper slurries carry out copy paper, paper pulp is scooped up by scooping oar, and by control scoop oar with
The frequency for swinging 30 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out to reach thickness
The requirement of uniform good toughness, is then extruded the copy paper on gauze by extruder so that the moisture extrusion in copy paper
And be molded, the copy paper after finally extruding is placed into low temp dryer is dried with 12 DEG C of low temperature, standby；
7) by step 6) obtained in copy paper cut by cutter by specification, obtain final product.
Embodiment 2
A kind of abrasion-proof stainless steel lining paper, is made up of the raw material of following weight portion, including 90 parts of stainless steel lining paper waste material, fibre long
Dimension 90 parts of sulfate wood pulp, 90 parts of softwood pulp, 34 parts of silicon disulfide, 39 parts of sodium metasilicate, 37 parts of potassium silicate, 27 parts of alumina silicate,
16 parts of silicic acid, 40 parts of ceramic powder, 19 parts of schmigel, 36 parts of polytetrafluoro emulsion, 9 parts of cellulase, 9 parts of hemicellulase, pectin
16 parts of enzyme, 17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 13 parts of enzyme of acid.
A kind of preparation method of abrasion-proof stainless steel lining paper, comprises the following steps：
1) 90- parts of stainless steel lining paper waste material is taken as raw material, is crushed and is put into by shredder and 6 are soaked in fermentation vat
Hour so that stainless steel lining paper water suction softens, and the stainless steel lining paper that then will soften to stainless steel lining paper as in Bellmer, entered
Row bleaching, then washing and starching machine by pressurized screen and vacuum carries out washing and screening, obtains the body paper slurries that concentration is 18%, standby；
2) by step 1) obtained in body paper slurries agitator hold, then add 90 parts of long fibre sulfate wood pulp and pin
90 parts of leaf wood pulp, and start mixer with the rotating speed running of 55r/min so that long fibre sulfate wood pulp and softwood pulp and original
Pulp liquor is well mixed, and supplements the string of body paper slurries, standby；
3) by step 2) obtained in body paper slurries pour into steam stove, then add 36 parts of polytetrafluoro emulsion, cellulase 9
Part, 9 parts of hemicellulase, 16 parts of pectase, 17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 13 parts of enzyme of acid, by stirring
Mix machine to be stirred with the rotating speed of 45r/min so that polytetrafluoro emulsion, cellulase, hemicellulase, pectase, poly galactolipin
Thuja acid enzyme and alpha-galactoside acid enzyme are well mixed with body paper slurries, and the temperature for then causing steam stove by heating is increased to 380
DEG C so that slurries boil, standby；
4) 34 parts of silicon disulfide, 39 parts of sodium metasilicate, -37 parts of potassium silicate, 27 parts of alumina silicate, 16 parts of silicic acid, ceramic powder 40 are taken
19 parts of part and schmigel are added in agitator, by weight 1:4 ratio addition water, then starts mixer with 65r/min
Rotating speed above-mentioned material is mixed with water, be obtained filler, it is standby；
5) by step 4) obtained in slurries be added to step 3) in it is obtained cleaning slurries in, then by mixer will starch
Liquid is stirred with mixed pulp with the rotating speed of 35r/min, and body paper slurries are obtained, and obtained body paper slurries are poured into pressure cooker
It is interior, and be 50KPa by the pressure set of pressure cooker, paper pulp raw material is then heated to 250 DEG C in the pressure of setting so that former
Pulp liquor reacts with ingredients at high temperature, strengthens the function of body paper slurries, standby；
6) by step 5) obtained in body paper slurries carry out copy paper, paper pulp is scooped up by scooping oar, and by control scoop oar with
The frequency for swinging 30 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out to reach thickness
The requirement of uniform good toughness, is then extruded the copy paper on gauze by extruder so that the moisture extrusion in copy paper
And be molded, the copy paper after finally extruding is placed into low temp dryer is dried with 26 DEG C of low temperature, standby；
7) by step 6) obtained in copy paper cut by cutter by specification, obtain final product.
Embodiment 3
A kind of abrasion-proof stainless steel lining paper, is made up of the raw material of following weight portion, including 125 parts of stainless steel lining paper waste material, length
80 parts of fiber sulfuric acid salt wood pulp, 80 parts of softwood pulp, 27 parts of silicon disulfide, 36 parts of sodium metasilicate, 34 parts of potassium silicate, alumina silicate 23
Part, 13 parts of silicic acid, 35 parts of ceramic powder, 17 parts of schmigel, 28 parts of polytetrafluoro emulsion, 8 parts of cellulase, 8 parts of hemicellulase, fruit
13 parts of glue enzyme, 14 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 11 parts of enzyme of acid.
A kind of preparation method of abrasion-proof stainless steel lining paper, comprises the following steps：
1) 125 parts of stainless steel lining paper waste material is taken as raw material, is crushed and is put into by shredder and 5 are soaked in fermentation vat
Hour so that stainless steel lining paper water suction softens, and the stainless steel lining paper that then will soften to stainless steel lining paper as in Bellmer, entered
Row bleaching, then washing and starching machine by pressurized screen and vacuum carries out washing and screening, obtains the body paper slurries that concentration is 17%, standby；
2) by step 1) obtained in body paper slurries agitator hold, then add 80 parts of long fibre sulfate wood pulp and pin
80 parts of leaf wood pulp, and start mixer with the rotating speed running of 55r/min so that long fibre sulfate wood pulp and softwood pulp and original
Pulp liquor is well mixed, and supplements the string of body paper slurries, standby；
3) by step 2) obtained in body paper slurries pour into steam stove, then add 20-36 parts of polytetrafluoro emulsion, cellulase
8 parts, 8 parts of hemicellulase, 13 parts of pectase, 14 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 11 parts of enzyme of acid, by stirring
Mix machine to be stirred with the rotating speed of 45r/min so that polytetrafluoro emulsion, cellulase, hemicellulase, pectase, poly galactolipin
Thuja acid enzyme and alpha-galactoside acid enzyme are well mixed with body paper slurries, and the temperature for then causing steam stove by heating is increased to
It is 300-380 DEG C so that slurries boil, standby；
4) 27 parts of silicon disulfide, 36 parts of sodium metasilicate, 34 parts of potassium silicate, 23 parts of alumina silicate, 13 parts of silicic acid, 35 parts of ceramic powder are taken
17 parts are added in agitator with schmigel, by weight 1:4 ratio addition water, then starts mixer with 65r/min's
Rotating speed mixes above-mentioned material with water, and filler is obtained, standby；
5) by step 4) obtained in slurries be added to step 3) in it is obtained cleaning slurries in, then by mixer will starch
Liquid is stirred with mixed pulp with the rotating speed of 35r/min, and body paper slurries are obtained, and obtained body paper slurries are poured into pressure cooker
It is interior, and be 50KPa by the pressure set of pressure cooker, paper pulp raw material is then heated to 210 DEG C in the pressure of setting so that former
Pulp liquor reacts with ingredients at high temperature, strengthens the function of body paper slurries, standby；
6) by step 5) obtained in body paper slurries carry out copy paper, paper pulp is scooped up by scooping oar, and by control scoop oar with
The frequency for swinging 30 times per minute uniformly spreads paper pulp out on gauze, can effectively control the copy paper that paper pulp is spread out to reach thickness
The requirement of uniform good toughness, is then extruded the copy paper on gauze by extruder so that the moisture extrusion in copy paper
And be molded, the copy paper after finally extruding is placed into low temp dryer is dried with 19 DEG C of low temperature, standby；
7) by step 6) obtained in copy paper cut by cutter by specification, obtain final product.
Experimental example
Following table is the technical indicator of stainless steel lining paper：
Above table is the technical requirements of stainless steel lining paper, according to the data of upper table, by abrasion-proof stainless steel of the invention
Lining paper is contrasted with other stainless steel lining papers, and record data.
Experimental products：Served as a contrast using the abrasion-proof stainless steel of common stainless steel lining paper, special stainless steel lining paper and the application
Paper is compared, and records concrete numerical value, as shown in the table：
With reference to upper table, the abrasion-proof stainless steel lining of common stainless steel lining paper, special stainless steel lining paper and the application is contrasted
Paper, abrasion-proof stainless steel lining paper all technical only of the invention reaches the standard of high-class product, therefore, it is stainless compared to common
Steel lining paper, special stainless steel lining paper, abrasion-proof stainless steel lining paper of the invention can more protrude that wear-resisting, intensity is high, tear-resistant and table
The features such as face smooths, the degree of wear of lining paper can be reduced by above feature, and then is increased the service life.
The technology of the present invention effect major embodiment is in the following areas：By with stainless steel lining paper waste material as primary raw material, adding
Long fibre sulfate wood pulp and softwood pulp and combine silicon disulfide, sodium metasilicate, silicon as the string added material of raw material
Sour potassium, alumina silicate, silicic acid, ceramic powder, schmigel, polytetrafluoro emulsion, cellulase, hemicellulase, pectase, poly gala
Glycuronide enzyme and the alpha-galactoside acid material such as enzyme, are obtained with wear-resisting, intensity is high, tear-resistant and the features such as smooth surface
Stainless steel lining paper, can when in use avoid being subject to the extruding and tear of steel plate, simultaneously because surface is smooth, can reduce
The degree of wear of lining paper, and then increase the service life.
Certainly, it is more than representative instance of the invention, in addition, the present invention can also have other various specific implementations
The technical scheme that mode, all use equivalents or equivalent transformation are formed, all falls within the scope of protection of present invention.
Claims (4)
1. a kind of abrasion-proof stainless steel lining paper, it is characterised in that：It is made up of the raw material of following weight portion, including stainless steel lining paper waste material
90-160 parts, 70-90 parts of long fibre sulfate wood pulp, softwood pulp 70-90 parts, silicon disulfide 20-34 parts, sodium metasilicate 33-39
Part, potassium silicate 31-37 parts, alumina silicate 19-27 parts, silicic acid 10-16 parts, ceramic powder 30-40 parts, schmigel 15-19 parts, polytetrafluoro
Emulsion 20-36 parts, cellulase 7-9 parts, hemicellulase 7-9 parts, pectase 10-16 parts, poly galactolipin thuja acid enzyme 11-17
Part and alpha-galactoside 9-13 parts of enzyme of acid.
2. a kind of abrasion-proof stainless steel lining paper as claimed in claim 1, it is characterised in that：It is made up of the raw material of following weight portion,
Including 160 parts of stainless steel lining paper waste material, 70 parts of long fibre sulfate wood pulp, 70 parts of softwood pulp, 20 parts of silicon disulfide, sodium metasilicate
33 parts, 31 parts of potassium silicate, 19 parts of alumina silicate, 10 parts of silicic acid, 30 parts of ceramic powder, 15 parts of schmigel, 20 parts of polytetrafluoro emulsion, fiber
7 parts of plain enzyme, 7 parts of hemicellulase, 10 parts of pectase, 11 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 9 parts of enzyme of acid.
3. a kind of abrasion-proof stainless steel lining paper as claimed in claim 1, it is characterised in that：It is made up of the raw material of following weight portion,
Including 90 parts of stainless steel lining paper waste material, 90 parts of long fibre sulfate wood pulp, 90 parts of softwood pulp, 34 parts of silicon disulfide, sodium metasilicate
39 parts, 37 parts of potassium silicate, 27 parts of alumina silicate, 16 parts of silicic acid, 40 parts of ceramic powder, 19 parts of schmigel, 36 parts of polytetrafluoro emulsion, fiber
9 parts of plain enzyme, 9 parts of hemicellulase, 16 parts of pectase, 17 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 13 parts of enzyme of acid.
4. a kind of abrasion-proof stainless steel lining paper as claimed in claim 1, it is characterised in that：It is made up of the raw material of following weight portion,
Including 125 parts of stainless steel lining paper waste material, 80 parts of long fibre sulfate wood pulp, 80 parts of softwood pulp, 27 parts of silicon disulfide, sodium metasilicate
36 parts, 34 parts of potassium silicate, 23 parts of alumina silicate, 13 parts of silicic acid, 35 parts of ceramic powder, 17 parts of schmigel, 28 parts of polytetrafluoro emulsion, fiber
8 parts of plain enzyme, 8 parts of hemicellulase, 13 parts of pectase, 14 parts of poly galactolipin thuja acid enzyme and alpha-galactoside 11 parts of enzyme of acid.