CN110128905A - 一种纤维基墙面装饰材料 - Google Patents

一种纤维基墙面装饰材料 Download PDF

Info

Publication number
CN110128905A
CN110128905A CN201910464067.3A CN201910464067A CN110128905A CN 110128905 A CN110128905 A CN 110128905A CN 201910464067 A CN201910464067 A CN 201910464067A CN 110128905 A CN110128905 A CN 110128905A
Authority
CN
China
Prior art keywords
wall surface
fiber base
decorative material
base decorative
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910464067.3A
Other languages
English (en)
Inventor
曾安然
张志斌
林燕禧
范琦迪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liming Vocational University
Original Assignee
Liming Vocational University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liming Vocational University filed Critical Liming Vocational University
Priority to CN201910464067.3A priority Critical patent/CN110128905A/zh
Publication of CN110128905A publication Critical patent/CN110128905A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种纤维基墙面装饰材料，包括下述重量份的各原料：海藻酸钙2‑4、贝壳粉6‑8、二氧化硅负载电气石/二氧化钛的复配物20‑30、改性天然纤维100‑130、氨基硅烷4‑7、过硫酸铵1‑2、香豆胶4‑6、丙烯酰胺20‑30，本发明选择海藻酸钙、贝壳粉等具有自阻燃和自防霉的材料，以减少非天然生物相容性材料，提高墙衣产品的亲和性。

Description

一种纤维基墙面装饰材料
技术领域
本发明属于材料领域，具体涉及一种纤维基墙面装饰材料。
背景技术
墙面材料是平整墙体表面的一种装饰凝材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品。涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。采用少量漆基、大量填料及适量的着色颜料配制而成，所用颜料主要是铁红、炭黑、铬黄等，填料主要是重碳酸钙、滑石粉等。墙面材料可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆干透后，施涂于底漆表面，要求附着性好、烘烤过程中不产生裂纹。目前，建筑墙体的装饰普遍使用传统的墙面材料粉，该墙面材料粉用白乳胶、107胶、钛白粉等制成，这种材料存在附着力差、不耐水、使用寿命短等缺点，并且墙体表面易卷皮、掉渣、龟裂、脱粉等；
随着人们生活水平的不断提高，对于墙面材料品质的要求也越来越高，赋予墙面更多的功能也是目前研究的重点，同时，随着绿色环保、循环利用概念的不断深入，如何利用废弃物资源，降低资源消耗，使得成品墙面具有很高的环保性的研究也是十分重要的。
发明内容
本发明的目的是提供一种纤维基墙面装饰材料。
为实现上述目的，本发明采用以下技术方案：
一种纤维基墙面装饰材料，它包括下述重量份的各原料：
海藻酸钙2-4、贝壳粉6-8、二氧化硅负载电气石/二氧化钛的复配物20-30、改性天然纤维100-130、氨基硅烷4-7、过硫酸铵1-2、香豆胶4-6、丙烯酰胺20-30。
所述改性天然纤维的制备方法为：
取天然纤维，干燥后磨成细粉，加入到其重量8-10倍的乙醚中，搅拌均匀，送入到60-65℃的恒温水浴中，保温搅拌3-5小时，蒸馏除去乙醚，即得。
所述天然纤维为棉纤维、木纤维、竹纤维、羊毛纤维中的至少一种。
所述的二氧化硅负载电气石/二氧化钛的复配物是以四异丙醇钛为钛源，正硅酸乙酯为硅源，电气石粉为负离子添加剂，通过溶胶凝胶法制备。
所述的氨基硅烷为硅烷偶联剂kh550。
所述纤维基墙面装饰材料的制备方法，包括以下步骤：
（1）取过硫酸铵，加入到其重量30-40倍的去离子水中，搅拌均匀；
（2）取二氧化硅负载电气石/二氧化钛的复配物，加入到其重量27-30倍的无水乙醇中，加入氨基硅烷，在60-65℃下保温搅拌1-2小时，得氨基溶液；
（3）取氨基溶液、改性天然纤维混合，搅拌均匀，送入到恒温水浴中，在80-85℃下保温搅拌100-130分钟，出料冷却，与丙烯酰胺混合，搅拌均匀，送入到反应釜中，通入氮气，调节反应釜温度为70-75℃，加入过硫酸铵水溶液，保温搅拌3-5小时，出料冷却，得聚合物乳液；
（4）取上述聚合物乳液，与海藻酸钙、贝壳粉、香豆胶混合，搅拌均匀，送入到烘箱中，干燥，即得。
步骤（4）中所述的干燥温度为90-95℃。
本发明的优点：
本发明的涂料使用方便，施工时只需按固液比1：6加水搅拌即可进行涂装，干燥后即可成为墙面材料，本项目所开发负离子墙衣，使用天然原生纤维，实现纤维废弃物的高值化回收利用，体现节能减排的理念，在同类墙衣产品中未提及；
本发明通过溶胶凝胶法制备SiO2负载TiO2/电气石粉制备负离子功能材料，实现苯去除率29-35%和甲醛去除率85-90%，在同类墙衣产品中为最佳，特别是除苯方面，同类墙衣产品通常报道自身不含苯，但没有除外界苯的功能；
本发明将天然纤维采用油酸处理，不仅提高了纤维的柔软性，提高了纤维的装饰效果，而且与氨基改性的负离子功能材料共混，之后与丙烯酰胺单体共混，在引发剂作用下聚合，从而改善了纤维、负离子功能材料在水中的分散相容性，从而降低了本发明材料的涂覆工序，只需要在水中搅拌分散即可涂覆；
本发明选择海藻酸钙、贝壳粉等具有自阻燃和自防霉的材料，以减少非天然生物相容性材料，提高墙衣产品的亲和性。
具体实施方式
实施例1
一种纤维基墙面装饰材料，它包括下述重量份的各原料：
海藻酸钙2、贝壳粉6、二氧化硅负载电气石/二氧化钛的复配物20、改性天然纤维100、氨基硅烷4、过硫酸铵1、香豆胶4、丙烯酰胺20。
所述改性天然纤维的制备方法为：
取天然纤维，干燥后磨成细粉，加入到其重量8倍的乙醚中，搅拌均匀，送入到60℃的恒温水浴中，保温搅拌3小时，蒸馏除去乙醚，即得。
所述天然纤维为棉纤维。
所述的二氧化硅负载电气石/二氧化钛的复配物是以四异丙醇钛为钛源，正硅酸乙酯为硅源，电气石粉为负离子添加剂，通过溶胶凝胶法制备。
所述的氨基硅烷为硅烷偶联剂kh550。
所述纤维基墙面装饰材料的制备方法，包括以下步骤：
（1）取过硫酸铵，加入到其重量30倍的去离子水中，搅拌均匀；
（2）取二氧化硅负载电气石/二氧化钛的复配物，加入到其重量27倍的无水乙醇中，加入氨基硅烷，在60℃下保温搅拌1小时，得氨基溶液；
（3）取氨基溶液、改性天然纤维混合，搅拌均匀，送入到恒温水浴中，在80℃下保温搅拌100分钟，出料冷却，与丙烯酰胺混合，搅拌均匀，送入到反应釜中，通入氮气，调节反应釜温度为70℃，加入过硫酸铵水溶液，保温搅拌3小时，出料冷却，得聚合物乳液；
（4）取上述聚合物乳液，与海藻酸钙、贝壳粉、香豆胶混合，搅拌均匀，送入到烘箱中，干燥，即得。
步骤（4）中所述的干燥温度为90℃。
实施例2
一种纤维基墙面装饰材料，它包括下述重量份的各原料：
海藻酸钙4、贝壳粉8、二氧化硅负载电气石/二氧化钛的复配物30、改性天然纤维130、氨基硅烷4、过硫酸铵2、香豆胶6、丙烯酰胺30。
所述改性天然纤维的制备方法为：
取天然纤维，干燥后磨成细粉，加入到其重量10倍的乙醚中，搅拌均匀，送入到65℃的恒温水浴中，保温搅拌5小时，蒸馏除去乙醚，即得。
所述天然纤维为羊毛纤维。
所述的二氧化硅负载电气石/二氧化钛的复配物是以四异丙醇钛为钛源，正硅酸乙酯为硅源，电气石粉为负离子添加剂，通过溶胶凝胶法制备。
所述的氨基硅烷为硅烷偶联剂kh550。
所述纤维基墙面装饰材料的制备方法，包括以下步骤：
（1）取过硫酸铵，加入到其重量40倍的去离子水中，搅拌均匀；
（2）取二氧化硅负载电气石/二氧化钛的复配物，加入到其重量30倍的无水乙醇中，加入氨基硅烷，在65℃下保温搅拌2小时，得氨基溶液；
（3）取氨基溶液、改性天然纤维混合，搅拌均匀，送入到恒温水浴中，在85℃下保温搅拌130分钟，出料冷却，与丙烯酰胺混合，搅拌均匀，送入到反应釜中，通入氮气，调节反应釜温度为75℃，加入过硫酸铵水溶液，保温搅拌5小时，出料冷却，得聚合物乳液；
（4）取上述聚合物乳液，与海藻酸钙、贝壳粉、香豆胶混合，搅拌均匀，送入到烘箱中，干燥，即得。
步骤（4）中所述的干燥温度为95℃。
性能测试：
本发明实施例1的纤维基墙面装饰材料：
苯去除率29.9%；
甲醛去除率86.1%；
本发明实施例2的纤维基墙面装饰材料：
苯去除率34.6%；
甲醛去除率89.7%。

Claims (7)

1.一种纤维基墙面装饰材料，其特征在于，它包括下述重量份的各原料：
海藻酸钙2-4、贝壳粉6-8、二氧化硅负载电气石/二氧化钛的复配物20-30、改性天然纤维100-130、氨基硅烷4-7、过硫酸铵1-2、香豆胶4-6、丙烯酰胺20-30。
2.根据权利要求1所述的一种纤维基墙面装饰材料，其特征在于，所述改性天然纤维的制备方法为：
取天然纤维，干燥后磨成细粉，加入到其重量8-10倍的乙醚中，搅拌均匀，送入到60-65℃的恒温水浴中，保温搅拌3-5小时，蒸馏除去乙醚，即得。
3.根据权利要求2所述的一种纤维基墙面装饰材料，其特征在于，所述天然纤维为棉纤维、木纤维、竹纤维、羊毛纤维中的至少一种。
4.根据权利要求1所述的一种纤维基墙面装饰材料，其特征在于，所述的二氧化硅负载电气石/二氧化钛的复配物是以四异丙醇钛为钛源，正硅酸乙酯为硅源，电气石粉为负离子添加剂，通过溶胶凝胶法制备。
5.根据权利要求1所述的一种纤维基墙面装饰材料，其特征在于，所述的氨基硅烷为硅烷偶联剂kh550。
6.根据权利要求1所述的一种纤维基墙面装饰材料，其特征在于，所述纤维基墙面装饰材料的制备方法，包括以下步骤：
（1）取过硫酸铵，加入到其重量30-40倍的去离子水中，搅拌均匀；
（2）取二氧化硅负载电气石/二氧化钛的复配物，加入到其重量27-30倍的无水乙醇中，加入氨基硅烷，在60-65℃下保温搅拌1-2小时，得氨基溶液；
（3）取氨基溶液、改性天然纤维混合，搅拌均匀，送入到恒温水浴中，在80-85℃下保温搅拌100-130分钟，出料冷却，与丙烯酰胺混合，搅拌均匀，送入到反应釜中，通入氮气，调节反应釜温度为70-75℃，加入过硫酸铵水溶液，保温搅拌3-5小时，出料冷却，得聚合物乳液；
（4）取上述聚合物乳液，与海藻酸钙、贝壳粉、香豆胶混合，搅拌均匀，送入到烘箱中，干燥，即得。
7.根据权利要求6所述的一种纤维基墙面装饰材料，其特征在于，步骤（4）中所述的干燥温度为90-95℃。
CN201910464067.3A 2019-05-30 2019-05-30 一种纤维基墙面装饰材料 Pending CN110128905A (zh)