CN110157141A - A kind of intellectual water meter shell ABS composite material and preparation method thereof - Google Patents
A kind of intellectual water meter shell ABS composite material and preparation method thereof Download PDFInfo
- Publication number
- CN110157141A CN110157141A CN201910481740.4A CN201910481740A CN110157141A CN 110157141 A CN110157141 A CN 110157141A CN 201910481740 A CN201910481740 A CN 201910481740A CN 110157141 A CN110157141 A CN 110157141A
- Authority
- CN
- China
- Prior art keywords
- parts
- water meter
- composite material
- intellectual water
- meter shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of intellectual water meter shell ABS composite materials, it is grouped as by each group of following parts by weight: 30-70 parts of ABS, 0.1-0.8 parts of antioxidant, 0.1-0.8 parts of compound age resisters, 0.1-0.7 parts of UV resistant agents, 5-9 parts of boron fibres, 6-10 parts of silicon carbide fibres, 8-12 parts of polyurethane elastomers；0.04-0.09 parts of spread powders；The invention also discloses the preparation methods of the ABS composite material；The intellectual water meter shell ABS composite material has lightweight, resistance to compression, tension, corrosion-resistant, acid and alkali-resistance, impact-resistant characteristic.
Description
Technical field
The invention belongs to technical field of polymer materials more particularly to intellectual water meter shell to be led with high polymer material technology
A kind of domain, and in particular to intellectual water meter shell ABS composite material.
Background technique
In recent years, the use of ABS material was very extensive, thus also produced a large amount of ABS defective materials or substandard products, recovery article, very
After mostly bad businessman simply processes substandard products, recovery article, refills in the middle of new ABS product, product quality is caused not reach
Mark, after a period of use, cracking, corrosion phenomena such as occur, requirement of the intellectual water meter shell to material is relatively high, in property
On energy, acid and alkali-resistance, corrosion-resistant, high temperature resistant and low temperature resistant are needed, while requiring that component is light, tension, compression strength are high, existing ABS
Composite material preparation process is complex, and cost is also corresponding higher, therefore, in the case where mass production, it is desirable that prepared
Journey is simplified, and cost reduces, while not influencing service performance.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide, a kind of ingredient is less, prepares simple intelligent water
Watch shell ABS composite material has lightweight, resistance to compression, tension, corrosion-resistant, acid and alkali-resistance, impact-resistant characteristic.
To reach above-mentioned technical purpose, present invention employs a kind of intellectual water meter shell ABS composite material, the intelligent waters
The composition of raw materials of watch shell ABS composite material is grouped as by each group of following parts by weight:
30-70 parts of ABS；
0.1-0.8 parts of antioxidant；
Compound age resister 0.1-0.8 parts；
0.1-0.7 parts of UV resistant agent；
5-9 parts of boron fibre；
6-10 parts of silicon carbide fibre；
8-12 parts of polyurethane elastomer；
0.04-0.09 parts of spread powder；
As the present invention it is preferably the compound age resister is made of anti-aging machine and radical scavenger, and the two is matched
It is 8 to 2 than ratio.
The preparation method of above-mentioned intellectual water meter shell ABS composite material includes the following steps:
(1) by boron fibre, silicon carbide fibre and polyurethane elastomer be prepared into it is powdered after, be sufficiently mixed, for use；
(2) ABS, antioxidant, compound age resister, UV resistant agent, spread powder are sufficiently mixed；
(3) step 1 mixing material is put into step (2) mixing material and is sufficiently mixed；
(4) step (3) mixing material is put into vaccum-pumping equipment and is vacuumized；
(5) mixing material after vacuumizing is put into double screw extruder, the melting mixing under certain high temperature；
(6) melt is put into cooling box after cooling, is put into pelleter and carries out pelletizing operation, collected pellet is the present invention
Intellectual water meter shell ABS composite material.
In above-mentioned preparation method, in the step (1), obtained by boron fibre, silicon carbide fibre and polyurethane elastomer
Powder be 500-600 mesh.
In above-mentioned preparation method, in the step (4), the time vacuumized is 2-3 hours.
In above-mentioned preparation method, in the step (5), the mixing material after vacuumizing is put into double screw extruder and is melted
The temperature for melting mixing is 225-250 degrees Celsius.
Intellectual water meter shell obtained by above-mentioned preparation is tested for the property with ABS composite material, as a result, it has been found that the ABS is compound
Material performance indexes meets or exceeds the standard of national water reticulation system, has lightweight, resistance to compression, tension, corrosion-resistant, acidproof
Alkali, impact-resistant characteristic.
Specific embodiment
Using specific embodiment, the present invention is further illustrated below.
Embodiment 1
The composition of raw materials of a kind of intellectual water meter shell ABS composite material, the intellectual water meter shell ABS composite material is by such as
The each group of lower parts by weight is grouped as:
30 parts of ABS；
0.1 part of antioxidant；
0.1 part of compound age resister；
0.1 part of UV resistant agent；
5 parts of boron fibre；
6 parts of silicon carbide fibre；
8 parts of polyurethane elastomer；
0.04 part of spread powder；
In the present embodiment, compound age resister is made of anti-aging machine and radical scavenger, and the ratio of the two is 8
Than 2.
The preparation method of above-mentioned intellectual water meter shell ABS composite material includes the following steps:
(1) by boron fibre, silicon carbide fibre and polyurethane elastomer be prepared into it is powdered after, be sufficiently mixed, for use；In the step
In rapid, powder obtained by boron fibre, silicon carbide fibre and polyurethane elastomer is 500-600 mesh.
(2) ABS, antioxidant, compound age resister, UV resistant agent, spread powder are sufficiently mixed；
(3) step 1 mixing material is put into step (2) mixing material and is sufficiently mixed；
(4) step (3) mixing material is put into vaccum-pumping equipment and is vacuumized；In this step, the time vacuumized is 2 small
When；
(5) mixing material after vacuumizing is put into double screw extruder, the melting mixing under certain high temperature；Above-mentioned preparation side
It is 225-250 by the temperature that the mixing material after vacuumizing is put into melting mixing in double screw extruder in this step in method
Degree Celsius.
(6) melt is put into cooling box after cooling, is put into pelleter and carries out pelletizing operation, collected pellet is this
The intellectual water meter shell ABS composite material of invention.
Table 1 is the performance test results of intellectual water meter shell ABS composite material.
Embodiment 2
The composition of raw materials of a kind of intellectual water meter shell ABS composite material, the intellectual water meter shell ABS composite material is by such as
The each group of lower parts by weight is grouped as:
70 parts of ABS；
0.8 part of antioxidant；
0.8 part of compound age resister；
0.7 part of UV resistant agent；
9 parts of boron fibre；
10 parts of silicon carbide fibre；
12 parts of polyurethane elastomer；
0.09 part of spread powder；
As the present invention it is preferably the compound age resister is made of anti-aging machine and radical scavenger, and the two is matched
It is 8 to 2 than ratio.
The preparation method of above-mentioned intellectual water meter shell ABS composite material includes the following steps:
(1) by boron fibre, silicon carbide fibre and polyurethane elastomer be prepared into it is powdered after, be sufficiently mixed, for use；In the step
In rapid, powder obtained by boron fibre, silicon carbide fibre and polyurethane elastomer is 600 mesh.
(2) ABS, antioxidant, compound age resister, UV resistant agent, spread powder are sufficiently mixed；
(3) step 1 mixing material is put into step (2) mixing material and is sufficiently mixed；
(4) step (3) mixing material is put into vaccum-pumping equipment and is vacuumized；In this step, the time vacuumized is 3 small
When；
(5) mixing material after vacuumizing is put into double screw extruder, the melting mixing under certain high temperature；Above-mentioned preparation side
It is 250 Celsius by the temperature that the mixing material after vacuumizing is put into melting mixing in double screw extruder in this step in method
Degree.
(6) melt is put into cooling box after cooling, is put into pelleter and carries out pelletizing operation, collected pellet is this
The intellectual water meter shell ABS composite material of invention.
Table 2 is the performance test results of intellectual water meter shell ABS composite material.
The above is only a preferred embodiment of the present invention, it is noted that those skilled in the art are come
It says, under the premise of not departing from technical principle of the invention, several improvements and modifications, these improvements and modifications can also be made
It should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of intellectual water meter shell ABS composite material, which is characterized in that the intellectual water meter shell ABS composite material
Composition of raw materials is grouped as by each group of following parts by weight:
30-70 parts of ABS；
0.1-0.8 parts of antioxidant；
Compound age resister 0.1-0.8 parts；
0.1-0.7 parts of UV resistant agent；
5-9 parts of boron fibre；
6-10 parts of silicon carbide fibre；
8-12 parts of polyurethane elastomer；
0.04-0.09 parts of spread powder.
2. a kind of intellectual water meter shell ABS composite material as described in claim 1, which is characterized in that described compound anti-ageing
Agent is made of anti-aging machine and radical scavenger, and the ratio of the two is 8 to 2.
3. a kind of preparation method of intellectual water meter shell ABS composite material as described in claim 1, which is characterized in that packet
Include following steps:
(1) by boron fibre, silicon carbide fibre and polyurethane elastomer be prepared into it is powdered after, be sufficiently mixed, for use；
(2) ABS, antioxidant, compound age resister, UV resistant agent, spread powder are sufficiently mixed；
(3) step 1 mixing material is put into step (2) mixing material and is sufficiently mixed；
(4) step (3) mixing material is put into vaccum-pumping equipment and is vacuumized；
(5) mixing material after vacuumizing is put into double screw extruder, the melting mixing under certain high temperature；
(6) melt is put into cooling box after cooling, is put into pelleter and carries out pelletizing operation, collected pellet is the present invention
Intellectual water meter shell ABS composite material.
4. the preparation method of intellectual water meter shell ABS composite material as claimed in claim 3, which is characterized in that the step
Suddenly in (1), powder obtained by boron fibre, silicon carbide fibre and polyurethane elastomer is 500-600 mesh.
5. the preparation method of intellectual water meter shell ABS composite material as claimed in claim 3, which is characterized in that the step
Suddenly in (4), the time vacuumized is 2-3 hours.
6. the preparation method of intellectual water meter shell ABS composite material as claimed in claim 3, which is characterized in that the step
It suddenly is 225-250 degrees Celsius by the temperature that the mixing material after vacuumizing is put into melting mixing in double screw extruder in (5).