CN1100761A - 铝带宽温高速阳极氧化法 - Google Patents

铝带宽温高速阳极氧化法 Download PDF

Info

Publication number
CN1100761A
CN1100761A CN 93118026 CN93118026A CN1100761A CN 1100761 A CN1100761 A CN 1100761A CN 93118026 CN93118026 CN 93118026 CN 93118026 A CN93118026 A CN 93118026A CN 1100761 A CN1100761 A CN 1100761A
Authority
CN
China
Prior art keywords
additive
add
washing
grams per
oxidation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 93118026
Other languages
English (en)
Inventor
李德海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 93118026 priority Critical patent/CN1100761A/zh
Publication of CN1100761A publication Critical patent/CN1100761A/zh
Pending legal-status Critical Current

Abstract

一种铝带宽温高速阳极氧化法，其属于金属氧化 工艺。这种工艺采用在草酸和硫酸的混合溶液中加 入四种添加剂，并增设了有机氟封闭工艺，使得整个 工艺流程操作简化，效率提高，氧化温度可在10～ 50℃范围内正常生产，氧化速度提高到2米/分以 上，生产中无气味，不用使用排气机，减少了环境噪 声，铝带的氧化膜软硬度适中，耐击穿电压提高为 200～450V，而且耐火耐腐蚀，显著提高了氧化膜铝 带的质量。

Description

一种铝带宽温高速阳极氧化法，其属于金属氧化工艺。
氧化膜铝带曾采用草酸氧化法，其优点是氧化膜软，是部分电磁产品理想的绕组材料，但草酸氧化法耗电大、毒性大、速度慢、成本高、成品耐压低。采用硫酸氧化法克服了草酸氧化法成本高、耗电大、毒性大等缺点，但仍气味大，氧化过程中放出大量的酸气，刺激气管;氧化膜脆性大，弯折时发出明显的膜碎声，弯曲度大的线圈绕组，出现膜脆，耐压不合格;成品吸湿性大，一般放置3～5天后，耐压下降，尤其是夏季或阴雨季节更为明显;溶液温度高时，形成的氧化膜松脆，其适宜温度在13～26℃，夏季气温高，常被迫停产。
本发明的目的在于，研制一种铝带宽温高速阳极氧化法，该氧化法应克服上述草酸氧化法或硫酸氧化法的缺点，使氧化工艺的适应温度范围大，氧化速度快，无味无毒性，氧化膜软硬度适中，耐击穿电压高，防水防腐蚀。
本发明的技术解决方案是：一种铝带宽温高速阳极氧化法，它主要由碱腐蚀、水洗、水洗、中和、氧化、水洗、水洗、沸水封闭、烘烤、检测，成品的工艺步骤组成，本发明的特殊之处在于，在上述的烘烤与检测的工艺步骤之间又加入了有机化合物封闭、烘烤二个工艺步骤，氧化工艺采用在草酸和硫酸的混合溶液中加入4种添加剂。
在1～3%浓度的草酸和15～25%浓度的硫酸的混合溶液中，加入的ADD-1添加剂为18～26克/升，ADD-2添加剂为24～32克/升，ADD-3添加剂为41～49克/升，ADD-4添加剂为0.10～0.20克/升。
在有机化合物封闭工艺中采用浓度为5～15%的有机氟封闭剂。
上述技术解决方案的指导思想是：氧化工艺采用在草酸和硫酸的混合溶液中加入了4种添加剂，其目的在于保持早先草酸法和硫酸法的优点，添加剂的加入使生产实现了宽温、高速、无味，产品质量高。由于在整个工艺流程中加入了有机氟封闭工艺，有机氟会停留在铝带表面封闭氧化膜微孔，起到防水、防腐蚀的保护作用。拓宽了产品的应用范围。
本发明的效果在于，这种铝带宽温高速阳极氧化法，由于采用了在草酸和硫酸的混合溶液中加入了4种添加剂，又增加了有机化合物封闭工艺步骤，使得整个工艺流程操作简化，效率提高，氧化温度可在10～50℃范围内正常生产，氧化速度由以前0.5米/分提高到2米/分以上，因采用了酸雾抑制剂、生产中无气味，可停止使用排风机，减少了环境噪声，铝带的氧化膜软硬度适中，耐击穿电压提高为200～450V，而且耐水耐腐蚀，明显提高了使用该种铝带作为原料的产品质量。
下面是本发明的一个实施例，通过对该实施例的描述给出本发明的细节。
上述的铝带宽温高速阳极氧化法其工艺步骤如下：碱腐蚀、水洗、水洗、中和、氧化、水洗、水洗、沸水封闭、烘烤、有机化合物封闭、烘烤、检测、成品。大部分工艺步骤与传统工艺相同，其中要介绍的是氧化和有机化合物封闭二个工艺步骤。在氧化工艺中，采用2%浓度的草酸和20%浓度的硫酸混合溶液，并加入ADD-1添加剂22克/升，ADD-2添加剂28克/升，ADD-3添加剂45克/升，ADD-4添加剂0.15克/升，当电流密度为2～4安培/分米2时，铝带氧化的速度为2～4米/分。在有机化合物封闭工艺步骤中，采用10%浓度的有机氟，封闭时间为1分钟，铝带氧化膜的击穿电压大于200V。

Claims (3)

1、一种铝带宽温高速阳极氧化法，它主要由碱腐蚀、水洗、水洗、中和、氧化、水洗、水洗、沸水封闭、烘烤、检测、成品的工艺步骤组成，本发明的特征在于，在上述的烘烤与检测的工艺步骤之间又加入了有机化合物封闭、烘烤二个工艺步骤，氧化工艺采用草酸和硫酸的混合溶液中加入4种添加剂。
2、据权利要求1所述的铝带宽温高速阳极氧化法，其特征在于，在1～3%浓度的草酸和15～25%浓度的硫酸混合浓液中，加入的ADD-1添加剂为18～26克/升，ADD-2添加剂为24～32克/升，ADD-3添加剂为41～49克/升，ADD-4添加剂为0.10～0.20克/升。
3、据权利要求2所述的铝带宽温高速阳极氧化法，其特征在于，在有机化合物封闭工艺中采用浓度为5～15%的有机氟封闭剂。
CN 93118026 1993-09-23 1993-09-23 铝带宽温高速阳极氧化法 Pending CN1100761A (zh)