CN110145095A - It is a kind of with can customized pattern artistic epoxide terrace - Google Patents
It is a kind of with can customized pattern artistic epoxide terrace Download PDFInfo
- Publication number
- CN110145095A CN110145095A CN201910458055.XA CN201910458055A CN110145095A CN 110145095 A CN110145095 A CN 110145095A CN 201910458055 A CN201910458055 A CN 201910458055A CN 110145095 A CN110145095 A CN 110145095A
- Authority
- CN
- China
- Prior art keywords
- pattern
- layer
- aggregate
- artistic
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to it is a kind of with can customized pattern artistic epoxide terrace, comprising: nanometer confining bed 1；Pave aggregate layer 2, and the lower section of the nanometer confining bed 1 is arranged in；The bottom of the aggregate layer 2 that paves is arranged in laser die sinking pattern 3, draws art pattern for placing；Priming paint 4, the bottom of the laser die sinking pattern 3 is set, the lower section setting of the priming paint 4, which is always or usually as specified, is located in reason layer 5, the present invention is the seamless integrated NEW TYPE OF COMPOSITE terrace formed with composite aggregate and transparent epoxy resin, it is freely arranged in pairs or groups by the composite aggregate of one or more different colours, form colourful color and pattern, with texture gracefulness, wear-resistant, anti-weight, it is resistant to chemical etching, anti-skidding, fire prevention, waterproof the advantages that, undope fleut or pigment, ensures the excellent chemical and physical properties of epoxy resin；And graininess composite aggregate, the graceful decorative performance of terrace is not only assigned, but also ensured the high pressure resistance and high-wearing feature of terrace.
Description
Technical field
The present invention relates to artistic epoxide terrace technical field, in particular to it is a kind of with can customized pattern artistic epoxy
Level ground.
Background technique
Conventional epoxy terrace is the high-performance ground coating material for different purposes and load, utilizes mechanical or hand
Epoxy floor paint is uniformly coated on earth's surface and solidified at room temperature by work, is formed in earth's surface one seamless, firm, high
Wear-resisting, acid-alkali-corrosive-resisting protective layer, is widely used in industrial premises, office block, underground parking garage, logistics warehouse, quotient
All kinds of places such as trade center, school, supermarket.But conventional epoxy terrace utilizes post coat technique, long construction period, ring of constructing
Border is severe.In addition, epoxy coating solidifies at room temperature, curing degree is not high, and the regularity of consolidated structures is not good enough, therefore exists easy
The defects of peeling, alice fall paint, and service life is shorter, it is difficult to which the requirement for meeting special engineering technology makes its application by certain
Limitation, the defect that epoxide terrace still has at present is that color is single, and pattern is dull, lacks artistry, is detached from the Nature
Aesthetic feeling.Therefore Water-borne modification, solvent free and the aesthetic feeling demand close to the Nature of floor coatings have become paint industry development
Inexorable trend.
Disclosed above- mentioned information are only used for reinforcing the understanding to background of the invention in the background technology, therefore it may be wrapped
Containing the information for not being formed as the prior art that those of ordinary skill in the art are known.
Summary of the invention
In view of this, the embodiment of the present invention be desirable to provide it is a kind of with can customized pattern artistic epoxide terrace, with solve
Or alleviate the technical problems existing in the prior art, a kind of beneficial selection is at least provided.
The technical solution of the embodiment of the present invention is achieved in that
According to one embodiment of present invention, provide it is a kind of with can customized pattern artistic epoxide terrace, comprising:
Nanometer confining bed；
Pattern layer, is arranged in the lower section of the nanometer confining bed, and the pattern layer includes laser die sinking pattern and is disposed around sharp
The aggregate layer that paves on photoetching mould pattern periphery, the laser die sinking pattern transfers nanometer confining bed are presented；
The bottom of the pattern layer is arranged in priming paint, and the lower section setting of the priming paint, which is always or usually as specified, is located in reason layer；
Wherein, the aggregate layer that paves is that composite aggregate and epoxy resin mix, and mixed proportion is 1:5~9, the composite aggregate
For the perfectly round type graininess quartz sand of rounding processing and/or the tip-angled shape quartz sand of non-rounding；The epoxy resin is using transparent
Solvent-free low viscosity resin, the laying depth of the aggregate layer that paves are 2~5mm.
Further, the nanometer confining bed with a thickness of 80 ± 10 μm.
Further, the present invention provide it is a kind of with can customized pattern artistic epoxide terrace preparation process, including with
Lower step:
Step 1: handle plainly: to cement mortar screeding is carried out plainly, ground is repaired and is cleared up in crack prospecting, and formin is located in
Manage layer；
Step 2: brushing seal coat: coating uniform makes whole surface glow uniform light in handling layer surface plainly
Pool；
Step 3: pattern is arranged: arranging laser die sinking pattern on prime coat；
Step 4: the aggregate that paves: graininess composite aggregate and high-performance epoxy resin being mixed, mixed proportion is 1:5~9, so
It is laid with the aggregate layer that paves with sanding gear afterwards, laying depth is 2~5mm, and carries out compacting leveling with trowelling machine, so that the aggregate that paves
Layer forms the pattern layer of integral seamless with laser die sinking pattern；
Step 5: brushing nanometer confining bed: the brushing nanometer confining bed in pattern layer.
It further, further include being stirred to epoxy resin in the step 4, mixing time is 1~3 minute, stirring
When simultaneously up and down stir so that the curing agent in epoxy resin deeply into lower layer's glue.
It further, further include carrying out preliminary grinding to pattern layer, mending slurry, fine grinding, fine grinding between the step 4 and step 5
After carry out surface polishing treatment.
Further, it is described to pattern layer carry out preliminary grinding, mend slurry, fine grinding, after fine grinding carry out surface polishing treatment include with
Lower step:
Step 1) is ground with 30# gold steel carries out whole polishing；It is polished one time with 100# resin abrasive disc；It is whole with color inhibition transparent resin
Body is scraped one time；It is polished one time with 100# resin abrasive disc after cured；It is polished one time with 200# resin abrasive disc；
Step 2 scratches color inhibition transparent resin to the region of hole again；
Step 3) is polished with 200# resin abrasive disc, is polishing to surfacing；It is polished one time, is polishing to 400# resin abrasive disc
Surface is smooth, no polishing scratch；It after laser die sinking pattern appears, then carries out epoxy resin and mends slurry, drying 22~26 is small after mending slurry
Shi Hou, polishing treatment.
Further, fracture repairing includes: that first to cut out depth along sealing with cutting machine be 1cm, width 1 in step 1
The notch of cm, then vertical direction in crack cut a same depth and width, and length is the notch of 8cm, be put into iron nail and/or
Steel bar, position are divided equally at crack, and the standoff distance of every vertical slot is in 15cm, then with epoxy resin by all cutting sections
Divide dry after filling up, striking off.
Further, when handling plainly, further include the steps that handling " hollowing " of ground, it is described to ground
" hollowing " carry out processing include crack " hollowing " after, mix composite aggregate with epoxy resin and tamped.
Further, the nanometer confining bed with a thickness of 80 ± 10 μm, the laying depth of the aggregate layer that paves is
2.5mm。
Further, further include the steps that making laser die sinking pattern before handle plainly, and close bottom brushing
Further include the steps that fundamental line is arranged on priming paint after paint.
The embodiment of the present invention due to using the technology described above, have the advantage that the present invention be with composite aggregate and
The seamless integrated NEW TYPE OF COMPOSITE terrace of transparent epoxy resin composition, by the composite aggregates of one or more different colours from
By arranging in pairs or groups, colourful color and pattern are formed, has that texture is graceful, it is wear-resistant, anti-weight, resistant to chemical etching, anti-skidding, anti-
The advantages that fire, waterproof；
The present invention uses solvent-free transparent epoxy resin, and undope fleut or pigment, ensures the excellent change of epoxy resin
And physical property；And graininess composite aggregate, the graceful decorative performance of terrace is not only assigned, but also ensured the highly resistance of terrace
Pressure property and high-wearing feature.
Above-mentioned general introduction is merely to illustrate that the purpose of book, it is not intended to be limited in any way.Except foregoing description
Schematical aspect, except embodiment and feature, by reference to attached drawing and the following detailed description, the present invention is further
Aspect, embodiment and feature, which will be, to be readily apparent that.
Detailed description of the invention
In the accompanying drawings, unless specified otherwise herein, otherwise indicate the same or similar through the identical appended drawing reference of multiple attached drawings
Component or element.What these attached drawings were not necessarily to scale.It should be understood that these attached drawings depict only according to the present invention
Disclosed some embodiments, and should not serve to limit the scope of the present invention.
Fig. 1 be the embodiment of the present invention have can customized pattern artistic epoxide terrace structure chart.
In figure: 1, nanometer confining bed；2, pave aggregate layer；3, laser die sinking pattern；4, priming paint；5, element ground process layer；20,
Pattern layer.
Specific embodiment
Hereinafter, certain exemplary embodiments are simply just described.As one skilled in the art will recognize that
Like that, without departing from the spirit or scope of the present invention, described embodiment can be modified by various different modes.
Therefore, attached drawing and description are considered essentially illustrative rather than restrictive.
In the description of the present invention, it is to be understood that, term " center ", " longitudinal direction ", " transverse direction ", " length ", " width ",
" thickness ", "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top", "bottom", "inner", "outside", " up time
The orientation or positional relationship of the instructions such as needle ", " counterclockwise " is to be based on the orientation or positional relationship shown in the drawings, and is merely for convenience of
The description present invention and simplified description, rather than the device or element of indication or suggestion meaning have specific orientation, with specific
Orientation construction and operation, therefore be not considered as limiting the invention.
In addition, term " first ", " second " are used for descriptive purposes only and cannot be understood as indicating or suggesting relative importance
Or implicitly indicate the quantity of indicated technical characteristic.Define " first " as a result, the feature of " second " can be expressed or
Implicitly include one or more of the features.In the description of the present invention, the meaning of " plurality " is two or more,
Unless otherwise specifically defined.
In the present invention unless specifically defined or limited otherwise, term " installation ", " connected ", " connection ", " fixation " etc.
Term shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or integral；It can be mechanical connect
It connects, is also possible to be electrically connected, can also be communication；It can be directly connected, can also indirectly connected through an intermediary, it can be with
It is the interaction relationship of the connection or two elements inside two elements.For the ordinary skill in the art, may be used
To understand the concrete meaning of above-mentioned term in the present invention as the case may be.
In the present invention unless specifically defined or limited otherwise, fisrt feature second feature "upper" or "lower"
It may include that the first and second features directly contact, also may include that the first and second features are not direct contacts but pass through it
Between other characterisation contact.Moreover, fisrt feature includes the first spy above the second feature " above ", " above " and " above "
Sign is right above second feature and oblique upper, or is merely representative of first feature horizontal height higher than second feature.Fisrt feature exists
Second feature " under ", " lower section " and " following " include fisrt feature right above second feature and oblique upper, or be merely representative of
First feature horizontal height is less than second feature.
Following disclosure provides many different embodiments or example is used to realize different structure of the invention.In order to
Simplify disclosure of the invention, hereinafter the component of specific examples and setting are described.Certainly, they are merely examples, and
And it is not intended to limit the present invention.In addition, the present invention can in different examples repeat reference numerals and/or reference letter,
This repetition is for purposes of simplicity and clarity, itself not indicate between discussed various embodiments and/or setting
Relationship.In addition, the present invention provides various specific techniques and material example, but those of ordinary skill in the art can be with
Recognize the application of other techniques and/or the use of other materials.
It is a kind of with can customized pattern artistic epoxide terrace, comprising:
Nanometer confining bed 1；
Pattern layer 20, is arranged in the lower section of the nanometer confining bed 1, and the pattern layer 20 includes laser die sinking pattern 3 and encloses
It is located at the aggregate layer 2 that paves on 3 periphery of laser die sinking pattern, the laser die sinking pattern 3 is presented through nanometer confining bed 1；
The bottom of the pattern layer 20 is arranged in priming paint 4, and the lower section setting of the priming paint 4, which is always or usually as specified, is located in reason layer 5；
Specific: the aggregate layer 2 that paves is that composite aggregate and epoxy resin mix, and mixed proportion is 1:5~9, and the present invention is excellent
The 1:7(epoxy resin of choosing: aggregate), the composite aggregate is the perfectly round type graininess quartz sand and/or non-rounding of rounding processing
Tip-angled shape quartz sand；The epoxy resin uses transparent solvent-free low viscosity resin.
Specific: the laying depth of the aggregate layer 2 that paves is 2~5mm, currently preferred 2.5mm, so that artistic ring
Oxygen terrace is high with intensity, rigidity is big, globality is strong.
It is specific: the nanometer confining bed 1 with a thickness of 80 ± 10 μm, currently preferred 80 μm, improve nanometer closing
The wearability of layer 1.
Embodiment 1
The embodiment of the invention provides it is a kind of with can customized pattern artistic epoxide terrace preparation process, including following step
It is rapid:
Step 1: handle plainly: first to cement mortar screeding is carried out plainly, ground is reconnoitred and repairs and clear up in crack, is formed
Plain ground process layer 5；
The cement mortar screeding is included in humidity 1%, is watered processing in proportion using interface treating agent, and moisturt register is adopted up to 3%
It is handled with epoxy primer 4, intensity C20, flatness 1.998m；
It includes: that first first to cut out depth with cutting machine along sealing be 1cm that the crack, which is reconnoitred and repaired, the notch of width 1cm,
The vertical direction in crack cuts a same depth and width again, and length is the notch of 8cm, is put into iron nail and/or/steel bar, position
Divide equally at crack, the standoff distance of every vertical slot is between 15cm.Then with epoxy resin that all cut-away portions are complete
It fills up, strike off entirely, after it is completely dried；
Clearing up ground includes: to handle " hollowing ", surface attachments and paint of ground, after " hollowing " cracks, uses epoxy
Resin mixes composite aggregate and is repaired, tamped；Paint, is completely removed, surface attachments with angle grinder, is thoroughly given a dinner of welcome with dust catcher
Afterwards, place is closed, the processing of brushing seal coat 4 is carried out；
Step 2: brushing seal coat 4: coating uniform is in earth's surface, so that whole surface glows uniform gloss；
Step 3: pattern is arranged: in 4 layers of priming paint upper arrangement laser die sinking pattern 3, it is possible to understand that, before pattern arrangement also
Include the steps that designing and making laser die sinking pattern 3, in order to more accurately arrange laser die sinking pattern in plain ground process layer 5
3, it further include that fundamental line is set on priming paint 4 after brushing seal coat 4, reference and positioning fixed laser by fundamental line
Die sinking pattern 3 further further includes the steps that arrangement and location device or anchor point on fundamental line, further to help pair
Laser die sinking pattern 3 positions.
Step 4: the aggregate that paves: graininess composite aggregate and high-performance epoxy resin are mixed, mixed proportion is generally 1:
5, it then is laid with aggregate layer, laying depth 2mm with sanding gear, and carry out compacting leveling with trowelling machine, forms integral seamless
Epoxy color sand layer, the configuration to epoxy resin, epoxy resin are sufficiently stirred, sufficiently anti-to guarantee that curing agent is uniformly contacted with glue
It answers, mixing time is 1 minute, while being stirred up and down, so that curing agent gos deep into lower layer's glue；
It should be understood that the aggregate that paves forms the aggregate layer 2 that paves, the aggregate layer 2 that paves on 3 periphery of laser die sinking pattern
It is disposed around laser die sinking periphery and laser die sinking pattern 3 forms pattern layer 20.
Preliminary grinding is carried out to pattern layer 20, mends slurry, fine grinding, surface polishing treatment is carried out after fine grinding, so that laser die sinking drawing
Case 3 appears, specifically, the following steps are included:
Step 1) is ground with 30# gold steel carries out whole polishing, and corner uses angle grinder manual polishing；It is polished with 100# resin abrasive disc
One time, corner uses angle grinder manual polishing, clears up ground；It is integrally scraped one time with color inhibition transparent resin；After the curing be complete
It is polished one time with 100# resin abrasive disc, corner uses angle grinder manual polishing；It is polished one time with 200# resin abrasive disc, corner uses
Angle grinder manual polishing；
Step 2 cleans out surface after dry, checks whether there is no hole comprehensively, scratches again one time to the progress of hole
Color inhibition transparent resin, until surface is without hole；
Step 3) is polished with 200# resin abrasive disc, is polishing to surfacing, no transparent resin protrusion phenomenon；With 400# resin
Grinding polishing one time, it is smooth to be polishing to surface, no polishing scratch；Art pattern is polished after coming, then carries out epoxy resin
Slurry is mended, after benefit slurry completion is 22 hours dry, then is processed by shot blasting
Step 5: brushing nanometer confining bed 1: first material being uniformly sprayed at sprayer 20 surface of pattern layer, then rolled with roller
It applies, it is possible to understand that, laser die sinking pattern 3 should be presented through nanometer confining bed 1, so that user is able to observe that laser
Die sinking pattern 3.
Embodiment 2
The embodiment of the invention provides it is a kind of with can customized pattern artistic epoxide terrace preparation process, including following step
It is rapid:
Step 1: handle plainly: first to cement mortar screeding is carried out plainly, ground is reconnoitred and repairs and clear up in crack, is formed
Plain ground process layer 5；
Step 2: brushing brush seal coat 4: coating uniform is in earth's surface, so that whole surface glows uniform gloss；
Step 3: pattern is arranged: in 4 layers of priming paint upper arrangement laser die sinking pattern 3；
Step 4: the aggregate that paves: graininess composite aggregate and high-performance epoxy resin being mixed, mixed proportion is generally 1:7, so
It is laid with aggregate layer, laying depth 2.5mm with sanding gear afterwards, and carries out compacting leveling with trowelling machine, forms the ring of integral seamless
Oxygen color sand layer, the configuration to epoxy resin, epoxy resin are sufficiently stirred, and to guarantee that curing agent is uniformly contacted with glue, sufficiently react,
Mixing time is 2 minutes, while being stirred up and down, guarantees that curing agent gos deep into lower layer's glue；
Preliminary grinding is carried out to composite aggregate after paving, mends slurry, fine grinding, carries out surface polishing treatment after fine grinding, comprising the following steps:
Step 1) is ground with 30# gold steel carries out whole polishing, and corner uses angle grinder manual polishing；It is polished with 100# resin abrasive disc
One time, corner uses angle grinder manual polishing, clears up ground；It is integrally scraped one time with color inhibition transparent resin；After the curing be complete
It is polished one time with 100# resin abrasive disc, corner uses angle grinder manual polishing；It is polished one time with 200# resin abrasive disc, corner uses
Angle grinder manual polishing；
Step 2 cleans out surface after dry, checks whether there is no hole comprehensively, scratches again one time to the progress of hole
Color inhibition transparent resin, until surface is without hole；
Step 3) is polished with 200# resin abrasive disc, is polishing to surfacing, no transparent resin protrusion phenomenon；With 400# resin
Grinding polishing one time, it is smooth to be polishing to surface, no polishing scratch；Art pattern is polished after coming, then carries out epoxy resin
Slurry is mended, after benefit slurry completion is 24 hours dry, then is processed by shot blasting
Step 5: brushing nanometer confining bed 1: material being uniformly first sprayed at terrazzo surface with sprayer, then with roller roller coating.
Embodiment 3
The embodiment of the invention provides it is a kind of with can customized pattern artistic epoxide terrace preparation process, including following step
It is rapid:
Step 1: handle plainly: first to cement mortar screeding is carried out plainly, ground is reconnoitred and repairs and clear up in crack, is formed
Plain ground process layer 5；
Step 2: brushing brush seal coat 4: coating uniform is in earth's surface, so that whole surface glows uniform gloss；
Step 3: pattern is arranged: in 4 layers of priming paint upper arrangement laser die sinking pattern 3；
Step 4: the aggregate that paves: graininess composite aggregate and high-performance epoxy resin being mixed, then mixed proportion 1:9 is used
Sanding gear is laid with aggregate layer, laying depth 5mm, and carries out compacting leveling with trowelling machine, forms the epoxy color sand of integral seamless
Layer, the configuration to epoxy resin, epoxy resin is sufficiently stirred, to guarantee that curing agent is uniformly contacted with glue, sufficiently reaction, when stirring
Between be 3 minutes, while stirring up and down, guarantee that curing agent gos deep into lower layer's glue；
Preliminary grinding is carried out to composite aggregate after paving, mends slurry, fine grinding, carries out surface polishing treatment after fine grinding, comprising the following steps:
Step 1) is ground with 30# gold steel carries out whole polishing, and corner uses angle grinder manual polishing；It is polished with 100# resin abrasive disc
One time, corner uses angle grinder manual polishing, clears up ground；It is integrally scraped one time with color inhibition transparent resin；After the curing be complete
It is polished one time with 100# resin abrasive disc, corner uses angle grinder manual polishing；It is polished one time with 200# resin abrasive disc, corner uses
Angle grinder manual polishing；
Step 2 cleans out surface after dry, checks whether there is no hole comprehensively, scratches again one time to the progress of hole
Color inhibition transparent resin, until surface is without hole；
Step 3) is polished with 200# resin abrasive disc, is polishing to surfacing, no transparent resin protrusion phenomenon；With 400# resin
Grinding polishing one time, it is smooth to be polishing to surface, no polishing scratch；Art pattern is polished after coming, then carries out epoxy resin
Slurry is mended, after benefit slurry completion is 26 hours dry, then is processed by shot blasting
Step 5: brushing nanometer confining bed 1: material being uniformly first sprayed at terrazzo surface with sprayer, then with roller roller coating.
The material of artistic epoxide terrace includes the following:
One, composite aggregate, also to have the tip-angled shape using not rounding using the perfectly round type graininess quartz sand by rounding processing
Quartz sand, but perfectly round type quartz sand and reasonable grain size proportion, just can guarantee the artistic epoxide terrace for producing high-quality；
Two, epoxy resin, using transparent solvent-free low viscosity resin, to ensure the high-quality quantity high performance of terrace.
Based on the various embodiments described above, the embodiment of the present invention with can customized pattern artistic epoxide terrace have it is following excellent
Point: the present invention is the seamless integrated NEW TYPE OF COMPOSITE terrace formed with composite aggregate and transparent epoxy resin, by a kind of or
The composite aggregate of a variety of different colours is freely arranged in pairs or groups, and colourful color and pattern are formed, graceful with texture, wear-resistant,
Anti- weight, it is resistant to chemical etching, anti-skidding, fire prevention, waterproof the advantages that；Performance: moulding production is simple, scene can make；Color is rich
Richness, texture is strong, great Modern Decorative style；Ground integral seamless, can also pattern-making as needed, and with ground one
Change, appearance elegance is luxurious；Have the excellent properties such as scratch resistance, anti-weight, shock resistance；Intensity is high, and hardness is big, has excellent wear-resisting
Property；Clean dustproof, watertightness surface can be subjected to high pressure washing or cleaning steam, maintenance easy to clean；With anti-skidding function outstanding
Can and the chemical properties such as excellent water-fast, waterproof, acid and alkali-resistance；Service life is longer；"dead" pollution, no pernicious gas are released
It puts, is green product；Corrosion resistance is strong, strong applicability: there is special ground pattern to create rendering request, have environment refined
Cause, the public place of cleaning and the functional requirements such as wear-resisting antiskid, as the hall Lou Tang, exhibit halls, museum, all kinds of odeums,
Superstore, commercial buildings, advanced entertainment place and stadiums etc.；With the place that high-cleanness, high requires, such as hospital writes
Building, office and organ building etc.；Ground with special requirement, such as to cleaning, fire prevention, waterproof requirement medical medicine and
The warehouse of food processing industry has office and the production and processing workshop, storehouse of the electronic communication industry of antistatic requirement, has resistance to
The processing manufacturing industry of requirements and warehouse or the storages in huge super market such as mill, anti-weight and cleaning, it is chemically resistant to require
Fine chemistry industry workshop and storehouse, ship deck etc.；Living room, the corridor Room, kitchen, toilet, parking house of residential housing etc..
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
Those familiar with the art in the technical scope disclosed by the present invention, can readily occur in its various change or replacement,
These should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be with the guarantor of the claim
It protects subject to range.
Claims (10)
1. it is a kind of with can customized pattern artistic epoxide terrace characterized by comprising
Nanometer confining bed；
Pattern layer, is arranged in the lower section of the nanometer confining bed, and the pattern layer includes laser die sinking pattern and is disposed around sharp
The aggregate layer that paves on photoetching mould pattern periphery, the laser die sinking pattern transfers nanometer confining bed are presented；
The bottom of the pattern layer is arranged in priming paint, and the lower section setting of the priming paint, which is always or usually as specified, is located in reason layer；
Wherein, the aggregate layer that paves is that composite aggregate and epoxy resin mix, and mixed proportion is 1:5~9, the composite aggregate
For the perfectly round type graininess quartz sand of rounding processing and/or the tip-angled shape quartz sand of non-rounding；The epoxy resin is using transparent
Solvent-free low viscosity resin, the laying depth of the aggregate layer that paves are 2~5mm.
2. it is as described in claim 1 have can customized pattern artistic epoxide terrace, which is characterized in that the nanometer confining bed
With a thickness of 80 ± 10 μm.
3. it is as described in claim 1 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that including
Following steps:
Step 1: handle plainly: to cement mortar screeding is carried out plainly, ground is repaired and is cleared up in crack prospecting, and formin is located in
Manage layer 5；
Step 2: brushing seal coat: coating uniform makes whole surface glow uniform light in handling layer surface plainly
Pool；
Step 3: pattern is arranged: arranging laser die sinking pattern on prime coat；
Step 4: the aggregate that paves: graininess composite aggregate and high-performance epoxy resin being mixed, mixed proportion is 1:5~9, so
It is laid with the aggregate layer 2 that paves with sanding gear afterwards, laying depth is 2~5mm, and carries out compacting leveling with trowelling machine, so that the bone that paves
The bed of material and laser die sinking pattern form the pattern layer of integral seamless；
Step 5: brushing nanometer confining bed: the brushing nanometer confining bed 1 in pattern layer.
4. it is as claimed in claim 3 have can customized pattern artistic epoxide terrace preparation process, it is characterised in that: it is described
It further include being stirred to epoxy resin in step 4, mixing time is 1~3 minute, is stirred up and down when stirring simultaneously, so that ring
Curing agent in oxygen resin is deeply into lower layer's glue.
5. it is as claimed in claim 4 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that it is described
Further include carrying out preliminary grinding to pattern layer, mending slurry, fine grinding between step 4 and step 5, carries out surface polishing treatment after fine grinding.
6. it is as claimed in claim 5 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that it is described
To pattern layer carry out preliminary grinding, mend slurry, fine grinding, after fine grinding carry out surface polishing treatment the following steps are included:
Step 1) is ground with 30# gold steel carries out whole polishing；It is polished one time with 100# resin abrasive disc；It is whole with color inhibition transparent resin
Body is scraped one time；It is polished one time with 100# resin abrasive disc after cured；It is polished one time with 200# resin abrasive disc；
Step 2 scratches color inhibition transparent resin to the region of hole again；
Step 3) is polished with 200# resin abrasive disc, is polishing to surfacing；It is polished one time, is polishing to 400# resin abrasive disc
Surface is smooth, no polishing scratch；It after laser die sinking pattern appears, then carries out epoxy resin and mends slurry, drying 22~26 is small after mending slurry
Shi Hou, polishing treatment.
7. it is as claimed in claim 6 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that in step
Fracture repairing includes: that first to cut out depth along sealing with cutting machine be 1cm in rapid one, the notch of width 1cm, then hanging down in crack
Histogram to cut a same depth and width, length be 8cm notch, be put into iron nail and/or steel bar, position is divided equally at crack,
The standoff distance of every vertical slot is dry after then all cut-away portions are filled up, struck off with epoxy resin in 15cm.
8. it is as claimed in claim 7 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that in element
When ground processing, further include the steps that handling " hollowing " of ground, " hollowing " to ground carries out processing and include
After cracking " hollowing ", composite aggregate is mixed with epoxy resin and is tamped.
9. it is as claimed in claim 7 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that it is described
Nanometer confining bed with a thickness of 80 ± 10 μm, the laying depth of the aggregate layer that paves is 2.5mm.
10. it is as claimed in claim 7 have can customized pattern artistic epoxide terrace preparation process, which is characterized in that
Further includes the steps that making laser die sinking pattern 3 before pattern arrangement, and after brushing seal coat further includes in priming paint
The step of upper setting fundamental line.