CN110066537A - A kind of mould proof varnish of Solid Door - Google Patents
A kind of mould proof varnish of Solid Door Download PDFInfo
- Publication number
- CN110066537A CN110066537A CN201711006170.0A CN201711006170A CN110066537A CN 110066537 A CN110066537 A CN 110066537A CN 201711006170 A CN201711006170 A CN 201711006170A CN 110066537 A CN110066537 A CN 110066537A
- Authority
- CN
- China
- Prior art keywords
- parts
- mould proof
- solid door
- proof varnish
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of mould proof varnish of Solid Door, including solid wood baseplate, the fungus resistant coating that is coated on the wax layer on the solid wood baseplate surface and is coated on the outside of said wax layer.The component of the fungus resistant coating is as follows according to parts by weight: without 30-40 parts of benzene low viscosity short oil-ity alcohol acid resin, 20-30 parts of hydroxyl polyurethane resin, 7-10 parts of organobentonite, 10-15 parts of titanium dioxide, 10-15 parts of butyl acetate, 10-15 parts of aromatic urethane acrylate, 15-20 parts of dimethylaminoethyl acrylate, 3-6 parts of defoaming agent, 2-4 parts of dispersing agent, 35-45 parts of diluent, 0.2-0.5 parts of mould inhibitor, 0.1-0.3 parts of preservative.Floor manufacture craft provided by the invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and anti-mold effect is good, has broad application prospects.
Description
Technical field
The present invention relates to solid wood window technology field more particularly to a kind of mould proof varnish of Solid Door.
Background technique
The door core of solid wood composite door is mostly bonded with pine, China fir or import packing material etc., outer patch density board and reality
Wood skin is made after high temperature hot pressing, and with solid wood line edge sealing, Solid Door is beautiful and generous, but it is noted that indoor when maintaining
Well-ventilated, keep indoor humidity, be in timber under normal temperature, humidity, prevent timber because of humidity, excessive temperature differentials and become
Shape is cracked or even mouldy, it is therefore desirable to a kind of varnish that can be mould proof.
Summary of the invention
To solve the above problems, the present invention provides a kind of mould proof varnish of Solid Door.
Technical scheme is as follows:
A kind of mould proof varnish of Solid Door, the component of the mould proof varnish are as follows according to parts by weight: self-crosslinking aqueous tree
60-70 parts of rouge, 15-20 parts of dioctyl terephthalate, 7-10 parts of natural pearlescence, 10-15 parts of titanium dioxide, organobentonite
10-15 parts, 10-15 parts of dimethylaminoethyl acrylate, 3-6 parts of defoaming agent, 0.5-0.8 parts of curing agent, 5-10 parts of dispersing agent, prevent
Mould dose 0.2-0.5 parts.
Further, the defoaming agent is one of polyoxypropylene ethylene oxide glycerin ether, dimethyl silicone polymer.
Further, curing agent is hydrophilic aliphatic polyisocyanate.
Further, the dispersing agent is 1,6- hexylene glycol double methacrylate (HDDA), one in lauryl sodium sulfate
Kind.
Further, the mould inhibitor is 3- iodo -2-propynyl formic acid butylamine.
Further, the mould proof varnish preparation method of a kind of Solid Door, it is characterised in that:
S1: self-crosslinking aqueous resin, dioctyl terephthalate, dimethylaminoethyl acrylate are placed in reaction kettle,
It is warming up to 40-60 DEG C, stirs at low speed reaction 1h.
S2: reaction kettle is warming up to 80 DEG C, natural pearlescence, titanium dioxide, organobentonite, high-speed stirred 5min is added；
S3: being cooled to 40-60 DEG C, and defoaming agent, curing agent, dispersing agent is added, and stirs at low speed reaction 1h；
S4: in a kettle be added mould inhibitor the reaction was continued for 24 hours, water-cooled cooling to room temperature can divide tank, obtain mould proof painting
Material.
According to the above aspect of the present invention, the present invention at least has the advantages that
Floor manufacture craft provided by the invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and anti-mold effect is good, tool
Have broad application prospects.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
A kind of mould proof varnish of Solid Door, the component of the mould proof varnish are as follows according to parts by weight: self-crosslinking aqueous tree
64 parts of rouge, 16 parts of dioctyl terephthalate, 7 parts of natural pearlescence, 12 parts of titanium dioxide, 10 parts of organobentonite, acrylic acid two
11 parts of methylamino ethyl ester, 4 parts of dimethyl silicone polymer, 0.6 part of hydrophilic aliphatic polyisocyanate, 1,6- hexylene glycol double third
7 parts of olefin(e) acid ester (HDDA), 3- iodo -0.4 part of 2-propynyl formic acid butylamine.
Preparation method includes the following steps:
S1: self-crosslinking aqueous resin, dioctyl terephthalate, dimethylaminoethyl acrylate are placed in reaction kettle,
It is warming up to 40-60 DEG C, stirs at low speed reaction 1h.
S2: reaction kettle is warming up to 80 DEG C, natural pearlescence, titanium dioxide, organobentonite, high-speed stirred 5min is added；
S3: being cooled to 40-60 DEG C, and defoaming agent, curing agent, dispersing agent is added, and stirs at low speed reaction 1h；
S4: in a kettle be added mould inhibitor the reaction was continued for 24 hours, water-cooled cooling to room temperature can divide tank, obtain mould proof painting
Material.
Embodiment 2
A kind of mould proof varnish of Solid Door, the component of the mould proof varnish are as follows according to parts by weight: self-crosslinking aqueous tree
67 parts of rouge, 18 parts of dioctyl terephthalate, 9 parts of natural pearlescence, 12 parts of titanium dioxide, 11 parts of organobentonite, acrylic acid two
13 parts of methylamino ethyl ester, 5 parts of polyoxypropylene ethylene oxide glycerin ether, 0.6 part of hydrophilic aliphatic polyisocyanate, dodecyl
8 parts of sodium sulphate, 3- iodo -0.4 part of 2-propynyl formic acid butylamine.
Preparation method includes the following steps:
S1: self-crosslinking aqueous resin, dioctyl terephthalate, dimethylaminoethyl acrylate are placed in reaction kettle,
It is warming up to 40-60 DEG C, stirs at low speed reaction 1h.
S2: reaction kettle is warming up to 80 DEG C, natural pearlescence, titanium dioxide, organobentonite, high-speed stirred 5min is added；
S3: being cooled to 40-60 DEG C, and defoaming agent, curing agent, dispersing agent is added, and stirs at low speed reaction 1h；
S4: in a kettle be added mould inhibitor the reaction was continued for 24 hours, water-cooled cooling to room temperature can divide tank, obtain mould proof painting
Material.
Embodiment 3
A kind of mould proof varnish of Solid Door, the component of the mould proof varnish are as follows according to parts by weight: self-crosslinking aqueous tree
67 parts of rouge, 17 parts of dioctyl terephthalate, 8 parts of natural pearlescence, 12 parts of titanium dioxide, 11 parts of organobentonite, acrylic acid two
13 parts of methylamino ethyl ester, 4 parts of dimethyl silicone polymer, 0.6 part of hydrophilic aliphatic polyisocyanate, 1,6- hexylene glycol double third
7 parts of olefin(e) acid ester (HDDA), 3- iodo -0.4 part of 2-propynyl formic acid butylamine.
Preparation method includes the following steps:
S1: self-crosslinking aqueous resin, dioctyl terephthalate, dimethylaminoethyl acrylate are placed in reaction kettle,
It is warming up to 40-60 DEG C, stirs at low speed reaction 1h.
S2: reaction kettle is warming up to 80 DEG C, natural pearlescence, titanium dioxide, organobentonite, high-speed stirred 5min is added；
S3: being cooled to 40-60 DEG C, and defoaming agent, curing agent, dispersing agent is added, and stirs at low speed reaction 1h；
S4: in a kettle be added mould inhibitor the reaction was continued for 24 hours, water-cooled cooling to room temperature can divide tank, obtain mould proof painting
Material.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of mould proof varnish of Solid Door, it is characterised in that: the component of the mould proof varnish is as follows according to parts by weight: selfing
Water-base resin 60-70 parts of connection, it is 15-20 parts of dioctyl terephthalate, 7-10 parts of natural pearlescence, 10-15 parts of titanium dioxide, organic
10-15 parts of bentonite, 10-15 parts of dimethylaminoethyl acrylate, 3-6 parts of defoaming agent, 0.5-0.8 parts of curing agent, dispersing agent 5-
10 parts, 0.2-0.5 parts of mould inhibitor.
2. the mould proof varnish of a kind of Solid Door according to claim 1, it is characterised in that: the defoaming agent is polyoxypropylene oxygen
Change one of Ethylene Glycol ether, dimethyl silicone polymer.
3. the mould proof varnish of a kind of Solid Door according to claim 1, it is characterised in that: curing agent is poly- for hydrophilic aliphatic
Isocyanates.
4. the mould proof varnish of a kind of Solid Door according to claim 1, it is characterised in that: the dispersing agent be 1,6- oneself two
One of alcohol double methacrylate (HDDA), lauryl sodium sulfate.
5. the mould proof varnish of a kind of Solid Door according to claim 1, it is characterised in that: the mould inhibitor is 3- iodo -2-
Propinyl formic acid butylamine.
6. the mould proof varnish preparation method of a kind of Solid Door according to claim 1, it is characterised in that:
S1: self-crosslinking aqueous resin, dioctyl terephthalate, dimethylaminoethyl acrylate are placed in reaction kettle, heating
To 40-60 DEG C, reaction 1h is stirred at low speed.
S2: reaction kettle is warming up to 80 DEG C, natural pearlescence, titanium dioxide, organobentonite, high-speed stirred 5min is added；
S3: being cooled to 40-60 DEG C, and defoaming agent, curing agent, dispersing agent is added, and stirs at low speed reaction 1h；
S4: in a kettle be added mould inhibitor the reaction was continued for 24 hours, water-cooled cooling to room temperature can divide tank, obtain mildew resistant paint.