CN110087346A - A kind of graphite-epoxy heat generating pastes - Google Patents
A kind of graphite-epoxy heat generating pastes Download PDFInfo
- Publication number
- CN110087346A CN110087346A CN201910275953.1A CN201910275953A CN110087346A CN 110087346 A CN110087346 A CN 110087346A CN 201910275953 A CN201910275953 A CN 201910275953A CN 110087346 A CN110087346 A CN 110087346A
- Authority
- CN
- China
- Prior art keywords
- parts
- graphite
- heat generating
- powder
- generating pastes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to graphite technology fields, in particular a kind of graphite-epoxy heat generating pastes, the slurry includes graphite, carbon black, metal powder, synthetic resin, corrosion-resistant agent, diluent and adhesive, and the weight proportion of the slurry is as follows, the graphite is 15~30 parts, the carbon black is 5~15 parts, the metal powder is 6~13 parts, the synthetic resin is 6~12 parts, the corrosion-resistant agent is 2~9 parts, the diluent is 5~10 parts, described adhesive is 3~6 parts, heat generating pastes use graphite, carbon black, metal powder and synthetic resin composition, heat generating pastes fever is fast when in use, temperature adjustment speed is high, can the stable use to normal production and living provide safeguard, reduce mechanical rate of breakdown, improve the efficiency of production and living, the heat generating pastes simultaneously, decaying Rate is slow, high stability, ensure that the service life of heat generating pastes.
Description
Technical field
The present invention relates to graphite technology field, specially a kind of graphite-epoxy heat generating pastes.
Background technique
Graphite is a kind of allotrope of elemental carbon, and the periphery of each carbon atom links the other three carbon atom (row
Column mode is in cellular multiple hexagons) with Covalent bonding together, covalent molecule is constituted, the fusing point of graphite is 3850 ± 50 DEG C,
Boiling point is 4250 DEG C, though through superhigh temperature electric arc calcination, the loss very little of weight, thermal expansion coefficient also very little.Graphite intensity with
Temperature improves and reinforces, and at 2000 DEG C, graphite intensity is doubled, and graphite and carbon product have excellent performance, application
Increasingly extensive, production capacity and benefit present a rapidly rising trend, and therefore, the demand to a kind of graphite-epoxy heat generating pastes is growing.
Currently there are most of heat generating pastes that there are electrothermal calefactive rates is slower, increase working time, stability
It is poor, and when the temperature is excessively high, the decaying of material can be caused, be unfavorable for the use of normal production and living, therefore, asked for above-mentioned
Topic proposes a kind of graphite-epoxy heat generating pastes.
Summary of the invention
The purpose of the present invention is to provide a kind of graphite-epoxy heat generating pastes, to solve mentioned above in the background art ask
Topic.
To achieve the above object, the invention provides the following technical scheme:
A kind of graphite-epoxy heat generating pastes, the slurry include graphite, carbon black, metal powder, synthetic resin, corrosion-resistant agent, dilution
Agent and adhesive, and the weight proportion of the slurry is as follows, and the graphite is 15~30 parts, and the carbon black is 5~15 parts, described
Metal powder be 6~13 parts, the synthetic resin be 6~12 parts, the corrosion-resistant agent be 2~9 parts, the diluent be 5~
10 parts, described adhesive is 3~6 parts.
Preferably, the ratio of the graphite, carbon black, metal powder and synthetic resin is 18~25 parts of graphite, carbon black 8
~14 parts, 6~10 parts of metal powder, 7~10 parts of synthetic resin.
Preferably, described adhesive is the high-temperature-resistant adhesive with heating conduction.
Preferably, the mass ratio of the corrosion-resistant agent, diluent and adhesive is 1: (1.5~2): (1.3~1.7).
It preferably, include iron powder, silver powder, copper powder and aluminium powder, the iron powder, silver powder, copper powder and aluminium in the metal powder
The mass ratio of powder is 2: 1: 3: 2.
Preferably, the synthetic resin is epoxy resin.
Compared with prior art, the beneficial effects of the present invention are:
In the present invention, heat generating pastes are formed using graphite, carbon black, metal powder and synthetic resin, when in use the heat generating pastes
Fever is fast, and temperature adjustment speed is high, can the stable use to normal production and living provide safeguard, reduce mechanical event
Hinder incidence, improves the efficiency of production and living, while the heat generating pastes, rate of decay is slow, high stability, ensure that fever
The service life of slurry has stronger practical value.
Specific embodiment
Embodiment 1:
A kind of graphite-epoxy heat generating pastes, the formula of raw material by weight are as follows: 20 parts of graphite, 13 parts of carbon black, synthetic resin 9
Part, 8 parts of metal powder, 3.5 parts of corrosion-resistant agent, 6 parts of diluent and 4.5 parts of adhesive.
It include iron powder, silver powder, copper powder and aluminium powder, the quality of the iron powder, silver powder, copper powder and aluminium powder in the metal powder
Than being 2: 1: 3: 2.
The synthetic resin is epoxy resin.
Embodiment 2:
A kind of graphite-epoxy heat generating pastes, the formula of raw material by weight are as follows: 15 parts of graphite, 10 parts of carbon black, synthetic resin 8
Part, 7 parts of metal powder, 2 parts of corrosion-resistant agent, 5 parts of diluent and 3 parts of adhesive.
It include iron powder, silver powder, copper powder and aluminium powder, the quality of the iron powder, silver powder, copper powder and aluminium powder in the metal powder
Than being 2: 1: 3: 2.
Embodiment 3:
A kind of graphite-epoxy heat generating pastes, the formula of raw material by weight are as follows: 25 parts of graphite, 14 parts of carbon black, synthetic resin 10
Part, 10 parts of metal powder, 5 parts of corrosion-resistant agent, 7 parts of diluent and 6 parts of adhesive.
It include iron powder, silver powder, copper powder and aluminium powder, the quality of the iron powder, silver powder, copper powder and aluminium powder in the metal powder
Than being 2: 1: 3: 2.
In conclusion the present invention is using graphite as primary raw material, and add carbon black, metal powder, synthetic resin, corrosion-resistant
Agent, diluent and adhesive make the heat generating pastes have many advantages, such as that fever is fast, stability is high, decaying is few, and are increasing the hair
Under the premise of hot slurry physical life, the working efficiency of heat generating pastes is improved.
Used herein a specific example illustrates the principle and implementation of the invention, the explanation of above example
It is merely used to help understand method and its core concept of the invention.The above is only a preferred embodiment of the present invention, it answers
When pointing out due to the finiteness of literal expression, and objectively there is unlimited specific structure, for the common skill of the art
For art personnel, without departing from the principle of the present invention, several improvement, retouching or variation can also be made, can also incited somebody to action
Above-mentioned technical characteristic is combined in the right way;These improve retouching, variation or combination, or the not improved structure by invention
Think and technical solution directly applies to other occasions, is regarded as protection scope of the present invention.
Claims (6)
1. a kind of graphite-epoxy heat generating pastes, which includes graphite, carbon black, metal powder, synthetic resin, corrosion-resistant agent, dilute
Agent and adhesive are released, and the weight proportion of the slurry is as follows, the graphite is 15~30 parts, and the carbon black is 5~15 parts, institute
Stating metal powder is 6~13 parts, and the synthetic resin is 6~12 parts, and the corrosion-resistant agent is 2~9 parts, and the diluent is 5
~10 parts, described adhesive is 3~6 parts.
2. a kind of graphite-epoxy heat generating pastes according to claim 1, it is characterised in that: the graphite, carbon black, metal powder
End and synthetic resin ratio be 18~25 parts of graphite, 8~14 parts of carbon black, 6~10 parts of metal powder, synthetic resin 7~
10 parts.
3. a kind of graphite-epoxy heat generating pastes according to claim 1, it is characterised in that: described adhesive is with thermally conductive
The high-temperature-resistant adhesive of performance.
4. a kind of graphite-epoxy heat generating pastes according to claim 1, it is characterised in that: the corrosion-resistant agent, diluent
Mass ratio with adhesive is 1: (2.5~3): (1.3~1.7).
5. a kind of graphite-epoxy heat generating pastes according to claim 1, it is characterised in that: include iron in the metal powder
Powder, silver powder, copper powder and aluminium powder, the iron powder, silver powder, copper powder and aluminium powder mass ratio be 2: 1: 3: 2.
6. a kind of graphite-epoxy heat generating pastes according to claim 1, it is characterised in that: the synthetic resin is asphalt mixtures modified by epoxy resin
Rouge.