CN110077052A - A kind of formula and processing technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer - Google Patents
A kind of formula and processing technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer Download PDFInfo
- Publication number
- CN110077052A CN110077052A CN201910341979.1A CN201910341979A CN110077052A CN 110077052 A CN110077052 A CN 110077052A CN 201910341979 A CN201910341979 A CN 201910341979A CN 110077052 A CN110077052 A CN 110077052A
- Authority
- CN
- China
- Prior art keywords
- buddha
- fire prevention
- warrior attendant
- grams
- super abrasive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of formula and processing technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, it include: a kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, every square metre of formula of the Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer includes 4-6 grams of diamond dust, 1-2 grams of PVC plastic, 1-3 grams of melamine resin, 2-5 grams of Polyamide-Polyamsne-Epichlorohydrin, 1 square metre of aluminum oxide abrasion-proof paper and 1 square metre of silica plate.The formula and processing technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, pass through being used cooperatively for diamond dust, PVC plastic, melamine resin, Polyamide-Polyamsne-Epichlorohydrin, aluminum oxide abrasion-proof paper and silica plate, it ensure that the fire line and wearability of floor surface layer well, aluminum oxide abrasion-proof paper and silica plate opposite adhesive are greatly reduced the cost of adhesive by the adhesiveness for borrowing PVC plastic, melamine resin and Polyamide-Polyamsne-Epichlorohydrin simultaneously.
Description
Technical field
The present invention relates to floor processing technique field, a kind of specially Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer is matched
Side and production technology.
Background technique
Stone plastic floor is popular a kind of novel light body floor decorative material in the world today, also referred to as " light body
Material ", using very extensive, such as family, hospital, school, office building, factory, public place, supermarket, business, etc. various fields
Institute, stone plastic floor just refers to the floor produced using pvc material, particularly as being to be with polyvinyl chloride and its copolymer resins
The auxiliary materials such as filler, plasticizer, stabilizer, colorant, on sheet continuous base material, coated technique or warp are added in primary raw material
Calendering, extrusion or extrusion process produce, and stone plastic floor in process, in order to increase its fireproof wear-resisting, often exists
Floor surface layer is added on its surface, carries out protection operation with this.
In the prior art, in order to guarantee that the production cost on floor generally uses the floor surface layer of single structure, it is difficult to
The fire line and wearability of floor surface layer are improved under the premise of guaranteeing floor production cost well, it is difficult to meet well
The better use demand of user, weakens the market competitiveness on floor.The patent of existing application number CN201620476225.9
Disclose a kind of moisture-proof mute flax solid wooden compound floor of high abrasion-resistant fireproof.Although the invention solves the problems, such as, but be somebody's turn to do
Patent is reinforced only with fire line and wearability of the mode that various material layers are superimposed to floor, and performance is only by material
Influence, the fire line and wearability of floor entirety be still difficult to meet the use demand of user well.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of formulas of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer
And production technology, it solves in the prior art, in order to guarantee that the production cost on floor generally uses the floor table of single structure
Surface layer, it is difficult to improve the fire line of floor surface layer and asking for wearability under the premise of guaranteeing floor production cost well
Topic.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs:
1. a kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, the Buddha's warrior attendant fire prevention super abrasive stone plastic floor table
Every square metre of formula of surface layer is more including 4-6 grams of diamond dust, 1-2 grams of PVC plastic, 1-3 grams of melamine resin, polyamide
2-5 grams of amine epoxychloropropane, 1 square metre of aluminum oxide abrasion-proof paper and 1 square metre of silica plate.
Preferably, the aluminum oxide abrasion-proof paper with a thickness of 0.1-0.2 millimeters.
Preferably, the silica plate with a thickness of 1-1.5 millimeters.
2. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, includes following operating procedure:
S1, the production of plastic cement liquid: 1-2 grams of PVC plastic is heated to 160-180 DEG C, 4- is added after 10-15 minutes in continuous heating
6 grams of diamond dust, are sufficiently stirred, and it is spare that plastic cement liquid is made；
S2, resin fusion liquid production: by 1-3 grams of melamine resin and 2-5 grams of Polyamide-Polyamsne-Epichlorohydrin
It is put into container, and is heated to 130-140 DEG C, be sufficiently stirred, it is spare that resin fusion liquid is made；
S3, the production of plate ontology: 1 square metre of silica plate is horizontally arranged, and is poured in separately to the middle part of its front surface
Enter the fusion liquid of resin obtained in step S2, holding ambient temperature range is then merged in resin in 80-90 DEG C during this
1 square metre of aluminum oxide abrasion-proof paper is placed on liquid, while guaranteeing aluminum oxide abrasion-proof paper and silica Board position weight
It closes, apply pressure and carries out fast cooling operation, temperature is dropped to 20-25 DEG C, temperature-fall period is for 20 seconds, with this manufactured Board
Ontology, and be placed in spare in room temperature environment；
S4, the production of floor surface layer: plate ontology obtained in step S3 is horizontally arranged, while making aluminum oxide resistance to
Grind the one side of paper upward, the plastic cement liquid brush that step S1 is obtained is placed in shady place and air-dries on aluminum oxide abrasion-proof paper
24 hours, floor surface layer is made with this；
S5, the reprocessing of floor surface layer use the remaining resin fusion liquid in grinding device removal floor surface layer side and modeling
Glue completes the production of floor surface layer with this.
Preferably, it in the step S1, stirs and needs to guarantee the surface temperature of PVC plastic not less than 160 DEG C when spare.
Preferably, in the step S1, the duration of stirring is at least 15 minutes.
Preferably, it in the step S2, stirs and needs to guarantee the surface temperature of resin fusion liquid not less than 130 when spare
℃。
Preferably, in the step S3, pressure applied is at least 1kpa.
Preferably, in the step S4, plastic cement liquid brush is on aluminum oxide abrasion-proof paper, the wherein thickness range of plastic cement liquid
It is 0.1-0.15 millimeters.
(3) beneficial effect
The present invention provides a kind of formula and processing technologies of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer.Have following
The utility model has the advantages that
The formula and processing technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, passes through diamond dust, PVC plastic, three
Melamine-formaldehyde resin, Polyamide-Polyamsne-Epichlorohydrin, aluminum oxide abrasion-proof paper and silica plate are used cooperatively,
It ensure that the fire line and wearability of floor surface layer well, while borrowing PVC plastic, melamine resin and polyamides
The adhesiveness of amine epoxy polyamine chloropropane greatly reduces aluminum oxide abrasion-proof paper and silica plate opposite adhesive viscous
The cost of mixture can be very good to improve the fire line of floor surface layer and wear-resisting under the premise of guaranteeing floor production cost
Property, it can be very good to meet the better use demand of user, strengthen the market competitiveness on floor.
Specific embodiment
Described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, Buddha's warrior attendant fire prevention super abrasive stone plastic floor surface
Every square metre of formula of layer includes 4 grams of diamond dust, 2 grams of PVC plastic, 1 gram of melamine resin, polyamide polyamines epoxy chlorine
1 square metre of 5 grams of propane, 1 square metre of aluminum oxide abrasion-proof paper and silica plate (wherein thickness of aluminum oxide abrasion-proof paper
Be 0.2 millimeter, silica plate with a thickness of 1.5 millimeters).
A kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, includes following operating procedure:
S1, the production of plastic cement liquid: being heated to 160 DEG C for 2 grams of PVC plastics, and 4 grams of diamond dust are added in continuous heating after ten minutes,
Be sufficiently stirred, be made plastic cement liquid it is spare (stirring and it is spare when need to guarantee PVC plastic surface temperature be 170 DEG C, stirring is held
The continuous time is 15 minutes)；
S2, resin fusion liquid production: 1 gram of melamine resin and 5 grams of Polyamide-Polyamsne-Epichlorohydrins are put into
In container, and be heated to 140 DEG C, be sufficiently stirred, be made resin fusion liquid it is spare (stirring and it is spare when need to guarantee resin merge
The surface temperature of liquid is 140 DEG C, pressure applied 1.5kpa)；
S3, the production of plate ontology: 1 square metre of silica plate is horizontally arranged, and is poured in separately to the middle part of its front surface
Enter the fusion liquid of resin obtained in step S2, holding environment temperature is then to put on resin fusion liquid in 85 DEG C during this
1 square metre of aluminum oxide abrasion-proof paper is set, while guaranteeing that aluminum oxide abrasion-proof paper and silica Board position are overlapped, is applied
Pressure simultaneously carries out fast cooling operation, and temperature is dropped to 20 DEG C, and temperature-fall period is for 20 seconds, with this manufactured Board ontology, and puts
It is placed in spare in room temperature environment；
S4, the production of floor surface layer: plate ontology obtained in step S3 is horizontally arranged, while making aluminum oxide resistance to
Grind the one side of paper upward, the plastic cement liquid brush that step S1 is obtained is placed in shady place and air-dries on aluminum oxide abrasion-proof paper
24 hours, with this be made floor surface layer (plastic cement liquid brush on aluminum oxide abrasion-proof paper, wherein plastic cement liquid with a thickness of 0.1
Millimeter)；
S5, the reprocessing of floor surface layer use the remaining resin fusion liquid in grinding device removal floor surface layer side and modeling
Glue completes the production of floor surface layer with this.
Embodiment 2
A kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, Buddha's warrior attendant fire prevention super abrasive stone plastic floor surface
Every square metre of formula of layer includes 5 grams of diamond dust, 1.5 grams of PVC plastic, 1.5 grams of melamine resin, polyamide polyamines ring
1 square metre of 2.5 grams of oxygen chloropropane, 1 square metre of aluminum oxide abrasion-proof paper and silica plate (wherein aluminum oxide abrasion-proof paper
With a thickness of 0.2 millimeter, silica plate with a thickness of 1.2 millimeters).
A kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, includes following operating procedure:
S1, the production of plastic cement liquid: 5 grams of Buddha's warrior attendants are added after 1.5 grams of PVC plastics are heated to 170 DEG C, continuous heating 13 minutes
Sand is sufficiently stirred, be made plastic cement liquid it is spare (stirring and it is spare when need to guarantee PVC plastic surface temperature be 200 DEG C, stirring
Duration be 20 minutes)；
S2, resin fusion liquid production: by 1.5 grams of melamine resins and 2.5 grams of Polyamide-Polyamsne-Epichlorohydrins
Be put into container, and be heated to 140 DEG C, be sufficiently stirred, be made resin fusion liquid it is spare (stirring and it is spare when need to guarantee resin
The surface temperature for merging liquid is 140 DEG C, pressure applied 1.3kpa)；
S3, the production of plate ontology: 1 square metre of silica plate is horizontally arranged, and is poured in separately to the middle part of its front surface
Enter the fusion liquid of resin obtained in step S2, holding environment temperature is then to put on resin fusion liquid in 85 DEG C during this
1 square metre of aluminum oxide abrasion-proof paper is set, while guaranteeing that aluminum oxide abrasion-proof paper and silica Board position are overlapped, is applied
Pressure simultaneously carries out fast cooling operation, and temperature is dropped to 25 DEG C, and temperature-fall period is for 20 seconds, with this manufactured Board ontology, and puts
It is placed in spare in room temperature environment；
S4, the production of floor surface layer: plate ontology obtained in step S3 is horizontally arranged, while making aluminum oxide resistance to
Grind the one side of paper upward, the plastic cement liquid brush that step S1 is obtained is placed in shady place and air-dries on aluminum oxide abrasion-proof paper
24 hours, with this be made floor surface layer (plastic cement liquid brush on aluminum oxide abrasion-proof paper, wherein plastic cement liquid with a thickness of 0.13
Millimeter)；
S5, the reprocessing of floor surface layer use the remaining resin fusion liquid in grinding device removal floor surface layer side and modeling
Glue completes the production of floor surface layer with this.
Embodiment 3
A kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, Buddha's warrior attendant fire prevention super abrasive stone plastic floor surface
Every square metre of formula of layer includes 6 grams of diamond dust, 1.5 grams of PVC plastic, 2.5 grams of melamine resin, polyamide polyamines ring
4 grams of oxygen chloropropane, 1 square metre of 1 square metre of aluminum oxide abrasion-proof paper and silica plate (wherein aluminum oxide abrasion-proof paper
With a thickness of 0.15 millimeter, silica plate with a thickness of 1.5 millimeters).
A kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, includes following operating procedure:
S1, the production of plastic cement liquid: 6 grams of Buddha's warrior attendants are added after 1.5 grams of PVC plastics are heated to 175 DEG C, continuous heating 15 minutes
Sand is sufficiently stirred, be made plastic cement liquid it is spare (stirring and it is spare when need to guarantee PVC plastic surface temperature be 180 DEG C, stirring
Duration be 20 minutes)；
S2, resin fusion liquid production: 2.5 grams of melamine resins and 4 grams of Polyamide-Polyamsne-Epichlorohydrins are put
Enter in container, and be heated to 140 DEG C, be sufficiently stirred, be made resin fusion liquid it is spare (stirring and it is spare when need to guarantee that resin melts
The surface temperature for closing liquid is 200 DEG C, pressure applied 2kpa)；
S3, the production of plate ontology: 1 square metre of silica plate is horizontally arranged, and is poured in separately to the middle part of its front surface
Enter the fusion liquid of resin obtained in step S2, holding environment temperature is then to put on resin fusion liquid in 85 DEG C during this
1 square metre of aluminum oxide abrasion-proof paper is set, while guaranteeing that aluminum oxide abrasion-proof paper and silica Board position are overlapped, is applied
Pressure simultaneously carries out fast cooling operation, and temperature is dropped to 25 DEG C, and temperature-fall period is for 20 seconds, with this manufactured Board ontology, and puts
It is placed in spare in room temperature environment；
S4, the production of floor surface layer: plate ontology obtained in step S3 is horizontally arranged, while making aluminum oxide resistance to
Grind the one side of paper upward, the plastic cement liquid brush that step S1 is obtained is placed in shady place and air-dries on aluminum oxide abrasion-proof paper
24 hours, with this be made floor surface layer (plastic cement liquid brush on aluminum oxide abrasion-proof paper, wherein plastic cement liquid with a thickness of 0.15
Millimeter)；
S5, the reprocessing of floor surface layer use the remaining resin fusion liquid in grinding device removal floor surface layer side and modeling
Glue completes the production of floor surface layer with this.
Its design parameter is as follows: (wherein comparative example is fireproof wear-resisting floor common in the art, the survey of fire endurance
Try object are as follows: two-sided single layer 12mm corresponds to limiting value model of the 90mm light partition wall composed by plate under canonical measure environment
It encloses)
| Floor | Fire endurance | The wear-resisting revolving speed of unit materials | Density kg/m3 |
| Comparative example | 4-6 hours | 9000-12000 revs/min | 0.8-1 |
| Embodiment 1 | 5.5-6.5 hour | 13000-15000 revs/min | 0.7-0.9 |
| Embodiment 2 | 6-6.5 hour | 12000-15000 revs/min | 0.8-0.9 |
| Embodiment 3 | 6.5-7.5 hour | 11000-13000 revs/min | 0.7-0.8 |
In conclusion the Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer formula and processing technology, by diamond dust,
PVC plastic, melamine resin, Polyamide-Polyamsne-Epichlorohydrin, aluminum oxide abrasion-proof paper and silica plate
Be used cooperatively, ensure that the fire line and wearability of floor surface layer well, while borrowing PVC plastic, melamine first
The adhesiveness of urea formaldehyde and Polyamide-Polyamsne-Epichlorohydrin is by aluminum oxide abrasion-proof paper and silica plate opposite adhesive, pole
The big cost for reducing adhesive can be very good to improve the anti-of floor surface layer under the premise of guaranteeing floor production cost
Fire and wearability can be very good to meet the better use demand of user, strengthen the market competitiveness on floor.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, it is characterised in that: the Buddha's warrior attendant fire prevention super abrasive stone
Mould every square metre of formula of floor surface layer include 4-6 grams of diamond dust, 1-2 grams of PVC plastic, 1-3 grams of melamine resin,
2-5 grams of Polyamide-Polyamsne-Epichlorohydrin, 1 square metre of aluminum oxide abrasion-proof paper and 1 square metre of silica plate.
2. a kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 1, it is characterised in that: institute
State aluminum oxide abrasion-proof paper with a thickness of 0.1-0.2 millimeters.
3. a kind of formula of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 1, it is characterised in that: institute
State silica plate with a thickness of 1-1.5 millimeters.
4. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer, it is characterised in that: include following operating procedure:
S1, the production of plastic cement liquid: 4-6 grams is added after 1-2 grams of PVC plastic is heated to 160-180 DEG C, continuous heating 10-15 minutes
Diamond dust is sufficiently stirred, and it is spare that plastic cement liquid is made；
S2, resin fusion liquid production: 1-3 grams of melamine resin and 2-5 grams of Polyamide-Polyamsne-Epichlorohydrin are put into
In container, and it is heated to 130-140 DEG C, be sufficiently stirred, it is spare that resin fusion liquid is made；
S3, the production of plate ontology: 1 square metre of silica plate is horizontally arranged, and pours into step to the middle section of its front surface
Resin obtained in rapid S2 merges liquid, and holding ambient temperature range is in 80-90 DEG C during this, then on resin fusion liquid
1 square metre of aluminum oxide abrasion-proof paper is placed, while guaranteeing that aluminum oxide abrasion-proof paper and silica Board position are overlapped, is applied
Plus-pressure simultaneously carries out fast cooling operation, and temperature is dropped to 20-25 DEG C, and temperature-fall period is for 20 seconds, with this manufactured Board ontology,
And it is placed in spare in room temperature environment；
S4, the production of floor surface layer: plate ontology obtained in step S3 is horizontally arranged, while making aluminum oxide abrasion-proof paper
One side upward, the plastic cement liquid brush that step S1 is obtained is placed in shady place to air-dry 24 small on aluminum oxide abrasion-proof paper
When, floor surface layer is made with this；
S5, the reprocessing of floor surface layer use the remaining resin fusion liquid in grinding device removal floor surface layer side and plastic cement
Liquid completes the production of floor surface layer with this.
5. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 4, feature exist
In: in step sl, stirs and need to guarantee the surface temperature of PVC plastic not less than 160 DEG C when spare.
6. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 4, feature exist
In: in step sl, the duration of stirring is at least 15 minutes.
7. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 4, feature exist
In: in step s 2, stirs and need to guarantee the surface temperature of resin fusion liquid not less than 130 DEG C when spare.
8. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 4, feature exist
In: in step s3, pressure applied is at least 1kpa.
9. a kind of production technology of Buddha's warrior attendant fire prevention super abrasive stone plastic floor superficial layer according to claim 4, feature exist
In: in step s 4, plastic cement liquid brush is on aluminum oxide abrasion-proof paper, and wherein the thickness range of plastic cement liquid is 0.1-0.15 milli
Rice.