CN110154183A - A kind of preparation method of ultraviolet shielded transparent timber - Google Patents
A kind of preparation method of ultraviolet shielded transparent timber Download PDFInfo
- Publication number
- CN110154183A CN110154183A CN201910513438.2A CN201910513438A CN110154183A CN 110154183 A CN110154183 A CN 110154183A CN 201910513438 A CN201910513438 A CN 201910513438A CN 110154183 A CN110154183 A CN 110154183A
- Authority
- CN
- China
- Prior art keywords
- timber
- ultraviolet shielded
- ultraviolet
- sample
- light transmittance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation of ultraviolet shielded transparent timber, wood sample, which is first carried out pretreatment, makes its profit rise, and is then handled with sodium chlorite and glacial acetic acid, by controlling delignification process, obtains the timber substrate of different lignin contents;Sample is carried out dehydrating using organic solvent gradient method, freeze-drying or supercritical drying, further obtains the timber substrate of dewatered different lignin contents;It is impregnated with the prepolymer of fiber refractive index close and high optics light transmittance, is then solidified.By probing into the ultraviolet shielded property of the different transparent timber of lignin content, a kind of transparent timber with ultraviolet shielding function is obtained.Ultraviolet shielded transparent timber is obtained with fabulous UV-screening properties and high translucency, wherein ultraviolet shielded effect has reached 90%, and light transmittance has reached 73% or more.
Description
Technical field
The invention belongs to wood technologies exploitation and technical field of modification, and in particular to a kind of system of ultraviolet shielded transparent timber
Preparation Method.
Background technique
Timber is a kind of natural macromolecular material with anisotropic, mainly by cellulose, hemicellulose and lignin group
At.Wherein cellulose orderly extends along plant growth direction, and lignin and half fiber element are distributed in together as filler and adhesive
Between the microfibre and intercellular layer of cell wall, flanking cell is bonded together, assign cell and plant it is very big machinery it is strong
Degree.
, mainly there is a two o'clock in the technical issues of the present invention is directed to prepare a kind of ultraviolet shielded transparent timber, relate generally to, and one
It is the ultraviolet shielded property regulation of timber, the other is the timber light transmission of timber is modified.
Timber to high translucency and good ultraviolet shielded property, then need first to timber carry out component tune
Control, the appropriate chromophoe constituent except in timber, the i.e. components such as the lignin containing chromophoric group and pectin, tannin, states mentioned then up
And go in chromophoe constituent material be added with the high light transmission upgrading component of cellulose refractive index close, it is high that timber on the one hand can be achieved
On the other hand translucency and uv-shielding capacity can assign timber high strength character.
Currently, both at home and abroad with regard to transparent timber correlative study it is fewer and fewer, and the existing research about transparent timber its
Preparation time is longer.The present invention greatly shortens preparation time, and the machinery of made transparent timber during timber transparence
It has excellent performance, light transmittance has high market application value up to 85% or more.
About the ultraviolet shielded property of transparent timber, at present both at home and abroad also without relevant article or report.Prepared by the present invention
Ultraviolet shielded transparent timber not only translucency with higher, but also there is good ultraviolet shielding function, can shield well
Cover ultraviolet light, can using in life and production.
In conclusion ultraviolet shielded transparent timber prepared by the present invention, not only appearance looks elegant high light transmission, but also can be used as
Construction material shielding ultraviolet rays have good social value, more there is higher economic value.
Summary of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the object of the present invention is to provide a kind of systems of ultraviolet shielded transparent timber
Standby, by wood components tune, polymer impregnates modification, solidification, prepares a kind of ultraviolet shielded transparent timber.
To achieve the goals above, the technical solution adopted by the present invention is that:
A kind of preparation method of ultraviolet shielded transparent timber, comprising the following steps:
1) first thin slice of wood sample being pre-processed, pretreatment mode is that sodium hydroxide moistens processing of rising, timber duct is opened,
Its specific process is as follows:
First sample (thin slice of wood) is placed in the closed container equipped with boiling water, makes wood chip using steam and high temperature liquid water
Quick humidification;
Sample after wetting is put into 3%-10% sodium hydroxide solution and is pre-processed, 70 DEG C -100 DEG C for the treatment of temperature, reacts 1-
2h is rinsed with deionized water to neutrality later;
It 2) is 3%-10% chlorite sodium with mass fraction by the pretreated sample of step 1), glacial acetic acid is handled, pH 3-6,
The degree that delignification is realized by the time of control processing, sets the reaction time as 0.5-4 h, is rinsed later with deionized water
To neutrality, the timber substrate with lignin content is obtained;
3) then timber substrate is dehydrated sample using organic solvent gradient method, freeze-drying or supercritical drying
Processing, further obtains dewatered timber substrate;
4) it finally selects with fiber refractive index close and the polymer impregnated wood substrate 4-8h of high optics light transmittance, 50-70 DEG C
Lower solidification obtains a kind of ultraviolet shielded transparent timber.
Organic solution is 40% ethyl alcohol or 60% ethyl alcohol or 80% ethyl alcohol or straight alcohol or second in the solvent gradient method
Alcohol: acetone 1:1 or acetone.
Described is polymethyl methacrylate, benzene second with the polymer of fiber refractive index close and high optics light transmittance
Or mixtures thereof alkene, epoxy resin, gaultherolin etc..
The beneficial effects of the present invention are:
1) growthform that the present invention still maintains timber natural;
2) present invention has the optics light transmittance higher than 73% or more;
3) present invention has UV-screening properties, can shield substantially and injure maximum medium wave (290 ~ 320nm) ultraviolet light to people, subtract
Few ultraviolet light causes harm to the human body;
4) present invention has good mechanical characteristic, drop resistant;
5) invention increases the added values of timber application, provide good social application value for renewable timber.
Detailed description of the invention
Fig. 1 is light transmittance of the transparent timber of different lignin contents in ultra-violet (UV) band wave band.
Fig. 2 is light transmittance of the transparent timber of different lignin contents in visible region wave band.
The ultraviolet ultraviolet shielded transparent timber of the property (lignin content: 6.68%) of Fig. 3.
Specific embodiment
The present invention is further discussed below with reference to embodiments, but the present invention is not limited to following embodiment.
Embodiment 1
(1) first sample is immersed in 5% sodium hydroxide solution, reacts 80min at 100 DEG C;
(2) will pretreatment treated that sample is washed till neutrality, being put into enough mass fractions is 7% chlorite sodium, acid condition
Under (pH 4) handle, handling duration 1h, measure lignin content be 6.68%;
(3) will treated timber distilled water flushing to neutrality, then use organic solvent gradient method (40% ethyl alcohol, 60% second
Alcohol, 80% ethyl alcohol, straight alcohol, ethyl alcohol: acetone 1:1, pure acetone, do not cause polymerization maceration extract monomer) be carried out dehydrating;
(4) then will decolourize timber pickling 4h in prepolymerized methyl methacrylate (MMA), solidify at 50 DEG C, obtain one
The ultraviolet shielded transparent timber of kind.
The ultraviolet shielded transparent timber of gained the light transmittance of shortwave and medium wave ultraviolet region (200nm~320nm) 5% with
Under, it is 10% in the light transmittance of long wave ultraviolet light area (320nm~400nm), in the light transmittance of visible region (400nm~800nm)
It is 73.46%.Such as Fig. 1, Fig. 2 and table 1.Fig. 3 is ultraviolet shielded transparent timber pictorial diagram.
Embodiment 2
Prepare ultraviolet shielded transparent timber, comprising the following steps:
(1) first sample is immersed in 5% sodium hydroxide solution, reacts 80min at 100 DEG C;
(2) will pretreatment treated that sample is washed till neutrality, being put into enough mass fractions is 7% chlorite sodium, acid condition
Under (pH 4) handle, handling duration 1.5h, measure lignin content be 2.36%;
(3) will treated timber distilled water flushing to neutrality, then use organic solvent gradient method (40% ethyl alcohol, 60% second
Alcohol, 80% ethyl alcohol, straight alcohol, ethyl alcohol: acetone 1:1, pure acetone, do not cause polymerization maceration extract monomer) be carried out dehydrating;
(4) then will decolourize timber pickling 4h into prepolymerized MMA, solidify at 50 DEG C, obtain a kind of ultraviolet shielded transparent wood
Material.
The ultraviolet shielded transparent timber of gained the light transmittance of shortwave and medium wave ultraviolet region (200nm~320nm) 5% with
Under, it is 40% in the light transmittance of long wave ultraviolet light area (320nm~400nm), in the light transmittance of visible region (400nm~800nm)
It is 78.35%.Such as Fig. 1, Fig. 2 and table 1.
Embodiment 3
Prepare ultraviolet shielded transparent timber, comprising the following steps:
(1) first sample is immersed in 5% sodium hydroxide solution, reacts 80min at 100 DEG C;
(2) will pretreatment treated that sample is washed till neutrality, being put into enough mass fractions is 7% chlorite sodium, acid condition
Under (pH 4) handle, handling duration 2h, measure lignin content be 0.23%;
(3) will treated timber distilled water flushing to neutrality, then use organic solvent gradient method (40% ethyl alcohol, 60% second
Alcohol, 80% ethyl alcohol, straight alcohol, ethyl alcohol: acetone 1:1, pure acetone, do not cause polymerization maceration extract monomer) be carried out dehydrating;
(4) then will decolourize timber pickling 4h into prepolymerized MMA, solidify at 50 DEG C, obtain a kind of ultraviolet shielded transparent wood
Material.
The ultraviolet shielded transparent timber of gained the light transmittance of shortwave and medium wave ultraviolet region (200nm~320nm) 5% with
Under, it is 53% in the light transmittance of long wave ultraviolet light area (320nm~400nm), in the light transmittance of visible region (400nm~800nm)
It is 80.23%.Such as Fig. 1, Fig. 2 and table 1.
Embodiment 4
Prepare ultraviolet shielded transparent timber, comprising the following steps:
(1) first sample is immersed in 5% sodium hydroxide solution, reacts 80min at 100 DEG C;
(2) will pretreatment treated that sample is washed till neutrality, being put into enough mass fractions is 7% chlorite sodium, acid condition
Under (pH 4) handle, handling duration 2.5h, measure lignin content be 0.15%;
(3) will treated timber distilled water flushing to neutrality, then use organic solvent gradient method (40% ethyl alcohol, 60% second
Alcohol, 80% ethyl alcohol, straight alcohol, ethyl alcohol: acetone 1:1, pure acetone, do not cause polymerization maceration extract monomer) be carried out dehydrating;
(4) then will decolourize timber pickling 4h into prepolymerized MMA, solidify at 50 DEG C, obtain a kind of ultraviolet shielded transparent wood
Material.
The ultraviolet shielded transparent timber of gained the light transmittance of shortwave and medium wave ultraviolet region (200nm~320nm) 5% with
Under, it is 58% in the light transmittance of long wave ultraviolet light area (320nm~400nm), in the light transmittance of visible region (400nm~800nm)
It is 82.15%.Such as Fig. 1, Fig. 2 and table 1.
。
Claims (3)
1. a kind of preparation method of ultraviolet shielded transparent timber, which comprises the following steps:
1) first thin slice of wood sample is pre-processed, pretreatment mode is that sodium hydroxide solution moistens the method that rises, specific process
It is as follows:
First sample (thin slice of wood) is placed in the closed container equipped with boiling water, keeps wood chip fast using steam and high temperature liquid water
Speed wetting;
Sample after wetting is put into 3%-10% sodium hydroxide solution and is pre-processed, 70 DEG C -100 DEG C for the treatment of temperature, reacts 1-
2h is rinsed with deionized water to neutrality later;
It 2) is 3%-10% chlorite sodium with mass fraction by the pretreated sample of step 1), glacial acetic acid is handled, pH 3-6,
The degree that delignification is realized by the time of control processing, sets the reaction time as 0.5-4 h, is rinsed later with deionized water
To neutrality, the timber substrate with lignin content is obtained;
3) then timber substrate is dehydrated sample using organic solvent gradient method, freeze-drying or supercritical drying
Processing, further obtains dewatered timber substrate;
4) it finally selects with fiber refractive index close and the polymer impregnated wood substrate 4-8h of high optics light transmittance, 50-70 DEG C
Lower solidification obtains a kind of ultraviolet shielded transparent timber.
2. the preparation method of the ultraviolet shielded transparent timber of one kind according to claim 1, which is characterized in that the machine is molten
Organic solution is 40% ethyl alcohol or 60% ethyl alcohol or 80% ethyl alcohol or straight alcohol or ethyl alcohol: acetone 1:1 or acetone in agent gradient method.
3. the preparation method of the ultraviolet shielded transparent timber of one kind according to claim 1, which is characterized in that described with fibre
The polymer for tieing up refractive index close and high optics light transmittance is polymethyl methacrylate, styrene, epoxy resin, salicylic acid first
Or mixtures thereof ester etc..