CN110067068A - A kind of temperature adjustment magnetic therapy health yarn fabric - Google Patents
A kind of temperature adjustment magnetic therapy health yarn fabric Download PDFInfo
- Publication number
- CN110067068A CN110067068A CN201910461878.8A CN201910461878A CN110067068A CN 110067068 A CN110067068 A CN 110067068A CN 201910461878 A CN201910461878 A CN 201910461878A CN 110067068 A CN110067068 A CN 110067068A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- fabric
- magnetic therapy
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of temperature adjustment magnetic therapy health yarn fabrics, woven fabric is woven into according to specific rule by the warp thread of two kinds of different function and the weft yarn of two kinds of different function, the warp thread includes the mixed yarn that the first is magnetic therapy fiber and Modal fibre and the mixed yarn that second of warp thread is temperature-regulating fiber and cotton fiber, and the warp thread of two kinds of different function alternates arrangement in fabric；The weft yarn include the first be also the mixed yarn of magnetic therapy fiber and Modal fibre and be also for second temperature-regulating fiber and cotton fiber mixed yarn, two kinds of weft yarns are alternately arranged according to specific rule in fabric；The warp and weft Yarn spinning method is all using match network compact spinning；The fabric tissue is using once twill-weave or plain weave is interleaved one on the other on two.The present invention can be undergone phase transition according to the variation of ambient temperature, and absorbed from the external world or outwardly discharged heat, the substantially invariable micro climate of formation temperature around textile, to realize temp regulating function.
Description
Technical field
The present invention relates to fabric technical fields, and in particular to one kind containing phase-changing and temperature-regulating functional fibre, magnetic therapy functions fiber,
The Multifunctional yarn fabric of Modal fibre and cotton fiber.
Background technique
Chinese medicine think when human body apoplex involving the channels and collaterals it is unsmooth, on channels and collaterals acupuncture point break down when, will yin and yang imbalance, perverse trend rise,
Thus generate disease.To certain diseases, acupuncture, massage, the corresponding meridian point of magnetic stimulation make acupuncture point rejuvenate, can swash
It sends out QI of channels and collaterals, dredging the channel, adjust weighing apparatus yin-yang, eliminating pathogen to support vital qi, to achieve the purpose that treat disease.The magnetic force energy of magnet makes hair
Blood magnetization in thin blood vessel increases free radical, promotes blood circulation, have the health cares such as reducing blood lipid, blood pressure lowering, relieving mental strain and helping sleep and
Assist in the treatment of the effect of certain diseases.People are in routine work and life, it is sometimes desirable to the biggish place of the temperature difference is frequently entered and left,
And when this difference variation is larger, people such as are easy to catch a cold the diseases, influence human health.
Magnetic therapy (property) fiber refers to, and fibrous inside is added when preparing fiber by permanent magnetism micropowder material, and organically combines
Together.By magnetic therapy pure fibers spin or with other fiber blends, the yarn with magnetic-therapy healthcare function can be obtained.This yarn is prepared into
After fabric, there is the magnetic fields with the pole N, S for fabric surface.Phase-changing and temperature-regulating fiber refer to will be surrounded by the microcapsules of phase-change material with
The viscose rayon of temperature-adjustable prepared by rayon spinning liquid co-blended spinning.Phase-change material (Phase Change Material
Abbreviation PCM) refer to and varies with temperature and change form and the substance of latent heat can be provided.Temperature controllable fiber energy containing phase-change material
It is enough undergone phase transition according to the variation of ambient temperature, and absorbs from the external world or discharge heat, formed around textile warm
Substantially invariable micro climate is spent, to realize temp regulating function.By phase-changing and temperature-regulating pure fibers spin or with other fiber blends, i.e.,
It can obtain the yarn with temp regulating function.Modal fibre is a kind of New Regenerated Cellulosic Fibers, it is in trees
Cellulose is completed under physical action by using organic solvent (NMMO) spinning technique, and entire manufacturing process is nontoxic, without dirt
Dye.Modal fibre product has that soft pendency, sense of touch uniqueness, air-moisture-permeable, elegant innervation, gloss is plain, noble quality is generous etc.
Feature, cotton fiber is soft, and product has good hygroscopicity and gas permeability, and product is comfortable and easy to wear, anti-fluffing and anti-pilling.But
It is that existing temperature adjustment magnetic therapy health yarn fabric does not have good Magnetotherapeutic health and temperature adjustment function and air-moisture-permeable, gloss element
Refined, soft pendency, comfort are poor.
Summary of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of temperature adjustment magnetic therapy health yarn faces
Material.
To achieve the above object, the technical solution adopted by the present invention is that: a kind of temperature adjustment magnetic therapy health yarn fabric, innovation
Point is: it is woven into woven fabric according to specific rule by the warp thread of two kinds of different function and the weft yarn of two kinds of different function,
The warp thread includes the mixed yarn that the first is magnetic therapy fiber and Modal fibre and second of warp thread is that temperature-regulating fiber and cotton are fine
The mixed yarn of dimension, the warp thread of two kinds of different function alternates arrangement in fabric；The weft yarn includes that the first is also magnetic therapy fibre
Dimension is also the mixed yarn of temperature-regulating fiber and cotton fiber with the mixed yarn of Modal fibre and second, in fabric two kinds of weft yarns according to
Specific rule is alternately arranged；The warp and weft Yarn spinning method is all using match network compact spinning；The fabric tissue uses two
On once twill-weave or plain weave is interleaved one on the other；The fabric through to density be 380~520/
10cm, latitudinal density are 360~480/10cm.
Further, the yarn count of the mixed yarn of the magnetic therapy fiber and Modal fibre is 32s~50s, in the mixed yarn
Magnetic therapy fiber content is 40%~70%, and Modal fibre content is 30%~60%；The temperature-regulating fiber and cotton fiber are blended
The yarn count of yarn is 32s~50s, temperature-regulating fiber content is 50%~70% in the mixed yarn, cotton fiber content is 30%~
50%；
Further, the yarn count of the mixed yarn of the magnetic therapy fiber and Modal fibre is 40s~50s, in the mixed yarn
Magnetic therapy fiber content is 60%~70%, and Modal fibre content is 30%~40%.
Further, the yarn count of the temperature-regulating fiber and cotton fiber mixed yarn is 40s~50s, temperature adjustment is fine in the mixed yarn
Dimension hplc is 60%~70%, and cotton fiber content is 30%~40%；
Further, the fabric through to density be 480/10cm, latitudinal density be 480/10cm.
Further, the fabric through to density be 460/10cm, latitudinal density be 460/10cm.
The invention has the following beneficial effects:
The present invention is using magnetic therapy fiber and modal fiber blended yarn and temperature-regulating fiber and cotton fiber mixed yarn as fabric
Warp thread and weft yarn, two kinds of warp thread and two kinds of weft yarns are alternately arranged according to certain rules respectively, are then interleaved, are obtained temperature adjustment magnetic therapy
The multifunctional blended yarn fabric of health, since the fabric count yarn count of use is identical, identical through latitudinal density, what fabric was formed
Magnetic field is relatively uniform, is conducive to Magnetotherapeutic health.Many N, S magnetic loops that countless magnetic particles generate in magnetic therapy fiber in the fabric
And the magnetic line of force launched, it is woven into one layer of invisible three-dimensional magnetic line of force net.This magnetic force gauze can to close to skin
Carry out comprehensive three-dimensional stimulation and massage.Skin surface is set to be in micromotion state, active cell metabolic capability promotes body
Microcirculation.The magnetic line of force of those magnetic particles being close to skin acupuncture point, sending can penetrate these acupuncture points, play such as Chinese medicine acupuncture
Same effect, therefore physical therapy can be carried out anywhere or anytime to wearer, play good magnetic therapeutic health function；The face simultaneously
Material can also be undergone phase transition according to the variation of ambient temperature, and absorbed from the external world or outwardly discharged heat, weaved
The substantially invariable micro climate of formation temperature around product, to realize temp regulating function.In addition, the fabric also has Modal fine
Dimension and cotton fiber product it is soft, drapability is good, and gloss is strong, noble generous, air-moisture-permeable, characteristic comfortable and easy to wear.
Detailed description of the invention
Fig. 1 and Fig. 2 is Multifunctional yarn fabric structure schematic diagram of the present invention；
Once twill-weave on Fig. 1: two, 1 warp thread (1), 2 warp thread (2), 3 weft yarns (1), 4 weft yarns (2).
Fig. 2: plain weave one on the other, 1 warp thread (1), 2 warp thread (2), 3 weft yarns (1), 4 weft yarns (2).
Specific embodiment
The present invention will be further described below with reference to the drawings.
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with attached drawing and specific implementation
Mode, the present invention will be described in further detail.It should be appreciated that the specific embodiments described herein are only to explain this
Invention, is not intended to limit the present invention.
Embodiment 1
A kind of Multifunctional yarn fabric containing magnetic therapy fiber, temperature-regulating fiber, Modal fibre and cotton fiber.
Warp and weft Yarn spinning method is all made of match network compact spinning.
Warp and weft fineness is 40s。
Warp thread 1 and warp thread 2 and weft yarn 1 and weft yarn 2 are woven into woven fabric, and fabric tissue is using once twill-weave on two
It is interleaved, as shown in Figure 1,
Warp thread 1 is magnetic therapy fiber and modal fiber blended yarn in Fig. 1；Magnetic therapy fiber content is 60% in yarn, Modal
Fiber content is 40%, and warp thread 2 is temperature-regulating fiber and cotton fiber mixed yarn, and temperature-regulating fiber content is 70% in yarn, and cotton fiber contains
Amount is 30%,
Weft yarn 1 is magnetic therapy fiber and modal fiber blended yarn in Fig. 1；Magnetic therapy fiber content is 60% in yarn, Modal
Fiber content is 40%, and weft yarn 2 is temperature-regulating fiber and cotton fiber mixed yarn, and temperature-regulating fiber content is 70% in yarn, and cotton fiber contains
Amount is 30%.
For fabric through being 480/10cm to density, latitudinal density is 480/10cm.
Warp thread 1 and warp thread 2 through inspection → winder → warping → sizing → wear button → with weft yarns (weaving) → fabric；
Weft yarn 1 and weft yarn 2 through inspection → winder → interweave (weaving) → fabric with warp thread.
In the present embodiment, using magnetic therapy fiber and modal fiber blended yarn as the warp thread 1 of fabric, by temperature-regulating fiber and cotton
Warp thread 2 of the fiber blend yarn as fabric, warp thread 1 and warp thread 2 are alternately arranged according to certain rules；Magnetic therapy fiber and Modal is fine
Mixed yarn and temperature-regulating fiber and weft yarn 1 and weft yarn 2 of the cotton fiber mixed yarn as fabric are tieed up, two kinds of weft yarns are handed over according to certain rules
For arrangement；The fabric of warp thread 1 and warp thread 2 and weft yarn 1 and weft yarn 2 after interweaving have Magnetotherapeutic health, temperature adjustment, moisture absorption it is ventilative,
Comfort is good etc. multi-functional.In addition, since the fabric count yarn count of use is identical, identical through latitudinal density, what fabric was formed
Magnetic field is relatively uniform, is conducive to Magnetotherapeutic health.
Embodiment 2
Warp and weft Yarn spinning method is all made of match network compact spinning.
Warp and weft fineness is 50s。
Warp thread 1 and warp thread 2 and weft yarn 1 and weft yarn 2 are woven into woven fabric, and fabric tissue is using plain weave one on the other
It is interleaved, as shown in Fig. 2,
Warp thread 1 is magnetic therapy fiber and modal fiber blended yarn in Fig. 2；Magnetic therapy fiber content is 70% in yarn, Modal
Fiber content is 30%, and warp thread 2 is temperature-regulating fiber and cotton fiber mixed yarn, and temperature-regulating fiber content is 60% in yarn, and cotton fiber contains
Amount is 40%,
Weft yarn 1 is magnetic therapy fiber and modal fiber blended yarn in Fig. 2；Magnetic therapy fiber content is 70% in yarn, Modal
Fiber content is 30%, and weft yarn 2 is temperature-regulating fiber and cotton fiber mixed yarn, and temperature-regulating fiber content is 60% in yarn, and cotton fiber contains
Amount is 40%.
For fabric through being 460/10cm to density, latitudinal density is 460/10cm.
Warp thread 1 and warp thread 2 through inspection → winder → warping → sizing → wear button → with weft yarns (weaving) → fabric；
Weft yarn 1 and weft yarn 2 through inspection → winder → interweave (weaving) → fabric with warp thread.
The present invention is using magnetic therapy fiber and modal fiber blended yarn as the warp thread 1 of fabric, by temperature-regulating fiber and cotton fiber
Warp thread 2 of the mixed yarn as fabric, warp thread 1 and warp thread 2 are alternately arranged according to certain rules；Magnetic therapy fiber is mixed with Modal fibre
Spinning and temperature-regulating fiber and weft yarn 1 and weft yarn 2 of the cotton fiber mixed yarn as fabric, two kinds of weft yarns are alternately arranged according to certain rules
Column；The fabric of warp thread 1 and warp thread 2 and weft yarn 1 and weft yarn 2 after interweaving has Magnetotherapeutic health, temperature adjustment, moisture absorption ventilative, comfortable
Property it is good etc. multi-functional.In addition, since the fabric count yarn count of use is identical, identical through latitudinal density, the magnetic field of fabric formation
It is relatively uniform, be conducive to Magnetotherapeutic health.
The above is only used to illustrate the technical scheme of the present invention and not to limit it, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (6)
1. a kind of temperature adjustment magnetic therapy health yarn fabric, it is characterised in that: by the warp thread and two kinds of different function of two kinds of different function
Weft yarn be woven into woven fabric according to specific rule, the warp thread includes the first for magnetic therapy fiber and Modal fibre
Mixed yarn and second of warp thread are the mixed yarn of temperature-regulating fiber and cotton fiber, and the warp thread of two kinds of different function alternates in fabric
Arrangement；The weft yarn include the first be also magnetic therapy fiber and Modal fibre mixed yarn and second be also temperature-regulating fiber with
The mixed yarn of cotton fiber, two kinds of weft yarns are alternately arranged according to specific rule in fabric；The warp and weft Yarn spinning method all uses
Match network compact spinning；The fabric tissue is using once twill-weave or plain weave is interleaved one on the other on two；Institute
Fabric is stated through being 380~520/10cm to density, latitudinal density is 360~480/10cm.
2. a kind of temperature adjustment magnetic therapy health yarn fabric according to claim 1, it is characterised in that: the magnetic therapy fiber with not
The yarn count of the mixed yarn of Dai Er fiber is 32s~50s, magnetic therapy fiber content is 40%~70% in the mixed yarn, and Modal is fine
Dimension hplc is 30%~60%；The yarn count of the temperature-regulating fiber and cotton fiber mixed yarn is 32s~50s, temperature adjustment in the mixed yarn
Fiber content is 50%~70%, and cotton fiber content is 30%~50%.
3. a kind of temperature adjustment magnetic therapy health yarn fabric according to claim 2, it is characterised in that: the magnetic therapy fiber with not
The yarn count of the mixed yarn of Dai Er fiber is 40s~50s, magnetic therapy fiber content is 60%~70% in the mixed yarn, and Modal is fine
Dimension hplc is 30%~40%.
4. a kind of temperature adjustment magnetic therapy health yarn fabric according to claim 2, it is characterised in that: the temperature-regulating fiber and cotton
The yarn count of fiber blend yarn is 40s~50s, temperature-regulating fiber content is 60%~70% in the mixed yarn, and cotton fiber content is
30%~40%..
5. a kind of temperature adjustment magnetic therapy health yarn fabric according to claim 1, it is characterised in that: the warp of the fabric
It is 480/10cm to density, latitudinal density is 480/10cm.
6. a kind of temperature adjustment magnetic therapy health yarn fabric according to claim 1, it is characterised in that: the warp of the fabric
It is 460/10cm to density, latitudinal density is 460/10cm.