CN110143753A - A kind of production technology of high borosilicate heat-proof glass vessel - Google Patents
A kind of production technology of high borosilicate heat-proof glass vessel Download PDFInfo
- Publication number
- CN110143753A CN110143753A CN201910460355.1A CN201910460355A CN110143753A CN 110143753 A CN110143753 A CN 110143753A CN 201910460355 A CN201910460355 A CN 201910460355A CN 110143753 A CN110143753 A CN 110143753A
- Authority
- CN
- China
- Prior art keywords
- glass
- high borosilicate
- degree
- proof glass
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production technology of high borosilicate heat-proof glass vessel, belongs to process of glass technical field.Stained glass pipe is placed in high borosilicate heat-proof glass semi-finished product opening, the two is merged under 1200 degree of thermal-flames, was had the high borosilicate heat-proof glass vessel at ferry；Naturally cool to 0-10 degree；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass and crosses ferry product.Product of the present invention is double coloured glass products, is dyed in transition oral area and bottom, quality-high and inexpensive and diversified, can be used for the glasswares such as glass, Double-layer cup, water bottle, kettle, tableware；Secondary operation can be carried out, 500 degree or more do not burst.
Description
Technical field
The invention belongs to process of glass technical fields, more particularly to a kind of production of high borosilicate heat-proof glass vessel
Technique.
Background technique
Existing high-boron-silicon glass pipe is all using bright material as production major ingredient, and small part colorant supplement, such as lamp work are blown
System, bright material cup are sub (vessel), are processed into glass (solid) adhering to the sub- outer wall medium position of bright material cup with few colorant stick, non-
Chang Shiyong and conveniently, also has and makees cup with colorant entirely, but high borosilicate colorant glass tubing price is very high, and ordinary consumer is difficult to
Receive its high retail price, heat resistant glass deep processing is troublesome, and cost is high, and consumer is caused to cannot afford or nowhere consume
Situation, and the pattern of heat-resisting high-boron-silicon glass product is homogeneous transparent material glassware on the market, and tone is single.
Summary of the invention
For the above technical problems, a kind of production technology of high borosilicate heat-proof glass vessel is provided, it is easy to operate,
High safety.
The purpose of the present invention is achieved through the following technical solutions:
The present invention uses multiple technologies scheme:
Scheme one: a kind of production technology of high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) stained glass pipe, diameter and high borosilicate heat-proof glass are placed in high borosilicate heat-proof glass semi-finished product opening
Semi-finished product opening is corresponding, merges the two under 1200 degree of thermal-flames, was had the high borosilicate heat-proof glass device at ferry
Ware；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
Scheme two: a kind of production technology of high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) make it using 1200 degree of high-temperature flame stained glass sticks in high borosilicate heat-proof glass semi-finished product opening
It is deposited in high borosilicate heat-proof glass semi-finished product opening, was had the high borosilicate heat-proof glass vessel at ferry；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
Preferably, the stained glass pipe or stained glass stick are that the heat-resisting stained glass pipe of high borosilicate or high borosilicate are heat-resisting
Stained glass stick.
Preferably, the height of the stained glass pipe or stained glass stick is 1.5-2cm.
Scheme three: a kind of production technology for stating high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) transparent or semitransparent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, is cut according to preset requirement
It cuts, high-boron-silicon glass pipe crosses ferry as glassware as glassware bottom, colored high-boron-silicon glass pipe, obtains with coloured silk
The semi-finished product high-boron-silicon glass pipe of colour transition mouth is put into die for molding using 1200 degree of fire burning softenings, obtains with transition
The high borosilicate heat-proof glass vessel of mouth；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
Preferably, colored high-boron-silicon glass length of tube is 1cm-2cm.
Scheme four: a kind of production technology for stating high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) transparent or semitransparent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, is cut according to preset requirement
It cuts, high-boron-silicon glass pipe is had as glassware upper body, colored high-boron-silicon glass pipe as glassware bottom
The semi-finished product high-boron-silicon glass pipe of coloured bottom is put into die for molding using 1200 degree of fire burning softenings, obtains band chromatic colour
The high borosilicate heat-proof glass vessel of bottom；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
Preferably, colored high-boron-silicon glass length of tube is 4cm-5cm.
The invention has the benefit that
The high borosilicate heat-proof glass appearance of product of the present invention is double color products, is dyed in transition oral area and bottom, object beauty
It is inexpensive and diversified, it can be used for the glasswares such as glass, Double-layer cup, water bottle, kettle, tableware；It can carry out secondary
Processing, 500 degree or more do not burst.
Specific embodiment
Below with reference to embodiment, the present invention will be described in detail.
Embodiment 1: a kind of production technology of high borosilicate heat-proof glass vessel of the present invention carries out in accordance with the following steps:
(1) stained glass pipe, diameter and high borosilicate heat-proof glass are placed in high borosilicate heat-proof glass semi-finished product opening
Semi-finished product opening is identical, merges the two under 1200 degree of thermal-flames, was had the high borosilicate heat-proof glass device at ferry
Ware；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
The heat-resisting stained glass pipe of stained glass Guan Weigao borosilicate.The height of the stained glass pipe is 1.5-
2cm, this example select 1.5cm.The high borosilicate heat-proof glass semi-finished product can be transparent or semitransparent glass.
Embodiment 2: a kind of production technology of high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) make it using 1200 degree of high-temperature flame stained glass sticks in high borosilicate heat-proof glass semi-finished product opening
It is deposited in high borosilicate heat-proof glass semi-finished product opening, was had the high borosilicate heat-proof glass vessel at ferry；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
The stained glass stick is the heat-resisting stained glass pipe of high borosilicate.The height of the stained glass stick is 1.5-
2cm, this example select 2cm.The high borosilicate heat-proof glass semi-finished product can be transparent or semitransparent glass.
Embodiment 3: a kind of production technology for stating high borosilicate heat-proof glass vessel carries out in accordance with the following steps:
(1) transparent or semitransparent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, is cut according to preset requirement
It cuts, high-boron-silicon glass pipe crosses ferry as glassware as glassware bottom, colored high-boron-silicon glass pipe, obtains with coloured silk
The semi-finished product high-boron-silicon glass pipe of colour transition mouth is put into die for molding using 1200 degree of fire burning softenings, obtains with transition
The high borosilicate heat-proof glass vessel of mouth；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
The colored high-boron-silicon glass length of tube is 1cm-2cm, and this example selects 1cm, 1.5cm, 2cm or 1cm-2cm
Between arbitrary height.It is Transparent color, top with colour transition ferry glass that glass product obtained, which is bottom, through this embodiment
Cup, Double-layer cup, water bottle or kettle.
Embodiment 4: a kind of production technology for stating high borosilicate heat-proof glass vessel, specific steps are as follows:
(1) transparent or translucent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, according to preset requirement
Cutting, high-boron-silicon glass pipe obtain band as glassware bottom as glassware upper body, colored high-boron-silicon glass pipe
The semi-finished product high-boron-silicon glass pipe of chromatic colour bottom is put into die for molding using 1200 degree of fire burning softenings, obtains with coloured silk
The high borosilicate heat-proof glass vessel of color bottom；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass mistake
Ferry product.
Colored high-boron-silicon glass length of tube is 4cm-5cm, and this example selects the arbitrary height between 4cm, 5cm or 4cm-5cm.
It is that Transparent color crosses ferry glass, double that glass product obtained, which is bottom belt chromatic colour, upper body, through this embodiment
Layer cup, water bottle or kettle.
Heretofore described stained glass pipe, glass bar, colour color spray therein is a kind of aqueous tempering ink, special
Point is nuisanceless.There is a hyacinthine, blackish green, peony, buff, purple or the multiple colors such as orange.
Claims (8)
1. a kind of production technology of high borosilicate heat-proof glass vessel, it is characterised in that: carry out in accordance with the following steps:
(1) place stained glass pipe in high borosilicate heat-proof glass semi-finished product opening, diameter and high borosilicate heat-proof glass half at
Product opening is corresponding, merges the two under 1200 degree of thermal-flames, was had the high borosilicate heat-proof glass vessel at ferry；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass and crosses ferry
Product.
2. a kind of production technology of high borosilicate heat-proof glass vessel, it is characterised in that: carry out in accordance with the following steps:
(1) make its accumulation using 1200 degree of high-temperature flame stained glass sticks in high borosilicate heat-proof glass semi-finished product opening
In high borosilicate heat-proof glass semi-finished product opening, the high borosilicate heat-proof glass vessel at ferry were had；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass and crosses ferry
Product.
3. the production technology of high borosilicate heat-proof glass vessel as claimed in claim 1 or 2, it is characterised in that: the colour
Glass tube or stained glass stick are the heat-resisting stained glass pipe of high borosilicate or the heat-resisting stained glass stick of high borosilicate.
4. the production technology of high borosilicate heat-proof glass vessel as claimed in claim 1 or 2, it is characterised in that: the colour
The height of glass tube or stained glass stick is 1.5-2cm.
5. a kind of production technology for stating high borosilicate heat-proof glass vessel, it is characterised in that: carry out in accordance with the following steps:
(1) transparent or semitransparent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, is cut according to preset requirement, it is high
Borosilicate glass tube crosses ferry as glassware as glassware bottom, colored high-boron-silicon glass pipe, obtains with colour transition
The semi-finished product high-boron-silicon glass pipe at ferry is put into die for molding using 1200 degree of fire burning softenings, was had ferry
High borosilicate heat-proof glass vessel；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass and crosses ferry
Product.
6. the production technology of high borosilicate heat-proof glass vessel as claimed in claim 5, it is characterised in that: colored high-boron-silicon glass
Length of tube is 1cm-2cm.
7. a kind of production technology for stating high borosilicate heat-proof glass vessel, it is characterised in that: carry out in accordance with the following steps:
(1) transparent or semitransparent high-boron-silicon glass pipe and colored high-boron-silicon glass pipe welding are selected, is cut according to preset requirement, it is high
Borosilicate glass tube obtains band chromatic colour as glassware bottom as glassware upper body, colored high-boron-silicon glass pipe
The semi-finished product high-boron-silicon glass pipe of bottom is put into die for molding using 1200 degree of fire burning softenings, obtains with coloured bottom
High borosilicate heat-proof glass vessel；
(2) 0-10 degree is naturally cooled to；Then 580 degree are warming up in 1 hour, taking-up obtains high borosilicate heat-proof glass and crosses ferry
Product.
8. the production technology of high borosilicate heat-proof glass vessel as claimed in claim 7, it is characterised in that: colored high-boron-silicon glass
Length of tube is 4cm-5cm.