CN110157199A - A kind of alginate gelatin hydrogel preparation method - Google Patents
A kind of alginate gelatin hydrogel preparation method Download PDFInfo
- Publication number
- CN110157199A CN110157199A CN201910414113.9A CN201910414113A CN110157199A CN 110157199 A CN110157199 A CN 110157199A CN 201910414113 A CN201910414113 A CN 201910414113A CN 110157199 A CN110157199 A CN 110157199A
- Authority
- CN
- China
- Prior art keywords
- solution
- alginate
- gelatin
- phosphate
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of alginate gelatin hydrogel preparation methods, the raw material for preparing hydrogel includes: gelatin, ethylenediamine, concentrated hydrochloric acid, carbodiimide, phosphate solution, oxidized sodium alginate, phosphate buffered saline solution, deionized water, described to prepare water-setting gluing method as follows: gelatin passes through phosphate, ethylenediamine carries out reacting obtained modified gelatin, quantitative oxidized sodium alginate and phosphate buffered saline solution are mixed to get alginate solution, it takes a certain amount of modified gelatin to be dissolved in deionized water again and obtains modified gelatin solution, then the modified gelatin solution of 10% alginate solution and 20% is mixed after being stirred 15s, it is pushed it into tissue culture plate using double syringe, it is placed in gel reaction 10min in 37 DEG C of insulating boxs, the present invention is to pass through periodic acid by oxidized sodium alginate Sodium is modified, so that oxidized sodium alginate has good degradation property, to solve the problems, such as that the degradation speed of previous seaweed salt itself is slow.
Description
Technical field
The present invention relates to hydrogel field more particularly to a kind of alginate gelatin hydrogel preparation methods.
Background technique
Sodium alginate and gelatin are natural biologic materials, because its is cheap, safe and reliable and biocompatibility is good,
It is widely used in organizational project and related fields, however the degradation speed of seaweed salt itself is slow, and hydrogel is water-soluble
Difference, these defects limit application of the seaweed salt in organizational project, and the property of easy gel is hydrogel under gelatin room temperature
Operation in preparation process brings certain trouble, therefore, it is proposed that a kind of alginate gelatin hydrogel preparation method.
Summary of the invention
The purpose of the present invention is to provide a kind of alginate gelatin hydrogel preparation method, solves institute in background technique
The problem of proposition.
To achieve the above object, the invention provides the following technical scheme: a kind of alginate gelatin hydrogel preparation method,
The raw material for preparing hydrogel includes: gelatin, ethylenediamine, concentrated hydrochloric acid, carbodiimide, phosphate solution, oxidation seaweed
Sour sodium, phosphate buffered saline solution, deionized water, described to prepare water-setting gluing method as follows: gelatin is carried out by phosphate, ethylenediamine
It reacts and modified gelatin is made, quantitative oxidized sodium alginate and phosphate buffered saline solution are mixed to get alginate solution, then
It takes a certain amount of modified gelatin to be dissolved in deionized water and obtains modified gelatin solution, then by 10% alginate solution and 20%
After the mixing of modified gelatin solution is stirred 15s, is pushed it into tissue culture plate using double syringe, be placed in 37 DEG C of constant temperature
Gel reaction 10min in case.
As a kind of preferred embodiment of the invention, the modified gelatin the preparation method is as follows: by 5g Gelatin in
In 0.1M phosphate solution, after being completely dissolved, 14g ethylenediamine is added, is carried out using magnetic agitation uniformly mixed, the dense of 6M is added
Then to 5 2.675 carbodiimides are added, then be settled to 250ml with phosphate solution, at 37 DEG C in salt acid for adjusting pH value
1h is reacted in insulating box, is cooled to room temperature, product is fitted into bag filter, is dialysed 3 days, is changed daily water 4 times, by it after having dialysed
It imports in frosting ware, is put into low temperature refrigerator pre-freeze for 24 hours, then be dried.
As a kind of preferred embodiment of the invention, the alginate solution is the preparation method is as follows: by quantitative oxygen
Then the phosphate buffered saline solution that change sodium alginate is dissolved in pH most 7.4 places it in 37 using magnetic agitation to being completely dissolved
DEG C insulating box in place 0.5h.
As a kind of preferred embodiment of the invention, the modified gelatin solution manufacturing method is as follows: quantitative is changed
Property gelatin is dissolved in deionized water, is prepared certain density solution, is first placed it in 50 DEG C of electric heating constant-temperature blowing drying box,
It is completely dissolved to it, goes in 37 DEG C of insulating box and place 0.5h.
As a kind of preferred embodiment of the invention, the phosphate solution passes through sodium dihydrogen phosphate and sodium hydroxide tune
Be made, and the pH value of phosphate solution be 5.
As a kind of preferred embodiment of the invention, the oxidized sodium alginate by sodium metaperiodate to sodium alginate into
Obtained by row oxidation modification.
Compared with prior art, beneficial effects of the present invention are as follows:
1. alginate gelatin hydrogel preparation method of the invention, by oxidized sodium alginate is changed by sodium metaperiodate
Property, so that oxidized sodium alginate has good degradation property, so that the degradation speed for solving previous seaweed salt itself is slow
The problem of.
2. alginate gelatin hydrogel preparation method of the invention utilizes ethylenediamine by the catalysis of carbodiimide
Gelatin is improved, so that the part carboxyl in original gelatin is changed into amino, modified gelatin viscosity is low, water-soluble
Improve to effective.
3. alginate gelatin hydrogel preparation method of the invention, by modified gelatin and oxidized sodium alginate in room temperature
Lower reaction can form the covalent hydrogel of alkali structure, so as to reduce the potential physiological-toxicity of aldehyde radical.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
A kind of alginate gelatin hydrogel preparation method, the raw material for preparing hydrogel include: gelatin, ethylenediamine,
Concentrated hydrochloric acid, carbodiimide, phosphate solution, oxidized sodium alginate, phosphate buffered saline solution, deionized water.
Preparation method: 1, modified gelatin is completely molten the preparation method is as follows: by 5g Gelatin in 0.1M phosphate solution
14g ethylenediamine is added in Xie Hou, is carried out using magnetic agitation uniformly mixed, and the concentrated hydrochloric acid that 6M is added adjusts pH value to 5, then plus
Enter 2.675 carbodiimides, then be settled to 250ml with phosphate solution, reacts 1h in 37 DEG C of insulating box, be cooled to room
Product is fitted into bag filter by temperature, is dialysed 3 days, is changed water 4 times daily, be conducted into frosting ware, be put into low after having dialysed
Temperature refrigerator pre-freeze for 24 hours, then is dried.
2, quantitative oxidized sodium alginate the preparation method is as follows: is dissolved in the phosphorus of pH most 7.4 by the alginate solution
Then acid buffering salting liquid places it in 37 DEG C of insulating box using magnetic agitation to being completely dissolved and places 0.5h.
3, the modified gelatin solution manufacturing method is as follows: quantitative modified gelatin being dissolved in deionized water, prepares one
Determine the solution of concentration, first place it in 50 DEG C of electric heating constant-temperature blowing drying box, be completely dissolved to it, goes to 37 DEG C of constant temperature
0.5h is placed in case
4,10% alginate solution and 20% modified gelatin solution mixing be stirred 15s after, utilize double syringe will
It is pushed into tissue culture plate, is placed in gel reaction 10min in 37 DEG C of insulating boxs and alginate gelatin hydrogel is made.
Wherein, the phosphate solution is made by sodium dihydrogen phosphate and sodium hydroxide allotment, and the pH of phosphate solution
Value is 5, and the oxidized sodium alginate carries out obtained by oxidation modification sodium alginate as sodium metaperiodate.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of alginate gelatin hydrogel preparation method, it is characterised in that: the raw material for preparing hydrogel includes: bright
Glue, ethylenediamine, concentrated hydrochloric acid, carbodiimide, phosphate solution, oxidized sodium alginate, phosphate buffered saline solution, deionization
Water, described to prepare water-setting gluing method as follows: gelatin carries out reacting obtained modified gelatin by phosphate, ethylenediamine, will be quantitative
Oxidized sodium alginate and phosphate buffered saline solution are mixed to get alginate solution, then take a certain amount of modified gelatin be dissolved in from
Sub- water obtains modified gelatin solution, then mixes 10% oxidation alginate solution and 20% modified gelatin solution and carries out
After stirring 15s, is pushed it into tissue culture plate using double syringe, be placed in gel reaction 10min in 37 DEG C of insulating boxs.
2. a kind of alginate gelatin hydrogel preparation method according to claim 1, it is characterised in that: the modification is bright
Glue after being completely dissolved, is added 14g ethylenediamine, utilizes magnetic the preparation method is as follows: by 5g Gelatin in 0.1M phosphate solution
Power stirring carry out it is uniformly mixed, be added 6M concentrated hydrochloric acid adjust pH value to 5,2.675 carbodiimides are then added, then use phosphorus
Acid salt solution is settled to 250ml, reacts 1h in 37 DEG C of insulating box, is cooled to room temperature, product is fitted into bag filter, dialysis
It 3 days, changes daily water 4 times, is conducted into after having dialysed in frosting ware, is put into low temperature refrigerator pre-freeze for 24 hours, then be dried i.e.
It can.
3. a kind of alginate gelatin hydrogel preparation method according to claim 1, it is characterised in that: the alginic acid
Salting liquid utilizes magnetic force the preparation method is as follows: quantitative oxidized sodium alginate to be dissolved in the phosphate buffered saline solution of pH most 7.4
Then stirring places it in 37 DEG C of insulating box to being completely dissolved and places 0.5h.
4. a kind of alginate gelatin hydrogel preparation method according to claim 1, it is characterised in that: the modification is bright
Sol solution is prepared certain density solution, is first set the preparation method is as follows: quantitative modified gelatin is dissolved in deionized water
It in 50 DEG C of electric heating constant-temperature blowing drying box, is completely dissolved to it, goes in 37 DEG C of insulating box and place 0.5h.
5. a kind of alginate gelatin hydrogel preparation method according to claim 1, it is characterised in that: the phosphate
Solution is made by sodium dihydrogen phosphate and sodium hydroxide allotment, and the pH value of phosphate solution is 5.
6. a kind of alginate gelatin hydrogel preparation method according to claim 1, it is characterised in that: the oxidation sea
Mosanom carries out obtained by oxidation modification sodium alginate as sodium metaperiodate.