CN110129136A - 一种玻璃水及应用 - Google Patents
一种玻璃水及应用 Download PDFInfo
- Publication number
- CN110129136A CN110129136A CN201910286755.5A CN201910286755A CN110129136A CN 110129136 A CN110129136 A CN 110129136A CN 201910286755 A CN201910286755 A CN 201910286755A CN 110129136 A CN110129136 A CN 110129136A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- bath
- solution
- titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种玻璃水及其应用，涉及化工产品技术领域，玻璃水包括重量份计的以下组分：乙醇10‑20份，丙二醇10‑20份，光触媒溶液5‑10份，表面活性剂5‑10份，聚硅氧烷0.1‑2份，去离子水30‑70份，香精0.2‑0.5份，对羟基苯甲酸酯类0.2‑1份；本发明的玻璃水具有光触媒催化分解功能，涂于玻璃，去除污渍效果更明显，能够更好保养玻璃，延长玻璃使用寿命；适用于各类玻璃表面的清洗，市场需求量巨大。
Description
技术领域
本发明涉及化工产品技术领域，尤其涉及一种玻璃水及应用。
背景技术
玻璃水是汽车清洗液俗称，属于汽车使用中的易耗品。汽车挡风玻璃水俗称玻璃水。
当车前挡风玻璃透明度下降的时候喷一喷玻璃水，就能够有明朗清晰的视野。特别是在夜间行车时，玻璃上的灰尘会散射光线，这时候就需要喷一喷玻璃水，让前挡风玻璃保持在最佳透明状态。有的车主认为清洗前挡风玻璃其实很简单，用不着小题大做。有个别的车主会放弃购买一瓶10-20元左右的专用玻璃水，选择"偏方"--自制的玻璃水，将酒精、洗洁精、洗涤剂或洗衣粉等兑一点水来替代专用玻璃水，认为又便宜又省心，但“偏方”玻璃水去污力不能满足玻璃实际应用；也有车主直接用清水充当玻璃水，作用清洁玻璃用，但清水对车窗上附着的脏污、虫尸等也没有比较彻底清洗的能力，而且使用清水在冬季很容易结冰。因此，需要一种抗污效果更佳的玻璃水。
发明内容
本发明针对以上问题，提供一种玻璃水，具抗污力更佳特点，能够更好保养玻璃，延长玻璃使用寿命。
所述玻璃水包括重量份计的以下组分：乙醇10-20份，丙二醇10-20份，光触媒溶液5-10份，表面活性剂5-10份，聚硅氧烷0.1-2份，去离子水30-70份，香精0.2-0.5份，对羟基苯甲酸酯类0.2-1份。
进一步，所述玻璃水包括重量份计的以下组分：乙醇15-20份，丙二醇15-20份，光触媒溶液8-10份，表面活性剂7-10份，聚硅氧烷0.1-2份，去离子水30-70份，香精0.2-0.5份，对羟基苯甲酸酯类0.2-1份。
进一步，所述表面活性剂为二辛基琥珀酸磺酸钠，十二烷基苯磺酸钠，甘胆酸钠一种或多种。
进一步，所述表面活性剂为十二烷基苯磺酸钠。
十二烷基苯磺酸钠是一种性能优良的合成阴离子表面活性剂，比肥皂更易溶于水，是一种黄色油状液体，由于泡沫粘度低既能快速气泡亦能易于消泡。有很好的脱脂能力并有很好的降低水的表面张力和润湿、渗透和乳化的性能。化学性质稳定，在酸性或碱性介质中以及加热条件下都不会分解。
进一步，所述光触媒溶液的有效成分为二氧化钛。
进一步，光触媒溶液的制备方法包括以下步骤：
S1：取二氧化钛前体溶液用离子交换树脂方法处理，得去离子化溶液。
S2:将S1去离子化溶液与螯合剂混合搅拌15-20min，得二氧化钛溶液。
降低溶液中离子的浓度有利于钛与螯合剂的螯合,二氧化钛前体与螯合剂，会极大提高光生载流子的分离效率和抑制电子-空穴的重新复合，从而进一步拓宽了二氧化钛的光波吸收范围，二氧化钛催化作用更好。
进一步，所述二氧化钛前体为四异丙氧基钛、正丙氧基钛、四正丁 氧基钛、四乙氧基钛和四甲氧基钛中的一种或多种。
进一步，所述螯合剂是二链烷醇胺或三链烷醇胺。
进一步，所述二氧化钛前体溶液与螯合剂按体积比8：2混合处理。
光触媒的作用机理是 ：在光照下,光子的能量大于半导体禁带宽度 ,其价带上的电子(e-) 就会被激发到导带上,同时在价带上产生空穴(h+)，激发态的导带电子和价带空穴又能重新合并,并产生热能或其他形式散发掉。当光触媒催化剂存在合适的俘获剂、表面缺陷或者其他因素时,电子和空穴的复合得到抑制,就会在光触媒催化剂表面发生氧化-还原反应。价带空穴是良好的氧化剂,导带电子是良好的还原剂,在半导体光催化反 应中, 一般与表面吸附的 H2O、O 2反应，生成氧化性很活泼的羟基自由基(·OH) 和超氧离子自由基(O2-)，能够把各种有机物直接氧化成CO2、H20等无机小分子,而且因为他们的氧化能力强,一般不停留在中间步骤,不产生中间产物，光触媒本身也不会被消耗。
相对于现有技术，本发明具有如下的优点及效果：
本发明的玻璃水具有光触媒催化分解功能，涂于玻璃，去除污渍效果更明显，能够更好保养玻璃，延长玻璃使用寿命；适用于各类玻璃表面的清洗，市场需求量巨大。
具体实施方式
以下结合具体实施例来进一步说明本发明，但实施例并不对本发明做任何形式的限定。除非特别说明，本发明采用的试剂、方法和设备为本技术领域常规试剂、方法和设备。
除非特别说明，本发明所用试剂和材料均为市购。
实施例1
一种玻璃水，玻璃水包括重量计的以下组分：
乙醇10份，丙二醇10份，光触媒溶液5份，表面活性剂5份，聚硅氧烷0.1份，去离子水30份，香精0.2份，对羟基苯甲酸酯类0.2份。
一种玻璃水制备方法：
S1：制备光触媒溶液：
取四异丙氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将去离子化溶液与二链烷醇胺按体积比8：2混合搅拌15min，得二氧化钛溶液。
S2：常温常压下,取乙醇，丙二醇，光触媒溶液，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精分别加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
实施例2
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇15份，丙二醇15份，光触媒溶液7份，二辛基琥珀酸磺酸钠7份，聚硅氧烷1份，去离子水50份，香精0.4份，对羟基苯甲酸酯类0.6份。
一种玻璃水制备方法：
S1：制备光触媒溶液：
取四异丙氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将去离子化溶液与二链烷醇胺按体积比8：2混合搅拌15min，得二氧化钛溶液。
S2：常温常压下,取乙醇，丙二醇，光触媒溶液，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精分别加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
实施例3
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇20份，丙二醇20份，光触媒溶液10份，甘胆酸钠10份，聚硅氧烷2份，去离子水70份，香精0.5份，对羟基苯甲酸酯类1份。
一种玻璃水制备方法：
S1：制备光触媒溶液：
取四正丁氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将去离子化溶液与二链烷醇胺按体积比8：2混合搅拌20min，得二氧化钛溶液。
S2：常温常压下,取乙醇、丙二醇、光触媒溶液、十二烷基苯磺酸钠、聚硅氧烷、对羟基苯甲酸酯类及香精分别加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
实施例4
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇15份，丙二醇15份，光触媒溶液7份，十二烷基苯磺酸钠7份，聚硅氧烷1份，去离子水50份，香精0.4份，对羟基苯甲酸酯类0.6份。
一种玻璃水制备方法：
S1：制备光触媒溶液：
取四乙氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将上述去离子化溶液与三链烷醇胺按体积比8：2混合搅拌20min，得二氧化钛溶液。
S2：常温常压下,取乙醇，丙二醇，光触媒溶液，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
实施例5
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇15份，丙二醇15份，光触媒溶液7份，十二烷基苯磺酸钠7份，聚硅氧烷1份，去离子水50份，香精0.4份，对羟基苯甲酸酯类0.6份。
一种玻璃水的制备方法：
S1：制备光触媒溶液：
取四甲氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将上述去离子化溶液与三链烷醇胺按体积比8：2混合搅拌20min，得二氧化钛溶液。
S2常温常压下,取乙醇、丙二醇、光触媒溶液、十二烷基苯磺酸钠、聚硅氧烷、对羟基苯甲酸酯类及香精加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
实施例6
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇15份，丙二醇15份，光触媒溶液7份，十二烷基苯磺酸钠7份，聚硅氧烷1份，去离子水50份，香精0.4份，对羟基苯甲酸酯类0.6份。
一种玻璃水的制备方法：
S1：制备光触媒溶液：
取四异丙氧基钛溶液用离子交换树脂方法处理，得去离子化溶液；
将S1去离子化溶液与三链烷醇胺按体积比8：2混合搅拌20min，得二氧化钛溶液。
S2：常温常压下,取乙醇，丙二醇，光触媒溶液，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
对比例1
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇20份，丙二醇20份，十二烷基苯磺酸钠10份，聚硅氧烷2份，去离子水70份，香精0.5份，对羟基苯甲酸酯类2份。
一种玻璃水制备方法：
常温常压下，取乙醇，丙二醇，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
对比例2
一种玻璃水，玻璃水包括重量份计的以下组分：
乙醇10份，丙二醇10份，十二烷基苯磺酸钠5份，聚硅氧烷0.1份，去离子水30份，香精0.2份，对羟基苯甲酸酯类0.2份。
常温常压下，取乙醇，丙二醇，十二烷基苯磺酸钠，聚硅氧烷，对羟基苯甲酸酯类，香精加入去离子水搅拌至完全溶解；形成稳定透明无沉淀的溶液，得玻璃水。
对所有实施例及对比例进行测试：
去污率测试：使标准人工污垢均匀附着于载玻片上，用玻璃水溶液在规定条件下洗涤后 ，测定污垢的去除百分率。
测试方法如下:
1.混合油配方 ：以牛油 ：猪油 ：植物油＝0.5：1：0.5的比例配制，将混合油置电炉上加热至 180°C,搅拌保持此温度 10 min，自然冷却至所需温度备用，得人工污垢;
2.取洁净载玻片用分析天平精确称重（准确至 1 mg）为MO，载玻片涂抹人工污垢后，放置在室外10天，得污片,污片再用分析天平精确称重（准确至 1 mg）为M1。
3.污片喷洒玻璃水,再用毛刷刷净,干燥后, 用分析天平精确称重（准确至 1 mg）为M2
计算结果:去污率%=(M1-M2)/(M1-M0)*100%。
M0： 涂污前载玻片质量,g；
M1： 涂污后载玻片质量,g；
M2：洗涤后污片的质量,g。
表1去污率测试表
。
从表1可以看出,实施例1-6中的去污效果好,对比例1-2去污效果差。
本公开中涉及的器件、装置、设备、系统的方框图仅作为示例性的例子并且不意图要求或暗示必须按照方框图示出的方式进行连接、布置、配置。如本领域技术人员将认识到的，可以按任意方式连接、布置、配置这些器件、装置、设备、系统。诸如“包括”、“包含”、“具有”等等的词语是开放性词汇，指“包括但不限于”，且可与其互换使用。这里所使用的词汇“或”和“和”指词汇“和/或”，且可与其互换使用，除非上下文明确指示不是如此。这里所使用的词汇“诸如”指词组“诸如但不限于”，且可与其互换使用。
另外，如在此使用的，在以“至少一个”开始的项的列举中使用的“或”指示分离的列举，例如“A、B或C的至少一个”的列举意味着A或B或C，或AB或AC或BC，或ABC（即A和B和C）。此外，措辞“示例的”不意味着描述的例子是优选的或者比其他例子更好。
提供所公开的方面的以上描述以使本领域的任何技术人员能够做出或者使用本公开。对这些方面的各种修改对于本领域技术人员而言是非常显而易见的，并且在此定义的一般原理可以应用于其他方面而不脱离本公开的范围。因此，本公开不意图被限制到在此示出的方面，而是按照与在此公开的原理和新颖的特征一致的最宽范围。
为了示例和描述的目的已经给出了以上描述。此外，此描述不意图将本公开的实施例限制到在此公开的形式。尽管以上已经讨论了多个示例方面和实施例，但是本领域技术人员将认识到其某些变型、修改、改变、添加和子组合。
Claims (9)
1.一种玻璃水，其特征在于，所述玻璃水包括重量份计的以下组分：乙醇10-20份，丙二醇10-20份，光触媒溶液5-10份，表面活性剂5-10份，聚硅氧烷0.1-2份，去离子水30-70份，香精0.2-0.5份，对羟基苯甲酸酯类0.2-1份。
2.根据权利要求1所述玻璃水，其特征在于，所述玻璃水包括重量份计的以下组分： 乙醇15-20份，丙二醇15-20份，光触媒溶液8-10份，表面活性剂7-10份，聚硅氧烷0.1-2份，去离子水30-70份，香精0.2-0.5份，对羟基苯甲酸酯类0.2-1份。
3.根据权利要求1或2所述玻璃水，其特征在于，所述表面活性剂为二辛基琥珀酸磺酸钠，十二烷基苯磺酸钠，甘胆酸钠一种或多种。
4.根据权利3所述玻璃水，其特征在于，所述表面活性剂为十二烷基苯磺酸钠。
5.根据权利要求1或2所述玻璃水，其特征在于，所述光触媒溶液的有效成分为二氧化钛。
6.根据权利要求1所述玻璃水，其特征在于，所述光触媒溶液的制备方法包括以下步骤：
S1：取二氧化钛前体溶液用离子交换树脂方法处理，得去离子化溶液；
S2:将S1去离子化溶液与螯合剂混合搅拌15-20min，得二氧化钛溶液。
7.根据权利要求6所述玻璃水，其特征在于，所述二氧化钛前体为四异丙氧基钛、正丙氧基钛、四正丁氧基钛、四乙氧基钛和四甲氧基钛中的一种或多种。
8.根据权利要求6所述方法，其特征在于，所述螯合剂是二链烷醇胺或三链烷醇胺。
9.根据权利要求6所述方法，其特征在于，所述二氧化钛前体溶液与螯合剂按体积比8：2混合处理。