CN110078428A - A kind of cork and cement mixing materials for wall - Google Patents
A kind of cork and cement mixing materials for wall Download PDFInfo
- Publication number
- CN110078428A CN110078428A CN201910405012.5A CN201910405012A CN110078428A CN 110078428 A CN110078428 A CN 110078428A CN 201910405012 A CN201910405012 A CN 201910405012A CN 110078428 A CN110078428 A CN 110078428A
- Authority
- CN
- China
- Prior art keywords
- wall
- cork
- cement
- water
- blender
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of cork and cement mixing materials for wall, it is related to the field of building materials, including following raw material: granulated cork, cement, blender, water and prefabricated wall shell, granulated cork, cement, blender, the mass ratio of water is 2-12:0-4:1-2:0-2, production method is versatile and flexible, it is required according to construction site, it can choose 3D spray and build technology injection, it can also be with Prefabricated block, inventive article has heat preservation, it is heat-insulated, sound insulation, fireproofing function, manufacturing process does not contain chemical components, naturally it polymerize, it is environmentally protective, it is non-toxic and tasteless, firmness degree is high, external structure is also very smooth, it will not be broken, it will not deform, after shell is removed, it can be with natural degradation.
Description
Technical field
The present invention relates to building material technical fields, and in particular to a kind of cork and cement mixing materials for wall.
Background technique
China's materials for wall is constituted in product, and overall craft is horizontal, and product quality is fallen significantly with using function etc.
Afterwards in industrially developed country.For a long time, fritter solid clay brick accounts for " absolutely system in China's materials for wall product composition
Control " status, Chinese " kingdom " for being referred to as fritter solid clay brick in the world is deposited for production with using fritter solid clay brick
Soil, high energy consumption and serious the problems such as polluting environment ruining are taken, the necessary Devoting Major Efforts To Developing in China and popularization section are native, and energy saving, benefit is given up, more
Function is good for the environment and meets all kinds of new shape materials for walls of sustainable development requirement, has not in this kind of materials for wall
It there has been 40 or five ten years in developed country less or the experience for producing with using of longer time, such as Thistle board, concrete be empty
Heart brick etc., but the present situation of China's materials for wall is combined, for traditional fritter solid clay brick, to China overwhelming majority
It is still more strange for people.
In the prior art, the building reinforced concrete light wall material of production be typically all use cementitious material, sand,
Water, water-reducing agent, foaming agent etc. are made, and wherein cementitious material generally uses 42.5 grades or more of full cement, production cost phase
To higher, in addition the method for the building reinforced concrete light wall material of existing production is generally all more complicated, influence
The development of light wall material.The wall or brick mix structure cement wall of traditional cement and foaming EVA particle, they
Heat preservation and heat-proof quality are low, usually using air conditioner refrigerating and heating, need to select powerful equipment, cause energy consumption larger,
After product is removed, it cannot degrade, pollution will cause to environment.In prefabricated building construction, heavier cement wall plate, originally for building
Body needs higher requirement, and installation and removal are extremely inconvenient.It is severe with traditional more difficult reply execution conditions of materials for wall, construction
Time insufficient engineering project.Brick mix structure wallboard weight is heavier, is formed in assembled building containing many places metal fittings
Frame, inconvenient using traditional walling material, the project amount for needing to put into is huge, such as: light steel house, weight steel house.With
Traditional materials for wall difficulty implements Waterborne movable building, and builds to the area that ground requires.With traditional materials for wall,
Form of construction work is single, site operation ratio be it is more, construction cost and material cost are high.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of cork and cement mixing materials for wall, materials for wall constructions
Mode can be coped with flexibly, and the single method of wall construction is got rid of, and inventive article can pour, filling, can also be pre- in advance
The building block of certain size is made, there is heat preservation, heat-insulated, sound insulation, fireproofing function.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of cork and cement mixing materials for wall, including following raw material: granulated cork, cement, blender, water and prefabricated wall
Shell, granulated cork, cement, blender, water mass ratio be 2-12:0-4:1-2:0-2.Granulated cork can be plurality of specifications
Granulated cork of different shapes, the grain that the dosage of granulated cork depends on cork is thick, and granulated cork is thick, cement just more
A bit, when granulated cork is tiny, the dosage of cement can be less.
Further, granulated cork, cement, blender, water mass ratio be 3:1:1:1.
Further, prefabricated wall shell is calcium silicate board, sheet metal, wood-plastic board, one of stone-plastic plate, ceramic tile.
Above-mentioned cork is with cement mixing materials for wall the preparation method comprises the following steps: granulated cork, cement, blender, water are mixed
It is adjusted to slurry, filling mode is built using 3D spray, prefabricated wall shell inner cavity is poured into thick mouth plastic cement pipeline, outside prefabricated wall
Shell inner cavity distribution bar item solidifies through a few hours until mixture slurry fills and leads up wall cavity, forms firm solid wall, obtain
Product.
Further, cork and cement mixing materials for wall are used to prepare building floating on water surface plate, floating on water surface plate
The preparation method comprises the following steps: prefabricated wall shell is cavity type aluminium alloy cuboid, inner cavity distribution bar item pours into granulated cork, adjusts
With the mixture slurry of both agent, makes its inner material solidification bonding, obtain the building floating on water surface plate with bearing capacity, adjust
It is PUR glue with agent.
Further, cork and cement mixing materials for wall are used to prepare land building board, the system of land building board
Preparation Method are as follows: prefabricated wall shell is calcium silicate board, by hollow out above and below calcium silicate board, inner cavity distribution bar item, by granulated cork,
Cement, blender, water mixing are adjusted to liquid pulpous state, are poured into steel structure module cavity with thick mouth plastic cement pipeline, make to mix
Liquid pulpous state fills full mould inside cavity, and after a few hours solidify, land building board is made.
Further, cork and cement mixing materials for wall are used to prepare land building board, the system of land building board
Preparation Method are as follows: prefabricated wall shell is wood-plastic board, by hollow out at the top of wood-plastic board, inner cavity distribution bar item, by granulated cork, water
Mud, blender, water mixing are adjusted to liquid pulpous state, are poured into steel structure module cavity with thick mouth plastic cement pipeline, make mixed liquor
Somaplasm shape fills full mould inside cavity, and after a few hours solidify, land building board is made.
(3) beneficial effect
The present invention provides a kind of corks and cement mixing materials for wall, have the following beneficial effects:
1, the formula of inventive article raw material and the configuration of the granulated cork and cement of proportion and different shape and specification, so that
Product has heat preservation, heat-insulated, sound insulation, fireproofing function.
2, inventive article manufacturing process itself does not contain chemical components, polymerize naturally, environmentally protective, non-toxic and tasteless.
3, the production method of inventive article is versatile and flexible, is required according to construction site, can choose 3D spray and builds technology note
Enter, it can also be with Prefabricated block.
4, inventive article is firm, and lighter in weight, is very suitable to renovation plus builds, builds light steel house, aquatic building
Deng the area required to ground load-bearing.
5, prefabricated wall shell can choose calcium silicate board and sheet metal, directly form prefabricated solid wall plate after perfusion,
Firmness degree is high, and external structure is also very smooth, instead of brick mix structure.
6, source material mutually blends inside inventive article, forms light firm solid wall, will not be broken, will not
Deformation.
It 7, can be with natural degradation after inventive article removes shell after removing.
Detailed description of the invention
In order to illustrate the technical solution of the embodiments of the present invention more clearly, required use in being described below to embodiment
Attached drawing be briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for this
For the those of ordinary skill of field, without creative efforts, it can also be obtained according to these attached drawings others
Attached drawing.
Fig. 1 materials for wall schematic diagram of the present invention；
In figure: the prefabricated wall shell of 1- granulated cork, 2- cement, 3-.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of cork and cement mixing materials for wall, including following raw material: granulated cork 1, cement 2, blender, water and dry wall
Body shell 3, granulated cork 1, cement 2, blender, water mass ratio be 3:1:1:1, preparation method are as follows: build and fill out using 3D spray
Mode is filled, granulated cork 1, cement 2, blender, water are mixed and are adjusted to slurry, pours into sheet metal with thick mouth plastic cement pipeline
In steel structure module cavity in prefabricated wall shell 3, until mixing mud fills and leads up wall cavity, solidify through a few hours, is formed
Firm solid wall, obtains product.
Embodiment 2:
A kind of cork and cement mixing materials for wall, including following raw material: granulated cork 1, cement 2, blender, water and dry wall
Body shell 3, granulated cork 1, cement 2, blender, water mass ratio be 3:1:1:1, preparation method are as follows: using pour filling
Calcium silicate board is made into wall and touches tool by mode, and insert number reinforcing bar is uniformly distributed it, and fixes position, by cork
Particle 1, blender and cement 2, investment touch in tool, water are then added, is adjusted to resulting mixture pulpous state, allow granulated cork using pouring
1 and cement 2 sufficiently and reinforcing bar contact, formation unitary solid, solidify through a few hours, materials for wall is formed.
Embodiment 3:
A kind of cork and cement mixing materials for wall, including following raw material: granulated cork 1, cement 2, blender, water and dry wall
Body shell 3, granulated cork 1, cement 2, blender, water mass ratio be 12:4:1:2, prefabricated wall shell 3 be stone-plastic plate,
The preparation method comprises the following steps: building filling mode using 3D spray, granulated cork 1, cement 2, blender, water are mixed and are adjusted to slurry, with thick mouth
Plastic cement pipeline pours into the steel structure module cavity in the prefabricated wall shell 3 of stone-plastic plate, until mixing mud fills and leads up wall
Cavity solidifies through a few hours, forms firm solid wall, obtains product.
Embodiment 4:
A kind of cork and cement mixing materials for wall, including following raw material: granulated cork 1, cement 2, blender, water and dry wall
Body shell 3, granulated cork 1, cement 2, blender, water mass ratio be 2:1:1:1, prefabricated wall shell 3 be aluminium alloy plate,
The preparation method comprises the following steps: building filling mode using 3D spray, granulated cork 1, cement 2, blender, water are mixed and are adjusted to slurry, with thick mouth
Plastic cement pipeline pours into the steel structure module cavity in the prefabricated wall shell 3 of aluminium alloy plate, until mixing mud fills and leads up wall
Body cavity, solidifies through a few hours, forms firm solid wall, obtains product.
Embodiment 5:
A kind of building floating on water surface plate, shell are cavity type aluminium alloy cuboid, and inner cavity distribution bar item pours into granulated cork
1, the mixture slurry of both blenders makes its inner material solidification bonding, obtains the building floating on water surface plate with bearing capacity
Material, granulated cork 1, the mass ratio of blender are 3:1:1, and blender is PUR glue.
Embodiment 6:
A kind of land building board, shell are calcium silicate board, by hollow out above and below calcium silicate board, inner cavity distribution bar item, by cork
Particle 1, cement 2, blender, water mixing are adjusted to liquid pulpous state, are poured into steel structure module cavity with thick mouth plastic cement pipeline,
So that mixing liquid pulpous state is filled full mould inside cavity, after a few hours solidify, land building board, the granulated cork is made
1, cement 2, blender, water mass ratio be 3:1:1:1.
Embodiment 7:
A kind of land building board, shell are wood-plastic board, by hollow out at the top of wood-plastic board, inner cavity distribution bar item, by granulated cork
1, cement 2, blender, water mixing are adjusted to liquid pulpous state, are poured into steel structure module cavity with thick mouth plastic cement pipeline, make to mix
It closes liquid pulpous state and fills full mould inside cavity, after a few hours solidify, land building board, the granulated cork 1, water is made
Mud 2, blender, water mass ratio be 3:1:1:1.
To sum up, the embodiment of the present invention has the following beneficial effects: 1-7 product of the embodiment of the present invention, has heat preservation, heat-insulated,
Sound insulation, fireproofing function, manufacturing process do not contain chemical components, polymerize naturally, environmentally protective, non-toxic and tasteless, and firmness degree is high, outside
Portion's structure is also very smooth, will not be broken, and will not deform, can be with natural degradation after shell is removed.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (7)
1. a kind of cork and cement mixing materials for wall, which is characterized in that including following raw material: granulated cork, cement, reconciliation
Agent, water and prefabricated wall shell, the granulated cork, cement, blender, water mass ratio be 2-12:0-4:1-2:0-2.
2. cork as described in claim 1 and cement mixing materials for wall, which is characterized in that the granulated cork, cement, tune
Mass ratio with agent, water is 3:1:1:1.
3. cork as described in claim 1 and cement mixing materials for wall, which is characterized in that the prefabricated wall shell is silicon
Sour calcium plate, sheet metal, wood-plastic board, one of stone-plastic plate, ceramic tile.
4. cork as described in any one of claims 1-3 and cement mixing materials for wall, which is characterized in that the materials for wall
It is adjusted to slurry the preparation method comprises the following steps: granulated cork, cement, blender, water are mixed, pours into dry wall with thick mouth plastic cement pipeline
Body shell inner cavity, the prefabricated wall shell inner cavity distribution bar item, until mixture slurry fills and leads up wall cavity, it is solid through a few hours
Change, forms firm solid wall, obtain product.
5. cork as claimed in claim 3 and cement mixing materials for wall, which is characterized in that the cork and cement mixing wall
Body material is used to prepare building floating on water surface plate, the floating on water surface plate the preparation method comprises the following steps: the prefabricated wall shell
For cavity type aluminium alloy cuboid, inner cavity distribution bar item pours into granulated cork, and the mixture slurry of both blenders makes in it
Portion's substance solidification bonding, obtains the building floating on water surface plate with bearing capacity, and the blender is PUR glue.
6. cork as claimed in claim 3 and cement mixing materials for wall, which is characterized in that the cork and cement mixing wall
Body material is used to prepare land building board, the land building board the preparation method comprises the following steps: the prefabricated wall shell is silicon
Sour calcium plate, by hollow out above and below calcium silicate board, granulated cork, cement, blender, water are mixed and are adjusted to liquid by inner cavity distribution bar item
Somaplasm shape is poured into steel structure module cavity with thick mouth plastic cement pipeline, so that mixing liquid pulpous state is filled full mould inside empty
Land building board is made after a few hours solidify in chamber.
7. cork as claimed in claim 3 and cement mixing materials for wall, which is characterized in that the cork and cement mixing wall
Body material is used to prepare land building board, the land building board the preparation method comprises the following steps: the prefabricated wall shell is wood
Mould plate, by hollow out at the top of wood-plastic board, granulated cork, cement, blender, water are mixed and are adjusted to slush pulp by inner cavity distribution bar item
Shape is poured into steel structure module cavity with thick mouth plastic cement pipeline, and mixing liquid pulpous state is made to fill full mould inside cavity, warp
After a few hours solidification, land building board is made.