CN110141523A - 一种制备义齿用热稳定性能优异的包埋粉 - Google Patents
一种制备义齿用热稳定性能优异的包埋粉 Download PDFInfo
- Publication number
- CN110141523A CN110141523A CN201910230109.7A CN201910230109A CN110141523A CN 110141523 A CN110141523 A CN 110141523A CN 201910230109 A CN201910230109 A CN 201910230109A CN 110141523 A CN110141523 A CN 110141523A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- artificial tooth
- thermal stability
- extract
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种制备义齿用热稳定性能优异的包埋粉，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯40‑60份、氧化锆25‑30份、氧化铈1‑4份、氧化钇1‑4份、氧化铝0.5‑0.8份、分散剂2‑3份、薄荷叶烯类提取物1‑1.5份、磷灰石4‑8份、绿茶提取物3‑5.7份、二烯丙基硫化物2.5‑3份。本发明通过加入氧化锆、氧化钇、氧化铈，具备较好的热塑性，为义齿的热塑过程的进行带来便利，通过加入二烯丙基硫化物，具备较好的杀菌效果，可以抑制口腔中细菌的生长，有利于使用者健康，通过加入薄荷叶烯类提取物，于口腔内可以在呼吸时保持口气清新，较为全面，通过加入磷灰石、绿茶提取物，义齿具备较好的抗酸防蛀效果，延长使用寿命。
Description
技术领域
本发明涉及义齿材料领域，尤其涉及一种制备义齿用热稳定性能优异的包埋粉。
背景技术
义齿就是人们常说的“假牙”，医学上是对上、下颌牙部分或全部牙齿缺失后制作的修复体的总称，义齿分为可摘与固定两种，固定义齿不能由患者自己取戴的，而可摘义齿可以由患者方便地取戴，活动义齿时患者可自行摘戴的假牙，适宜于全口多数牙缺失，余留牙少的情况，优点是患者可摘下清洁，余留牙负担较小，但也存在咀嚼效率较低，患者需要饭后摘下清洗等诸多不便，固定义齿是利用缺失牙两侧的健康牙做支持，把假牙固定在口腔内，适用于少数牙缺失，间歇缺牙，余留牙健康状态好的情况，固定义齿咀嚼效率高，患者戴用舒适，异物感小，不用摘戴，缺点是修复时要对缺失牙两侧的健康牙磨除部分牙体组织后进行全冠修复，在义齿的定制制作过程中，现有的义齿制备的包埋粉其主要成分之一是二氧化硅的同素异形体，用来调整所需的热膨胀系数，之二是结合剂，有石膏结合剂，适用于铸造低熔点合金，还有磷酸盐和硅酸盐结合剂，适用于高熔点合金，是义齿生产中不可缺少的材料。
上述制备义齿用包埋粉在使用时存在一定的弊端，热稳定性能较差，定制塑性过程中加热时材料自身易发生损坏的现象，为义齿的定制塑性带来不便，其次，所制成义齿的抗菌效果较差，不利于使用者健康，还有，不具备促进口气清新的效果，不够全面，不具备抗酸防蛀的效果，降低义齿的使用寿命。
发明内容
本发明的目的是提供一种制备义齿用热稳定性能优异的包埋粉，解决了传统义齿用包埋粉热稳定性较差，制成义齿的抗菌效果较差，不具备促进口气清新，抗酸防蛀效果较差的问题。
为了达到上述目的，本发明是通过以下技术方案实现的：
本发明提供一种制备义齿用热稳定性能优异的包埋粉，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯40-60份、氧化锆25-30份、氧化铈1-4份、氧化钇1-4份、氧化铝0.5-0.8份、分散剂2-3份、薄荷叶烯类提取物1-1.5份、磷灰石4-8份、绿茶提取物3-5.7份、二烯丙基硫化物2.5-3份。
优选的，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯40份、氧化锆30份、氧化铈4份、氧化钇4份、氧化铝0.8份、分散剂3份、薄荷叶烯类提取物1.5份、磷灰石8份、绿茶提取物5.7份、二烯丙基硫化物3份。
优选的，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯50份、氧化锆27份、氧化铈4份、氧化钇4份、氧化铝0.5份、分散剂3份、薄荷叶烯类提取物1份、磷灰石5份、绿茶提取物3份、二烯丙基硫化物2.5份。
优选的，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯60份、氧化锆25份、氧化铈1份、氧化钇1份、氧化铝0.5份、分散剂2份、薄荷叶烯类提取物1份、磷灰石4份、绿茶提取物3份、二烯丙基硫化物2.5份。
优选的，所述聚甲基丙烯酸甲酯呈粉末状，通过甲基丙烯酸甲酯与过氧化苯甲酰在高温环境下反应分离回收后制得，所述分散剂为聚丙烯酰胺。
优选的，所述氧化锆为白色重质无定形粉末，通过将1 mol/L的高纯氧氯化锆溶液喷入温度为1000℃的分解炉中，水分蒸发后水解制得氧化锆。
优选的，所述氧化钇与氧化铈均为稳定剂，所述氧化铈为淡黄或黄褐色助粉末，通过氯化铈溶液加入草酸调节Ph值为2，沉淀出草酸铈再经加热熟化、分离、洗涤、烘干后于900～1000℃灼烧制成，所述氧化钇为白色略带黄色粉末，通过分解褐钇铌矿所得的混合稀土溶液经萃取、酸溶、萃取、直接浓缩、灼烧制得。
优选的，所述氧化铝呈白色粉末状，通过氢氧化铝粉和氢氧化钠配制成的偏铝酸钠溶液后通入二氧化碳成胶，并于500-700℃焙烧制得。
本发明还提供一种制备义齿用热稳定性能优异的包埋粉的加工方法，具体包括以下步骤：
（1）按特定的组分及重量成分组成准备聚甲基丙烯酸甲酯、氧化锆、氧化铈、氧化钇、氧化铝、分散剂、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物原材料；
（2）将氧化锆、氧化铝、氧化铈与氧化钇混合并搅拌均匀，加热至1100℃，氧化锆转变为四相晶相，氧化铈与氧化钇确保所得氧化锆四相晶体的稳定，形成混合物后保持温度2小时；
（3）将聚甲基丙烯酸甲酯、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物充分混合并搅拌均匀；
（4）将上述（3）中所得混合物加入上述（2）中保温2小时的混合物中，充分搅拌并混合均匀，待水分烘干冷却后制得包埋粉。
二烯丙基硫化物为二烯丙基一硫化物、二烯丙基二硫化物、二烯丙基三硫化物和蒜氨酸硫化物，具有抗氧化、抗肿瘤、抗感染、防治心脑血管疾病、调节肝脏药物代谢酶、抗神经变性等广泛的药理学作用，可以起到较好的杀菌效果，二烯丙基硫化物可以由洋葱的鳞茎为原料进行提取。
薄荷叶烯类提取物为柠檬烯、莰烯与蔽烯，可以通过薄荷叶进行提取，在制成义齿后，于口腔内可以在呼吸时保持口气清新，通过将薄荷叶混合打浆，并加入乙醇溶液搅拌均匀后再加入乙酸乙酯后提取混合液，将混合液加热蒸发后得到烯类提取物。
绿茶提取物为氟，可以与磷石灰结合，增加表面硬度，从而具备较好的抗酸防蛀效果，将茶叶置于100℃-120℃的蒸汽中进行杀青处理，随后将茶叶粉碎，加入95%乙醇溶液进行提取，将提取液取出后进行真空浓缩处理即可制得。
磷灰石为浅黄色粉末，磷石灰是指磷以晶质磷灰石形式存在于火成岩和变质岩中的含磷矿石，是一系列含钙的磷酸盐矿物的总称，同时人类牙齿部分的主要无机物，也是一种重要的生物材料。
本发明的有益效果：本发明通过加入氧化锆、氧化钇、氧化铈，将氧化锆加热至1100℃形成四相晶相，同时由氧化钇与氧化铈作为氧化锆的稳定剂，防止冷却后四相晶相的产品开裂，提高稳定性，在制成义齿后，进行义齿的热塑后，冷却后义齿不易开裂变形，具备较好的热塑性，为义齿的热塑过程进行带来便利，通过加入二烯丙基硫化物，制成义齿后，由于二烯丙基一硫化物、二烯丙基二硫化物、二烯丙基三硫化物和蒜氨酸硫化物具备较好的抗氧化、抗肿瘤、抗感染、防治心脑血管疾病、调节肝脏药物代谢酶、抗神经变性等广泛的药理学作用，进而起到较好的杀菌效果，抑制口腔中细菌的生长，有利于使用者健康，通过加入薄荷叶烯类提取物，在制成义齿后，于口腔内可以在呼吸时保持口气清新，较为全面，通过加入磷灰石、绿茶提取物，绿茶提取物与磷灰石共同结合，使得义齿的表面硬度，防止受到侵蚀，从而使义齿具备较好的抗酸防蛀效果，延长使用寿命。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
制作方法具体步骤如下：
（1）按照组分及重量成分组成准备：聚甲基丙烯酸甲酯40份、氧化锆30份、氧化铈4份、氧化钇4份、氧化铝0.8份、分散剂3份、薄荷叶烯类提取物1.5份、磷灰石8份、绿茶提取物5.7份、二烯丙基硫化物3份；
（2）将氧化锆、氧化铝、氧化铈与氧化钇混合并搅拌均匀，加热至1100℃，氧化锆转变为四相晶相，氧化铈与氧化钇确保所得氧化锆四相晶体的稳定，形成混合物后保持温度2小时；
（3）将聚甲基丙烯酸甲酯、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物充分混合并搅拌均匀；
（4）将上述（3）中所得混合物加入上述（2）中保温2小时的混合物中，充分搅拌并混合均匀，待水分烘干冷却后制得包埋粉。
实施例2
制作方法具体步骤如下：
（1）按照组分及重量成分组成准备：聚甲基丙烯酸甲酯50份、氧化锆27份、氧化铈4份、氧化钇4份、氧化铝0.5份、分散剂3份、薄荷叶烯类提取物1份、磷灰石5份、绿茶提取物3份、二烯丙基硫化物2.5份；
（2）将氧化锆、氧化铝、氧化铈与氧化钇混合并搅拌均匀，加热至1100℃，氧化锆转变为四相晶相，氧化铈与氧化钇确保所得氧化锆四相晶体的稳定，形成混合物后保持温度2小时；
（3）将聚甲基丙烯酸甲酯、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物充分混合并搅拌均匀；
（4）将上述（3）中所得混合物加入上述（2）中保温2小时的混合物中，充分搅拌并混合均匀，待水分烘干冷却后制得包埋粉。
实施例3
制作方法具体步骤如下：
（1）按照组分及重量成分组成准备：聚甲基丙烯酸甲酯50份、氧化锆27份、氧化铈4份、氧化钇4份、氧化铝0.5份、分散剂3份、薄荷叶烯类提取物1份、磷灰石5份、绿茶提取物3份、二烯丙基硫化物2.5份；
（2）将氧化锆、氧化铝、氧化铈与氧化钇混合并搅拌均匀，加热至1100℃，氧化锆转变为四相晶相，氧化铈与氧化钇确保所得氧化锆四相晶体的稳定，形成混合物后保持温度2小时；
（3）将聚甲基丙烯酸甲酯、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物充分混合并搅拌均匀；
（4）将上述（3）中所得混合物加入上述（2）中保温2小时的混合物中，充分搅拌并混合均匀，待水分烘干冷却后制得包埋粉。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (9)
1.一种制备义齿用热稳定性能优异的包埋粉，其特征在于，该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯40-60份、氧化锆25-30份、氧化铈1-4份、氧化钇1-4份、氧化铝0.5-0.8份、分散剂2-3份、薄荷叶烯类提取物1-1.5份、磷灰石4-8份、绿茶提取物3-5.7份、二烯丙基硫化物2.5-3份。
2.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯40份、氧化锆30份、氧化铈4份、氧化钇4份、氧化铝0.8份、分散剂3份、薄荷叶烯类提取物1.5份、磷灰石8份、绿茶提取物5.7份、二烯丙基硫化物3份。
3.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯50份、氧化锆27份、氧化铈4份、氧化钇4份、氧化铝0.5份、分散剂3份、薄荷叶烯类提取物1份、磷灰石5份、绿茶提取物3份、二烯丙基硫化物2.5份。
4.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,该制备义齿用热稳定性能优异的包埋粉的组分及重量成分组成包括：聚甲基丙烯酸甲酯60份、氧化锆25份、氧化铈1份、氧化钇1份、氧化铝0.5份、分散剂2份、薄荷叶烯类提取物1份、磷灰石4份、绿茶提取物3份、二烯丙基硫化物2.5份。
5.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,所述聚甲基丙烯酸甲酯呈粉末状，通过甲基丙烯酸甲酯与过氧化苯甲酰在高温环境下反应分离回收后制得，所述分散剂为聚丙烯酰胺。
6.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,所述氧化锆为白色重质无定形粉末，通过将1 mol/L的高纯氧氯化锆溶液喷入温度为1000℃的分解炉中，水分蒸发后水解制得氧化锆。
7.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,所述氧化钇与氧化铈均为稳定剂，所述氧化铈为淡黄或黄褐色助粉末，通过氯化铈溶液加入草酸调节Ph值为2，沉淀出草酸铈再经加热熟化、分离、洗涤、烘干后于900～1000℃灼烧制成，所述氧化钇为白色略带黄色粉末，通过分解褐钇铌矿所得的混合稀土溶液经萃取、酸溶、萃取、直接浓缩、灼烧制得。
8.根据权利要求1所述的一种制备义齿用热稳定性能优异的包埋粉，其特征在于,所述氧化铝呈白色粉末状，通过氢氧化铝粉和氢氧化钠配制成的偏铝酸钠溶液后通入二氧化碳成胶，并于500-700℃焙烧制得。
9.根据权利要求1-8任一项所述的一种制备义齿用热稳定性能优异的包埋粉的加工方法，其特征在于，具体包括以下步骤：
（1）根据权利要求1-4任意一条所述的组分及重量成分组成准备聚甲基丙烯酸甲酯、氧化锆、氧化铈、氧化钇、氧化铝、分散剂、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物原材料；
（2）将氧化锆、氧化铝、氧化铈与氧化钇混合并搅拌均匀，加热至1100℃，氧化锆转变为四相晶相，氧化铈与氧化钇确保所得氧化锆四相晶体的稳定，形成混合物后保持温度2小时；
（3）将聚甲基丙烯酸甲酯、薄荷叶烯类提取物、磷灰石、绿茶提取物、二烯丙基硫化物充分混合并搅拌均匀；
（4）将上述（3）中所得混合物加入上述（2）中保温2小时的混合物中，充分搅拌并混合均匀，待水分烘干冷却后制得包埋粉。